CN103910811A - 一种低电内渗琼脂糖的制备方法 - Google Patents
一种低电内渗琼脂糖的制备方法 Download PDFInfo
- Publication number
- CN103910811A CN103910811A CN201410130997.2A CN201410130997A CN103910811A CN 103910811 A CN103910811 A CN 103910811A CN 201410130997 A CN201410130997 A CN 201410130997A CN 103910811 A CN103910811 A CN 103910811A
- Authority
- CN
- China
- Prior art keywords
- agarose
- filtrate
- electroendosmosis
- preparation
- low electroendosmosis
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种低电内渗琼脂糖的制备方法,包括如下步骤:A称取琼脂粉加入pH4.4磷酸氢二钠—柠檬酸缓冲液,琼脂粉的添加量为20~100g·L-1;B搅拌;C趁热抽滤,收集滤液;D用蒸馏水反复洗涤至滤液呈中性;E烘干、粉碎得初级琼脂糖;F称取1重量份初级琼脂糖,加入150-250重量份蒸馏水,加热溶解;G加入3-7重量份经过预处理的DEAE-纤维素树脂;H趁热抽滤,留滤渣;I用85℃以上高温蒸馏水洗涤滤渣,收集滤液;J将滤液烘干,粉碎得低电内渗琼脂糖。本发明所使用的原料,制备方法都简单,获得的琼脂糖电内渗值低,可以低于0.1以下。
Description
技术领域
本发明涉及生化领域,具体涉及一种低电内渗琼脂糖的制备方法。
背景技术
电内渗是琼脂糖的重要质量标准之一,它在一定程度上反映了琼脂糖凝胶带负电荷的量。电内渗对电泳,尤其是对等电聚焦电泳的影响很大。用琼脂糖作电泳介质时,琼脂糖中含有的硫酸基、丙酮基等带负电荷的基团使琼脂糖凝胶带负电荷。电泳时,在电场力的作用下,凝胶本身虽然不向正极移动,但凝胶中的水在水合氢离子的作用下向阴极移动,样品中的中性分子随着水也向阴极移动。电内渗使电泳过程变得复杂起来,更重要的是电内渗产生静水压头,使一端电极有水渗出,另一端电极的水越来越少,破坏了凝胶结构,打破了电泳场的均一性。低电内渗琼脂糖被广泛用作各种电泳和分子筛色谱的稳定介质,其价格远高于初级琼脂糖。
电内渗是琼脂糖的重要质量标准之一,其数值越低越有利。现有技术中利用琼脂(琼胶)制备琼脂糖的方法有聚乙二醇沉淀法、DEAE-纤维素树脂法、乙酰化法等,但这些方法所制备的琼脂糖其电内渗值偏高。例如,直接采用DEAE-纤维素树脂法从江蓠琼脂中制备琼脂糖,其电内渗值都在0.2以上。另有文献报道采用DEAE-纤维素树脂法从石花菜琼脂中制备的琼脂糖其电内渗值为0.12,但此数值仍然较高;其次只用DEAE-纤维素树脂法不适用于其他红藻来源的琼脂。
发明内容
本发明的目的在于提供一种低电内渗琼脂糖的制备方法,其可从琼脂中分离制备出更低电内渗琼脂糖,从而提升琼脂的价值。
本发明提供的技术方案如下:
一种低电内渗琼脂糖的制备方法,所述低电内渗琼脂糖,其电内渗值至少低于0.1,包括如下步骤:
A称取琼脂粉加入pH4.4磷酸氢二钠—柠檬酸缓冲液,琼脂粉的添加量为20-100g·L-1;
B在40℃-80℃下,缓慢匀速搅拌6小时以上;
C趁热抽滤,收集滤液;
D用蒸馏水反复洗涤至滤液呈中性,再用超纯水洗涤1-3次;
E烘干、粉碎得初级琼脂糖;
F称取1重量份初级琼脂糖,加入150-250重量份蒸馏水,加热溶解;
G DEAE-纤维素树脂先进行如下的预处理:依次用5-15%NaCl浸泡15-25小时,5-15%HCl浸泡3-7小时,3-5%NaOH浸泡2-6小时;将3-7重量份经过预处理的DEAE-纤维素树脂加入步骤F所得溶液,在65℃-80℃下先缓慢匀速搅拌1-3.5小时,再静置10分钟-100分钟;
