CN103879164B - The technique of printing antenna for mobile phone - Google Patents
The technique of printing antenna for mobile phone Download PDFInfo
- Publication number
- CN103879164B CN103879164B CN201410123418.1A CN201410123418A CN103879164B CN 103879164 B CN103879164 B CN 103879164B CN 201410123418 A CN201410123418 A CN 201410123418A CN 103879164 B CN103879164 B CN 103879164B
- Authority
- CN
- China
- Prior art keywords
- mobile phone
- printed
- antenna
- technique
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
<b> the invention provides a kind of technique of printing antenna for mobile phone, comprise the following steps: (</b><bGreatT.Gre aT.GT1</b><bGrea tT.GreaT.GT) provides the base material of antenna for mobile phone to be printed, base material has part to be printed, </b><bGreatT.Gre aT.GT part to be printed has relative upper surface and lower surface, and </b><bGreatT.Gre aT.GT part to be printed offers one or more hole, (</b><bGreatT.Gre aT.GT2</b><bGrea tT.GreaT.GT) prints conductive silver paste respectively on relative upper and lower two surfaces of part to be printed, a glue is carried out in (</b><bGreatT.Gre aT.GT3</b><bGrea tT.GreaT.GT) hole to two surface printings in the part to be printed of conductive silver paste, and hole inwall is covered by conductive silver paste, (</b><bGreatT.Gre aT.GT4</b><bGrea tT.GreaT.GT) dries </b><bGreatT.Gre aT.GT30 ~ 60</b><bGreatT.G reaT.GT minute at </b><bGreatT.Gre aT.GT80 ~ 150</b><bGreatT. is GreaT.GT DEG C, obtained antenna for mobile phone.Technique of the present invention is simple, easy to operate and cost is low, and the stuctures and properties of made antenna for mobile phone is all more stable, has a good application prospect.</b>
Description
Technical field
the present invention relates to the field of the antenna of wireless terminal device, relate more specifically to a kind of technique of printing antenna for mobile phone.
Background technology
along with making rapid progress of science and technology, conductive silver paste replaces traditional electro-coppering, nickel gradually as the transmitting medium of antenna for mobile phone, and the manufacture craft of antenna for mobile phone is also gradually to simply, convenient, the future development of environmental protection.
but, antenna for mobile phone manufacture craft traditional is in the market mainly following several mode: application number a kind of employing flexible printed circuit board explained hereafter built-in antenna of mobile phone that has been the patent application publication of 200920214043.4, this technique can be pasted in plane or 2 dimension curved surfaces, 3 dimensions and above curved surface and be provided with feedback point joint face on can not paste; Application number a kind of LDS technique that has been the patent application publication of 201310460603.5, by the laser hardening of glue, carry out shaping to antenna position, the mode of fluid bed is adopted by conductive powder to be attached to glue surface, form electroplated conductive layer, then by traditional electroplating technique, finer and close conductive layer is attached to conductive powder surface, forms antenna.This process costs higher (laser equipment is expensive), complex process, raw material are single, and electroplating technology pollutes larger; In addition, application number be 20110206089.3 application discloses a kind of PDS technique, in the antenna prototype that injection mo(u)lding is good, the ink that bat printing can be plated, printing part carrying out copper facing and nickel plating.This technology process is complicated, and poor stability, cost is relatively high, and employs electroplating technique equally, pollutes larger.A kind of typography is also had to be that an installing hole is set on plastic housing, in installing hole, insert PIN needle, be generally copper pin, in order to prevent the coming off of electrically conductive ink in the printing of PIN needle position, in advance at the ink of PIN needle position printing last layer strong adhesion, printing process should be which increased.
