CN103831735A - 一种陶瓷铬刚玉砂轮 - Google Patents

一种陶瓷铬刚玉砂轮 Download PDF

Info

Publication number
CN103831735A
CN103831735A CN201410047990.4A CN201410047990A CN103831735A CN 103831735 A CN103831735 A CN 103831735A CN 201410047990 A CN201410047990 A CN 201410047990A CN 103831735 A CN103831735 A CN 103831735A
Authority
CN
China
Prior art keywords
parts
powder
emery wheel
grinding wheel
sodium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410047990.4A
Other languages
English (en)
Inventor
胡光胜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DANGTU COUNTY NANFANG HONGYUE GRINDING TOOL ABRASIVES Co Ltd
Original Assignee
DANGTU COUNTY NANFANG HONGYUE GRINDING TOOL ABRASIVES Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DANGTU COUNTY NANFANG HONGYUE GRINDING TOOL ABRASIVES Co Ltd filed Critical DANGTU COUNTY NANFANG HONGYUE GRINDING TOOL ABRASIVES Co Ltd
Priority to CN201410047990.4A priority Critical patent/CN103831735A/zh
Publication of CN103831735A publication Critical patent/CN103831735A/zh
Pending legal-status Critical Current

Abstract

本发明涉及砂轮制造技术领域，具体涉及一种陶瓷铬刚玉砂轮及其生产工艺，该砂轮由以下重量份的原料制成：铬刚玉磨料40-45、白刚玉磨料34-38、玄武岩纤维4-5、石蜡3-4、V2O52-3、CuO1-2、Bi2O32-3、三聚磷酸钠5-6、海藻酸钠3-4、助剂7-9；本发明砂轮采用V2O5、CuO、Bi2O3以及玄武岩纤维等原料制成的陶瓷结合剂，具有化学性能稳定，高强度耐磨，质轻柔韧、热膨胀系数小等优点，再结合三聚磷酸钠、石蜡等原料，使得结合剂与磨料的把持强度大，粘结牢固，本发明制备的铬刚玉砂轮具有良好的磨削性能，较传统铬刚玉砂轮经久耐用。