H趁热抽滤,留滤渣;
I用85℃以上高温蒸馏水洗涤滤渣,收集滤液;
J将滤液烘干,粉碎得低电内渗琼脂糖。
所述低电内渗琼脂糖,其电内渗值低于0.08。更好地,所述低电内渗琼脂糖,其电内渗值为0.08-0.065。
其中,步骤G中,静置时需要保温,
其中,步骤J将滤液烘干之前,滤液可以先浓缩,再烘干。
较佳地,前述低电内渗琼脂糖的制备方法包括如下步骤:
A称取琼脂粉加入pH4.4磷酸氢二钠—柠檬酸缓冲液,琼脂粉的添加量为20g·L-1;
B在70℃下,缓慢匀速搅拌12小时;
C趁热抽滤,收集滤液;
D用蒸馏水反复洗涤至滤液呈中性,再用超纯水洗涤2次;
E烘干、粉碎得初级琼脂糖;
F称取1重量份初级琼脂糖,加入200重量份蒸馏水,加热溶解;
G加入5重量份经过预处理的DEAE-纤维素树脂,在70℃下先缓慢匀速搅拌2小时,再静置30分钟;预处理程序为:依次用10%NaCl浸泡20h,10%HCl浸泡4h,4%NaOH浸泡4h;
H趁热抽滤,留滤渣;
I用85℃以上高温蒸馏水洗涤滤渣,收集滤液;
J将滤液烘干,粉碎得低电内渗琼脂糖。
本发明所使用的原料,制备方法都简单,经过本发明方法,获得的琼脂糖电内渗值低,可以达到0.08以下,大大提升了琼脂的价值。本发明方法适合工业化生产,并且适用于各种红藻来源的琼脂。
具体实施方式
实施例一
1、从琼脂中分离制备初级琼脂糖
称取4g琼脂粉(石花菜琼脂)加入200mL pH4.4磷酸氢二钠—柠檬酸缓冲液中。
(磷酸氢二钠—柠檬酸缓冲液,pH4.4磷酸氢二钠—柠檬酸缓冲液配制方法:
A----配制0.2mol/L磷酸氢二钠溶液:称取十二水合磷酸氢二钠(Na2HPO4.12H2O--分子量358.14)71.63g,用蒸馏水溶解,定容至1L。
B----配制0.1mol/L柠檬酸溶液:称取一水合柠檬酸(分子量210.14)42.03g,用蒸馏水溶解,定容至2L。
C----分别量取0.2mol/L磷酸氢二钠溶液882ml、0.1mol/L柠檬酸溶液1118ml,混合,可得pH4.4磷酸氢二钠—柠檬酸缓冲液),在70℃恒温下以每分钟15转的转速搅拌12小时。趁热抽滤,收集滤液。用蒸馏水反复洗涤至滤液呈中性,再用超纯水洗涤两次。置于60℃电热恒温鼓风干燥箱烘干,称重,粉碎得3.09g初级琼脂糖,得率为77.25%。经测定,其电内渗值为0.22。
2、从琼脂中分离制备低电内渗级琼脂糖
称取2.0g磷酸氢二钠—柠檬酸缓冲液法制备的初级琼脂糖,加入200ml蒸馏水,加热溶解,加入5g经过预处理的DEAE-纤维素树脂(依次用10%NaCl浸泡20h,10%HCl浸泡4h,4%NaOH浸泡4h),在70℃下以转速15r/min匀速搅拌2h。静置保温0.5h后趁热抽滤,用100ml90℃蒸馏水洗涤滤饼。滤液回收,50℃旋转蒸发浓缩至浓稠状,置于60℃鼓风干燥箱烘干,称重,粉碎得低电内渗琼脂糖1.51g,得率为75.50%,经测定其电内渗值为0.065。
其中电内渗值的测定方法为碱性巴比妥法,具体测定过程为:取0.3g琼脂糖样品加20ml pH8.6巴比妥缓冲液,加热配成1.5%琼脂糖胶液,趁热倒入胶板上,立即放上梳子,防渗漏,20min后取下挡板和梳子,将胶板和架放入电泳槽,加pH8.6巴比妥缓冲液,液面没过胶板不超过1cm,取葡聚糖和血清蛋白配成的溶液5ul,上样,室温下恒压75V,电泳1.5h,取出琼脂糖胶板,脱色剂浸泡15min,洗去溴百里酚蓝,染色剂浸泡20min染色,然后再用脱色剂浸泡,中间更换2次脱色剂,测量正极蓝斑到上样位置的距离OA,负极白斑到上样处距离OD,则电内渗=OD/(OA+OD)*100%。
实施例二
1、从琼脂中分离制备初级琼脂糖
称取12g琼脂粉(江蓠琼脂)加入200mL pH4.4磷酸氢二钠—柠檬酸缓冲液中,在50℃恒温下以每分钟20转的转速搅拌18小时。趁热抽滤,收集滤液。用蒸馏水反复洗涤至滤液呈中性,再用超纯水洗涤两次。置于50℃电热恒温鼓风干燥箱烘干,称重,粉碎得9.23g初级琼脂糖,得率为76.9%。经测定,其电内渗值为0.20。
