CN103818175A - Manufacturing technology for copper mold glass painting - Google Patents
Manufacturing technology for copper mold glass painting Download PDFInfo
- Publication number
- CN103818175A CN103818175A CN201410044530.6A CN201410044530A CN103818175A CN 103818175 A CN103818175 A CN 103818175A CN 201410044530 A CN201410044530 A CN 201410044530A CN 103818175 A CN103818175 A CN 103818175A
- Authority
- CN
- China
- Prior art keywords
- copper
- painting
- copper sheet
- pattern
- glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing technology for a copper mold glass painting. The manufacturing technology comprises the following steps: selecting a high-quality flawless copper sheet as a bottom mold, mechanically cutting the copper sheet according to different specification of the painting, mechanically compressing the periphery of the copper sheet to a height of 0.4 mm as a closing side, removing rust from the surface of the copper sheet, regulating an oven to be 800-1000 DEG C and roasting the copper sheet for 45-60 minutes, taking out the copper sheet, soaking the copper sheet with diluted oxalic acid for 10-15 minutes, painting a pattern on the surface of the copper sheet, shaping a red copper wire according to decorative design and lines of the pattern to be welded onto the corresponding decorative design and lines on the copper sheet by using argon arc welding , blending a pure natural cloisonne enamel with a white emulsion, using an oil painting scraper knife and a sucker to fill the enamel according to the colors of the pattern till reaching the thickness of the copper wire, conveying the dried copper plate painting into an electric oven, roasting the painting at 800 DEG C for 24-28 hours, and forming the copper mold glass painting after cooling. The copper mold glass painting is rich in colors, strong in stereoscopic impression, firm, not easy to break, and good in visual effect.
Description
Technical field
The present invention relates to a kind of method of craft articles, specifically the manufacture craft of copper tire glass-painting.
Background technology
In prior art, the word on handicraft or pattern be generally adopt carve, directly write, shell carving or carve and make with feather.Engraving or shell carving complex process, time-consuming, paste feather cost is higher, look also very beautiful although directly write, lack stereoeffect.
Summary of the invention
The object of the present invention is to provide a kind of manufacture craft of copper tire glass-painting, this manufacture craft is to use the theory of Modern Industry Products development and Design, should adapt to modern way of life and Social Culture in line with Traditional Handcraft Industry, the requirement following the laws of the market economy, utilize modern high tech method and in conjunction with traditional technology, form method thinkling sound's painting making technology flow process a set of novelty, ripe, artistic value, enjoying value, memorial value, place value, the practical value of drawing from truly improving glass method thinkling sound.
The technical scheme adopting is:
The manufacture craft of copper tire glass-painting, is characterized in that comprising following process steps:
1, select the copper plate of the indefectible 0.3mm of high-quality as end tire, cut out plate by the different size machinery of picture.
2, the height that copper coin periphery is depressed into 0.4mm with machinery is as receiving limit.
3, with pin mill steel brush, copper is removed in copper coin surface and embroider processing.
4, again the high temperature of 800～1000 degrees Celsius of baking oven modulation is baked to 45～60 minutes, after taking out, with low oxalic acid immersion 10～15 minutes, makes it copper coin hardness suitable and reach corrosion-resistant object.
5, use Chinese realistic painting lines manual drawing on copper coin surface in the pattern that will make.
6, the red copper wire of 0.1 × 0.5mm according to the decorative pattern of pattern, lines, pinch good shaping with sub-arc welding on the copper coin of corresponding decorative pattern, line image.
7, select the blending of pure natural cloisonne enamel glaze and white glue with vinyl, fill out the thickness of glaze to copper cash by the color of pattern with oil painting perching knife and suction pipe.
8, the copperplate print after drying is sent in electric oven, in the temperature of 800 degrees Celsius, bake to 24-28 hour, form after cooling the porcelain shape fine copper tire glass-painting beautiful in colour that copper and glaze are integrated, as occur flaw private, need again to fill up glaze, again fire by above program.
9, water grinding abrasive disk picture is ground smooth, then with polishing machine polishing repeatedly, until complete glittering and translucent copper tire glass-painting finished product.
The present invention has the following advantages:
(1) color is enriched nature: copper tire glass-painting is to be made up of the color of the versicolor glaze of occurring in nature itself, and color and luster is soft, natural, true, original.Picture color transition nature, just like the picture effect as photo.
