CN103835042B - A kind of production technology of multicomponent fibre mixture fabric - Google Patents
A kind of production technology of multicomponent fibre mixture fabric Download PDFInfo
- Publication number
- CN103835042B CN103835042B CN201410087049.5A CN201410087049A CN103835042B CN 103835042 B CN103835042 B CN 103835042B CN 201410087049 A CN201410087049 A CN 201410087049A CN 103835042 B CN103835042 B CN 103835042B
- Authority
- CN
- China
- Prior art keywords
- mixture
- fibre
- cotton
- dyeing
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the production technology of a kind of multicomponent fibre mixture fabric, cotton is carried out mixture with regenerated celulose fibre and extraordinary ultra-fine polyester fiber, spins, be woven into fabric, finished product after dyeing and finishing is processed.Regenerated celulose fibre and ultra-fine polyester fiber mixture are the ∞ curved composite fibre of disjunctor helical coil by the present invention, in weaving process, hair times general cotton product frequently is high, looped pile will not be produced excessively lodge, affect the phenomenon of the plentiful degree of fabric outward appearance, service life is long, and fiber fluffy degree and pliability are good.
Description
Technical field
Present invention relates particularly to the production technology of a kind of multicomponent fibre mixture fabric.
Background technology
Cotton, regenerated celulose fibre (high wet modulus) and ultra-fine polyester fiber are in modulus, hydroscopicity, fracture strength and dyeing
The index aspects such as temperature, have preferable complementarity.And the material of known bedding, washing series products is based on cotton, nothing
Method has the feature of its cofibre concurrently, and this series products is during life-time service, and fiber fluffy degree and pliability are gradually reduced, impact
Comfort level that product uses and life-span.
Summary of the invention
Goal of the invention: the present invention provides the production technology of a kind of multicomponent fibre mixture fabric.
Technical scheme: the production technology of a kind of multicomponent fibre mixture fabric, by cotton and regenerated celulose fibre and special type
Ultra-fine polyester fiber carries out mixture, spins, is woven into fabric, finished product after dyeing and finishing is processed；
Concrete operation step is as follows:
1), material: the material of selection is medium staple cotton, regenerated celulose fibre and extraordinary ultra-fine polyester fiber；
2), mixed cotton: medium staple cotton, regenerated celulose fibre and extraordinary ultra-fine polyester fiber are carried out mixture, mixture according under
The parts by weight of row component are carried out: medium staple cotton 40-70 part, regenerated celulose fibre 10-20 part, polyster fibre 20-40 part；Its
In, regenerated celulose fibre and ultra-fine polyester fiber mixture are the ∞ curved composite fibre of disjunctor helical coil；
3), weaving: the end is through (medium staple cotton) * back weft (medium staple cotton) * circle warp thread (the curved composite fibre of ∞ disjunctor helical coil), warp
Weft density is 124*190*124 root/10cm, hair multiple proportions 3-9, due to the spy that " the curved composite fibre of ∞ disjunctor helical coil " is elastic
Point, it is high that hair compares general cotton product again, will not produce looped pile and excessively lodge, affect the phenomenon of the plentiful degree of fabric outward appearance；
4), dyeing:
A. dye solution formula:
X-type active red 0.2～1(is relative to fabric weight)；
Sodium bicarbonate 8～10 g L-1；
Sodium carbonate 1～3 g L-1；
Liquid measure 130～180 L；
B. concrete dyeing flow process and condition:
At room temperature, being poured in cylinder body by dyestuff and dye, the time is 30～40min → at normal temperatures, cold water wash 5～
8 minutes → hot water wash, temperature was 50～60 DEG C, the time is 5-10 minute → and soaps, temperature is 90～95 DEG C, and the time is 10-15
Minute → hot water wash, and temperature is 50～60 DEG C, the time is 5-10 minute → at normal temperatures, cold water washes 5～8 minutes.
As optimization: the concrete specification respectively knitting line in described step 3 is: the end is (thin through (medium staple cotton 29.6tex/2) * back weft
Floss cotton 36.4tex) * circle warp thread (curved composite fibre 36.4tex of ∞ disjunctor helical coil).
As optimization: in described step 4 concrete dyeing flow process and condition, the concrete formula components soaped is: soap powder
2-3g/L, detergent 1-2g/L.
As optimization: in the room temperature dyeing of described step 4 concrete dyeing flow process and condition, the consumption of dyestuff is relatively same
Class cotton product reduces 10-15% under square one.
As optimization: in the room temperature dyeing of described step 4 concrete dyeing flow process and condition, dye solution divides 3-5 time
Add, after i.e. beginning just to add, added once every 5 minutes.
Beneficial effect: regenerated celulose fibre and ultra-fine polyester fiber mixture are that ∞ disjunctor helical coil is curved mixed by the present invention
Condensating fiber, in weaving process, it is high that hair compares general cotton product again, will not produce looped pile and excessively lodge, affect fabric outward appearance
The phenomenon of plentiful degree, service life is long, and fiber fluffy degree and pliability are good.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention will be described in detail.
