CN103864366B - A kind of ceramic tile waste particle thermal insulation mortar and preparation method thereof - Google Patents
A kind of ceramic tile waste particle thermal insulation mortar and preparation method thereof Download PDFInfo
- Publication number
- CN103864366B CN103864366B CN201410046431.1A CN201410046431A CN103864366B CN 103864366 B CN103864366 B CN 103864366B CN 201410046431 A CN201410046431 A CN 201410046431A CN 103864366 B CN103864366 B CN 103864366B
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- waste particle
- tile waste
- thermal insulation
- insulation mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of ceramic tile waste particle thermal insulation mortar, it is characterized in that, be made up of the raw material of following weight portion: cement 290-330, ceramic tile waste particle 200-245, calcium sulfate crystal whiskers 35-50, Muscovitum 85-105, aluminum nitride powder 90-110, Kaolin 105-130, phragmites communis stalk 75-90, naphthalene series high-efficiency water-reducing agent 9-13, sodium tripolyphosphate 8-12, calcium saccharate 6-9, auxiliary agent 3-6; Unit weight of the present invention is light, corrosion resistance is excellent, heat preservation and soundproof performance is good, heat conductivity is low, good water-retaining property, the stable physical property of product, do not ftracture, not hollowing, aging resistance, long service life, this product adds water and just can apply, easy to use, it may be achieved civilized construction; Product is nontoxic, tasteless, harmless, free from environmental pollution, belongs to environment protecting thermal insulating energy-saving material.
Description
Technical field
The present invention relates to thermal insulation mortar technical field, be specifically related to a kind of ceramic tile waste particle thermal insulation mortar and preparation method thereof.
Background technology
In recent years, various solid wastes and urban construction removal that industrial processes produce remake the solid waste etc. brought and annoying the living environment of resident always, solid waste is added in thermal insulation mortar as raw material by the present invention, achieve the cyclic utilization of waste, decrease the pollution to environment, meet strategy of sustainable development requirement.
Thermal insulation mortar is with various light materials for aggregate, with cement for gelating material, admixes some property-modifying additives, adds water through manufacturing enterprise and stirs a kind of premixing dry powder and mortar mixed and make. Can be not only used for external wall external thermal insulation, it is also possible to for exterior wall internal insulation, or be incubated inside and outside exterior wall simultaneously, and the thermal insulation layer of the insulation on roof and underground heat, for the motility that the design offer of energy-saving system is certain. There is the advantages such as easy construction, good endurance, light weight, insulation, thermal insulation be good. But existing tradition mortar heat preserving and insulating material, such as poly-stupid granule heat-insulating mortar, Margarita thermal insulation mortar etc., in use expose many defects, such as surface hollowing, ftracture, come off, easily go mouldy, it addition, the porosity of major part thermal insulation mortar is higher, therefore overall water absorption rate is all significantly high, not only can reduce the intensity of material after water suction, and its heat-insulating property can be reduced greatly. Therefore, a kind of novel anti-aging, corrosion-resistant, cracking resistance, insect protected, thermal insulation mortar that the multi-functional intensity such as degerming is high demand extremely urgent.
Summary of the invention
It is an object of the invention to provide a kind of ceramic tile waste particle thermal insulation mortar and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of ceramic tile waste particle thermal insulation mortar, it is characterized in that, be made up of the raw material of following weight portion: cement 290-330, ceramic tile waste particle 200-245, calcium sulfate crystal whiskers 35-50, Muscovitum 85-105, aluminum nitride powder 90-110, Kaolin 105-130, phragmites communis stalk 75-90, naphthalene series high-efficiency water-reducing agent 9-13, sodium tripolyphosphate 8-12, calcium saccharate 6-9, auxiliary agent 3-6.
Described auxiliary agent is made up of following raw materials in part by weight: flyash 5-9, aluminium powder 0.001-0.003, polyvinylidene fluoride 1.3-3.1, silicon carbide powder 2-4, titanium dioxide 2-5, Ludox 0.2-0.4, redispersible latex powder 0.2-0.7, citronella oil 3-6, Borneolum Syntheticum 1-3, ultra micro wax powder 0.7-0.9, vine 4-7, its preparation method is each crushing material to add suitable quantity of water stir 30-40 minute, mixing, pelletize, balling-up particle diameter is in 0.5-1mm, drying.
The preparation method of described a kind of ceramic tile waste particle thermal insulation mortar, it is characterised in that comprise the following steps:
(1) Muscovitum is put in 1 �� iron chloride and 0.5 �� calcium chloride composite solutions and impregnate 10-12 hour, take out and dry, pulverize;
(2) take out after calcining 3-6 hour at ceramic tile waste particle, calcium sulfate crystal whiskers, Kaolin one being arised from 620-790 DEG C and pulverize, add naphthalene series high-efficiency water-reducing agent stirring and evenly mixing;
(3) after step (1), (2) reaction mass, sodium tripolyphosphate, phragmites communis stalk being pulverized and stir mixing in 5-8 minute, then mix 20-30 minute with stirring in other residual components input blender, the material automatic packaging machine being stirred is wrapped and be get final product.