Description

一种陶瓷铬刚玉砂轮
技术领域
本发明涉及砂轮制造技术领域，具体涉及一种陶瓷铬刚玉砂轮及其生产工艺。
背景技术
砂轮是磨具中使用范围最为广泛的一种工具，主要对金属或非金属工件的型面进行粗磨、半精磨、精磨以及开槽、切断等处理，在使用时处于高速旋转状态，需要承受较大的冲击力，因此对砂轮的强度、抗冲击性、耐热性以及抗腐性能等均有较高的要求；砂轮主要由磨料和结合剂经压坯、干燥、焙烧制成，磨料的种类多种多样，常见的主要有刚玉、碳化硅、金刚石以及立方氮化硼等，这些磨料都有着良好的硬度以及一定的韧性，而其强度、抗冲击性、耐热性以及抗腐性能均取决于结合剂，常见的结合剂为树脂结合剂、陶瓷结合剂、橡胶结合剂以及金属结合剂，各结合剂均有不同的特性，在实际应用中应根据砂轮工件使用条件，选择合适的结合剂，以增强磨料粘结牢固强度，提高磨具强度，改善磨削性能，赋予砂轮良好的使用性能。
发明内容
本发明的目的在于，提供一种陶瓷铬刚玉砂轮，以改善传统铬刚玉砂轮的磨削性能，为了实现上述目的，本发明采用的技术方案如下：
一种陶瓷铬刚玉砂轮，其特征在于，本发明砂轮由以下重量份的原料制成：铬刚玉磨料40-45、白刚玉磨料34-38、玄武岩纤维4-5、石蜡3-4、V2O52-3、CuO1-2、Bi2O32-3、三聚磷酸钠5-6、海藻酸钠3-4、助剂7-9。
所述的助剂由以下重量份的原料制成：冰晶石15-20、铝酸钙6-8、木质素磺酸钠2-3、纸浆废液6-8、硅酸铝3-4、铁粉10-12、锰粉2-3、膨润土22-25、粘土粉25-28、白垩12-15，制备方法如下：先将冰晶石、铝酸钙、硅酸铝、膨润土、粘土粉、白垩充分混合均匀后，在2200-2300℃下保温2-3h，经自然冷却后，球磨至200-300目粉体，再将木质素磺酸钠与适量的水混合，搅拌至木质素磺酸钠完全溶解后，加入上述粉体及其它剩余成分，球磨3-4h，烘干、即得。
所述磨料的粒径为80-200目。
所述的一种陶瓷铬刚玉砂轮，其生产工艺如下：
（1）将V2O5、CuO、Bi2O3混合，加热至800-900℃搅拌10-12min，随后自然冷却至室温，球磨至200-300目粉体后，加入玄武岩纤维、助剂，充分搅拌均匀备用；
（2）将三聚磷酸钠与适量的水混合，搅拌至三聚磷酸钠完全溶解即可，再加入石蜡、海藻酸钠，混合搅拌15-20min，加入其它剩余物料，充分混合后备用；
（3）将步骤（1）与步骤（2）所得的物料混合，混合均匀后送入模具中压制成型，成型条件：模具设定温度80-90℃，在45-50MPa条件下保压5-6min，出模得胚体；
（4）将胚体进行烧结处理，胚体先在15-20min内升温至350-380℃，保温4-6小时，再按10-15℃/min升温至1200-1440℃，保温10-12小时后取出，自然冷却后即得。
本发明的优点在于：采用V2O5、CuO、Bi2O3以及玄武岩纤维等原料制成的陶瓷结合剂，具有化学性能稳定，高强度耐磨，质轻柔韧、热膨胀系数小等优点，再结合三聚磷酸钠、石蜡等原料，使得结合剂与磨料的把持强度大，粘结牢固，本发明制备的铬刚玉砂轮具有良好的磨削性能，较传统铬刚玉砂轮经久耐用。
具体实施方式
实施例1
本实施例砂轮由以下重量份原料制成：铬刚玉磨料45、白刚玉磨料38、玄武岩纤维4、石蜡3、V2O53、CuO1、Bi2O33、三聚磷酸钠6、海藻酸钠3、助剂7。
助剂由以下重量份的原料制成：冰晶石20、铝酸钙8、木质素磺酸钠2、纸浆废液6、硅酸铝4、铁粉10、锰粉3、膨润土25、粘土粉25、白垩15，制备方法如下：先将冰晶石、铝酸钙、硅酸铝、膨润土、粘土粉、白垩充分混合均匀后，在2300℃下保温2h，经自然冷却后，球磨至300目粉体，再将木质素磺酸钠与适量的水混合，搅拌至木质素磺酸钠完全溶解后，加入上述粉体及其它剩余成分，球磨3h，烘干、即得。
所述磨料的粒径均为80目。
所述的一种陶瓷铬刚玉砂轮，其生产工艺如下：
（1）将V2O5、CuO、Bi2O3混合，加热至900℃搅拌10min，随后自然冷却至室温，球磨至300目粉体后，加入玄武岩纤维、助剂，充分搅拌均匀备用；
（2）将三聚磷酸钠与适量的水混合，搅拌至三聚磷酸钠完全溶解即可，再加入石蜡、海藻酸钠，混合搅拌20min，加入其它剩余物料，充分混合后备用；
（3）将步骤（1）与步骤（2）所得的物料混合，混合均匀后送入模具中压制成型，成型条件：模具设定温度90℃，在50MPa条件下保压5min，出模得胚体；
（4）将胚体进行烧结处理，胚体先在20min内升温至350℃，保温6小时，再按15℃/min升温至1440℃，保温10小时后取出，自然冷却后即得。
实施例2
本实施例砂轮由以下重量份原料制成：铬刚玉磨料45、白刚玉磨料34、玄武岩纤维5、石蜡4、V2O52、CuO2、Bi2O32、三聚磷酸钠5、海藻酸钠4、助剂9。
助剂由以下重量份的原料制成：冰晶石15、铝酸钙6、木质素磺酸钠3、纸浆废液8、硅酸铝3、铁粉12、锰粉2、膨润土22、粘土粉28、白垩12，制备方法如下：先将冰晶石、铝酸钙、硅酸铝、膨润土、粘土粉、白垩充分混合均匀后，在2200℃下保温3h，经自然冷却后，球磨至200目粉体，再将木质素磺酸钠与适量的水混合，搅拌至木质素磺酸钠完全溶解后，加入上述粉体及其它剩余成分，球磨4h，烘干、即得。
所述磨料的粒径均为200目。
所述的一种陶瓷铬刚玉砂轮，其生产工艺如下：
（1）将V2O5、CuO、Bi2O3混合，加热至800℃搅拌12min，随后自然冷却至室温，球磨至200目粉体后，加入玄武岩纤维、助剂，充分搅拌均匀备用；
（2）将三聚磷酸钠与适量的水混合，搅拌至三聚磷酸钠完全溶解即可，再加入石蜡、海藻酸钠，混合搅拌15min，加入其它剩余物料，充分混合后备用；
（3）将步骤（1）与步骤（2）所得的物料混合，混合均匀后送入模具中压制成型，成型条件：模具设定温度80℃，在45MPa条件下保压6min，出模得胚体；
（4）将胚体进行烧结处理，胚体先在15min内升温至380℃，保温4小时，再按10℃/min升温至1200℃，保温12小时后取出，自然冷却后即得。
上述实施例砂轮测试得到的技术指标如下：
Figure BDA0000464933710000041
砂轮的性能测试均遵循相关标准进行，测试中被磨削材料为工具钢，磨削方式为横向磨削，砂轮圆周速度：25m/s，工作台速度：0.05m/s，磨削深度：0.025mm。本发明制备的砂轮较普通铬刚玉砂轮的硬度、磨削性能等均获得提高，磨削比提高14-17%，实际使用时修整间隔时间延长4-5倍，使用寿命延长6-8倍。

