CN103880335A - 一种复合保温材料及其制备方法 - Google Patents
一种复合保温材料及其制备方法 Download PDFInfo
- Publication number
- CN103880335A CN103880335A CN201410036821.0A CN201410036821A CN103880335A CN 103880335 A CN103880335 A CN 103880335A CN 201410036821 A CN201410036821 A CN 201410036821A CN 103880335 A CN103880335 A CN 103880335A
- Authority
- CN
- China
- Prior art keywords
- parts
- insulating material
- compound insulating
- diphenylmethanediisocyanate
- inorganic materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种复合保温材料,由如下重量份数的原料组成:二苯基甲烷二异氰酸酯:100~185份;聚醚型多元醇:40~90份;环戊烷:2~11.5份;无机材料:300~800份。本发明提供了一种采用有机-无机材料机械共混法生产的复合保温材料,其克服单一材料的缺点,结合有机无机材料的优点而生产的新型保温材料,其具有保温性能好、防火性能好、耐久性好、强度高等优点。
Description
技术领域
本发明涉及一种保温材料,特别是涉及一种用于建筑墙体保温的复合保温材料及其制备方法。
背景技术
目前墙体保温材料中有机保温材料具有重量轻、保温隔热性能好、可加工性好等优点,但其缺点则是不防火、稳定性差、不耐老化;无机保温材料具有强度高、防火性能好属于不然材料、耐久性好,其缺点为重量大、保温隔热性能差,单一材料应用在墙体保温施工中存在安全隐患。因此,制备得到将无机材料和有机材料结合的复合保温材料是非常必要的。
发明内容
本发明要解决的技术问题是提供一种成本低、保温隔热性能好、强度高、耐久性好的复合保温材料。
一种复合保温材料,由如下重量份数的原料组成:
二苯基甲烷二异氰酸酯:100~185份;
聚醚型多元醇:40~90份;
环戊烷:2~11.5份;
无机材料:300~800份。
本发明所述的复合保温材料,其中所述无机材料为闭孔玻化微珠或陶砂或二者的混合物。
本发明所述的复合保温材料,其中所述无机材料为A组份和B组份的混合物,所述混合物中的B组份的质量分数小于3%,所述B组份为滑石粉,所述A组份为闭孔玻化微珠或陶砂或二者的混合物。
本发明所述的复合保温材料,其中所述聚醚型多元醇为聚乙二醇或聚丙二醇。
本发明所述的复合保温材料,由如下重量份数的原料组成:
二苯基甲烷二异氰酸酯:185份;
聚乙二醇:40份;
环戊烷:11.5份;
闭孔玻化微珠:300份;
滑石粉:6份。
本发明所述的复合保温材料,由如下重量份数的原料组成:
二苯基甲烷二异氰酸酯:150份;
聚乙二醇:70份;
环戊烷:6份;
闭孔玻化微珠:500份;
陶砂:150份;
滑石粉:8.5份。
本发明所述的复合保温材料的制备方法,包括如下步骤:
先将聚醚型多元醇与无机材料搅拌均匀,并静置5~15分钟,加入到温度为5~8℃的低温搅拌罐中,搅拌均匀,同时加入二苯基甲烷二异氰酸酯,在2000转/分钟的速度下搅拌均匀10~25秒,加入环戊烷作为发泡剂搅拌10~20秒至均匀,后按照3~15倍的发泡倍数倒入专用模具中,模具温度为35~45℃度,静置固化8~10分钟、熟化后开模,得到产品;
其中,发泡原液二苯基甲烷二异氰酸酯的温度为18~20℃,熟化时间≥6min。
本发明复合保温材料与现有技术不同之处在于:
本发明提供了一种采用有机-无机材料机械共混法生产的复合保温材料,其克服单一材料的缺点,结合有机无机材料的优点而生产的新型保温材料,其具有保温性能好、防火性能好、耐久性好、强度高等优点。
