CN103880347A - Mordenite thermal mortar and manufacture method thereof - Google Patents
Mordenite thermal mortar and manufacture method thereof Download PDFInfo
- Publication number
- CN103880347A CN103880347A CN201410046329.1A CN201410046329A CN103880347A CN 103880347 A CN103880347 A CN 103880347A CN 201410046329 A CN201410046329 A CN 201410046329A CN 103880347 A CN103880347 A CN 103880347A
- Authority
- CN
- China
- Prior art keywords
- parts
- mordenite
- mortar
- minute
- grape vine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses mordenite thermal mortar. The thermal mortar is characterized by being prepared from the following raw materials in parts by weight: 330-390 parts of cement, 160-190 parts of iron tailings, 140-180 parts of mordenite, 120-150 parts of ardealite, 90-120 parts of straw stalk, 80-90 parts of closed cell perlite, 9-11 parts of polypropylene fiber, 20-26 parts of hollow glass beads, 50-70 parts of grape vine, 14-18 parts of steel fibers and 5-7 parts of auxiliaries. The mordenite thermal mortar has low heat conductivity coefficient, excellent adhesion performance, water and seepage resistance, cracking resistance and heat insulation performance, is applicable to building and plastering construction of wall materials, has the characteristics of low material consumption, environmental friendliness, no toxicity, no cracking and the like, has very good market competitiveness as compared with common mortar, and can be widely popularized and used.
Description
Technical field
The present invention relates to thermal insulation mortar technical field, be specifically related to a kind of mordenite thermal insulation mortar and preparation method thereof.
Background technology
In recent years, the various solid wastes that Industrial processes produce and urban construction are removed and are remake the solid waste brought etc. and perplexing always resident's living environment, the present invention adds in thermal insulation mortar solid waste as starting material, realize the cyclic utilization of waste, reduce the pollution to environment, met strategy of sustainable development requirement.
Thermal insulation mortar is take various light materials as aggregate, take cement as gelating material, admixes some property-modifying additives, through manufacturing enterprise's a kind of premixing dry-mix being uniformly mixed and make that adds water.Not only can be incubated outward for external wall, can also be used for exterior wall internal insulation, or insulation simultaneously inside and outside exterior wall, and the insulation on roof and the thermofin of underground heat, for the design of energy-saving system provides certain handiness.There is the advantages such as easy construction, good endurance, light weight, insulation, heat insulating ability be good.But existing traditional mortar heat preserving and insulating material, as poly-stupid granule heat-insulating mortar, pearl thermal insulation mortar etc., many defects are in use exposed, as surperficial hollowing, ftracture, come off, easily go mouldy etc., in addition, the porosity of most of thermal insulation mortar is higher, therefore overall water-intake rate is all very high, after water suction, not only can reduce the intensity of material, and can reduce greatly its heat-insulating property.The demand of the thermal insulation mortar that therefore, the multi-functional intensity such as a kind of novel anti-aging, corrosion-resistant, cracking resistance, insect protected, degerming is high is extremely urgent.
Summary of the invention
Object of the present invention is just to provide a kind of mordenite thermal insulation mortar and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of mordenite thermal insulation mortar, it is characterized in that, made by the raw material of following weight part: cement 330-390, iron tailings 160-190, mordenite 140-180, phosphogypsum 120-150, rice straw 90-120, closed perlite 80-90, polypropylene fibre 9-11, hollow glass micropearl 20-26, grape vine 50-70, steel fiber 14-18, auxiliary agent 5-7.
Described auxiliary agent is made up of following raw materials in part by weight: flyash 5-9, aluminium powder 0.001-0.003, poly(vinylidene fluoride) 1.3-3.1, silicon carbide powder 2-4, titanium dioxide 2-5, silicon sol 0.2-0.4, redispersible latex powder 0.2-0.7, pamorusa oil 3-6, borneol 1-3, ultra micro wax powder 0.7-0.9, grape vine 4-7, its preparation method is each crushing material to be added to suitable quantity of water stir 30-40 minute, mix, granulation, balling-up particle diameter, at 0.5-1mm, is dried and be get final product.