Summary of the invention
in order to overcome the problems referred to above of the prior art, the invention provides a kind of technique of printing antenna for mobile phone, this technical process is simple, and cost is lower and the qualification rate of product is higher.
the technical solution used in the present invention is: a kind of technique of printing antenna for mobile phone, comprises the following steps successively:
(1) provide the base material of antenna for mobile phone to be printed, base material has part to be printed, and part to be printed has relative upper surface and lower surface, and part to be printed offers one or more hole;
(2) on relative upper and lower two surfaces of part to be printed, print conductive silver paste respectively, the conductive silver paste after this printing is used for the upper printed circuit board (PCB) arranged with base material (casing or frame) and is electrically connected, and forms conductive channel;
(3) glue is carried out in the hole to two surface printings in the part to be printed of conductive silver paste, hole inwall is covered by conductive silver paste, like this, the conductive silver paste on two surfaces of the conductive silver paste on aperture inwall and part to be printed forms conductive path, forms the structure of antenna for mobile phone;
(4) dry 30 ~ 60 minutes at 80 ~ 150 DEG C, obtained antenna for mobile phone.
in step (1), the material of base material is selected from Merlon (PC), the mixture (wherein the mass fraction of glass fibre accounts for the 10-50% of mixture) of Merlon (PC) and glass fibre, polyamide (PA) and the mixture (wherein the mass fraction of glass fibre accounts for the 10-50% of mixture) of glass fibre or the mixture (PC/ABS) of Merlon and acrylonitrile-butadiene-styrene copolymer.
typography of the present invention is applicable to the base material (hand set machine shell or frame) of various material, and the selectable scope of base material is relatively wider, and is not limited to above-mentioned cited range of choice.
preferably, in step (2), the mode of printing is bat printing.
preferably, in step (2), the number of times of printing is 1 ~ 4 time, more preferably 3 times.
preferably, in step (3), put glue to carry out under the pressure of 3 ~ 5kg.
preferably, in step (3), the time of putting glue is 3 ~ 6 seconds.
further, with the gross weight of conductive silver paste for benchmark, conductive silver paste mixes primarily of the component of following percentage composition: modified epoxy, 10 ~ 20%; Silver powder, 50 ~ 70%; Solvent, 10 ~ 30%; Dispersant, 0.5 ~ 2%; Defoamer, 0.5 ~ 2%; Thixotropic agent, 0.5 ~ 1%; Coupling agent, 2 ~ 5%.
more preferably, solvent is one or both in ketone, esters solvent.
again preferably, ketones solvent is one or both in cyclohexanone, your ketone of different fluorine.Esters solvent is one or both in ethylene glycol ether acetate, 1-Methoxy-2-propyl acetate.
preferably, dispersant is the silane alcohol base ammonium salt of the block interpolymers of acidic-group, and defoamer is Polyether Modified Polysiloxanes Defoaming Agent.
preferably, thixotropic agent is aerosil, and coupling agent is silane coupler.
in addition, modified epoxy can be the polyurethane-modified bisphenol A type epoxy resin of thermoplastic hydroxy.
each constituent of above-mentioned conductive silver paste is directly buied from the market by commercial sources.
compared with prior art, the present invention has the following advantages: the present invention at the surperficial bat printing conductive silver paste of base material (mobile phone shell or frame on), and also prints conductive silver paste in the back side same position of mobile phone shell or frame.In addition, the position of the printing conductive silver paste in mobile phone shell or frame of the present invention has aperture, and the aperture inwall made by the mode of a glue also prints upper conductive silver paste, is coupled together by the conductive silver paste of the front and back of mobile phone shell or frame preferably.Like this, effectively can avoid the loose contact caused because of Long-Time Service of the antenna for mobile phone inserting conductive copper pin in traditional handicraft in installing hole or the shortcoming of damage, and decrease the technique of printing-ink again around copper pin.At the tow sides printing conductive inks of mobile phone frame or plastic housing, then by the mode of some glue, double-edged electrically conductive ink being connected is method more more effective than installation PIN needle.The first, reduce operation.PIN needle need not be installed, also just without the need to printing the ink of strong adhesion on PIN, decrease printing process, saving manpower, reducing cost.The second, the ink of tow sides printed antenna and all ink of some glue are all conductive silver paste, can better be connected, ensure that electric conductivity with wiring board.Thus, the typography of antenna for mobile phone of the present invention is simpler, and the stuctures and properties of antenna is more stable, and cost is lower, and efficiency is higher, has a good application prospect.
