CN103834770A - 高速钢的热处理工艺 - Google Patents

高速钢的热处理工艺 Download PDF

Info

Publication number
CN103834770A
CN103834770A CN201210491974.5A CN201210491974A CN103834770A CN 103834770 A CN103834770 A CN 103834770A CN 201210491974 A CN201210491974 A CN 201210491974A CN 103834770 A CN103834770 A CN 103834770A
Authority
CN
China
Prior art keywords
preheating
treatment process
temperature
carry out
quenching
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210491974.5A
Other languages
English (en)
Inventor
李新栋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DALIAN QIANBAO CAST IRON FOUNDRY Co Ltd
Original Assignee
DALIAN QIANBAO CAST IRON FOUNDRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DALIAN QIANBAO CAST IRON FOUNDRY Co Ltd filed Critical DALIAN QIANBAO CAST IRON FOUNDRY Co Ltd
Priority to CN201210491974.5A priority Critical patent/CN103834770A/zh
Publication of CN103834770A publication Critical patent/CN103834770A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高速钢的热处理工艺，包括以下步骤：A、进行退火处理，退火保温时间应在3-4h以上；B、进行淬火处理，淬火时进行1-3次预热；C、进行高温回火处理。本发明高速钢的热处理工艺，在淬火过程中进行三次预热，保证了淬火的工艺要求，增强了材料的冲击韧性，进行三次回火处理，使回火更加充分。

Description

高速钢的热处理工艺
技术领域
本发明涉及一种高速钢的热处理工艺。
背景技术
现有技术中，高速钢的热处理工艺淬火温度过高，产生过热，其特点是晶粒粗大碳化物溶解多，溶解充分，数量少，奥氏体合金化程度高，淬火、回火后工件有较高的硬度和热硬性，但碳化物溶解同时晶粒长大，降低材料的冲击韧性，增加了脆性，刀具使用时容易崩裂，回火不充分，回火过程新产生的马氏体引起内应力不能得到消除，有时材料硬度较难反应，但其脆性较大，使用时容易发生刀具崩刃或开裂，有资料表明，回火不足的高速钢抗拉强度和挠度也达不到最满意的水平。
发明内容
本发明的目的是提供一种高速钢的热处理工艺。
本发明为实现上述目的所采用的技术方案是：一种高速钢的热处理工艺，其特征在于：包括以下步骤：
A、进行退火处理，退火保温时间应在3-4h以上；
B、进行淬火处理，淬火时进行1-3次预热；
C、进行高温回火处理。
所述步骤B中，第一次预热为低温预热，低温预热温度为450-500°C，保温1-1.5min/mm。
所述步骤B中，第二次预热为中温预热，中温预热温度为800-850°C，保温0.4-1.0min/mm。
所述步骤B中，第三次预热为高温预热，高温预热温度为1050-1100°C。
所述步骤C中至少进行三次回火处理。
本发明一种高速钢的热处理工艺，在淬火过程中进行三次预热，保证了淬火的工艺要求，增强了材料的冲击韧性，进行三次回火处理，使回火更加充分。
具体实施方式
高速钢的热处理工艺，高速钢的热处理工艺，包括以下步骤：A、进行退火处理，退火保温时间应在3-4h以上，保温后可采用10-20°C/小时的速度冷却至500°C以下出炉，也可冷却至740-760°C停留4-6h，在冷却到600°C以下出炉的等温退火方式；B、进行淬火处理，淬火时进行1-3次预热，步骤B中，第一次预热为低温预热，低温预热温度为450-500°C，保温1-1.5min/mm，步骤B中，第二次预热为中温预热，中温预热温度为800-850°C，保温0.4-1.0min/mm；C、进行高温回火处理，步骤C中至少进行三次回火处理，第一次回火只能是对淬火马氏体起到回火的作用；第二次回火才能对马氏体得到回火，并消除内应力和减少脆性；第三次回火硬度不降反升，本发明高速钢的热处理工艺，在淬火过程中进行三次预热，保证了淬火的工艺要求，增强了材料的冲击韧性，进行三次回火处理，使回火更加充分。

Claims (5)

1.一种高速钢的热处理工艺，其特征在于：包括以下步骤：
A、进行退火处理，退火保温时间应在3-4h以上；
B、进行淬火处理，淬火时进行1-3次预热；
C、进行高温回火处理。
2.根据权利要求1所述的一种高速钢的热处理工艺，其特征在于：所述步骤B中，第一次预热为低温预热，低温预热温度为450-500°C，保温1-1.5min/mm。
3.根据权利要求1所述的一种高速钢的热处理工艺，其特征在于：所述步骤B中，第二次预热为中温预热，中温预热温度为800-850°C，保温0.4-1.0min/mm。
4.根据权利要求1所述的一种高速钢的热处理工艺，其特征在于：所述步骤B中，第三次预热为高温预热，高温预热温度为1050-1100°C。
5.根据权利要求1所述的一种高速钢的热处理工艺，其特征在于：所述步骤C中至少进行三次回火处理。
CN201210491974.5A 2012-11-28 2012-11-28 高速钢的热处理工艺 Pending CN103834770A (zh)