2、从琼脂中分离制备低电内渗级琼脂糖
称取6.0g磷酸氢二钠—柠檬酸缓冲液法制备的初级琼脂糖,加入600ml蒸馏水,加热溶解,加入5g经过预处理的DEAE-纤维素树脂(依次用10%NaCl浸泡20h,10%HCl浸泡4h,4%NaOH浸泡4h),在70-75℃下以转速10-20r/min匀速搅拌2-2.5h。静置保温0.5-1h后趁热抽滤,用300ml95℃蒸馏水洗涤滤饼。滤液回收,55℃旋转蒸发浓缩至浓稠状,置于50℃鼓风干燥箱烘干,称重,粉碎得低电内渗琼脂糖4.5g,得率为75.0%,经测定其电内渗值为0.08。
实施例三
1、从琼脂中分离制备初级琼脂糖
称取20g琼脂粉(江蓠琼脂)加入200mL pH4.4磷酸氢二钠—柠檬酸缓冲液中,在40℃恒温下以每分钟15转的转速搅拌24小时。趁热抽滤,收集滤液。用蒸馏水反复洗涤至滤液呈中性,再用超纯水洗涤两次。置于55℃电热恒温鼓风干燥箱烘干,称重,粉碎得15.45g初级琼脂糖,得率为77.25%。经测定,其电内渗值为0.21。
2、从琼脂中分离制备低电内渗级琼脂糖
称取10g磷酸氢二钠—柠檬酸缓冲液法制备的初级琼脂糖,加入1000ml蒸馏水,加热溶解,加入25g经过预处理的DEAE-纤维素树脂(依次用10%NaCl浸泡20h,10%HCl浸泡4h,4%NaOH浸泡4h),在75℃下以转速20r/min匀速搅拌2.5h。静置保温1h后趁热抽滤,用450ml98℃蒸馏水洗涤滤饼。滤液回收,60℃旋转蒸发浓缩至浓稠状,置于55℃鼓风干燥箱烘干,称重,粉碎得低电内渗琼脂糖7.5g,得率为75.0%,经测定其电内渗值为0.068。
Claims (6)
1.一种低电内渗琼脂糖的制备方法,所述低电内渗琼脂糖,其电内渗值低于0.1,包括如下步骤:
A称取琼脂粉加入pH4.4磷酸氢二钠—柠檬酸缓冲液,琼脂粉的添加量为20-100g·L-1;
B在40℃-80℃下,缓慢匀速搅拌6小时以上;
C趁热抽滤,收集滤液;
D用蒸馏水反复洗涤至滤液呈中性,再用超纯水洗涤1-3次;
E烘干、粉碎得初级琼脂糖;
F称取1重量份初级琼脂糖,加入150-250重量份蒸馏水,加热溶解;
G DEAE-纤维素树脂先进行如下的预处理:依次用5-15%NaCl浸泡15-25小时,5-15%HCl浸泡3-7小时,3-5%NaOH浸泡2-6小时;将3-7重量份经过预处理的DEAE-纤维素树脂加入步骤F所得溶液,在65℃-80℃下先缓慢匀速搅拌1-3.5小时,再静置10分钟-100分钟;
H趁热抽滤,留滤渣;
I用85℃以上高温蒸馏水洗涤滤渣,收集滤液;
J将滤液烘干,粉碎得低电内渗琼脂糖。
2.如权利要求1所述的一种低电内渗琼脂糖的制备方法,其特征在于:所述低电内渗琼脂糖,其电内渗值低于0.08。
3.如权利要求1所述的一种低电内渗琼脂糖的制备方法,其特征在于:所述低电内渗琼脂糖,其电内渗值为0.08-0.065。
4.如权利要求1所述的一种低电内渗琼脂糖的制备方法,其特征在于:步骤G中,静置时需要保温。
5.如权利要求1所述的一种低电内渗琼脂糖的制备方法,其特征在于:步骤J将滤液烘干之前,滤液可以先浓缩,再烘干。
6.如权利要求1所述的一种低电内渗琼脂糖的制备方法,包括如下步骤:
A称取琼脂粉加入pH4.4磷酸氢二钠—柠檬酸缓冲液,琼脂粉的添加量为20g·L-1;
B在70℃下,缓慢匀速搅拌12小时;
C趁热抽滤,收集滤液;
D用蒸馏水反复洗涤至滤液呈中性,再用超纯水洗涤2次;
E烘干、粉碎得初级琼脂糖;
F称取1重量份初级琼脂糖,加入200重量份蒸馏水,加热溶解;
G加入5重量份经过预处理的DEAE-纤维素树脂,在70℃下先缓慢匀速搅拌2小时,再静置30分钟;预处理程序为:依次用10%NaCl浸泡20h,10%HCl浸泡4h,4%NaOH浸泡4h;
H趁热抽滤,留滤渣;
I用85℃以上高温蒸馏水洗涤滤渣,收集滤液;
J将滤液烘干,粉碎得低电内渗琼脂糖。