CN103819146A - Jade-imitated texture coating method for diatom ooze coating - Google Patents
Jade-imitated texture coating method for diatom ooze coating Download PDFInfo
- Publication number
- CN103819146A CN103819146A CN201410014296.2A CN201410014296A CN103819146A CN 103819146 A CN103819146 A CN 103819146A CN 201410014296 A CN201410014296 A CN 201410014296A CN 103819146 A CN103819146 A CN 103819146A
- Authority
- CN
- China
- Prior art keywords
- coating
- diatom ooze
- jade
- stirring
- batch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a jade-imitated texture coating method for a diatom ooze coating. The jade-imitated texture coating method comprises the following steps: firstly, weighing various components according to the weight percentage and sequentially carrying out crushing, vibration screening, automatic metering, stirring, primary matching, premix addition and secondary matching on the components to obtain the diatom ooze coating; secondly, uniformly mixing and stirring the diatom ooze coating with clear water according to the proportion of 1:0.9 to form a paste shape and obtaining batch coating; thirdly, uniformly mixing and stirring the diatom ooze coating with clear water according to the proportion of 1:1.2 to form a paste shape and obtaining point coating; fourthly, producing jade-imitated textures on the wall surface by using the batch coating and the point coating. The jade-imitated texture coating method disclosed by the invention is very suitable for the diatom ooze coating; the diatom ooze coating can be used for preparing jade-imitated textures and can be directly used for construction of concrete, bricks, gypsum boards, compositeboards, old wall bodies and other wall surfaces.
Description
Technical field
The invention belongs to upholstery field, be specifically related to a kind of jade bag road coating process of diatom ooze coating.
Background technology
On Chinese invention patent ZL200510129955.8 basis, invented a kind of diatom ooze coating take diatomite as main raw material(s), this coating is composed of the following components:
Above-mentioned diatom ooze coating connects active group and forms reticulated structure and reversible electrostatic double layer with-Si-O-Si-key, adopts nano silicon, permanent electrode material, effective catalyst M
+deng the breathing coating of new high-tech material system construction, produce continuously micro-current electroanalysis water, can be automatically, anion releasing for good and all.Under the condition without extra power, M
+the catalysis negative oxygen ion that circulates is repeatedly oxidized from obnoxious flavoures such as indoor formaldehyde, ammonia and oxynitrides, make it innoxious, and the air floating dust of neutralization, subsiding belt positive electricity, room air is purified, and there is the multiple functions such as the moisture absorption, mildew-resistant, sterilization, but coating process of the prior art be not suitable for this diatom ooze coating.
Summary of the invention
The object of the invention is to overcome prior art defect, a kind of jade bag road coating process of diatom ooze coating is provided.
Concrete technical scheme of the present invention is as follows:
A jade bag road coating process for diatom ooze coating, comprises the steps:
(1) take as following weight percent each component, and successively through pulverizing, shaking-sieving, automatic gauge, stirring, coordinate for the first time, add premix and coordinate and make described diatom ooze coating for the second time:
(2) by above-mentioned diatom ooze coating and clear water in the ratio mixing and stirring of 1:0.9 to being paste, make batch coating;
(3) by above-mentioned diatom ooze coating and clear water in the ratio mixing and stirring of 1:1.2 to being cream pulpous state, make a coating;
(4) on metope, make jade bag road with batch coating and some coating.
In a preferred embodiment of the invention, described step (4) comprising:
A, use batch coating are criticized and are coated with twice on metope;
B, the pattern that is concave-convex sense that rolls out of the surface uniform that coats will just be criticized with pineapple cylinder;
C, described in the 100-150 millimeter spot printing of sponge block interval, put coating, then atomized water spray and floating;
D, after surface 90% is dry, receive light, and arrange corner and health, make jade bag road.
In a preferred embodiment of the invention, two times thickness of described batch of painting are 1.5～2.0mm, and the thickness of second time is greater than the thickness of first pass, the rectangle that is shaped as 80 × 100mm of described sponge block.
The invention has the beneficial effects as follows:
1, the very applicable described diatom ooze coating of method of the present invention, can prepare jade bag road effect with above-mentioned diatom ooze coating, can be directly used in the construction of the metopes such as concrete, brick, plasterboard, composition board and old body of wall, and effectively adjustment indoor air humidity and heat insulation, fire-retardant, moisture absorption mildew-resistant etc.;
2, procedure of the present invention is simple, and prepared lines effect is attractive in appearance changeable and true lastingly;
3, in method of the present invention without any objectionable impurities, all water is as dispersion agent, nontoxic, tasteless, safety, environmental protection, in construction process, can not cause damage to workmen's healthy and environment, can be widely used in the indoor decorating of villa, high-end residential, star hotel, public place of entertainment, gymnasium, gymnasium, hospital, school, kindergarten, office, meeting room, storage, waiting room and boarding lounge etc.