(2) persistence: through special crystal frosted technical finesse, this picture decades, upper a century also can not fade, year picture is still aobvious outmoded for a long time, and there is acid and alkali-resistance, antiultraviolet, the feature such as can clean.
(3) picture smooth: after special exclusive refrigeration technique is processed, picture is as crystal, like glittering and translucent amber.There is extremely strong innervation, third dimension.
(4) solid not broken: product adopts special tire plate and moulding bed and unique fork-join technology, glaze and wire are organically synthesized together by the infiltration of special crystal liquid, strengthened integral hardness, picture core can not rupture and can not occur the phenomenon of fracture yet, is applicable to transporting for long-distance.
(5) be not water funkly afraid of humidity: be that one is synthetic owing to drawing core and tire plate, directly to be contained in picture frame, to make finished product and draw, with air insulated, do not need mounting glass, unique material and technique make picture core not water funk, be not afraid of humidity, be applicable to very much the special occasions such as luxurious bath center, Saunas clinic, Household bathroom and decorate.
(6) good visual effect: smooth wire lines, rough natural colored glaze, naturally abundant color, mixes various patterns, and every width picture all makes people stop to look around, noticeable, has extraordinary visual effect.
(7) expressive force is strong: it is in extensive range that product is got figure, relates to works modelled after an antique, famous person's calligraphy and painting, as the works of the various styles such as oil painting, traditional Chinese Painting, photo, Chinese realistic painting, freehand brushwork.
The specific embodiment
The manufacture craft of copper tire glass-painting, specifically comprises following processing step:
1, select the copper plate of the indefectible 0.3mm of high-quality as end tire, cut out plate by the different size machinery of picture.
2, the height that copper coin periphery is depressed into 0.4mm with machinery is as receiving limit.
3, with pin mill steel brush, copper is removed in copper coin surface and embroider processing.
4, again the high temperature of 900 degrees Celsius of baking oven modulation is baked to 50 minutes, after taking out, with low oxalic acid immersion 12 minutes, makes it copper coin hardness suitable and reach corrosion-resistant object.
5, use Chinese realistic painting lines manual drawing on copper coin surface in the pattern that will make.
6, the red copper wire of 0.1 × 0.5mm according to the decorative pattern of pattern, lines, pinch good shaping with sub-arc welding on the copper coin of corresponding decorative pattern, line image.
7, select the blending of pure natural cloisonne enamel glaze and white glue with vinyl, fill out the thickness of glaze to copper cash by the color of pattern with oil painting perching knife and suction pipe.
8, the copperplate print after drying is sent in electric oven, in the temperature of 800 degrees Celsius, bake to 26 hours, form after cooling the porcelain shape fine copper tire glass-painting beautiful in colour that copper and glaze are integrated, as occur flaw flaw, need again to fill up glaze, again fire by above program.
9, water grinding abrasive disk picture is ground smooth, then with polishing machine polishing repeatedly, until complete glittering and translucent copper tire glass-painting finished product.
Claims (1)
1. the manufacture craft of copper tire glass-painting, is characterized in that comprising following processing step:
A, select the copper plate of the indefectible 0.3mm of high-quality as end tire, cut out plate by the different size machinery of picture;
B, copper coin periphery are depressed into the height of 0.4mm as receiving limit with machinery;
C, with pin mill steel brush, copper is removed in copper coin surface and embroider and process;
D, again the high temperature of 800～1000 degrees Celsius of baking oven modulation is baked to 45～60 minutes, after taking out, with low oxalic acid immersion 10～15 minutes, makes it copper coin hardness suitable and reach corrosion-resistant object;
E, the pattern that will make with Chinese realistic painting lines manual drawing on copper coin surface;
F, the red copper wire of 0.1 × 0.5mm according to the decorative pattern of pattern, lines, pinch good shaping with sub-arc welding on the copper coin of corresponding decorative pattern, line image;
G, select the blending of pure natural cloisonne enamel glaze and white glue with vinyl, fill out the thickness of glaze to copper cash by the color of pattern with oil painting perching knife and suction pipe;
H, dry after copperplate print send in electric oven, in the temperature of 800 degrees Celsius, bake to 26 hours, form after cooling the porcelain shape fine copper tire glass-painting beautiful in colour that copper and glaze are integrated, as occur flaw flaw, need again to fill up glaze, again fire by above program;
I, water grinding abrasive disk grind picture smooth, then with polishing machine polishing repeatedly, until complete glittering and translucent copper tire glass-painting finished product.