Detailed description of the invention
below in conjunction with specific embodiment, the present invention is described in further detail, so that those skilled in the art can understand the present invention better, thus more explicit defining is made to protection scope of the present invention.
embodiment 1
present embodiments provide a kind of technique of printing antenna for mobile phone, comprise the following steps successively:
(1) provide the base material of antenna for mobile phone to be printed, the material of this base material is Merlon (PC), and base material has part to be printed, and this part to be printed has relative upper surface and lower surface, and part to be printed offers the aperture at two intervals;
(2) on relative upper and lower two surfaces of part to be printed, print conductive silver paste respectively by bat printing, and print twice respectively, the thickness of the steel plate used in printing is 24 μm;
(3) glue is carried out in two holes to two surface printings in the part to be printed of conductive silver paste, glue is put 6 seconds under the pressure of 3kg, hole inwall is covered, with the structure making the conductive silver paste on two of part to be printed surfaces and the conductive silver paste on aperture inwall jointly form antenna for mobile phone by conductive silver paste;
(4) dry 60 minutes at 80 DEG C, obtained antenna for mobile phone.
wherein, with the gross weight of conductive silver paste for benchmark, it is mixed by following component: the polyurethane-modified bisphenol A type epoxy resin of thermoplastic hydroxy, 20%; Silver powder, 55%; Different fluorine that ketone, 19%; Dispersant (the silane alcohol base ammonium salt of the block interpolymers of acidic-group), 1%; Polyether Modified Polysiloxanes Defoaming Agent, 1%; Thixotropic agent (aerosil), 1%; Silane coupler, 3%.
embodiment 2
present embodiments provide a kind of technique of printing antenna for mobile phone, comprise the following steps successively:
(1) base material of antenna for mobile phone to be printed is provided, the material of this base material is the mixture (wherein the mass fraction of glass fibre accounts for the 10-50% of mixture) of Merlon (PC) and glass fibre, base material has part to be printed, this part to be printed has relative upper surface and lower surface, and part to be printed offers the aperture at two intervals;
(2) on relative upper and lower two surfaces of part to be printed, print conductive silver paste respectively by bat printing, and print 3 times respectively, the thickness of the steel plate used in printing is 25 μm;
(3) glue is carried out in two holes to two surface printings in the part to be printed of conductive silver paste, glue is put 4 seconds under the pressure of 4kg, hole inwall is covered, with the structure making the conductive silver paste on two of part to be printed surfaces and the conductive silver paste on aperture inwall jointly form antenna for mobile phone by conductive silver paste;
(4) dry 40 minutes at 100 DEG C, obtained antenna for mobile phone.
wherein, with the gross weight of conductive silver paste for benchmark, it is mixed by following component: thermoplastic hydroxy's polyurethane-epoxy resin, 10%; Silver powder, 60%; Cyclohexanone, 22%; Dispersant (the silane alcohol base ammonium salt of the block interpolymers of acidic-group), 1.5%; Polyether Modified Polysiloxanes Defoaming Agent, 1.5%; Thixotropic agent (aerosil), 1%; Silane coupler, 4%.
