CN103893028A

CN103893028A - Seaweed facial mask

Info

Publication number: CN103893028A
Application number: CN201210569291.7A
Authority: CN
Inventors: 不公告发明人
Original assignee: Qingdao Hifun Marine Biological Technology Co Ltd
Current assignee: Qingdao Hifun Marine Biological Technology Co Ltd
Priority date: 2012-12-25
Filing date: 2012-12-25
Publication date: 2014-07-02

Abstract

The invention relates to a seaweed facial mask and a preparing method thereof. The seaweed facial mask can overcome shortcomings and deficiencies of conventional facial masks, makes full use of marine algae and marine biological resources, has the advantages of natural film-forming property, moisture retention property, antibacterial property, no toxicity, no stimulation and no any side effect, has no addition of any chemical additive, is suitable for long-term use, and has significant roles in restraining, retaining moisture, softening, diminishing inflammation, resisting wrinkles, removing freckles, alleviating skin sclerosis and cornification. The selected formula of the seaweed facial mask comprises the following components by weight percentage: 30-50% of seaweed (powder), 10-20% of spirulina (powder), 10-15% of algin, 0.5-2% of chitosan, and the balance deionized water.

Description

A kind of seaweeds facial film

Technical field

The present invention relates to a kind of configuration product of the skin as cosmetics, be particularly related to a kind of skin surface that is coated in to reach the facial film that nourishes moisturizing, skin whitening, antibacterial anti-acne effect, its mainly with: the one-tenth such as Algin, Sargassum (powder), spirulina (powder), sodium alginate, chitosan are grouped into.This facial film is without any side effects, safe and reliable, can work to nourish, promote metabolism to healthy skin, can beauty face-whitening-nourishing, the effect such as moistening skin and eliminating spot, wrinkle removal, convergence pore.

Background technology

At present like product its mainly add the antiseptic, wetting agent, oil content etc. of chemical composition, mercurous and plumbous, likely facial skin is caused to artificial injury, not only not treatment and skin-care effect, may increase the weight of to damage on the contrary facial skin.

Summary of the invention

The object of this invention is to provide a kind of seaweed mask and preparation method thereof.That the multiple pure natural oceanic algae of employing is the seaweed mask that primary raw material is developed, overcome the shortcoming and defect of existing facial film, make full use of marine algae and living marine resources, natural filming performance, performance of keeping humidity, bacteriostasis property, nontoxic non-stimulated, without any side effects, and do not add any chemical addition agent, be applicable to life-time service, skin is had to convergence, moisturizing, softness, antiinflammatory, crease-resistant, speckle dispelling, alleviation skin sclerosis and cornified remarkable effect.

The formula following (component and percentage by weight % thereof) that the present invention selects: Sargassum (powder) 30-50; Spirulina (powder) 10-20; Algin 10-15; Chitosan 0.5-2; Surplus is deionized water.

Sargassum (powder) fineness is the fine powder that 140 mesh sieves sieve, mainly with Brown algae powder, there is to good maintenance action on rough skin surface, it is rich in organic or inorganic material, trace element, vitamin etc., it impels subepidermal little blood vessel circulation, improve microcirculation disturbance, play the effect of skin care, skin protection; Spirulina (powder) fineness is the fine powder that 160 mesh sieves sieve, in its frustule, contain photosynthetic synusia (thylakoid), vitamin, crude protein, crude fat, fatty acid, carbohydrate, mineral, carotene, polysaccharide etc., have the effect of radioprotective defying age whitening; Algin fineness is the fine powder that 200 mesh sieves sieve; contain a large amount of phlegmatic temperaments and starch; can borrow its high viscosity on skin, to form gluey protecting film; play the effect of insulation, skin-moisturizing, skin; skin surface temperature raises; can improve the blood circulation of blood capillary and capillary vessel; skin surface temperature increases; can soften epidermis cutin, dried gluey film, can make skin-tightening; wrinkle is stretched and evened up; thereby play wrinkle resistant, anti-ageing effect, can make powder raw material dissolve each other and coagulate together, easily take off and do not hinder skin.

Chitosan contains highly active functional group in its complicated space structure, shows the antibiotic feature of class, can suppress the growth of various bacteria with active.Skin is had to well affine, osmosis, and also have antibacterial action, there is effect of extremely strong antiinflammatory, reparation, adjusting fat secretion, be printed on effective to comedo, skin sore, can effectively prevent that acne from occurring, therefore be a kind of desirable macromolecular compound used for cosmetic, substituted chemicals antiseptic in the past.