Embodiment
By embodiment, technical scheme of the present invention is further detailed and is described below.
Embodiment 1
Diatom ooze coating, batch coating and some coating that following embodiment 2 uses are all by the technological process preparation of the present embodiment.
(1) take as following weight percent each component, and successively through pulverizing, shaking-sieving, automatic gauge, stirring, coordinate for the first time, add premix and coordinate and make described diatom ooze coating for the second time:
Can add different inorganic colors and form different colours.
(2) above-mentioned diatom ooze coating is mixed and makes batch coating in the ratio of 1:0.9 with clear water, specific as follows: the amount that measures the required clear water of each stirring and diatom ooze coating, first pour in corresponding stirred vessel 90% of metering clear water, slowly put into again the diatom ooze coating measuring, stir and be paste with hand-operated high speed stirring machine, churning time is not less than 10 minutes, leave standstill the clear water that makes it to pour into again after complete slaking residue 10% for 10 minutes thoroughly stir (3～5 minutes) can criticize painting;
(3) above-mentioned diatom ooze coating is mixed and makes a coating in the ratio of 1:1.2 with clear water, specific as follows: the amount that measures the required clear water of each stirring and diatom ooze coating, first pour in corresponding stirred vessel 60% of metering clear water, slowly put into again the diatom ooze coating measuring, stir and be paste with hand-operated high speed stirring machine, churning time is not less than 10 minutes, leaving standstill the clear water that makes it to pour into again after complete slaking residue 40% for 10 minutes thoroughly stirs and is cream pulpous state (3～5 minutes), stir again (3～5 minutes) with 60 object filtering nets filtrations and get final product spot printing.
Embodiment 2
A, will criticize coating batch be coated with twice with batch cutter on metope, batch two times thickness that are coated with are 1.5～2.0mm, and the thickness of second time is greater than the thickness of first pass,
B, the pattern that is concave-convex sense that rolls out of the surface uniform that coats will just be criticized with pineapple cylinder;
C, with roller coating material described in the rectangle sponge block interval 100-150 millimeter spot printing of 80 × 100mm, atomized water spray and floating again, this is floating as follows: criticize cutter with different directions or curved floating whole coat side by Thin Stainless Steel, allow the described diatom ooze coating of different colours straggly melt mutually, have deeply have shallow, have and far have closely, have very strong visual impression.；
D, after surface 90% is dry, receive finishing tool with plastic cement and receive light, arrange corner with hairbrush, and by the clean towel wipe surfaces of white to clean out the powder that may carry in receipts photoreduction process, make jade bag road.
The above, be only preferred embodiment of the present invention, therefore can not limit according to this scope of the invention process, the equivalence done according to the scope of the claims of the present invention and description changes and modifies, and all should still belong in the scope that the present invention contains.
Claims (3)
1. a jade bag road coating process for diatom ooze coating, is characterized in that: comprise the steps:
(1) take as following weight percent each component, and successively through pulverizing, shaking-sieving, automatic gauge, stirring, coordinate for the first time, add premix and coordinate and make described diatom ooze coating for the second time:
(2) by above-mentioned diatom ooze coating and clear water in the ratio mixing and stirring of 1:0.9 to being paste, make batch coating;
(3) by above-mentioned diatom ooze coating and clear water in the ratio mixing and stirring of 1:1.2 to being cream pulpous state, make a coating;
(4) on metope, make jade bag road with batch coating and some coating.
2. the jade bag road coating process of a kind of diatom ooze coating as claimed in claim 1, is characterized in that: described step (4) comprising:
A, use batch coating are criticized and are coated with twice on metope;
B, the pattern that is concave-convex sense that rolls out of the surface uniform that coats will just be criticized with pineapple cylinder;
C, described in the 100-150 millimeter spot printing of sponge block interval, put coating, then atomized water spray and floating;
D, after surface 90% is dry, receive light, and arrange corner and health, make jade bag road.
3. the jade bag road coating process of a kind of diatom ooze coating as claimed in claim 2, is characterized in that: the thickness of second time of described batch of painting is 1.5～2.0mm and the thickness that is greater than first pass, the rectangle that is shaped as 80 × 100mm of described sponge block.