CN110317044A - A kind of ecological garden environmental protection brick and preparation method thereof using the preparation of full waste material - Google Patents
A kind of ecological garden environmental protection brick and preparation method thereof using the preparation of full waste material Download PDFInfo
- Publication number
- CN110317044A CN110317044A CN201910556483.6A CN201910556483A CN110317044A CN 110317044 A CN110317044 A CN 110317044A CN 201910556483 A CN201910556483 A CN 201910556483A CN 110317044 A CN110317044 A CN 110317044A
- Authority
- CN
- China
- Prior art keywords
- parts
- waste
- environmental protection
- protection brick
- useless
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of ecological garden environmental protection bricks and preparation method thereof using the preparation of full waste material, the ecological garden environmental protection brick contains following constituent: 60-80 parts of building waste residue sand, useless 10-25 parts of porcelain grain, 5-15 parts of waste glass powder, 5-10 parts of coal ash powder, 3-8 parts of cement dust, 2-5 parts of waste glass fibre, slag 2-4 parts, 5-19 parts of sludge of paint.The present invention makes environmental protection brick using building waste residue sand, useless porcelain grain, waste glass powder, coal ash powder as primary raw material, the discharge amount that building, porcelain production, glass production and industrialness coal waste material can be reduced turns waste into wealth, solve the problems, such as environmental pollution, the production cost of environmental protection brick can also be reduced, large-scale production is suitble to；Material is pressed using brick machine, can be improved the intensity and density of full waste material brick, reduces the through-hole inside environmental protection brick, improves the waterproof performance of environmentally friendly brick.
Description
Technical field
The present invention relates to environmental protection brick production field, it is specially a kind of using full waste material preparation ecological garden environmental protection brick and its
Preparation method.
Background technique
Building waste residue be city generated during construction discarded concrete waste material, generate during fitting-up
Cullet, useless tile, waste marble granite fragment, the useless brick and tile generated in reconstruction of the old city town removal work progress and old wall it is useless
The solid waste of slag mixing.With China's rapid development of economy, the whole nation is every year because removing solid caused by old building
Waste reaches 200,000,000 tons or more, generate about 100,000,000 tons of solid waste, 40,000,000,000 m2 of China's existing building of new building, according to
It calculates within building service life 100 years, average annual old building of removing is in 400,000,000 m2, average annual generation Old building solid waste about 500,000,000
Ton, in addition newly-built construction, decorations etc., China will generate building solid castoff at 600,000,000 tons or more every year.
Currently, prepared by the way of vitrified bond when most of brickmaking, but with the increase of clay yield, clay
Resource is increasingly deficient, not only increases cost of winning, while also causing to seriously affect to ecological environment, therefore need to optimize and change
Into existing brick-making method to change the status quo.Nowadays there is the brick-making method using riverway sludge as primary raw material, not only
It solves and administers the mud placement issue that river channel sedimentation generates, also substitute traditional brick-making raw material, reduce the destruction to environment.So
And such as ceramics, cement, coal mine industry also produce many solid wastes, occupying a large amount of soils fixed point stacks, as can rationally benefit
With to brickmaking field, the destruction caused by environment of above-mentioned industry can be slowed down very well, it is therefore desirable to which improving existing brick-making method can
The brick for meeting production standard is prepared using Various Wastes.
Summary of the invention
The ecological garden environmental protection brick and preparation method thereof that the purpose of the present invention is to provide a kind of to be prepared using full waste material, with
Solve the problems mentioned above in the background art.
To achieve the above object, the invention provides the following technical scheme: a kind of ecological garden ring prepared using full waste material
Brick is protected, the ecological garden environmental protection brick contains following constituent: 60-80 parts of building waste residue sand, give up 10-25 parts of porcelain grain, gives up
5-15 parts of glass powder, 5-10 parts of coal ash powder, 3-8 parts of cement dust, 2-5 parts of waste glass fibre, paint slag 2-4 parts, 5-19 parts of sludge.
Preferably, ecological garden environmental protection brick contains following constituent: 60 parts of building waste residue sand, give up 15 parts of porcelain grain, gives up
5 parts of glass powder, 10 parts of coal ash powder, 5 parts of cement dust, 2 parts of waste glass fibre, paint 2 parts of slag, 10 parts of sludge.
Preferably, coal ash powder is the waste residue being discharged after coal power generation by waste combustion, removes old metal by sorting, crushing, magnetic separation
It is the powder less than 3mm that partial size is made afterwards.