复合材料是指结合两种或两种以上不同有机、无机相的物质以有机料化学方式胶凝结合而成,撷取各组成成分的优点,以构成需要之结构材。往往以一种材料为基体,另一种材料为增强体组合而成的材料。各种材料在性能上互相取长补短,产生协同效应,使复合材料的综合性能优于原组成材料而满足各种不同的要求。
具体实施方式
实施例1
一种复合保温材料,由如下重量份数的原料组成:
二苯基甲烷二异氰酸酯:100;
聚醚型多元醇:90份;
环戊烷:2份;
无机材料:800份。
所述无机材料为闭孔玻化微珠,所述聚醚型多元醇为聚丙二醇。
实施例2
一种复合保温材料,由如下重量份数的原料组成:
二苯基甲烷二异氰酸酯:185份;
聚乙二醇:40份;
环戊烷:11.5份;
闭孔玻化微珠:300份;
滑石粉:6份。
实施例3
一种复合保温材料,由如下重量份数的原料组成:
二苯基甲烷二异氰酸酯:150份;
聚乙二醇:70份;
环戊烷:6份;
闭孔玻化微珠:500份;
陶砂:150份;
滑石粉:8.5份。
实施例4
一种复合保温材料,由如下重量份数的原料组成:
二苯基甲烷二异氰酸酯:125份;
聚醚型多元醇:60份;
环戊烷:3份;
无机材料:300份。
所述无机材料为陶砂,所述聚醚型多元醇为聚丙二醇。
实施例5
一种所述的复合保温材料的制备方法,包括如下步骤:
先将聚醚型多元醇与无机材料搅拌均匀,并静置5分钟,加入到温度为8℃的低温搅拌罐中,搅拌均匀,同时加入二苯基甲烷二异氰酸酯,在2000转/分钟的速度下搅拌均匀10秒,加入环戊烷作为发泡剂搅拌20秒至均匀,后按照3倍的发泡倍数倒入专用模具中,模具温度为45℃度,静置固化8分钟、熟化后开模,得到产品;
其中,发泡原液二苯基甲烷二异氰酸酯的温度为20℃,熟化时间≥6min。
实施例6
一种所述的复合保温材料的制备方法,其特征在于:包括如下步骤:
先将聚醚型多元醇与无机材料搅拌均匀,并静置15分钟,加入到温度为5℃的低温搅拌罐中,搅拌均匀,同时加入二苯基甲烷二异氰酸酯,在2000转/分钟的速度下搅拌均匀25秒,加入环戊烷作为发泡剂搅拌10秒至均匀,后按照15倍的发泡倍数倒入专用模具中,模具温度为35℃度,静置固化10分钟、熟化后开模,得到产品;
其中,发泡原液二苯基甲烷二异氰酸酯的温度为18℃,熟化时间≥6min。
以上所述的实施例仅仅是对本发明的优选实施方式进行描述,并非对本发明的范围进行限定,在不脱离本发明设计精神的前提下,本领域普通技术人员对本发明的技术方案作出的各种变形和改进,均应落入本发明权利要求书确定的保护范围内。
Claims (7)
1.一种复合保温材料,其特征在于:由如下重量份数的原料组成:
二苯基甲烷二异氰酸酯:100~185份;
聚醚型多元醇:40~90份;
环戊烷:2~11.5份;
无机材料:300~800份。
2.根据权利要求1所述的复合保温材料,其特征在于:所述无机材料为闭孔玻化微珠或陶砂或二者的混合物。
3.根据权利要求1所述的复合保温材料,其特征在于:所述无机材料为A组份和B组份的混合物,所述混合物中的B组份的质量分数小于3%,所述B组份为滑石粉,所述A组份为闭孔玻化微珠或陶砂或二者的混合物。
4.根据权利要求2或3所述的复合保温材料,其特征在于:所述聚醚型多元醇为聚乙二醇或聚丙二醇。
5.根据权利要求3所述的复合保温材料,其特征在于:由如下重量份数的原料组成:
二苯基甲烷二异氰酸酯:185份;
聚乙二醇:40份;
环戊烷:11.5份;
闭孔玻化微珠:300份;
滑石粉:6份。
6.根据权利要求3所述的复合保温材料,其特征在于:由如下重量份数的原料组成:
二苯基甲烷二异氰酸酯:150份;
聚乙二醇:70份;
环戊烷:6份;
闭孔玻化微珠:500份;
陶砂:150份;
滑石粉:8.5份。
7.权利要求1~6中任意一种所述的复合保温材料的制备方法,其特征在于:包括如下步骤:
先将聚醚型多元醇与无机材料搅拌均匀,并静置5~15分钟,加入到温度为5~8℃的低温搅拌罐中,搅拌均匀,同时加入二苯基甲烷二异氰酸酯,在2000转/分钟的速度下搅拌均匀10~25秒,加入环戊烷作为发泡剂搅拌10~20秒至均匀,后按照3~15倍的发泡倍数倒入专用模具中,模具温度为35~45℃度,静置固化8~10分钟、熟化后开模,得到产品;
其中,发泡原液二苯基甲烷二异氰酸酯的温度为18~20℃,熟化时间≥6min。