CN103833394B - 中间包涂料 - Google Patents

中间包涂料 Download PDF

Info

Publication number
CN103833394B
CN103833394B CN201410009524.7A CN201410009524A CN103833394B CN 103833394 B CN103833394 B CN 103833394B CN 201410009524 A CN201410009524 A CN 201410009524A CN 103833394 B CN103833394 B CN 103833394B
Authority
CN
China
Prior art keywords
magnesia
coating
tundish
granularity
tundish paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410009524.7A
Other languages
English (en)
Other versions
CN103833394A (zh
Inventor
李开胜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGXING MINGSHENG METALLURGICAL FURNACE CHARGE Co Ltd
Original Assignee
CHANGXING MINGSHENG METALLURGICAL FURNACE CHARGE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGXING MINGSHENG METALLURGICAL FURNACE CHARGE Co Ltd filed Critical CHANGXING MINGSHENG METALLURGICAL FURNACE CHARGE Co Ltd
Priority to CN201410009524.7A priority Critical patent/CN103833394B/zh
Publication of CN103833394A publication Critical patent/CN103833394A/zh
Application granted granted Critical
Publication of CN103833394B publication Critical patent/CN103833394B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及中间包涂料，由以下重量百分比的组分组成：2～3mm镁砂11.8～13.7%、1～2mm镁砂13.5～15.6%、0.5～1mm镁砂13.6～16.1%、0～0.5mm镁砂15.9～17.8%、180目的镁砂30～40%、硅微粉2.75～3.25%、广西泥0.26～0.35%、木质素磺酸钙0.27～0.36%、三聚磷酸钠0.48～0.67%、纸纤维0.99～1.38%、矾土水泥0.45～0.64%、金属铝粉0～0.15%；本发明的优点：通过上述组分混合制成的中间包涂料具有良好的保温性能和使用寿命，能适应浇铸钢的品种变化和浇铸同一种钢的产量的浇注，降低涂料的热导率，改善涂料的施工性能。

Description

中间包涂料
技术领域
本发明涉及中间包涂料。
背景技术
在钢水供应十分充足的建筑钢等品种的生产中，特别是在水口能在线快速更换的条件下，需要的中间包具有使用寿命长等特点，现有的中间包通过高性能的镁质预制件、镁质涂料及镁铝铬质涂料等原料来提高使用寿命，随着中间包冶金技术的发展，优质钢和特殊钢的比例增加，受浇铸钢的品种变化和浇铸同一种钢的产量限制导致对中间包的使用寿命要求不高，而无法满足浇注钢质量，需要对中间包具有良好的保温效果。
发明内容
本发明要解决的技术问题现有中间包的保温效果差导致浇注钢质量差，从而提供中间包涂料。
为了解决上述技术问题，本发明是通过以下技术方案实现的：中间包涂料，由以下重量百分比的组分组成：2～3mm镁砂11.8～13.7%、1～2mm镁砂13.5～15.6%、0.5～1mm镁砂13.6～16.1%、0～0.5mm镁砂15.9～17.8%、粒度为180目的镁砂30～40%、硅微粉2.75～3.25%、广西泥0.26～0.35%、木质素磺酸钙0.27～0.36%、三聚磷酸钠0.48～0.67%、纸纤维0.99～1.38%、矾土水泥0.45～0.64%、金属铝粉0～0.15%。
优选的，由以下重量百分比的组分组成：2～3mm镁砂13.7%、1～2mm镁砂15.6%、0.5～1mm镁砂16.1%、0～0.5mm镁砂17.8%、粒度为180目的镁砂30%、硅微粉3.25%、广西泥0.35%、木质素磺酸钙0.36%、三聚磷酸钠0.67%、纸纤维1.38%、矾土水泥0.64%、金属铝粉0.15%，通过上述组分比例混合后的涂料具有保温性能好，稳定性能好，能有效的降低涂料的热导率，改善涂料的施工性能，保证了涂料不受温度限制及操作限制，生产成本低。
优选的，由以下重量百分比的组分组成：2～3mm镁砂13%、1～2mm镁砂15%、0.5～1mm镁砂15%、0～0.5mm镁砂17%、粒度为180目的镁砂34%、硅微粉3%、广西泥0.3%、木质素磺酸钙0.3%、三聚磷酸钠0.6%、纸纤维1.2%、矾土水泥0.5%、金属铝粉0.1%，通过上述组分比例混合后的涂料具有保温性能好，稳定性能好，能有效的降低涂料的热导率，改善涂料的施工性能，保证了涂料不受温度限制及操作限制，生产成本低。
优选的，由以下重量百分比的组分组成：2～3mm镁砂11.8%、1～2mm镁砂13.5%、0.5～1mm镁砂13.6%、0～0.5mm镁砂15.9%、粒度为180目的镁砂40%、硅微粉2.75%、广西泥0.26%、木质素磺酸钙0.27%、三聚磷酸钠0.48%、纸纤维0.99%、矾土水泥0.45%，通过上述组分比例混合后的涂料具有保温性能好，稳定性能好，能有效的降低涂料的热导率，改善涂料的施工性能，保证了涂料不受温度限制及操作限制，生产成本低。
优选的,粒度为180目的镁砂中MgO的含量为95%，MgO能很好的抵抗钢水渣的侵蚀，提高中间包的使用寿命。
综上所述，本发明的优点：将2～3mm镁砂、1～2mm镁砂、0.5～1mm镁砂、0～0.5mm镁砂、粒度为180目的镁砂、硅微粉、广西泥、木质素磺酸钙、三聚磷酸钠、纸纤维、矾土水泥、金属铝粉混合制成的中间包涂料具有良好的保温性能和使用寿命，能适应浇铸钢的品种变化和浇铸同一种钢的产量的浇注，能有效的降低涂料的热导率，改善涂料的施工性能，保证了涂料不受温度限制及操作限制，生产成本低。
具体实施方式
实施例一：
中间包涂料，由以下重量百分比的组分组成：2～3mm镁砂13.7%、1～2mm镁砂15.6%、0.5～1mm镁砂16.1%、0～0.5mm镁砂17.8%、粒度为180目的镁砂30%、硅微粉3.25%、广西泥0.35%、木质素磺酸钙0.36%、三聚磷酸钠0.67%、纸纤维1.38%、矾土水泥0.64%、金属铝粉0.15%。
实施例二：
中间包涂料，由以下重量百分比的组分组成：2～3mm镁砂13%、1～2mm镁砂15%、0.5～1mm镁砂15%、0～0.5mm镁砂17%、粒度为180目的镁砂34%、硅微粉3%、广西泥0.3%、木质素磺酸钙0.3%、三聚磷酸钠0.6%、纸纤维1.2%、矾土水泥0.5%、金属铝粉0.1%。
实施例三：
中间包涂料，由以下重量百分比的组分组成：2～3mm镁砂11.8%、1～2mm镁砂13.5%、0.5～1mm镁砂13.6%、0～0.5mm镁砂15.9%、粒度为180目的镁砂40%、硅微粉2.75%、广西泥0.26%、木质素磺酸钙0.27%、三聚磷酸钠0.48%、纸纤维0.99%、矾土水泥0.45%。
粒度为180目的镁砂中MgO的含量为95%，MgO能很好的抵抗钢水渣的侵蚀，提高中间包的使用寿命。
将2～3mm镁砂、1～2mm镁砂、0.5～1mm镁砂、0～0.5mm镁砂、粒度为180目的镁砂、硅微粉、广西泥、木质素磺酸钙、三聚磷酸钠、纸纤维、矾土水泥、金属铝粉混合制成的中间包涂料具有良好的保温性能和使用寿命，能适应浇铸钢的品种变化和浇铸同一种钢的产量的浇注，能有效的降低涂料的热导率，改善涂料的施工性能，保证了涂料不受温度限制及操作限制，生产成本低。