Specific embodiment 1:
The production technology of a kind of multicomponent fibre mixture fabric, by fine with regenerated celulose fibre and extraordinary super fine polyester for cotton
Dimension carries out mixture, spins, is woven into fabric, finished product after dyeing and finishing is processed；
Concrete operation step is as follows:
1), material: the material of selection is medium staple cotton, regenerated celulose fibre and extraordinary ultra-fine polyester fiber；
2), mixed cotton: medium staple cotton, regenerated celulose fibre and extraordinary ultra-fine polyester fiber are carried out mixture, mixture according under
The parts by weight of row component are carried out: medium staple cotton 40-70 part, regenerated celulose fibre 10-20 part, polyster fibre 20-40 part；Its
In, regenerated celulose fibre and ultra-fine polyester fiber mixture are the ∞ curved composite fibre of disjunctor helical coil；
3), weaving: the end is through (medium staple cotton) * back weft (medium staple cotton) * circle warp thread (the curved composite fibre of ∞ disjunctor helical coil), warp
Weft density is 124*190*124 root/10cm, and hair multiple proportions is 3；
4), dyeing:
A. dye solution formula:
X-type active red 0.2(is relative to fabric weight)；
Sodium bicarbonate 8g L-1；
Sodium carbonate 1g L-1；
Liquid measure 130L；
B. concrete dyeing flow process and condition:
At room temperature, being poured in cylinder body by dyestuff and dye, the time is 30min → at normal temperatures, cold water wash 5 minutes →
Hot water wash, temperature is 50 DEG C, the time is 5 minutes → soaps, temperature is 90 DEG C, and the time is 10 minutes → hot water wash, and temperature is 50
DEG C, the time is 5 minutes → at normal temperatures, and cold water washes 5 minutes.
Wherein, the concrete specification respectively knitting line in described step 3 is: the end is through (medium staple cotton 29.6tex/2) * back weft (medium staple cotton
36.4tex) * circle warp thread (curved composite fibre 36.4tex of ∞ disjunctor helical coil).
In step 4 concrete dyeing flow process and condition, the concrete formula components soaped is: soap powder 2g/L, detergent
1g/L。
In the room temperature dyeing of step 4 concrete dyeing flow process and condition, the consumption more similar cotton product of dyestuff is same
When reduce 10%.
In the room temperature dyeing of step 4 concrete dyeing flow process and condition, dye solution divides 3 additions, i.e. begins just to add
After, added once every 5 minutes.
Specific embodiment 2:
The production technology of a kind of multicomponent fibre mixture fabric, by fine with regenerated celulose fibre and extraordinary super fine polyester for cotton
Dimension carries out mixture, spins, is woven into fabric, finished product after dyeing and finishing is processed；
Concrete operation step is as follows:
1), material: the material of selection is medium staple cotton, regenerated celulose fibre and extraordinary ultra-fine polyester fiber；
2), mixed cotton: medium staple cotton, regenerated celulose fibre and extraordinary ultra-fine polyester fiber are carried out mixture, mixture according under
The parts by weight of row component are carried out: medium staple cotton 40-70 part, regenerated celulose fibre 10-20 part, polyster fibre 20-40 part；Its
In, regenerated celulose fibre and ultra-fine polyester fiber mixture are the ∞ curved composite fibre of disjunctor helical coil；
3), weaving: the end is through (medium staple cotton) * back weft (medium staple cotton) * circle warp thread (the curved composite fibre of ∞ disjunctor helical coil), warp
Weft density is 124*190*124 root/10cm, and hair multiple proportions is 9；
4), dyeing:
A. dye solution formula:
X-type active red 1(is relative to fabric weight)；
Sodium bicarbonate 10 g L-1；
Sodium carbonate 3 g L-1；
Liquid measure 180 L；
B. concrete dyeing flow process and condition:
At room temperature, being poured in cylinder body by dyestuff and dye, the time is 40min → at normal temperatures, cold water wash 8 minutes →
Hot water wash, temperature is 60 DEG C, the time is 10 minutes → soaps, temperature is 95 DEG C, and the time is 15 minutes → hot water wash, and temperature is 60
DEG C, the time is 10 minutes → at normal temperatures, and cold water washes 8 minutes.
Wherein, the concrete specification respectively knitting line in described step 3 is: the end is through (medium staple cotton 29.6tex/2) * back weft (medium staple cotton
36.4tex) * circle warp thread (curved composite fibre 36.4tex of ∞ disjunctor helical coil).
In step 4 concrete dyeing flow process and condition, the concrete formula components soaped is: soap powder 3g/L, detergent
2g/L。
In the room temperature dyeing of step 4 concrete dyeing flow process and condition, the consumption more similar cotton product of dyestuff is same
When reduce 15%.
In the room temperature dyeing of step 4 concrete dyeing flow process and condition, dye solution divides 5 additions, i.e. begins just to add
After, added once every 5 minutes.
