CN103864384A - Fireproof moth-proof thermal mortar and preparation method thereof - Google Patents

Fireproof moth-proof thermal mortar and preparation method thereof Download PDF

Info

Publication number
CN103864384A
CN103864384A CN201410046321.5A CN201410046321A CN103864384A CN 103864384 A CN103864384 A CN 103864384A CN 201410046321 A CN201410046321 A CN 201410046321A CN 103864384 A CN103864384 A CN 103864384A
Authority
CN
China
Prior art keywords
parts
powder
attapulgite
minute
moth
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410046321.5A
Other languages
Chinese (zh)
Inventor
许盟凯
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI ZHONGKAI FRAME INDUSTRY Co Ltd
Original Assignee
ANHUI ZHONGKAI FRAME INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI ZHONGKAI FRAME INDUSTRY Co Ltd filed Critical ANHUI ZHONGKAI FRAME INDUSTRY Co Ltd
Priority to CN201410046321.5A priority Critical patent/CN103864384A/en
Publication of CN103864384A publication Critical patent/CN103864384A/en
Pending legal-status Critical Current

Abstract

The invention discloses fireproof moth-proof thermal mortar which is characterized in that the thermal mortar is prepared from the following raw materials in parts by weight: 310-360 parts of high-alumina cement, 200-250 parts of expanded perlite, 180-210 parts of attapulgite, 90-110 parts of waste polystyrene foam plastic crushed particles, 80-130 parts of starch, 120-160 parts of pyrite dross, 6-9 parts of sodium silicate, 18-35 parts of sierozem powder, 10-13 parts of aluminum hydroxide, 8-11 parts of cellulose formaldehyde, 0.4-0.8 part of dipterex, 12-15 parts of redispersible latex powder, 7-9 parts of benzenesulfonic acid and 3-6 parts of aids. The thermal mortar prepared from the raw materials such as the cement, expanded perlite, waste polystyrene foam plastic crushed particles, attapulgite and pyrite dross is light in volume weight, does not crack and has the advantages of fire resistance, moth resistance, high flame retardant property, non-toxicity, high adhesive force, high construction property, high cracking resistance and excellent weather resistance. Moreover, by adoption of the production process, the operation is simple and convenient, the quality is easily controlled, the performance is stable, and batch production is conveniently performed.

