CN103881265A - 一种90℃pvc电缆绝缘护套的配方 - Google Patents

一种90℃pvc电缆绝缘护套的配方 Download PDF

Info

Publication number
CN103881265A
CN103881265A CN201410065455.1A CN201410065455A CN103881265A CN 103881265 A CN103881265 A CN 103881265A CN 201410065455 A CN201410065455 A CN 201410065455A CN 103881265 A CN103881265 A CN 103881265A
Authority
CN
China
Prior art keywords
parts
formula
benzene
sheath
pvc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410065455.1A
Other languages
English (en)
Inventor
闵海光
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI JIUZHOU GAOFENZI TECHNOLOGY Co Ltd
Original Assignee
ANHUI JIUZHOU GAOFENZI TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI JIUZHOU GAOFENZI TECHNOLOGY Co Ltd filed Critical ANHUI JIUZHOU GAOFENZI TECHNOLOGY Co Ltd
Priority to CN201410065455.1A priority Critical patent/CN103881265A/zh
Publication of CN103881265A publication Critical patent/CN103881265A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种90℃PVC电缆绝缘护套的配方，该配方包括树脂、钙粉、高岭土、对苯、邻苯、液体蜡、稳定剂、硬钡、脂蜡酸、硬蜡、偏苯和塑化剂，各组分的重量份数如下：树脂49～51份、钙粉18～20份、高岭土4～6.5份、对苯6.6～7.3份、邻苯8～9.5份、液体蜡9.2～9.7份、稳定剂1.7～2.1份、硬钡0.77～0.82份、脂蜡酸0.4～0.6份、硬蜡0.45～0.55份、偏苯6.5～8份、塑化剂0.65～0.72份。本发明具有材料搭配合理、制造成本低和使用寿命长等优点，能够提高护套自身绝缘性能，有效的避免了高压击穿现象的发生，确保了电缆的正常使用，并为人们的生命财产安全提供保障。

Description

一种90℃PVC电缆绝缘护套的配方
技术领域
本发明涉及电缆加工制造技术领域，具体的说是一种90℃PVC电缆绝缘护套的配方。
背景技术
PVC电缆即聚氯乙烯电缆，产品分为固定布线用无护套电缆、固定布线用护套电缆、轻型无护套软电缆、一般用途护套软电缆、安装用电线和屏蔽电线、特殊用途护套软电缆、聚氯乙烯绝缘阻燃/耐火电缆等产品。而传统的90℃PVC电缆护套由于自身配料不合理，制成的护套绝缘性能一般，时间一长出现护套老化时容易在使用的过程中被高压击穿，使得电缆烧损，无法正常使用，甚至引起火灾，危害到人们的生命财产安全。
发明内容
本发明所要解决的技术问题在于提供一种材料搭配合理的、制造成本低的、使用寿命长的，能够提高护套自身绝缘性能的配方，即一种90℃PVC电缆绝缘护套的配方。
本发明所要解决的技术问题采用以下技术方案来实现：
一种90℃PVC电缆绝缘护套的配方，该配方包括树脂、钙粉、高岭土、对苯、邻苯、液体蜡、稳定剂、硬钡、脂蜡酸、硬蜡、偏苯和塑化剂，各组分的重量份数如下：
Figure BDA0000469260380000011
Figure BDA0000469260380000021
所述各组分所占的最佳重量份数如下：
Figure BDA0000469260380000022
部分组分的性能及作用如下：
钙粉：钙粉是一种化合物，化学式是CaCO3，呈碱性，基本上不溶于水，溶于酸，添加钙粉后，钙粉是橡胶工业中使用量最大大填充剂之一，钙粉大量填充在橡胶之中，可增加其制品的容积，并节约昂贵的天然橡胶，从而大大降低成本，钙粉填入橡胶中，能获得比纯橡胶硫化物更高的抗张强度、撕裂强度和耐磨性，从而改善了成型后护套的性能。
高岭土：具有白度高、质软、易分散悬浮于水中、良好的可塑性和高的粘结性、优良的电绝缘性能，从而能够改善护套的绝缘性能，有效的避免了高压击穿现象的发生；具有良好的抗酸溶性、很低的阳离子交换量、较好的耐火性等理化性质，能够提高护套自身的阻燃特性。
液体蜡：能够将各组分更好的胶合在一起，增加了混合后混合物的可塑性，确保护套能够顺利挤出。
稳定剂：能增加溶液、胶体、固体、混合物的稳定性能，它可以减慢反应，保持化学平衡，降低表面张力，防止光、热分解或氧化分解等作用，从而能够防止电缆护套在实际使用的过程中发生老化的现象，延长护套的使用寿命。
脂蜡酸：为硬脂酸与棕榈酸的混合物，并含有少量油酸，微有牛油样气味，极微溶于冷水，易溶于苯、甲苯、氯仿、四氯化碳、二硫化碳、乙酸戊酯等，也溶于乙醇、丙酮。
硬蜡：又称合成石蜡，具有良好的抗破碎性、优良的绝缘性、强的抗水性。这样在脂蜡酸和硬蜡混合后，能够增加护套的绝缘性能，提高护套的抗拉强度，改善护套的韧性，可在护套实际的使用过程中，有效的避免弯曲、扯拉对护套造成的破坏。
偏苯：作为增塑剂，具有良好的耐热性、低挥发性、耐油性以及可加工性，广泛用作PVC耐热增塑剂、抗溶剂交联氯乙烯树脂的增塑剂，可以使护套的柔韧性增强，容易加工。
塑化剂：能够增加护套的韧性，方便护套的挤出加工。
本发明的有益效果是：本发明具有材料搭配合理、制造成本低和使用寿命长等优点，能够提高护套自身绝缘性能，有效的避免了高压击穿现象的发生，确保了电缆的正常使用，并为人们的生命财产安全提供保障。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面对本发明进一步阐述。
实施例一：
一种90℃PVC电缆绝缘护套的配方，该配方包括树脂、钙粉、高岭土、对苯、邻苯、液体蜡、稳定剂、硬钡、脂蜡酸、硬蜡、偏苯和塑化剂，各组分的重量份数如下：
Figure BDA0000469260380000031
Figure BDA0000469260380000041
实施例二：
一种90℃PVC电缆绝缘护套的配方，该配方包括树脂、钙粉、高岭土、对苯、邻苯、液体蜡、稳定剂、硬钡、脂蜡酸、硬蜡、偏苯和塑化剂，各组分的重量份数如下：
Figure BDA0000469260380000042
实施例三：
一种90℃PVC电缆绝缘护套的配方，该配方包括树脂、钙粉、高岭土、对苯、邻苯、液体蜡、稳定剂、硬钡、脂蜡酸、硬蜡、偏苯和塑化剂，各组分的重量份数如下：
Figure BDA0000469260380000051
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (2)

1.一种90℃PVC电缆绝缘护套的配方，其特征在于：该配方包括树脂、钙粉、高岭土、对苯、邻苯、液体蜡、稳定剂、硬钡、脂蜡酸、硬蜡、偏苯和塑化剂，各组分的重量份数如下：
Figure FDA0000469260370000011
2.根据权利要求1所述的一种90℃PVC电缆绝缘护套的配方，其特征在于：所述各组分所占的最佳重量份数如下：
Figure FDA0000469260370000012
CN201410065455.1A 2014-02-25 2014-02-25 一种90℃pvc电缆绝缘护套的配方 Pending CN103881265A (zh)