Specific embodiment 3:
The production technology of a kind of multicomponent fibre mixture fabric, by fine with regenerated celulose fibre and extraordinary super fine polyester for cotton
Dimension carries out mixture, spins, is woven into fabric, finished product after dyeing and finishing is processed；
Concrete operation step is as follows:
1), material: the material of selection is medium staple cotton, regenerated celulose fibre and extraordinary ultra-fine polyester fiber；
2), mixed cotton: medium staple cotton, regenerated celulose fibre and extraordinary ultra-fine polyester fiber are carried out mixture, mixture according under
The parts by weight of row component are carried out: medium staple cotton 40-70 part, regenerated celulose fibre 10-20 part, polyster fibre 20-40 part；Its
In, regenerated celulose fibre and ultra-fine polyester fiber mixture are the ∞ curved composite fibre of disjunctor helical coil；
3), weaving: the end is through (medium staple cotton) * back weft (medium staple cotton) * circle warp thread (the curved composite fibre of ∞ disjunctor helical coil), warp
Weft density is 124*190*124 root/10cm, and hair multiple proportions is 5；
4), dyeing:
A. dye solution formula:
X-type active red 0.7(is relative to fabric weight)；
Sodium bicarbonate 9g L-1；
Sodium carbonate 2g L-1；
Liquid measure 160L；
B. concrete dyeing flow process and condition:
At room temperature, being poured in cylinder body by dyestuff and dye, the time is 35min → at normal temperatures, cold water wash 7 minutes →
Hot water wash, temperature is 55 DEG C, the time is 8 minutes → soaps, temperature is 93 DEG C, and the time is 13 minutes → hot water wash, and temperature is 58
DEG C, the time is 8 minutes → at normal temperatures, and cold water washes 6 minutes.
Wherein, the concrete specification respectively knitting line in described step 3 is: the end is through (medium staple cotton 29.6tex/2) * back weft (medium staple cotton
36.4tex) * circle warp thread (curved composite fibre 36.4tex of ∞ disjunctor helical coil).
In step 4 concrete dyeing flow process and condition, the concrete formula components soaped is: soap powder 2.5g/L, detergent
1.5g/L。
In the room temperature dyeing of step 4 concrete dyeing flow process and condition, the consumption more similar cotton product of dyestuff is same
When reduce 13%.
In the room temperature dyeing of step 4 concrete dyeing flow process and condition, dye solution divides 4 additions, i.e. begins just to add
After, added once every 5 minutes.
Claims (5)
1. the production technology of a multicomponent fibre mixture fabric, it is characterised in that: by cotton and regenerated celulose fibre and special type
Ultra-fine polyester fiber carries out mixture, spins, is woven into fabric, finished product after dyeing and finishing is processed；Concrete operation step is as follows:
1), material: the material of selection is medium staple cotton, regenerated celulose fibre and extraordinary ultra-fine polyester fiber；
2), mixed cotton: regenerated celulose fibre and extraordinary ultra-fine polyester fiber are carried out resultant yarn after mixture, then with fine fleece cotton yarn mixture
Weaving, mixture is carried out according to the parts by weight of following component: medium staple cotton 40-70 part, regenerated celulose fibre 10-20 part, terylene
Fiber 20-40 part；Wherein, regenerated celulose fibre and ultra-fine polyester fiber mixture are the ∞ curved composite fibre of disjunctor helical coil；
3), weaving: through * medium staple cotton back weft * ∞ disjunctor helical coil curved composite fibre circle warp thread at the bottom of medium staple cotton, thread count is
124*190*124 root/10cm, hair multiple proportions 3-9；
4), dyeing:
A. dye solution formula:
B. concrete dyeing flow process and condition:
At room temperature, dyestuff to be poured in cylinder body and dyes, the time is 30～40min → at normal temperatures, cold water washes 5～8 points
Clock → hot water wash, temperature is 50～60 DEG C, the time is 5-10 minute → soaps, temperature is 90～95 DEG C, and the time is 10-15 minute
→ hot water wash, temperature is 50～60 DEG C, the time is 5-10 minute → at normal temperatures, cold water washes 5～8 minutes.
The production technology of multicomponent fibre mixture fabric the most according to claim 1, it is characterised in that: in described step 3
The concrete specification respectively knitting line is: through the 29.6tex/2* medium staple cotton back weft 36.4tex* ∞ curved mixing of disjunctor helical coil at the bottom of medium staple cotton
Fibrous loop warp thread 36.4tex.
The production technology of multicomponent fibre mixture fabric the most according to claim 1, it is characterised in that: described step 4 has
In body dyeing flow process and condition, the concrete formula components soaped is: soap powder 2-3g/L, detergent 1-2g/L.
The production technology of multicomponent fibre mixture fabric the most according to claim 1, it is characterised in that: described step 4 has
In the room temperature dyeing of body dyeing flow process and condition, the consumption more similar cotton product of dyestuff reduces 10-under square one
15%.
The production technology of multicomponent fibre mixture fabric the most according to claim 1, it is characterised in that: described step 4 has
In the room temperature dyeing of body dyeing flow process and condition, dye solution divides 3-5 addition, after i.e. beginning just to add, adds every 5 minutes
Enter once.