Description

A kind of fire prevention insect-preventing and heat-insulating mortar and preparation method thereof
Technical field
The present invention relates to thermal insulation mortar technical field, be specifically related to a kind of fire prevention insect-preventing and heat-insulating mortar and preparation method thereof.
Background technology
In recent years, the various solid wastes that Industrial processes produce and urban construction are removed and are remake the solid waste brought etc. and perplexing always resident's living environment, the present invention adds in thermal insulation mortar solid waste as starting material, realize the cyclic utilization of waste, reduce the pollution to environment, met strategy of sustainable development requirement.
Thermal insulation mortar is taking various light materials as aggregate, taking cement as gelating material, admixes some property-modifying additives, through manufacturing enterprise's a kind of premixing dry-mix being uniformly mixed and make that adds water.Not only can be incubated outward for external wall, can also be used for exterior wall internal insulation, or insulation simultaneously inside and outside exterior wall, and the insulation on roof and the thermofin of underground heat, for the design of energy-saving system provides certain handiness.There is the advantages such as easy construction, good endurance, light weight, insulation, heat insulating ability be good.But existing traditional mortar heat preserving and insulating material, as poly-stupid granule heat-insulating mortar, pearl thermal insulation mortar etc., many defects are in use exposed, as surperficial hollowing, ftracture, come off, easily go mouldy etc., in addition, the porosity of most of thermal insulation mortar is higher, therefore overall water-intake rate is all very high, after water suction, not only can reduce the intensity of material, and can reduce greatly its heat-insulating property.The demand of the thermal insulation mortar that therefore, the multi-functional intensity such as a kind of novel anti-aging, corrosion-resistant, cracking resistance, insect protected, degerming is high is extremely urgent.
Summary of the invention
Object of the present invention is just to provide a kind of fire prevention insect-preventing and heat-insulating mortar and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of fire prevention insect-preventing and heat-insulating mortar, it is characterized in that, made by the raw material of following weight part: high-alumina cement 310-360, pearlstone 200-250, attapulgite 180-210, waste and old polyphenyl foam plastics particle 90-110, starch 80-130, pyrite slag 120-160, water glass 6-9, grey calcium powder 18-35, aluminium hydroxide 10-13, formaldehyde Mierocrystalline cellulose 8-11, Trichlorphon 0.4-0.8, redispersion latex powder 12-15, Phenylsulfonic acid 7-9, auxiliary agent 3-6.
Described auxiliary agent is made up of following raw materials in part by weight: flyash 5-9, aluminium powder 0.001-0.003, poly(vinylidene fluoride) 1.3-3.1, silicon carbide powder 2-4, titanium dioxide 2-5, silicon sol 0.2-0.4, redispersible latex powder 0.2-0.7, pamorusa oil 3-6, borneol 1-3, ultra micro wax powder 0.7-0.9, grape vine 4-7, its preparation method is each crushing material to be added to suitable quantity of water stir 30-40 minute, mix, granulation, balling-up particle diameter, at 0.5-1mm, is dried and be get final product.
The preparation method of described a kind of insect-preventing and heat-insulating mortar of preventing fires, is characterized in that comprising the following steps:
(1) pearlstone is put into 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions flood 10-12 hour, taken out and dry, pulverize;
(2) attapulgite, pyrite slag one are arised from 630-790 DEG C and calcine after 3-6 hour and take out, add Phenylsulfonic acid, formaldehyde Mierocrystalline cellulose stirring and evenly mixing;
(3) step (1), (2) reaction mass, redispersion latex powder, starch are stirred and mixed for 5-8 minute, then drop in stirrer and be uniformly mixed 20-30 minute with other remaining component, the material being stirred is wrapped and be get final product with automatic packing machine.When use, add suitable quantity of water mixing and stirring.
The present invention has following beneficial effect: the thermal insulation mortar unit weight that the present invention makes as raw material taking cement, pearlstone, waste and old polyphenyl foam plastics particle, attapulgite, pyrite slag etc. gently, does not ftracture, and has that fire prevention insect protected, fire-retardant good, nontoxic, strong adhesion, application property are good, splitting resistance and an advantage such as weathering resistance is good.And adopt that production technique of the present invention is easy and simple to handle, quality is easy to control, stable performance, be convenient to batch production.
Embodiment
Described one fire prevention insect-preventing and heat-insulating mortar, it is characterized in that, made by the raw material of following weight part: high-alumina cement 330, pearlstone 220, attapulgite 180, waste and old polyphenyl foam plastics particle 90, starch 80, pyrite slag 120, water glass 6, grey calcium powder 18, aluminium hydroxide 13, formaldehyde Mierocrystalline cellulose 8, Trichlorphon 0.48, redispersion latex powder 12, Phenylsulfonic acid 7, auxiliary agent 3.
Described auxiliary agent is made up of following raw materials in part by weight: flyash 8, aluminium powder 0.001, poly(vinylidene fluoride) 1.31, silicon carbide powder 2, titanium dioxide 5, silicon sol 0.2, redispersible latex powder 0.2, pamorusa oil 6, borneol 1, ultra micro wax powder 0.7, grape vine 4, its preparation method is each crushing material to be added to suitable quantity of water stir 30-40 minute, mix, granulation, balling-up particle diameter, at 0.5-1mm, is dried and be get final product.
Making method comprises the following steps:
(1) pearlstone is put into 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions flood 10-12 hour, taken out and dry, pulverize;
(2) attapulgite, pyrite slag one are arised from 630-790 DEG C and calcine after 3-6 hour and take out, add Phenylsulfonic acid, formaldehyde Mierocrystalline cellulose stirring and evenly mixing;
(3) step (1), (2) reaction mass, redispersion latex powder, starch are stirred and mixed for 5-8 minute, then drop in stirrer and be uniformly mixed 20-30 minute with other remaining component, the material being stirred is wrapped and be get final product with automatic packing machine.
The technical indicator of processing the thermal insulation mortar obtaining by above-described embodiment is as follows:
(1) thermal conductivity (25 ± 2 DEG C of medial temperatures): 0.074W/ (mk);
(2) ultimate compression strength (28d): 304kPa;
(3) high temperature resistant and metope tight bond, seamless;
(4) dry density: 312kg/m 3.

Claims (2)

1. a fire prevention insect-preventing and heat-insulating mortar, it is characterized in that, made by the raw material of following weight part: high-alumina cement 310-360, pearlstone 200-250, attapulgite 180-210, waste and old polyphenyl foam plastics particle 90-110, starch 80-130, pyrite slag 120-160, water glass 6-9, grey calcium powder 18-35, aluminium hydroxide 10-13, formaldehyde Mierocrystalline cellulose 8-11, Trichlorphon 0.4-0.8, redispersion latex powder 12-15, Phenylsulfonic acid 7-9, auxiliary agent 3-6; Described auxiliary agent is made up of following raw materials in part by weight: flyash 5-9, aluminium powder 0.001-0.003, poly(vinylidene fluoride) 1.3-3.1, silicon carbide powder 2-4, titanium dioxide 2-5, silicon sol 0.2-0.4, redispersible latex powder 0.2-0.7, pamorusa oil 3-6, borneol 1-3, ultra micro wax powder 0.7-0.9, grape vine 4-7, its preparation method is each crushing material to be added to suitable quantity of water stir 30-40 minute, mix, granulation, balling-up particle diameter, at 0.5-1mm, is dried and be get final product.
2. the making method of a kind of insect-preventing and heat-insulating mortar of preventing fires according to claim 1, is characterized in that comprising the following steps:
(1) pearlstone is put into 1 ‰ iron(ic) chloride and 0.5 ‰ calcium chloride composite solutions flood 10-12 hour, taken out and dry, pulverize;
(2) attapulgite, pyrite slag one are arised from 630-790 DEG C and calcine after 3-6 hour and take out, add Phenylsulfonic acid, formaldehyde Mierocrystalline cellulose stirring and evenly mixing;
(3) step (1), (2) reaction mass, redispersion latex powder, starch are stirred and mixed for 5-8 minute, then drop in stirrer and be uniformly mixed 20-30 minute with other remaining component, the material being stirred is wrapped and be get final product with automatic packing machine.
CN201410046321.5A 2014-02-10 2014-02-10 Fireproof moth-proof thermal mortar and preparation method thereof Pending CN103864384A (en)