CN101089102A - Green paint preparing process - Google Patents
Green paint preparing process Download PDFInfo
- Publication number
- CN101089102A CN101089102A CN 200610044827 CN200610044827A CN101089102A CN 101089102 A CN101089102 A CN 101089102A CN 200610044827 CN200610044827 CN 200610044827 CN 200610044827 A CN200610044827 A CN 200610044827A CN 101089102 A CN101089102 A CN 101089102A
- Authority
- CN
- China
- Prior art keywords
- green paint
- making method
- charcoal
- minutes
- scratched
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is scratched green paint producing process, and features that the scratched green paint consists of silica sol 4-7 wt%, modified acrylic acid 10-16 wt%, calcium carbonate powder 30-38 wt%, charcoal powder 8-10 wt%, regulator D 5-6 wt%, phenolic resin glue 7-11 wt%, and talcum powder 20-26 wt%. The scratched green paint has high water tolerance, and can regulate humidity well through absorbing moisture under high humidity and releasing moisture in low humidity. In addition, the scratched green paint can eliminate smell and harmful matter in room and has excellent heat insulating and energy saving characteristic.
Description
Technical field
The invention belongs to building coating.
Technical background
Charcoal be timber or wood material through incomplete combustion, perhaps pyrolysis under the condition of secluding air, residual Vandyke brown or black porosu solid fuel.Be the impure decolorizing carbon that keeps residual tar in original structure of timber and the hole.Charcoal is all used in the bronze work of China's Shang dynasty and the smelting of period in Spring and Autumn and Warring States's epoch ironware, utilizes its water absorbability to observe climate change etc.Except that still doing the life fuel, also be used as the fuel of Metal smelting, food and light industry now, the reductive agent of electrosmelting, not oxidized when metal is refining as insulating covering agent protection metal.On chemical industry, often make the raw material of dithiocarbonic anhydride and gac etc.In addition in application of aspects such as grinding, drawing, cosmetic, medicine, gunpowder, carburizing, powder metallurgies.Raw material by the usefulness of making charcoal can be divided into: 1. hard wealthy charcoal.By hard pourous wood such as Fagaceae Quercus acutissima belong to, the Castanopsis trees are main, accessory also have Betula etc.2. broad-leaved charcoal.Charcoal by hard, soft pourous wood mixed sintering.3. pine charcoal.The charcoal of firing by pine or other softwoods.Bamboo charcoal that useful in addition bamboo class is fired and the fruit stone charcoal of firing with shell, fruit stone wood materials such as (Exocarpium cocois (Cocos nucifera L), peach-pits).The faggot and charcoal of collecting from home furnace then is commonly called as the small wooden raft charcoal.After charcoal is pulverized, mix, carry out hematocrit moulding and roasting again and then make the hematocrit charcoal with suitable adhesive.Divide hard charcoal and black wood charcoal by the technology of making charcoal.The charcoal main component is a carbon, also has hydrogen, oxygen, nitrogen and a spot of other elements in addition, and the relation of its content and seeds is little, depends primarily on the outlet temperature of charing.Charcoal belongs to the hydrophobic nature material, ash oontent is in 6%, hole accounts for the charcoal volume more than 7%, proportion is generally 1.3~1.4, thermal value depends on carbonization condition, generally about 8000 kcal/kg, the reducing power of charcoal is greater than coke, thereby as the reductive agent and the insulating covering agent of Metal smelting.Charcoal has a large amount of micropores and transitional pore, makes it that higher specific surface area not only be arranged, and after tar material is excluded in the hole good attraction performance will be arranged, so be the important source material of preparation gac.People's charcoal heating commonly used, fuel, particularly machine-made charcoal that barbecue, chafing dish are used, because its no smoke, thermal value is big, combustion time is long, so more and more be subjected to people's favor.Countless in length and breadth holes is arranged on the charcoal, and the function that these holes have the various materials of absorption and put out the material that is adsorbing is so people make dehumidizier with it.When humidity, charcoal can absorb moisture, and in the time of exsiccant, its can provide the humidity that has absorbed out, thereby the effect of humidity is regulated in performance with flying colors.In addition, charcoal can also be eliminated smell in the room and objectionable impurities etc.Present spread coated paint for building (having another name called putty) comprises interior wall and exterior coating, usually uses after the putty levelling material as the look face.Putty polyvinyl alcohol glue commonly used and filler are made.Finishing in first procedure putty construction remakes coating application (two procedures), because material, foaming, delamination, not water-fast Xian, not durable etc. has been the knotty problem on the engineering.The invention provides a kind of green paint, this coating can overcome the deficiency of existing coating and putty function, but double as coating and putty use, can contemporaryly use again for coating and putty, it can change an operation into by former two operations and finish (having reduced by an operation), and its surface has weather resistance, water tolerance and the good effect of heat insulation that can not replace beautiful sense organ and material.When humidity, can absorb moisture, the exsiccant time, its can provide the humidity that has absorbed out, thus the effect of humidity is regulated in performance with flying colors.In addition, can also eliminate smell in the room and objectionable impurities etc.
