CN103788919A - 水溶性常温复合胶及其制备方法 - Google Patents

水溶性常温复合胶及其制备方法 Download PDF

Info

Publication number
CN103788919A
CN103788919A CN201410050018.2A CN201410050018A CN103788919A CN 103788919 A CN103788919 A CN 103788919A CN 201410050018 A CN201410050018 A CN 201410050018A CN 103788919 A CN103788919 A CN 103788919A
Authority
CN
China
Prior art keywords
water
temperature composite
soluble
preparation
normal temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410050018.2A
Other languages
English (en)
Other versions
CN103788919B (zh
Inventor
朱青东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410050018.2A priority Critical patent/CN103788919B/zh
Publication of CN103788919A publication Critical patent/CN103788919A/zh
Application granted granted Critical
Publication of CN103788919B publication Critical patent/CN103788919B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种水溶性常温复合胶及其制备方法,属于瓦楞纸粘合剂制备技术领域。其主要成份为动物胶、高岭土或碳酸钙、水,制备方法为:在搅拌机中加入10-50份的水,在搅拌下加入1-60份碳酸钙或高岭土,然后加入30-90份动物胶,加热升温至40-80℃,搅拌速度为40-80转/每分钟,搅拌2-4小时,在常温下冷却即为水溶性常温复合胶产品。本发明配制方法简单,加热为液体,常温下为固体,含水量少,且该复合胶干燥快,不被粘合体吸收,不易变形,用量少,大大降低了生产成本。

Description

水溶性常温复合胶及其制备方法
技术领域
本发明涉及一种水溶性常温复合胶及其制备方法,属于粘合剂制备技术领域。
背景技术
自包装行业生产瓦楞纸板已有140多年历史,在这140多年里,瓦楞纸板制造时主要采用淀粉胶为粘合剂,主要成份由淀粉、水、粘土、硼砂、片碱,辅料:氧化水、消泡剂按比例合成。由于玉米淀粉价格低廉,因此玉米淀粉胶使用范围更广,但玉米淀粉胶存在着质量不稳定,贮存期短,贮存时易发生分子间缔合,流动性差,颜色较深等缺点,且玉米淀粉胶在使用中需加水在机器上加热糊化。玉米淀粉胶在糊化过程中对温度要求较高且含水量大,因此,在实际使用过程中需要加热来消除胶水中的水份,这不仅造成大量的能源消耗,而且碳排放也会对环境造成一定的污染。
发明内容
本发明的目的是为了解决现有技术中瓦楞纸板粘合胶水需要加热,含水量较高的缺点,提供一种粘度适中且无需加热,常温固化,不但无需能源加热还无碳排放,比原有胶水少50%以上水份的水溶性常温复合胶及其制备方法。
按照本发明提供的技术方案,水溶性常温复合胶包括以下组分,按重量份数计为:动物胶30-90份,填充料碳酸钙或高岭土1-60份,水10-50份。
进一步的,水溶性常温复合胶的制备方法:在搅拌机中加入10-50份的水,在搅拌下加入1-60份碳酸钙或高岭土,然后加入30-90份动物胶,加热升温至40-80℃,搅拌2-4小时,在常温下冷却即为水溶性常温复合胶产品。
进一步的,水溶性常温复合胶粘度为1-3.2Pa·s,含水率20-45%,冻力165 Bloom Grams,固含量55-80%,灰份30-65%。
本发明配制方法简单,加热为液体,常温下为固体,含水量少且该复合胶干燥快,不被粘合体吸收,不易变形,用量少,大大降低了生产成本。
具体实施方式
下面将结合具体实施方式对本发明作进一步的说明,(其中各组分按重量份数计)。
动物胶:主要是以动物的皮、骨或筋等为原料,将其中所含的胶原经过部分水解、萃取和干燥制成的蛋白质固形物。颜色呈淡黄色或棕色,能溶于水,微溶于酒精,不溶于有机溶剂。其水溶液具有表面活性,粘度较高,冷却后会冻结成有弹性的凝胶,受热后又恢复为溶液,粘度为3.4 Pa·s,含水量为10%。
高岭土:具有较好的增稠效果,避免配制的水溶性常温复合胶发生沉淀,可以起到分散的作用。
碳酸钙:可以增加水溶性常温复合胶的丰满度,起到填充物的作用。
动物胶粘度大,一级胶的标准为3.4 Pa·s,但实际生产中没有必要全部采用粘力大的胶水,只需要达到需要的强度即可,因此,通过在动物胶中加入一定比例的填充料和水,可以使胶水达到各种纸张复合时对粘合牢度的要求,大大降低生产成本。
实施例一:
将水10份加入搅拌机中,在搅拌下加入高岭土1份,再加入动物胶89份,升温至80℃,搅拌速度为40转/每分钟,搅拌2小时,在常温下冷却即为水溶性常温复合胶产品。
本发明制备得到的产品经检测可知:粘度为3-3.2Pa·s ,含水率为20-25%,冻力为165Bloom Grams,固含量75-80%,灰份30-35%,该胶适用于高密度纸。
实施例二:
将水25份加入搅拌机,在搅拌下加入碳酸钙25份,再加入动物胶50份,升温至65℃,搅拌速度为60转/每分钟,搅拌3小时,在常温下冷却即为水溶性常温复合胶产品。
本发明制备得到的产品经检测可知:粘度为2-2.5Pa·s,含水率为30-35%,冻力165 Bloom Grams,固含量65-70%,灰份30-35%,该胶适用于瓦楞纸的复合。
实施例三:
将水50份加入搅拌机,在搅拌下加入碳酸钙60份,再加入动物胶30份,加温至50℃,搅拌速度为80转/每分钟,搅拌4小时,在常温下冷却即为水溶性常温复合胶产品。
本发明制备得到的产品经检测可知:粘度为1-1.5Pa·s,含水率40-45%,冻力165 Bloom Grams,固含量55-60%,灰份60-65%,该胶适用于工业纸板。

Claims (3)

1.一种水溶性常温复合胶,其特征在于:包括以下组分,按重量份数计为,动物胶30-90份,填充料碳酸钙或高岭土1-60份,水10-50份;
在搅拌机中加入水、填充料碳酸钙或高岭土及动物胶,经搅拌、加温、冷却为水溶性常温复合胶。
2.如权利要求1所述的一种水溶性常温复合胶的制备方法,其特征在于:在搅拌机中加入10-50份的水,在搅拌下加入1-60份碳酸钙或高岭土,然后加入30-90份动物胶,加热升温至40-80℃,搅拌速度为40-80转/每分钟,搅拌2-4小时;在常温下冷却即为水溶性常温复合胶产品。
3.如权利要求1所述的一种水溶性常温复合胶的制备方法,其特征在于:所述水溶性常温复合胶粘度为1-3.2Pa·s,含水率20-45%,冻力165 Bloom Grams,固含量55-80%,灰份30-65%。
CN201410050018.2A 2014-02-13 2014-02-13 水溶性常温复合胶及其制备方法 Active CN103788919B (zh)