CN1038263A - 二次浇注用的环氧树脂水泥沙浆 - Google Patents
二次浇注用的环氧树脂水泥沙浆 Download PDFInfo
- Publication number
- CN1038263A CN1038263A CN 89105042 CN89105042A CN1038263A CN 1038263 A CN1038263 A CN 1038263A CN 89105042 CN89105042 CN 89105042 CN 89105042 A CN89105042 A CN 89105042A CN 1038263 A CN1038263 A CN 1038263A
- Authority
- CN
- China
- Prior art keywords
- resins
- epoxy
- pouring
- cement mortar
- diamino
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种新的建筑材料，具体地说，它是
大中型机械设备基础二次浇注用的环氧树脂水泥沙
浆。
本发明提供的配方组成包括环氧树脂、水泥、河
沙及一定量的稀释剂及固化剂。依据本发明提供的
配方所制得的环氧树脂水泥沙浆，具有优良的粘结性
能，较高的稳定性及抗震能力。特别对高频率、大振
幅，对基础要求严格的设备适应性特别强。本发明适
用于石油、化工、钢铁、煤炭、发电等部门大中型机械
设备基础的二次浇注。
Description
本发明提供的环氧树脂水泥沙浆是用来浇注大中型机械设备基础的二次浇注材料，属于建筑材料类产品。
目前国内大中型机械设备基础的二次浇注一般都使用普通水泥沙浆，由于其本身抗压强度低（120Kg/Cm2），粘接力较差，对酸、碱及各种油品的抗腐蚀能力弱，高温下易变形的缺点，这时对基础要求特别严格、振动频率快、振幅较大的大型机械设备，很不适应，使沙浆层迅速疲劳破坏，局部开裂，松动脱落，而使设备振动地愈加厉害，只能长时间低速动转。这既抑制设备功率的发挥，又影响了设备的使用寿命。基础损坏严重的只能停机，拆毁基础，重新施工。不但影响生产的正常进行，而且浪费大量原材料，使生产成本上升。
苏联专利SU2465775叙述了一种用来添补混凝土裂缝的环氧树脂混合物，以增加裂缝的耐热力及应力抗阻。其组成是环氧树脂、胺交联、矿物添加剂、低分子聚乙丁烯。
日本专利JP7966878叙述了一种用于安装螺丝到地面基座的树脂混合物，其组成是环氧树脂、丙烯酸盐、脂类、水泥及表面活性剂。
日本专利JP8447218叙述了一种可以修复因盐类腐蚀而造成强化混凝土结构损坏的合成树脂表面活性剂聚合物。
因此上述现有技术的专利均没有提出或建议含有环氧树脂的组合物用于大中型机械设备基础的二次浇注。
本发明的目的就是克服现有技术及先有专利技术的不足之处而选择一种抗压、抗震、粘结性能好，承受破坏载荷高，耐酸、碱及各种油品腐蚀能力强的组合物-环氧树脂水泥沙浆，作为大中型机械设备基础的二次浇注材料。
本发明的目的是这样实现的：
构成环氧树脂水泥沙浆的各组分及各组分之间的重量百分比如下：
填充料 河沙 （中沙） 70.92%
填充料 水泥 （450＃） 17.56-17.73%
粘结剂 环氧树脂 （E44） 8.87%
稀释剂 丙酮 1.17%
固化剂 乙二氨 0.71-0.88%
其配制过程如下：
1、半成品的配制
首先将占总含量8.87%的粘结剂环氧树脂倒入容器内溶化，温度控制在45°-55°之间，并同时搅拌。然后加入1.77%的稀释剂丙酮，并搅拌均匀。混合液体即为半成品，装入容器内备用。
2、填充料的配制
将炒干后的河沙（中沙）按70.92%∶17.56-17.73%的比例与水泥搅拌均匀后备用。
3、成品的配制
在10.64%的半成品溶液中加固化剂乙二氨0.71-0.88%，并同时搅拌2分钟。然后加入混合均匀的填充料88.48-88.65%，并同时搅拌，2-5分钟后成品配制完成，并应立即浇注。
根据二次浇注时的环境温度，固化剂乙二氨的掺加量应作灵活调整。乙二氨掺加量的不同，二次基础养生期也略有变化，具体情况如下：
环境温度 乙二氨掺加量 养生期
-10℃-10℃ 0.88% 7-9天
11℃-20℃ 0.79% 5-7天
21℃-30℃ 0.71% 3-5天
二次浇注前应注意的是：一次基础表面应干燥、清洁;光滑的一次基础表面应凿成粗糙面;必须在一次基础表面喷涂打底子的浆料。（浆料的配制是在半成品溶液中加入等比例的固化剂乙二氨，搅拌均匀即成）
参照下列实施例将会更好地理解本发明。
实施例1
取8.87克环氧树脂倒入容器内溶化，温度保持在45℃-50℃之间。然后将1.77克丙酮倒入熔化的溶液中，搅拌均匀。如二次浇注时的环境温度在-10-10℃时，将0.71克乙二氨倒入已配好的半成品溶液中并同时搅拌。2分钟后加入混合好的填充料88.65克，继续搅拌，2分钟后立即浇注。
实施例2
取8.87克环氧树脂倒入容器内溶化，温度控制在50℃-55℃之间。然后将1.77克丙酮倒入溶化的溶液中，搅拌均匀。如二次浇注时的环境温度在11℃-20℃时，将0.79克乙二氨倒入已配好的半成品溶液中并同时搅拌。2分钟后加入混合好的填充料88.57克，继续搅拌，3分钟后立即浇注。
实施例3
取8.87克环氧树脂倒入容器内溶化，温度控制在50℃-55之间。然后将1.77克丙酮倒入溶化的溶液中，搅拌均匀。如二次浇注时环境温度在21℃-30℃时，将0.88克乙二氨倒入已配好的半成品溶液中并同时搅拌。2分钟后加入混合好的填充料88.48克，继续搅拌，4分钟后立即浇注。
依据本发明提供的配方及配制方法所获得环氧树脂水泥沙浆，其抗压强度、承受破坏载荷的能力成倍地增强。所获得的结果如下：
它还具有优良的粘结性能，能使设备（底座）和一次基础牢牢地形成一个整体。除保证机械设备的载荷能够均匀地传递给基础，有较高的稳定性之外，还表现出对酸、碱及各种油品有较强的抗腐蚀能力。表现突出的是对机械设备的高频率、大振幅有特殊的吸收能力。本发明所提供的产品，适用于石油、化工、钢铁、煤炭、发电等企业中的大中型机械设备基础的二次浇注。
Claims (4)
1、一种可作为设备基础二次浇注使用的环氧树脂水泥沙浆，其组成包括环氧树脂、水泥、河沙及一定量的稀释剂及固化剂，其特征在于所说的固化剂为乙二氨，结构式为：
2、根据权利要求1所述的环氧树脂水泥沙浆其特征在于所说的稀释剂为丙酮，其结构式为：
3、根据权利要求1或2所述的环氧树脂水泥沙浆其特征在于各组分的重量百分比如下：
河沙（中沙） 70.92%
水泥（450＃） 17.56-17.73%
环氧树脂（E44） 8.87%
丙酮 1.17%
乙二氨 0.71-0.88%
4、根据权利要求1所述的环氧树脂水泥沙浆其特征在于应根据二次浇注时一次基础所处的环境温度乙二氨的掺加量有所变化，具体如下：
环境温度 掺加量
-10℃-10℃ 0∶88%
11℃-20℃ 0.79%
21℃-30℃ 0.71%