Preferably, the porcelain grain that gives up is to be crushed useless ceramic tile, ball milling, the granular substance obtained after sieving；The useless glass
Glass powder is to be crushed waste broken glass bits, and grinding, sieving obtains.
Preferably, waste glass fibre is no alkali fiber, middle alkali fiber, high alkali fiber, chemically-resistant fiber, special glass fibre
Dimension, glass fiber powder, levigate fiber, high-strength glass fibre, any one or more mixtures in simple glass fiber.
Preferably, the preparation of building waste residue sand includes the following steps: a: construction waste is collected to and is carried out artificial separation, it will
House refuse and industrial refuse are chosen, and construction waste is left；B: the construction waste after sorting is put into crusher be crushed,
Discarded building materials of the diameter less than 10 millimeters are obtained after magnetic separation, filtering；C: discarded building materials being put into grinder and are ground, and will grinding
Discarded building materials afterwards cross 20-50 mesh, obtain granular substance；D: the granular substance in step c is sent into sand making machine, manufactured sand
Grain obtains the building waste residue sand by vibrating screen.
The present invention also provides above-mentioned ecological garden environmental protection brick and preparation method thereof, including the following steps:
S1: weigh following each components respectively by following mass percent: 60 parts of building waste residue sand, give up 15 parts of porcelain grain, gives up
5 parts of glass powder, 10 parts of coal ash powder, 5 parts of cement dust, 2 parts of waste glass fibre, paint 2 parts of slag, 10 parts of sludge；
S2: taking coal ash powder in S1, sludge, paint slag levigate rear respectively and be delivered to proportioning machine, mixed through charging mixer ingredient
Close to obtain useless mixing one；
S3: building waste residue sand, useless porcelain grain, waste glass powder, cement dust are added into useless mixing one and is mixed through ingredient
Machine ingredient mixes to obtain useless mixing two, and useless mixing two is delivered to blender by conveyer and carries out secondary agitation mixing；
S4: the useless mixing two mixed in S3 through secondary agitation is delivered to edge runner and is rolled and is carried out after rolling ripe
Change；
S5: being delivered to brick machine for the material cured in S4 and carry out being squeezed into base, after brick is at base at normal temperatures and pressures into
Row drying；
S6: the adobe after will be dry in S5 is piled up to be sintered in kiln, and is sent to after sintering naturally cold on spreading for cooling platform
But to the ecological garden environmental protection brick is made after room temperature.
Compared with prior art, the beneficial effects of the present invention are:
The present invention makes environmental protection brick using building waste residue sand, useless porcelain grain, waste glass powder, coal ash powder as primary raw material, can
Turned waste into wealth with reducing the discharge amount of building, porcelain production, glass production and industrialness coal waste material, solves environmental pollution
Problem can also reduce the production cost of environmental protection brick, be suitble to large-scale production；Material is pressed using brick machine, energy
The intensity and density of full waste material brick are enough improved, the through-hole inside environmental protection brick is reduced, improves the waterproof performance of environmentally friendly brick；Simultaneously
Compared to Cement Environment Protection brick it is with short production cycle, do not needed prolonged curing period, and be sintered the intensity of the environmental protection brick come out
It is bigger than the intensity of Cement Environment Protection brick, have the advantages that good water permeability, intensity are high, light-weight, environmentally friendly, ageing-resistant.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment 1: the present invention provides a kind of technical solution: a kind of ecological garden environmental protection brick prepared using full waste material, institute
State ecological garden environmental protection brick and contain following constituent: 60-80 parts of building waste residue sand, give up 10-25 parts of porcelain grain, waste glass powder 5-
15 parts, 5-10 parts of coal ash powder, 3-8 parts of cement dust, 2-5 parts of waste glass fibre, paint slag 2-4 parts, 5-19 parts of sludge.
Above-mentioned ecological garden environmental protection brick and preparation method thereof, including the following steps:
S1: weigh following each components respectively by following mass percent: 60 parts of building waste residue sand, give up 15 parts of porcelain grain, gives up
5 parts of glass powder, 10 parts of coal ash powder, 5 parts of cement dust, 2 parts of waste glass fibre, paint 2 parts of slag, 10 parts of sludge；
S2: taking coal ash powder in S1, sludge, paint slag levigate rear respectively and be delivered to proportioning machine, mixed through charging mixer ingredient
Close to obtain useless mixing one；
S3: building waste residue sand, useless porcelain grain, waste glass powder, cement dust are added into useless mixing one and is mixed through ingredient
Machine ingredient mixes to obtain useless mixing two, and useless mixing two is delivered to blender by conveyer and carries out secondary agitation mixing；
S4: the useless mixing two mixed in S3 through secondary agitation is delivered to edge runner and is rolled and is carried out after rolling ripe
Change；
S5: being delivered to brick machine for the material cured in S4 and carry out being squeezed into base, after brick is at base at normal temperatures and pressures into
Row drying；
S6: the adobe after will be dry in S5 is piled up to be sintered in kiln, and is sent to after sintering naturally cold on spreading for cooling platform
But to the ecological garden environmental protection brick is made after room temperature.