Preparation method of the present invention: above Brown algae and spirulina are screened respectively the flushing unnecessary impurity of removal and sand by (1); (2) Brown algae of handling well and spirulina are put into warm braw dehydrator and carry out dewatered drying, the drying and dewatering time is 30-60 minute, and temperature is 100 ℃-120 ℃; (3) dried Brown algae and spirulina polishing are ground to form to powdery, be modulated into powder dosage form; (4) add Algin, chitosan, deionized water by metering preparation again, together put into homogenizer and at the uniform velocity stir 30-40 minute, rotating speed is per minute 90 to turn, temperature is 25 ℃-40 ℃ of constant temperature, after temperature is cooling voluntarily, can slowly form blackish green paste, become seaweed mask.

Using method of the present invention: the order of face mask film will be according to the order of cervical region, lower jaw, cheek, nose, lip, forehead, and apply from bottom to top, note getting around around eyes, eyebrow, lips, suggestion is from the driest position starts to be coated with, first be coated with T block, repaste U block.Apply after enough 15 minutes at facial film, press gently with finger, feel tack-free, just can, from the edge of facial film, take off at leisure from bottom to top facial film.Conventionally facial film can make skin tighten after being dried, and easily occurs wrinkle, so just take off before facial film does not have desiccation, applies and to obtain overlong time (being no more than more than 30 minutes).

The present invention is described in further detail below in conjunction with embodiment for the specific embodiment:

Be configured according to following table institute column data (percentage by weight %) and described step thereof:

Example 1

Formula one:

Sargassum powder 50

Spirulina powder 20

Algin 15

Chitosan 1

Deionized water adds to 100

_______________________________________________________ _____ __ ___

Preparation method: by Sargassum powder 50, Spirulina powder 20, Algin 15, chitosan 1, deionized water 14, mixes and put into homogenizer and at the uniform velocity stir 30-40 minute, rotating speed is per minute 90 to turn, temperature is 25 ℃-40 ℃ of constant temperature.Again by prepared seaweed mask filling bottle, packing, case, take out material detect.

Example 2

Formula two:

Sargassum powder 40

Spirulina powder 15

Algin 10

Chitosan 0.5

Deionized water adds to 100

_______________________________________________________ _____ __

Preparation method: by Sargassum powder 40, Spirulina powder 15, Algin 10, chitosan 0.5, deionized water 34.5, mixes and put into homogenizer and at the uniform velocity stir 30-40 minute, rotating speed is per minute 90 to turn, temperature is 25 ℃-40 ℃ of constant temperature.Again by prepared seaweed mask filling bottle, packing, case, take out material detect.

Example 3

Formula three:

Sargassum powder 45

Spirulina powder 15

Algin 15

Chitosan 1.5

Deionized water adds to 100

_______________________________________________________ _____ __

Preparation method: by Sargassum powder 45, Spirulina powder 15, Algin 15, chitosan 1.5, deionized water 23.5, mixes and put into homogenizer and at the uniform velocity stir 30-40 minute, rotating speed is per minute 90 to turn, temperature is 25 ℃-40 ℃ of constant temperature.Again by prepared seaweed mask filling bottle, packing, case, take out material detect.

1, physical detection: color is blackish green paste, is applied to skin moist half an hour, can peel, and film property is good.

2, chemical detection: the content of lead, hydrargyrum, arsenic is no more than state-set standard.

3, microorganism detection: do not contain the pathogenic bacterium such as escherichia coli, gold-coloured staphylococci, Candida albicans.

Claims

1. a seaweed mask, is characterized in that, formula following (component and percentage by weight % thereof): Sargassum (powder) 30-50; Spirulina (powder) 10-20; Algin 10-15; Chitosan 0.5-2; Surplus is deionized water.

2. according to the preparation of a kind of seaweed mask of claim 1: above Brown algae and spirulina are screened respectively the flushing unnecessary impurity of removal and sand by (1); (2) Brown algae of handling well and spirulina are put into warm braw dehydrator and carry out dewatered drying, the drying and dewatering time is 30-60 minute, and temperature is 100 ℃-120 ℃; (3) dried Brown algae and spirulina polishing are ground to form to powdery, be modulated into powder dosage form; (4) add Algin, chitosan, deionized water by metering preparation again, together put into homogenizer and at the uniform velocity stir 30-40 minute, rotating speed is per minute 90 to turn, temperature is 25 ℃-40 ℃ of constant temperature, after temperature is cooling voluntarily, can slowly form blackish green paste, become seaweed mask.