The preparation method of described a kind of mordenite thermal insulation mortar, is characterized in that comprising the following steps:
(1) mordenite, closed perlite are put into 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions flood 10-12 hour, take out and dry, pulverize;
(2) iron tailings, phosphogypsum, grape vine one are arised from 610-790 ℃ and calcine after 3-6 hour and take out and pulverize, add polypropylene fibre, steel fiber stirring and evenly mixing;
(3) step (1), (2) reaction mass, rice straw are pulverized and stirred within 5-8 minute, mix, then drop in stirrer and be uniformly mixed 20-30 minute with other remaining component, the material being stirred is wrapped and be get final product with automatic packing machine.When use, add suitable quantity of water mixing and stirring.
The present invention has following beneficial effect: mordenite thermal insulation mortar of the present invention has that thermal conductivity is low, bond properties is good, water proof anti-seepage, cracking resistance and thermal and insulating performance, be applicable to building by laying bricks or stones and plastering construction of materials for wall, have that materials are few, environment-protecting asepsis, the characteristic such as do not ftracture, have market competitiveness with ordinary mortar ratio, can extensively promote the use of.
Embodiment
Described a kind of mordenite thermal insulation mortar, it is characterized in that, made by the raw material of following weight part: cement 330, iron tailings 160, mordenite 140, phosphogypsum 120, rice straw 90, closed perlite 85, polypropylene fibre 9, hollow glass micropearl 20, grape vine 50, steel fiber 14, auxiliary agent 5.
Described auxiliary agent is made up of following raw materials in part by weight: flyash 8, aluminium powder 0.001, poly(vinylidene fluoride) 1.3, silicon carbide powder 3, titanium dioxide 2, silicon sol 0.3, redispersible latex powder 0.7, pamorusa oil 6, borneol 1, ultra micro wax powder 0.7, grape vine 4, its preparation method is each crushing material to be added to suitable quantity of water stir 30-40 minute, mix, granulation, balling-up particle diameter, at 0.5-1mm, is dried and be get final product.
Making method comprises the following steps:
(1) mordenite, closed perlite are put into 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions flood 10-12 hour, take out and dry, pulverize;
(2) iron tailings, phosphogypsum, grape vine one are arised from 610-790 ℃ and calcine after 3-6 hour and take out and pulverize, add polypropylene fibre, steel fiber stirring and evenly mixing;
(3) step (1), (2) reaction mass, rice straw are pulverized and stirred within 5-8 minute, mix, then drop in stirrer and be uniformly mixed 20-30 minute with other remaining component, the material being stirred is wrapped and be get final product with automatic packing machine.
The technical indicator of processing the thermal insulation mortar obtaining by above-described embodiment is as follows:
(1) thermal conductivity (25 ± 2 ℃ of medial temperatures): 0.0655W/ (mk);
(2) ultimate compression strength (28d): 314kPa;
(3) high temperature resistant and metope tight bond, seamless.
Claims (2)
1. a mordenite thermal insulation mortar, it is characterized in that, made by the raw material of following weight part: cement 330-390, iron tailings 160-190, mordenite 140-180, phosphogypsum 120-150, rice straw 90-120, closed perlite 80-90, polypropylene fibre 9-11, hollow glass micropearl 20-26, grape vine 50-70, steel fiber 14-18, auxiliary agent 5-7; Described auxiliary agent is made up of following raw materials in part by weight: flyash 5-9, aluminium powder 0.001-0.003, poly(vinylidene fluoride) 1.3-3.1, silicon carbide powder 2-4, titanium dioxide 2-5, silicon sol 0.2-0.4, redispersible latex powder 0.2-0.7, pamorusa oil 3-6, borneol 1-3, ultra micro wax powder 0.7-0.9, grape vine 4-7, its preparation method is each crushing material to be added to suitable quantity of water stir 30-40 minute, mix, granulation, balling-up particle diameter, at 0.5-1mm, is dried and be get final product.
2. the making method of a kind of mordenite thermal insulation mortar according to claim 1, is characterized in that comprising the following steps:
(1) mordenite, closed perlite are put into 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions flood 10-12 hour, take out and dry, pulverize;
(2) iron tailings, phosphogypsum, grape vine one are arised from 610-790 ℃ and calcine after 3-6 hour and take out and pulverize, add polypropylene fibre, steel fiber stirring and evenly mixing;
(3) step (1), (2) reaction mass, rice straw are pulverized and stirred within 5-8 minute, mix, then drop in stirrer and be uniformly mixed 20-30 minute with other remaining component, the material being stirred is wrapped and be get final product with automatic packing machine.