CN103840171A - 经过钼的化合物处理的正极铝箔集流体的制备方法 - Google Patents
经过钼的化合物处理的正极铝箔集流体的制备方法 Download PDFInfo
- Publication number
- CN103840171A CN103840171A CN201410125069.7A CN201410125069A CN103840171A CN 103840171 A CN103840171 A CN 103840171A CN 201410125069 A CN201410125069 A CN 201410125069A CN 103840171 A CN103840171 A CN 103840171A
- Authority
- CN
- China
- Prior art keywords
- molybdate
- aluminium foil
- positive pole
- molybdenum
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及经过钼的化合物处理的正极铝箔集流体的制备方法，其特征在于：将铝箔用钼酸盐处理液在45℃～98℃温度区间处理1min～150min，用水冲洗干净，最后自然干燥或用70℃～180℃温度区间的热空气干燥，制得经过钼的化合物处理的正极铝箔集流体。所述的钼酸盐处理液的组成如下：钼酸盐1g/L～15g/L，氯化铵3g/L～15g/L，浓氨水2ml/L～15ml/L。制备的正极铝箔集流体在电池或超级电容器中使用时，具有耐折性好、与正极材料的粘结力强、阻抗小、充放电性能优异等优点。
Description
技术领域
本发明属于电池和超级电容器制备的技术领域，具体涉及一种可用于锂电池、锂离子电池、聚合物电池和超级电容器的经过钼的化合物处理的正极铝箔集流体的制备方法。
技术背景
锂离子电池具有电池电压高、能量密度高、无记忆效应、循环寿命长、自放电低等优点，正极材料的性能对锂离子电池的性能起着决定的作用。目前，锂离子电池主要由有机电解液（聚合物电解质）、隔膜、正极、负极、集流体等部件组成。由于锂离子电池使用的液态有机电解液(或聚合物电解质)的导电能力较弱，为了实现锂离子电池的大电流充放电性能，锂离子电池的正极材料和负极材料一般都加工成粉末状，再将正极材料的粉末或负极材料的粉末用粘合剂等粘结在集流体上，实现电流的收集。因此，对于锂离子电池来说，集流体的表面状况、集流体与正极材料和负极材料间的接触阻抗、集流体在充放电过程中表面状况变化情况对电池的性能有很大的影响。例如，充电时，锂离子电池的正极铝箔集流体容易发生钝化而增大电极的极化，使电池的充放电性能明显下降；锂离子电池的正极铝箔集流体与正极材料间粘接不牢固而出现掉粉的现象，影响电池的充放电性能和电池的安全性。
锂离子电池的正极材料的粉末与铝箔集流体粘结时，粘结部分是由被粘铝箔、粘胶剂和石墨导电剂等部分组成。其中每一部分都影响粘结性能。目前，对被粘结铝箔表面进行处理的研究较少，主要通过在锂离子电池正极的铝箔集流体上预先涂覆石墨烯或碳粉等改善铝箔的性能，以实现以下作用。如，抑制电池极化，减少热效应，提高倍率性能、降低电池内阻，明显降低循环过程的动态内阻增幅；提高电池的一致性，增加电池的循环寿命；提高活性物质与集流体的粘附力，降低极片制造成本；保护集流体不被电解液腐蚀；提高磷酸铁锂电池的高温和低温性能，改善磷酸铁锂、钛酸锂材料的加工性能。不过，上述预先在铝箔集流体上涂覆石墨烯、碳粉等方法对于改善正极铝箔集流体性能的作用有限，且制备工艺复杂、成本高，为此本发明采用简单的表面处理的方法改善锂离子电池正极铝箔集流体的表面性能，减少锂离子电池正极铝箔集流体与正极材料间的阻抗、减少正极的掉粉现象。
发明内容
为避免现有技术的不足，本发明采用简单的表面处理的方法改善电池的正极铝箔集流体的表面性能，减小正极铝箔集流体与正极材料间阻抗、减少正极的掉粉现象、改善电池的一致性，使样品的大电流放电性能明显改善。
为实现本发明的目的所采用的技术方案是:
将铝箔用钼酸盐处理液在45℃～98℃温度区间处理1min～150 min，然后用水冲洗干净，最后自然干燥或用70℃～180℃温度区间的热空气干燥，制得经过钼的化合物处理的正极铝箔集流体。
所述的钼酸盐处理液的组成如下：钼酸盐 1 g/L～15 g/L，氯化铵 3 g/L～15 g/L，浓氨水 2 ml/L～15 ml/L。
所述的浓氨水的浓度在25 w.t.%～28 w.t.%范围内。
所述的钼酸盐是钼酸钠、钼酸钾、钼酸钙、钼酸镁或钼酸铵。
经过钼的化合物处理的正极铝箔集流体在电池或超级电容器中使用时，具有耐折性好、与正极材料的粘结力强、阻抗小、充放电性能优异等优点。
具体实施方式
下面结合实施例对本发明进行进一步的说明。实施例仅是对本发明的进一步补充和说明，而不是对发明的限制。