Claims (3)

1.一种陶瓷铬刚玉砂轮，其特征在于，该砂轮由以下重量份的原料制成：铬刚玉磨料40-45、白刚玉磨料34-38、玄武岩纤维4-5、石蜡3-4、V2O5 2-3、CuO 1-2、Bi2O3 2-3、三聚磷酸钠5-6、海藻酸钠3-4、助剂7-9；
所述的助剂由以下重量份的原料制成：冰晶石15-20、铝酸钙6-8、木质素磺酸钠2-3、纸浆废液6-8、硅酸铝3-4、铁粉10-12、锰粉2-3、膨润土22-25、粘土粉25-28、白垩12-15，制备方法如下：先将冰晶石、铝酸钙、硅酸铝、膨润土、粘土粉、白垩充分混合均匀后，在2200-2300℃下保温2-3h，经自然冷却后，球磨至200-300目粉体，再将木质素磺酸钠与适量的水混合，搅拌至木质素磺酸钠完全溶解后，加入上述粉体及其它剩余成分，球磨3-4h，烘干、即得。
2.如权利要求1所述的一种陶瓷铬刚玉砂轮，其特征在于，所述磨料的粒径为80-200目。
3.如权利要求1所述的一种陶瓷铬刚玉砂轮，其工艺如下：
（1）将V2O5、CuO、Bi2O3混合，加热至800-900℃搅拌10-12min，随后自然冷却至室温，球磨至200-300目粉体后，加入玄武岩纤维、助剂，充分搅拌均匀备用；
（2）将三聚磷酸钠与适量的水混合，搅拌至三聚磷酸钠完全溶解即可，再加入石蜡、海藻酸钠，混合搅拌15-20min，加入其它剩余物料，充分混合后备用；
（3）将步骤（1）与步骤（2）所得的物料混合，混合均匀后送入模具中压制成型，成型条件：模具设定温度80-90℃，在45-50MPa条件下保压5-6min，出模得胚体；
（4）将胚体进行烧结处理，胚体先在15-20min内升温至350-380℃，保温4-6小时，再按10-15℃/min升温至1200-1440℃，保温10-12小时后取出，自然冷却后即得。
CN201410047990.4A 2014-02-11 2014-02-11 一种陶瓷铬刚玉砂轮 Pending CN103831735A (zh)