Coal ash powder is the waste residue being discharged after coal power generation by waste combustion, and grain is made after sorting, crushing, magnetic separation removal old metal
Diameter is the powder less than 3mm.
Useless porcelain grain is to be crushed useless ceramic tile, ball milling, the granular substance obtained after sieving；The waste glass powder be by
Waste broken glass bits are crushed, and grinding, sieving obtains.
Waste glass fibre is no alkali fiber, middle alkali fiber, high alkali fiber, chemically-resistant fiber, special glass fibre, glass fibers
Tie up powder, levigate fiber, high-strength glass fibre, any one or more mixtures in simple glass fiber.
The preparation of building waste residue sand includes the following steps: a: construction waste being collected to and carried out artificial separation, by life rubbish
Rubbish and industrial refuse are chosen, and construction waste is left；B: the construction waste after sorting is put into crusher be crushed, magnetic separation,
Discarded building materials of the diameter less than 10 millimeters are obtained after filtering；C: discarded building materials being put into grinder and are ground, and will be after grinding
Discarded building materials cross 20-50 mesh, obtain granular substance；D: the granular substance in step c is sent into sand making machine, manufactured sand grains warp
It crosses vibrating screen and obtains the building waste residue sand.
Embodiment 2:
S1: weigh following each components respectively by following mass percent: 60 parts of building waste residue sand, give up 25 parts of porcelain grain, gives up
15 parts of glass powder, 5 parts of coal ash powder, 5 parts of cement dust, 5 parts of waste glass fibre, paint 4 parts of slag, 10 parts of sludge；
S2: taking coal ash powder in S1, sludge, paint slag levigate rear respectively and be delivered to proportioning machine, mixed through charging mixer ingredient
Close to obtain useless mixing one；
S3: building waste residue sand, useless porcelain grain, waste glass powder, cement dust are added into useless mixing one and is mixed through ingredient
Machine ingredient mixes to obtain useless mixing two, and useless mixing two is delivered to blender by conveyer and carries out secondary agitation mixing；
S4: the useless mixing two mixed in S3 through secondary agitation is delivered to edge runner and is rolled and is carried out after rolling ripe
Change；
S5: being delivered to brick machine for the material cured in S4 and carry out being squeezed into base, after brick is at base at normal temperatures and pressures into
Row drying；
S6: the adobe after will be dry in S5 is piled up to be sintered in kiln, and is sent to after sintering naturally cold on spreading for cooling platform
But to the ecological garden environmental protection brick is made after room temperature.
Embodiment 2 is identical as above-described embodiment material, procedure of processing, the difference is that the proportion of the two is different.
Embodiment 3:
S1: weigh following each components respectively by following mass percent: 80 parts of building waste residue sand, give up 25 parts of porcelain grain, gives up
5 parts of glass powder, 10 parts of coal ash powder, 8 parts of cement dust, 2 parts of waste glass fibre, paint 4 parts of slag, 5 parts of sludge；
S2: taking coal ash powder in S1, sludge, paint slag levigate rear respectively and be delivered to proportioning machine, mixed through charging mixer ingredient
Close to obtain useless mixing one；
S3: building waste residue sand, useless porcelain grain, waste glass powder, cement dust are added into useless mixing one and is mixed through ingredient
Machine ingredient mixes to obtain useless mixing two, and useless mixing two is delivered to blender by conveyer and carries out secondary agitation mixing；
S4: the useless mixing two mixed in S3 through secondary agitation is delivered to edge runner and is rolled and is carried out after rolling ripe
Change；
S5: being delivered to brick machine for the material cured in S4 and carry out being squeezed into base, after brick is at base at normal temperatures and pressures into
Row drying；
S6: the adobe after will be dry in S5 is piled up to be sintered in kiln, and is sent to after sintering naturally cold on spreading for cooling platform
But to the ecological garden environmental protection brick is made after room temperature.