Suitable quantity of water mixing and stirring is added during use.
The present invention has following beneficial effect: unit weight of the present invention is light, corrosion resistance is excellent, heat preservation and soundproof performance is good, heat conductivity is low, good water-retaining property, the stable physical property of product, do not ftracture, not hollowing, aging resistance, long service life, this product adds water and just can apply, easy to use, it may be achieved civilized construction; Product is nontoxic, tasteless, harmless, free from environmental pollution, belongs to environment protecting thermal insulating energy-saving material.
Detailed description of the invention
Described a kind of ceramic tile waste particle thermal insulation mortar, it is characterized in that, be made up of the raw material of following weight portion: cement 290, ceramic tile waste particle 200, calcium sulfate crystal whiskers 35, Muscovitum 85, aluminum nitride powder 90, Kaolin 105, phragmites communis stalk 75, naphthalene series high-efficiency water-reducing agent 9, sodium tripolyphosphate 8, calcium saccharate 6, auxiliary agent 3.
Described auxiliary agent is made up of following raw materials in part by weight: flyash 5, aluminium powder 0.001, polyvinylidene fluoride 1.3, silicon carbide powder 2, titanium dioxide 5, Ludox 0.2, redispersible latex powder 0.7, citronella oil 5, Borneolum Syntheticum 1, ultra micro wax powder 0.7, vine 4, its preparation method is each crushing material to add suitable quantity of water stir 30-40 minute, mixing, pelletize, balling-up particle diameter is in 0.5-1mm, drying.
Manufacture method comprises the following steps:
(1) Muscovitum is put in 1 �� iron chloride and 0.5 �� calcium chloride composite solutions and impregnate 10-12 hour, take out and dry, pulverize;
(2) take out after calcining 3-6 hour at ceramic tile waste particle, calcium sulfate crystal whiskers, Kaolin one being arised from 620-790 DEG C and pulverize, add naphthalene series high-efficiency water-reducing agent stirring and evenly mixing;
(3) after step (1), (2) reaction mass, sodium tripolyphosphate, phragmites communis stalk being pulverized and stir mixing in 5-8 minute, then mix 20-30 minute with stirring in other residual components input blender, the material automatic packaging machine being stirred is wrapped and be get final product.
The technical specification being processed the thermal insulation mortar obtained by above-described embodiment is as follows:
(1) heat conductivity (mean temperature 25 �� 2 DEG C): 0.063W/ (m k);
(2) comprcssive strength (28d): 306kPa;
(3) high temperature resistant and metope tight bond, seamless;
(4) dry density: 260kg/m3��
Claims (1)
1. a ceramic tile waste particle thermal insulation mortar, it is characterized in that, be made up of the raw material of following weight portion: cement 290-330, ceramic tile waste particle 200-245, calcium sulfate crystal whiskers 35-50, Muscovitum 85-105, aluminum nitride powder 90-110, Kaolin 105-130, phragmites communis stalk 75-90, naphthalene series high-efficiency water-reducing agent 9-13, sodium tripolyphosphate 8-12, calcium saccharate 6-9, auxiliary agent 3-6;Described auxiliary agent is made up of following raw materials in part by weight: flyash 5-9, aluminium powder 0.001-0.003, polyvinylidene fluoride 1.3-3.1, silicon carbide powder 2-4, titanium dioxide 2-5, Ludox 0.2-0.4, redispersible latex powder 0.2-0.7, citronella oil 3-6, Borneolum Syntheticum 1-3, ultra micro wax powder 0.7-0.9, vine 4-7, its preparation method is each crushing material to add suitable quantity of water stir 30-40 minute, mixing, pelletize, balling-up particle diameter is in 0.5-1mm, drying;
The manufacture method of described ceramic tile waste particle thermal insulation mortar comprises the following steps:
(1) Muscovitum is put in 1 �� iron chloride and 0.5 �� calcium chloride composite solutions and impregnate 10-12 hour, take out and dry, pulverize;
(2) take out after calcining 3-6 hour at ceramic tile waste particle, calcium sulfate crystal whiskers, Kaolin one being arised from 620-790 DEG C and pulverize, add naphthalene series high-efficiency water-reducing agent stirring and evenly mixing;
(3) after step (1), (2) reaction mass, sodium tripolyphosphate, phragmites communis stalk being pulverized and stir mixing in 5-8 minute, then mix 20-30 minute with stirring in other residual components input blender, the material automatic packaging machine being stirred is wrapped and be get final product.