Summary of the invention
Green paint of the present invention is made up of modified acroleic acid and silicon sol, and its prescription comprises: (weight) silicon sol 4-7%, modified acroleic acid 10-16%, Paris white 30-38%, wood charcoal powder 8-10%, conditioning agent fourth 5-6%, Phenol aldehyde resin 7 one 11%, talcum powder 20-26%.
The making method of green paint of the present invention:
1) earlier vinylformic acid is carried out modification, make it meet high-effective water-proof and other material mutual solubility, under normal temperature condition, carry out.
2) under high-speed condition, the raw material in the above-mentioned prescription is mixed.
3), the conditioning agent fourth can be packed respectively by single, double component requirement.
Concrete steps comprise:
In synthesis reactor, add vinylformic acid (commercially available), at room temperature, add the conditioning agent fourth, high-speed stirring 120 minutes obtains expansion and contraction and is 700% colloid film forming, add silicon sol (commercially available) then, chlorinated paraffin, high-speed stirring 30 minutes adds Phenol aldehyde resin and other additive at last, high-speed stirring 65 minutes, drawing films is product milky white, bright shape.High-speed stirring is 200 rev/mins.---300 rev/mins.
Embodiment:
In synthesis reactor, add 16 kilograms in vinylformic acid, add 28 kilograms of talcum powder at 15-35 ℃, 5 kilograms of conditioning agent fourths, stirred 120 minutes, obtaining colloid film forming expansion and contraction is 700%, (200 rev/mins one 300 rev/mins of speed) adds 6 kilograms of silicon sol under the high-speed stirring then, and chlorinated paraffin, and high-speed stirring is 30 minutes again.Add 40 kilograms of Paris whites, 10 kilograms of wood charcoal powders, 9 kilograms of Phenol aldehyde resins at last, stirred 65 minutes, drawing films is product milky white, bright shape.
Green paint provided by the present invention is compared with now general coating (putty) and is had the following advantages and effect:
1, excellent resistance to water: putty commonly used is responsive to water, under water soaking, and adhesion strength Constantly descend, this product adhesion strength during water logging can not reduce.
2, use object more extensive: product provided by the present invention, can be coated in brick, stone, asbestos shingle, The surfaces of various materials such as concrete, and effects on surface require not strict, even at the environment of humidity Lower its result of use that also do not affect. When humidity, can absorb moisture, in drying, it Can provide the humidity that has absorbed out, thereby the effect of humidity be regulated in performance with flying colors. In addition, Can also eliminate smell in the room and harmful substance etc.
3, can be used as and exempt from coating type putty and use: present putty commonly used, after wall uses, Must cover again other coating, make wall surface brighter, water-fast, and use of the present invention Product, after wall uses, because surface-brightening, water-fast, good hand touch must not exist again The surface is coated with other coating.
4, good heat-insulating and energy-saving characteristic: product of the present invention is at brick, concrete, asbestos shingle etc. Surface scumbling 1-2mm can the decrease surface temperature, during such as 63 ℃ of brick surface temperatures, Coating table temperature be 35 ℃ on average: big cooling is 27. 4 ℃. Product ratio of the present invention The like product effect of heat insulation improves about 30%.
Claims (5)
1, a kind of making method of green paint, it is characterized in that being made up of modified acroleic acid and silicon sol, the formulation weight composition comprises as follows: silicon sol 4-7%, modified acroleic acid 10-16%, Paris white 30-38%, wood charcoal powder 8-10%, conditioning agent fourth 5-6%, Phenol aldehyde resin 7-11%, talcum powder 20-26%.
2,, it is characterized in that described resol is the synthesizing alcohol type according to the making method of a kind of green paint described in the claim 1.
3, according to the making method of a kind of green paint described in the claim 1, it is acrylic acid modified to it is characterized in that this method comprises, each component is mixed, by single, double component requirement the conditioning agent fourth is packed respectively, concrete steps: in synthesis reactor, add vinylformic acid, at room temperature, add the conditioning agent fourth, stirred 120 minutes, obtain expansion and contraction and be 700% colloid film forming, add silicon sol then, chlorinated paraffin stirred 30 minutes, added Phenol aldehyde resin and other additive at last, stirred 65 minutes, drawing films is product milky white, bright shape.
4,, it is characterized in that described agitation condition is that 200-300 changes according to the making method of the green paint described in the claim 2 | divide.
5,, it is characterized in that described each component is to form to mix according to weight in the prescription described in the claim 1 to make according to the making method of the green paint described in the claim 2.