CN103866610A - 一种纸浆用消泡剂及其制备方法 - Google Patents

一种纸浆用消泡剂及其制备方法 Download PDF

Info

Publication number
CN103866610A
CN103866610A CN201410063493.3A CN201410063493A CN103866610A CN 103866610 A CN103866610 A CN 103866610A CN 201410063493 A CN201410063493 A CN 201410063493A CN 103866610 A CN103866610 A CN 103866610A
Authority
CN
China
Prior art keywords
defoamer
paper pulp
parts
preparation
polyethylene glycol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410063493.3A
Other languages
English (en)
Other versions
CN103866610B (zh
Inventor
邓强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Heng Kang New Material Co Ltd
Original Assignee
Suzhou Heng Kang New Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Heng Kang New Material Co Ltd filed Critical Suzhou Heng Kang New Material Co Ltd
Priority to CN201410063493.3A priority Critical patent/CN103866610B/zh
Publication of CN103866610A publication Critical patent/CN103866610A/zh
Application granted granted Critical
Publication of CN103866610B publication Critical patent/CN103866610B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种纸浆用消泡剂及其制备方法，该纸浆用消泡剂由包含以下重量份的组分制成：聚乙醚20-50份、海藻酸钠20-30份、聚氧化乙烯10-14份、十八烷醇5-10份、三油酸甘油酯4-8份和氢氧化钠0.5-2份。本发明的纸浆用消泡剂通过将上述组合物在高压均质机中混合制得，制得的消泡剂具有无毒、流动性好、使用方便、消泡效果优良等特点，可用于造纸工业中。