Claims (5)

1.中间包涂料，其特征在于：由以下重量百分比的组分组成：2～3mm镁砂11.8～13.7%、1～2mm镁砂13.5～15.6%、0.5～1mm镁砂13.6～16.1%、0～0.5mm镁砂15.9～17.8%、粒度为180目的镁砂30～40%、硅微粉2.75～3.25%、广西泥0.26～0.35%、木质素磺酸钙0.27～0.36%、三聚磷酸钠0.48～0.67%、纸纤维0.99～1.38%、矾土水泥0.45～0.64%、金属铝粉0～0.15%。
2.根据权利要求1所述的中间包涂料，其特征在于：由以下重量百分比的组分组成：2～3mm镁砂13.7%、1～2mm镁砂15.6%、0.5～1mm镁砂16.1%、0～0.5mm镁砂17.8%、粒度为180目的镁砂30%、硅微粉3.25%、广西泥0.35%、木质素磺酸钙0.36%、三聚磷酸钠0.67%、纸纤维1.38%、矾土水泥0.64%、金属铝粉0.15%。
3.根据权利要求1所述的中间包涂料，其特征在于：由以下重量百分比的组分组成：2～3mm镁砂13%、1～2mm镁砂15%、0.5～1mm镁砂15%、0～0.5mm镁砂17%、粒度为180目的镁砂34%、硅微粉3%、广西泥0.3%、木质素磺酸钙0.3%、三聚磷酸钠0.6%、纸纤维1.2%、矾土水泥0.5%、金属铝粉0.1%。
4.根据权利要求1所述的中间包涂料，其特征在于：由以下重量百分比的组分组成：2～3mm镁砂11.8%、1～2mm镁砂13.5%、0.5～1mm镁砂13.6%、0～0.5mm镁砂15.9%、粒度为180目的镁砂40%、硅微粉2.75%、广西泥0.26%、木质素磺酸钙0.27%、三聚磷酸钠0.48%、纸纤维0.99%、矾土水泥0.45%。
5.根据权利要求1至4任一项所述的中间包涂料，其特征在于：粒度为180目的镁砂中MgO的含量为95%。
CN201410009524.7A 2014-01-08 2014-01-08 中间包涂料 Expired - Fee Related CN103833394B (zh)