实施例1
将铝箔用钼酸钠处理液在68℃处理10min，然后用水冲洗干净，最后自然干燥，制得经过钼的化合物处理的正极铝箔集流体。所述的钼酸钠处理液的组成如下：钼酸钠 8 g/L，氯化铵 8 g/L，25 wt.% 浓氨水 5 ml/L。经过钼的化合物处理的正极铝箔集流体对折180°后回复至原来状态记为180°，再折180°记为360°，依此类推，试验表明，经过钼的化合物处理的正极铝箔集流体连续折7200°时不会断。将3g聚偏氟乙烯树脂溶于29ml二甲基乙酰胺制备粘胶。将该粘胶涂覆在经过钼的化合物处理的正极铝箔集流体上，经过180℃加热处理10min后的剥离强度达到0.05523 N/mm2以上。当将铝箔和经过钼的化合物处理的正极铝箔分别作为锂离子电池的磷酸亚铁锂正极的集流体时，用2C倍率电流充放电时，以铝箔作为正极集流体的第1循环放电容量为91mAh/g;而以经过钼的化合物处理的铝箔作为正极集流体的第1循环放电容量为112mAh/g。
经过钼的化合物处理的正极铝箔集流体作为锂离子电池的正极集流体时，具有耐折性好、与正极材料的粘结力强、阻抗小、充放电性能优异等优点。
实施例2
将铝箔用钼酸钠处理液在98℃处理150 min，用水冲洗干净，然后自然干燥，制得经过钼的化合物处理的正极铝箔集流体。
所述的钼酸钠处理液的组成如下：钼酸钠15 g/L，氯化铵15 g/L， 28 wt.% 浓氨水15 ml/L。
经过钼的化合物处理的正极铝箔集流体作为锂离子电池的正极集流体时，具有耐折性好、与正极材料的粘结力强、阻抗小、充放电性能优异等优点。
实施例3
将铝箔用钼酸钾处理液在45℃处理1min，用水冲洗干净，然后用100℃热空气干燥，制得经过钼的化合物处理的正极铝箔集流体。
所述的钼酸钾处理液的组成如下：钼酸钾 1 g/L，氯化铵 3 g/L， 26 wt.% 浓氨水2 ml/L。
经过钼的化合物处理的正极铝箔集流体作为锂离子电池的正极集流体时，具有耐折性好、与正极材料的粘结力强、阻抗小、充放电性能优异等优点。
实施例4
将铝箔用钼酸钙处理液在98℃处理100min，用水冲洗干净，然后用180℃的热空气干燥，制得经过钼的化合物处理的正极铝箔集流体。
所述的钼酸钙处理液的组成如下：钼酸钙 5 g/L，氯化铵 5 g/L，25 wt.% 浓氨水 10 ml/L。
经过钼的化合物处理的正极铝箔集流体作为锂离子电池的正极集流体时，具有耐折性好、与正极材料的粘结力强、阻抗小、充放电性能优异等优点。
实施例5
将铝箔用钼酸钠处理液在98℃处理1min，用水冲洗干净，然后用70℃的热空气干燥，制得经过钼的化合物处理的正极铝箔集流体。
所述的钼酸钠处理液的组成如下：钼酸钠 10 g/L，氯化铵 3 g/L，28 wt.% 浓氨水15 ml/L。
经过钼的化合物处理的正极铝箔集流体作为锂离子电池的正极集流体时，具有耐折性好、与正极材料的粘结力强、阻抗小、充放电性能优异等优点。
实施例6
将铝箔用钼酸镁处理液先在55℃处理150 min，用水冲洗干净，然后用170℃的热空气干燥，制得经过钼的化合物处理的正极铝箔集流体。
所述的钼酸镁处理液的组成如下：钼酸镁 1 g/L，氯化铵15 g/L，26 wt.% 浓氨水15 ml/L。
经过钼的化合物处理的正极铝箔集流体作为锂离子电池的正极集流体时，具有耐折性好、与正极材料的粘结力强、阻抗小、充放电性能优异等优点。
实施例7
将铝箔用钼酸铵处理液先在45℃处理1min，用水冲洗干净，然后用70℃的热空气干燥，制得经过钼的化合物处理的正极铝箔集流体。
所述的钼酸铵处理液的组成如下：钼酸铵15 g/L，氯化铵 3 g/L， 28 wt.% 浓氨水2 ml/L。
经过钼的化合物处理的正极铝箔集流体作为锂离子电池的正极集流体时，具有耐折性好、与正极材料的粘结力强、阻抗小、充放电性能优异等优点。
Claims (4)
1.一种经过钼的化合物处理的正极铝箔集流体的制备方法，其特征在于将铝箔用钼酸盐处理液在45℃～98℃温度区间处理1min～150 min，用水冲洗干净，最后自然干燥或用70℃～180℃温度区间的热空气干燥，制得经过钼的化合物处理的正极铝箔集流体；
所述的钼酸盐处理液的组成如下：钼酸盐 1 g/L～15 g/L，氯化铵 3 g/L～15 g/L，浓氨水 2 ml/L～15 ml/L。
2.根据权利要求1所述的经过钼的化合物处理的正极铝箔集流体的制备方法，其特征在于所述的钼酸盐是钼酸钠、钼酸钾、钼酸钙、钼酸镁或钼酸铵。
3.根据权利要求1所述的经过钼的化合物处理的正极铝箔集流体的制备方法，其特征在于所述的浓氨水的浓度在25 w.t.%～28 w.t.%范围内。
4.根据权利要求1所述的经过钼的化合物处理的正极铝箔集流体的制备方法，其特征在于所述的经过钼的化合物处理的正极铝箔集流体用于锂电池、锂离子电池、聚合物电池或超级电容器。