Embodiment 3 is identical as above-described embodiment material, procedure of processing, the difference is that the proportion of the two is different.
By proportion described in embodiment 1-3 and ecological garden environmental protection brick obtained by preparation method, to its intensity and acidproof
Alkalinity etc. is tested, and is as a result evaluated by A, B, C, D, as shown in the table:
| Sample | Intensity | Resistance to acid and alkali |
| Embodiment 1 | A | A |
| Embodiment 2 | B | A |
| Embodiment 3 | A | C |
It can be seen from table according to described in embodiment 1 proportion with preparation method obtained by ecological garden environmental protection brick,
Effect is preferable in terms of intensity and resistance to acid and alkali.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (7)
1. it is a kind of using full waste material prepare ecological garden environmental protection brick, which is characterized in that the ecological garden environmental protection brick contain as
Lower constituent: 60-80 parts of building waste residue sand, give up 10-25 parts of porcelain grain, and 5-15 parts of waste glass powder, 5-10 parts of coal ash powder, cement
3-8 parts of dust, 2-5 parts of waste glass fibre, paint slag 2-4 parts, 5-19 parts of sludge.
2. a kind of ecological garden environmental protection brick prepared using full waste material according to claim 1, which is characterized in that the life
State gardens environmental protection brick contains following constituent: 60 parts of building waste residue sand, give up 15 parts of porcelain grain, and 5 parts of waste glass powder, coal ash powder 10
Part, 5 parts of cement dust, 2 parts of waste glass fibre, paint 2 parts of slag, 10 parts of sludge.
3. a kind of ecological garden environmental protection brick prepared using full waste material according to claim 1, which is characterized in that the coal
Ashes is the waste residue being discharged after coal power generation by waste combustion, be made after sorting, crushing, magnetic separation removal old metal partial size be less than
The powder of 3mm.
4. a kind of ecological garden environmental protection brick prepared using full waste material according to claim 1, which is characterized in that described useless
Porcelain grain is to be crushed useless ceramic tile, ball milling, the granular substance obtained after sieving；The waste glass powder be by waste broken glass bits into
Row is broken, and grinding, sieving obtains.
5. a kind of ecological garden environmental protection brick prepared using full waste material according to claim 1, which is characterized in that described useless
Glass fibre is no alkali fiber, middle alkali fiber, high alkali fiber, chemically-resistant fiber, special glass fibre, glass fiber powder, levigate
Fiber, high-strength glass fibre, any one or more mixtures in simple glass fiber.
6. a kind of ecological garden environmental protection brick prepared using full waste material according to claim 1, which is characterized in that described to build
The preparation for building waste residue sand includes the following steps: a: construction waste being collected to and carried out artificial separation, by house refuse and industrial rubbish
Rubbish is chosen, and construction waste is left；B: the construction waste after sorting is put into crusher and is crushed, magnetic separation, obtained after filtering
Discarded building materials of the diameter less than 10 millimeters；C: discarded building materials being put into grinder and are ground, and by the discarded building materials mistake after grinding
20-50 mesh, obtains granular substance；D: the granular substance in step c is sent into sand making machine, manufactured sand grains is obtained by vibrating screen
The building waste residue sand.
7. a kind of preparation method of ecological garden environmental protection brick using the preparation of full waste material according to claim 1, feature
It is, including the following steps:
S1: weigh following each components respectively by following mass percent: 60 parts of building waste residue sand, give up 15 parts of porcelain grain, cullet
5 parts of powder, 10 parts of coal ash powder, 5 parts of cement dust, 2 parts of waste glass fibre, paint 2 parts of slag, 10 parts of sludge；
S2: it takes coal ash powder in S1, sludge, paint slag levigate rear respectively and is delivered to proportioning machine, mixed through charging mixer ingredient
Useless mixing one；
S3: building waste residue sand, useless porcelain grain, waste glass powder, cement dust are added into useless mixing one and matches through charging mixer
Material mixes to obtain useless mixing two, and useless mixing two is delivered to blender by conveyer and carries out secondary agitation mixing；
S4: the useless mixing two mixed in S3 through secondary agitation is delivered to edge runner and is rolled and is cured after rolling；
S5: the material cured in S4 is delivered to brick machine and carries out being squeezed into base, is done at normal temperatures and pressures after brick is at base
It is dry；
S6: the adobe after will be dry in S5 is piled up to be sintered in kiln, and is sent on spreading for cooling platform and is naturally cooled to after sintering
The ecological garden environmental protection brick is made after room temperature.