Description

一种纸浆用消泡剂及其制备方法
技术领域
本发明属于造纸技术领域，特别涉及一种纸浆用消泡剂及其制备方法。
背景技术
在纸浆的制造过程中，通常会用到很多助剂，如蒸煮剂、助留剂、湿强剂、施胶剂等，这些物质大都以高分子化合物为主体，在水中形成的泡沫因高分子的吸附而增强了泡膜的强度，使得消泡变得困难。
由于大多纸浆主要以植物纤维为原料，天然植物纤维素虽然含有较多的羟基，但却不溶于水，其细小纤维表面、内部都会吸附大量微小气泡，由于植物纤维的特殊结构，其上所附着的气泡用普通的消泡剂难以消除，为了生产质地均匀的高档纸张，急需能解决纤维表面和内部的气泡问题且消泡效果良好的消泡剂。 
发明内容
针对上述的需求，本发明的目的在于提供了一种纸浆用消泡剂及其制备方法，制得的消泡剂具有无毒、流动性好、使用方便、消泡效果优良，可用作造纸工业中纸浆的消泡剂。
本发明的目的可以通过以下技术方案实现：
一种纸浆用消泡剂，由包含以下重量份的组分制成：
聚乙醚                  20-50份，
海藻酸钠                20-30份，
聚氧化乙烯              10-14份，
十八烷醇                 5-10份，
三油酸甘油酯              4-8份，
氢氧化钠                 0.5-2份。
所述聚乙醚的相对分子量为2000-4000。          
所述聚氧化乙烯的相对分子量为1500-3000。        
一种纸浆用消泡剂的制备方法，该方法包括以下步骤：
（1）将聚乙醚20-50份、海藻酸钠20-30份、聚氧化乙烯10-14份、十八烷醇5-10份、三油酸甘油酯4-8份和氢氧化钠0.5-2份在45-55℃下，加入高压均质机中混合1-2小时，
（2）将步骤（1）的产物冷却至室温，用盐酸将其pH调节为6.5，得到纸浆用消泡剂。
所述高压均质机的第一段均质压力为17-20MPa，第二段均质压力为3-4.9MPa。
有益效果：
本发明采用聚乙醚、海藻酸钠、十八烷醇作为主要消泡成分，加入氢氧化钠、三油酸甘油酯和聚氧化乙烯来促进整个体系的均匀分散，由于海藻酸钠与植物纤维都具有羟基结构，并且在碱性条件下能促进各个成分的相容性和分散性，通过各个组分的一定量的添加使得该纸浆用消泡剂具有良好的消泡效果。同时，该产品无毒，且具有良好的流动性好、使用方便，可用作造纸工业中纸浆的消泡剂。
具体实施方式
以下结合实施例对本发明作进一步的说明。
消泡性能的测试方法：分别向4个带有空气鼓泡气头的 500ml 量筒内装入等量的造纸浆料，并向三个量筒中分别加入等质量的实施例1、实施例2或实施例3的产物作为消泡剂；以相同质量的十八烷醇作为对比样，放入第四个量筒中；分别记录各量筒中泡沫达到一定体积的对应时间，泡沫达到同一体积所需的时间越长，表示消泡剂的消泡性能越好，测试结果见表1。
实施例1
（1）相对分子量为2000的聚乙醚30kg、海藻酸钠20kg、相对分子量为2000的聚氧化乙烯12kg、十八烷醇7kg、三油酸甘油酯6kg和氢氧化钠1kg在55℃下，加入高压均质机中进行混合1小时，高压均质机的第一段均质压力为17MPa，第二段均质压力为3MPa，
（2）将步骤（1）的产物冷却至室温，用盐酸将其pH调节为6.5，得到纸浆用消泡剂，
制得消泡剂的性能测试结果如表1所示。
实施例2
（1）将相对分子量为4000的聚乙醚20k、海藻酸钠30kg、相对分子量为1500的聚氧化乙烯10kg、十八烷醇5kg、三油酸甘油酯4kg和氢氧化钠2kg在45℃下，加入高压均质机中混合2小时，高压均质机的第一段均质压力为20MPa，第二段均质压力为4.9Mpa，
（2）将步骤（1）的产物冷却至室温，用盐酸将其pH调节为6.5，得到纸浆用消泡剂。
制得消泡剂的性能测试结果如表1所示。
实施例3
（1）将相对分子量为3000的聚乙醚50k、海藻酸钠20kg、相对分子量为3000的聚氧化乙烯14kg、十八烷醇10kg、三油酸甘油酯8kg和氢氧化钠0.5kg在50℃下，加入高压均质机中混合2小时，高压均质机的第一段均质压力为18MPa，第二段均质压力为4MPa，
（2）将步骤（1）的产物冷却至室温，用盐酸将其pH调节为6.5，得到纸浆用消泡剂。
制得消泡剂的性能测试结果如表1所示。
表1
Figure 875988DEST_PATH_IMAGE002
     本发明制得的消泡剂具有良好的消泡效果，从表1中可以看出，35℃下的消泡效果好于25℃下的消泡效果，这是由于消泡剂的组分在温度较高时分子链的舒展性能越好，消泡效果也就越好。
本发明不限于上述实施例，本领域技术人员根据本发明的揭示，不脱离本发明范畴所做出的改进和修改都应该在本发明的保护范围之内。

Claims (5)

1.一种纸浆用消泡剂，其特征在于，由包含以下重量份的组分制成：
聚乙醚                  20-50份，
海藻酸钠                20-30份，
聚氧化乙烯              10-14份，
十八烷醇                 5-10份，
三油酸甘油酯              4-8份，
氢氧化钠                 0.5-2份。
2.根据权利要求1所述的纸浆用消泡剂，其特征在于，所述聚乙醚的相对分子量为2000-4000。
3.根据权利要求1所述的纸浆用消泡剂，其特征在于，所述聚氧化乙烯的相对分子量为1500-3000。
4.一种纸浆用消泡剂的制备方法，其特征在于，该方法包括以下步骤：
（1）将聚乙醚20-50份、海藻酸钠20-30份、聚氧化乙烯10-14份、十八烷醇5-10份、三油酸甘油酯4-8份和氢氧化钠0.5-2份在45-55℃下，加入高压均质机中混合1-2小时；
（2）将步骤（1）的产物冷却至室温，用盐酸将其pH调节为6.5，得到纸浆用消泡剂。
5.根据权利要求4所述的纸浆用消泡剂的制备方法，其特征在于，所述高压均质机的第一段均质压力为17-20MPa，第二段均质压力为3-4.9MPa。
CN201410063493.3A 2014-02-25 2014-02-25 一种纸浆用消泡剂及其制备方法 Active CN103866610B (zh)