CN103897360A - 一种pbt制造工艺 - Google Patents

一种pbt制造工艺 Download PDF

Info

Publication number
CN103897360A
CN103897360A CN201410143180.9A CN201410143180A CN103897360A CN 103897360 A CN103897360 A CN 103897360A CN 201410143180 A CN201410143180 A CN 201410143180A CN 103897360 A CN103897360 A CN 103897360A
Authority
CN
China
Prior art keywords
nucleator
pbt
liquid
phase tackifying
lubricant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410143180.9A
Other languages
English (en)
Inventor
王君
吴德峰
吕震东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yangzhou Jinsen Optoelectronics Co Ltd
Original Assignee
Yangzhou Jinsen Optoelectronics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yangzhou Jinsen Optoelectronics Co Ltd filed Critical Yangzhou Jinsen Optoelectronics Co Ltd
Priority to CN201410143180.9A priority Critical patent/CN103897360A/zh
Publication of CN103897360A publication Critical patent/CN103897360A/zh
Pending legal-status Critical Current

Abstract

本发明涉及PBT制造工艺。利用1,4-丁二醇、对苯二甲酸和催化剂经液相增粘制得粘度为1.05-1.35dL/g的聚对苯二甲酸丁二醇酯（PBT）；在液相增粘后，添加原料总重量0.02～1%的润滑剂，混合均匀；然后再添加原料总重量0.02～1%的成核剂，混合均匀。本发明在液相增粘过程后，采用添加0.02～1%润滑剂，混合均匀，可以提高松套管的表面光洁度，管径均匀，稳定；然后再添加0.02～1%成核剂，混合均匀，对于提高硬度和提高抗侧压性有很大效果。

Description

一种PBT制造工艺
技术领域
本发明涉及PBT制造工艺，属于聚合物制造工艺技术领域。
背景技术
聚对苯二甲酸丁二醇酯(PBT)，PBT又可称为热塑性聚酯塑料，适用于不同加工业者使用，一般多少会加入添加剂，或与其它塑料掺混，随着添加物比例不同，可制造不同规格的产品，用作光纤二次被覆材料，作为光纤松套管。以前，经液相增粘生产的PBT在制作光纤光缆松套管时，出现松套管硬度不够，抗侧压性差，造成光纤光缆在铺设后出现压破压断的现象，另外还出现松套管表面不光滑，管径不均匀，波动较大，成缆过程中出现包块，甚至出现开裂现象，对于光纤光缆成缆带来麻烦,因此，液相增粘的PBT不能直接应用于光缆生产过程中的光纤二次被覆材料。
发明内容
本发明针对上述缺陷，目的在于提供一种能提高PBT性能的PBT制造工艺。
为此本发明采用技术方案是：本发明利用1,4-丁二醇、对苯二甲酸和催化剂经液相增粘制得粘度为1.05-1.35dL/g的聚对苯二甲酸丁二醇酯（PBT）；
在液相增粘后，添加原料总重量0.02～1%的润滑剂，混合均匀；
然后再添加原料总重量0.02～1%的成核剂，混合均匀。
所述成核剂为聚合物成核剂。
所述成核剂为PET成核剂、PP成核剂或聚酰胺成核剂。
所述成核剂为PET成核剂。
所述润滑剂为白油、液体石蜡或聚乙烯蜡。
所述润滑剂为液体石蜡。
本发明的优点是：本发明在液相增粘过程后，采用添加0.02～1%润滑剂，混合均匀，可以提高松套管的表面光洁度，管径均匀，稳定；然后再添加0.02～1%成核剂，混合均匀，对于提高硬度和提高抗侧压性有很大效果。
具体实施方式
实施例一：
本发明利用1,4-丁二醇、对苯二甲酸和催化剂经液相增粘制得粘度为1.05-1.35dL/g的聚对苯二甲酸丁二醇酯（PBT）；
在液相增粘后，添加原料总重量0.2%的润滑剂，混合均匀；
然后再添加原料总重量0.2%的成核剂，混合均匀。
所述成核剂为PP成核剂。
所述润滑剂为白油。
实施例二：
本发明利用1,4-丁二醇、对苯二甲酸和催化剂经液相增粘制得粘度为1.05-1.35dL/g的聚对苯二甲酸丁二醇酯（PBT）；
在液相增粘后，添加原料总重量0.2%的润滑剂，混合均匀；
然后再添加原料总重量0.2%的成核剂，混合均匀。
所述成核剂为聚酰胺成核剂。
所述润滑剂为白油。
实施例三：
本发明利用1,4-丁二醇、对苯二甲酸和催化剂经液相增粘制得粘度为1.05-1.35dL/g的聚对苯二甲酸丁二醇酯（PBT）；
在液相增粘后，添加原料总重量0.2%的润滑剂，混合均匀；
然后再添加原料总重量0.2%的成核剂，混合均匀。
所述成核剂为pp成核剂。
所述润滑剂为聚乙烯蜡。
实施例四：
本发明利用1,4-丁二醇、对苯二甲酸和催化剂经液相增粘制得粘度为1.05-1.35dL/g的聚对苯二甲酸丁二醇酯（PBT）；
在液相增粘后，添加原料总重量0.2%的润滑剂，混合均匀；
然后再添加原料总重量0.2%的成核剂，混合均匀。
所述成核剂为PET成核剂。
所述润滑剂为白油。
利用转矩流变仪检测扭矩，从而反映松套管的表面光洁度，管径均匀。
实施例五：
本发明利用1,4-丁二醇、对苯二甲酸和催化剂经液相增粘制得粘度为1.05-1.35dL/g的聚对苯二甲酸丁二醇酯（PBT）。
经过实验，各实施得到的PBT具有以下数据。
 
序号 料温℃ 压力Mpa 转速rpm 扭矩Nm
实施例一 257 106.5 60 20.8
实施例二 257 106.5 60 24.0
实施例三 257 106.5 60 23.1
实施例四 257 106.5 60 23.7
实施例五 257 106.5 60 38.2
利用转矩流变仪检测扭矩，从而反映松套管的表面光洁度，管径均匀。
PBT物理机械性能对比(按GB/T20186.1-2006标准检测)
Figure DEST_PATH_IMAGE002AAA
由以上数据可得，选用实施例一得到的PBT其各项性能明显优于选用其他润滑剂和成核剂的性能，但加入润滑剂、成核剂得到的PBT性能又明显优于不加人润滑剂、成核剂的性能。

Claims (6)

1.PBT制造工艺，其特征在于，利用1,4-丁二醇、对苯二甲酸和催化剂经液相增粘制得粘度为1.05-1.35dL/g的聚对苯二甲酸丁二醇酯（PBT）；
在液相增粘后，添加原料总重量0.02～1%的润滑剂，混合均匀；
然后再添加原料总重量0.02～1%的成核剂，混合均匀。
2.根据权利要求1所述的PBT制造工艺，其特征在于，所述成核剂为聚合物成核剂。
3.根据权利要求2所述的PBT制造工艺，其特征在于，所述成核剂为PET成核剂、PP成核剂或聚酰胺成核剂。
4.根据权利要求3所述的PBT制造工艺，其特征在于，所述成核剂为PET成核剂。
5.根据权利要求1所述的PBT制造工艺，其特征在于，所述润滑剂为白油、液体石蜡或聚乙烯蜡。
6.根据权利要求4所述的PBT制造工艺，其特征在于，所述润滑剂为液体石蜡。
CN201410143180.9A 2014-04-11 2014-04-11 一种pbt制造工艺 Pending CN103897360A (zh)