embodiment 3
present embodiments provide a kind of technique of printing antenna for mobile phone, comprise the following steps successively:
(1) base material of antenna for mobile phone to be printed is provided, the material of this base material is the mixture (PC/ABS) of Merlon and acrylonitrile-butadiene-styrene copolymer, base material has part to be printed, this part to be printed has relative upper surface and lower surface, and part to be printed offers the aperture at two intervals;
(2) on relative upper and lower two surfaces of part to be printed, print conductive silver paste respectively by bat printing, and print three times respectively, the thickness of the steel plate used in printing is 26 μm;
(3) glue is carried out in two holes to two surface printings in the part to be printed of conductive silver paste, glue is put 3 seconds under the pressure of 5kg, hole inwall is covered, with the structure making the conductive silver paste on two of part to be printed surfaces and the conductive silver paste on aperture inwall jointly form antenna for mobile phone by conductive silver paste;
(4) dry 30 minutes at 150 DEG C, obtained antenna for mobile phone.
wherein, with the gross weight of conductive silver paste for benchmark, it is mixed by following component: the polyurethane-modified bisphenol A type epoxy resin of thermoplastic hydroxy, 10%; Silver powder, 70%; Ethylene glycol ether acetate, 10%; Dispersant (the silane alcohol base ammonium salt of the block interpolymers of acidic-group), 2%; Polyether Modified Polysiloxanes Defoaming Agent, 2%; Thixotropic agent (aerosil), 1%; Silane coupler, 5%.
the technological operation of printing antenna for mobile phone of the present invention is easy, and production efficiency is high and cost is lower, and obtained antenna structure and performance are all more stable, and can be adapted to multiple base material (mobile phone shell or frame), applied range.
above specific embodiment of the present invention is illustrated; but protection content of the present invention is not only limited to above embodiment; in art of the present invention, the usual knowledge of a GPRS, just can carry out diversified change within the scope of its technology main idea.
Claims (9)
1. print a technique for antenna for mobile phone, it is characterized in that, comprise the following steps successively:
(1) provide the base material of antenna for mobile phone to be printed, described base material has part to be printed, and described part to be printed has relative upper surface and lower surface, and described part to be printed offers one or more hole;
(2) on relative upper and lower two surfaces of described part to be printed, conductive silver paste is printed respectively;
(3) glue is carried out to the hole that two surfaces have been printed in the part to be printed of conductive silver paste respectively, hole inwall is covered by conductive silver paste;
(4) dry 30 ~ 60 minutes at 80 ~ 150 DEG C, obtained antenna for mobile phone;
With the gross weight of conductive silver paste for benchmark, described conductive silver paste mixes primarily of following percentage composition component: modified epoxy, 10 ~ 20%; Silver powder, 50 ~ 70%; Solvent, 10 ~ 30%; Dispersant, 0.5 ~ 2%; Defoamer, 0.5 ~ 2%; Thixotropic agent, 0.5 ~ 1%; Coupling agent, 2 ~ 5%.
2. the technique of printing antenna for mobile phone according to claim 1, it is characterized in that: in step (1), the material of described base material is selected from the mixture of the mixture of Merlon, Merlon and glass fibre, polyamide and glass fibre or the mixture of Merlon and acrylonitrile-butadiene-styrene copolymer.
3. the technique of printing antenna for mobile phone according to claim 1, is characterized in that: in step (2), and the mode of printing is bat printing.
4. the technique of the printing antenna for mobile phone according to claim 1 or 3, is characterized in that: in step (2), and the number of times of printing is 1 ~ 4 time.
5. the technique of printing antenna for mobile phone according to claim 1, is characterized in that: in step (3), and some glue carries out under the pressure of 3 ~ 5kg.
6. the technique of printing antenna for mobile phone according to claim 1, is characterized in that: in step (3), and the time of some glue is 3 ~ 6 seconds.
7. the technique of printing antenna for mobile phone according to claim 1, is characterized in that: described solvent is one or both in ketone, esters solvent.
8. the technique of printing antenna for mobile phone according to claim 1, is characterized in that: described dispersant is the silane alcohol base ammonium salt of the block interpolymers of acidic-group, and described defoamer is Polyether Modified Polysiloxanes Defoaming Agent.
9. the technique of printing antenna for mobile phone according to claim 1, is characterized in that: described thixotropic agent is aerosil, and described coupling agent is silane coupler.