CN103788729A - 一种防锈涂料 - Google Patents

一种防锈涂料 Download PDF

Info

Publication number
CN103788729A
CN103788729A CN201310668547.4A CN201310668547A CN103788729A CN 103788729 A CN103788729 A CN 103788729A CN 201310668547 A CN201310668547 A CN 201310668547A CN 103788729 A CN103788729 A CN 103788729A
Authority
CN
China
Prior art keywords
parts
agent
proof paint
silicon powder
antirust coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310668547.4A
Other languages
English (en)
Inventor
刘连河
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QINGDAO ADVANCED MARINE MATERIAL TECHNOLOGY Co Ltd
Original Assignee
QINGDAO ADVANCED MARINE MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QINGDAO ADVANCED MARINE MATERIAL TECHNOLOGY Co Ltd filed Critical QINGDAO ADVANCED MARINE MATERIAL TECHNOLOGY Co Ltd
Priority to CN201310668547.4A priority Critical patent/CN103788729A/zh
Publication of CN103788729A publication Critical patent/CN103788729A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防锈涂料,由以下组分按重量份数组成:铝锌钙硅合金粉50-65份、纳米二氧化硅气凝胶3-9份、去离子水10-15份、粘结剂2-5份、防腐防霉剂0.3-0.8份、分散剂0.2-0.4份、增稠剂1-1.5份、附着力促进剂2-4份、耐盐雾助剂2-5份。采用铝锌钙硅合金粉与粘结剂、分散剂、防腐防霉剂、耐盐雾剂等组合,并选用了适合该系统的附着力促进剂,使其按配比混合成为耐海洋气候的防锈涂料,施工简单,可喷涂,刷涂,并且涂层具有耐腐蚀、耐磨性,适合于恶劣的海洋气候,为各种海洋工程部件提供了优异的防锈方法。

Description

一种防锈涂料
技术领域
本发明涉及一种防锈涂料,具体涉及一种耐海洋气候防锈涂料。
背景技术
在现代工业和日常生活中,各种腐蚀随处可见,尤其是海洋中工程装备处于潮湿、高盐、多风、强气流环境中,为极端恶劣环境,裸露在外的部件容易受到严重的腐蚀,使其使用寿命降低,成分增加。
因此,开发既具有防水、耐强紫外线、耐盐、耐强气流等性能的耐海洋气候的涂料十分重要。
发明内容
为解决上述问题,本发明公开了如下技术方案:
一种防锈涂料,其特征在于:由以下组分按重量份数组成:
铝锌钙硅合金粉50-65份、纳米二氧化硅气凝胶3-9份、去离子水10-15份、粘结剂2-5份、防腐防霉剂0.3-0.8份、分散剂0.2-0.4份、增稠剂1-1.5份、附着力促进剂2-4份、耐盐雾助剂2-5份。
进一步的,所述粘结剂为硼酸盐胶粘剂。
进一步的,所述增稠剂为羟乙基纤维素。
进一步的,所述铝锌钙硅合金粉中各组成成份质量百分比为: Al:Zn:Ca:Si =3-8:50-55:30-55:0.5-2。
进一步的,所述铝锌钙硅合金粉的平均粒径为30-100微米。
本发明的积极效果在于:采用铝锌钙硅合金粉与粘结剂、分散剂、防腐防霉剂、耐盐雾剂等组合,并选用了适合该系统的附着力促进剂,使其按配比混合成为耐海洋气候的防锈涂料,施工简单,可喷涂,刷涂,并且涂层具有耐腐蚀、耐磨性,适合于恶劣的海洋气候,为各种海洋工程部件提供了优异的防锈方法。
具体实施方式
下面结合实施例详细说明本发明的技术方案,但保护范围并不受此限制。
实施例1 
铝锌钙硅合金粉50份、纳米二氧化硅气凝胶3份、去离子水10份、硼酸盐胶粘剂2份、防腐防霉剂YN-300 0.3份、分散剂0.2份、增稠剂羟乙基纤维素1份、附着力促进剂2份、耐盐雾助剂2份。所述铝锌钙硅合金粉中各组成成份质量百分比为: Al:Zn:Ca:Si =3:50: 55:2。所述铝锌钙硅合金粉的平均粒径为30-100微米。
实施例2
铝锌钙硅合金粉65份、纳米二氧化硅气凝胶9份、去离子水15份、硼酸盐胶粘剂5份、防腐防霉剂RD-BLB 0.8份、分散剂0.4份、增稠剂羟乙基纤维素1.5份、附着力促进剂4份、耐盐雾助剂5份,所述铝锌钙硅合金粉中各组成成份质量百分比为: Al:Zn:Ca:Si =8: 55: 55:0.5,所述铝锌钙硅合金粉的平均粒径为30-100微米。
实施例3
铝锌钙硅合金粉60份、纳米二氧化硅气凝胶8份、去离子水12份、硼酸盐胶粘剂4份、防腐防霉剂0.5份、分散剂0.3份、增稠剂羟乙基纤维素1.2份、附着力促进剂3份、耐盐雾助剂4份,所述铝锌钙硅合金粉中各组成成份质量百分比为: Al:Zn:Ca:Si =5:52:40:1,所述铝锌钙硅合金粉的平均粒径为30-100微米。

Claims (5)

1.一种防锈涂料,其特征在于:由以下组分按重量份数组成:
铝锌钙硅合金粉50-65份、纳米二氧化硅气凝胶3-9份、去离子水10-15份、粘结剂2-5份、防腐防霉剂0.3-0.8份、分散剂0.2-0.4份、增稠剂1-1.5份、附着力促进剂2-4份、耐盐雾助剂2-5份。
2.根据权利要求1所述的一种防锈涂料,其特征在于:所述粘结剂为硼酸盐胶粘剂。
3.根据权利要求1所述的一种防锈涂料,其特征在于:所述增稠剂为羟乙基纤维素。
4.根据权利要求1所述的一种防锈涂料,其特征在于:所述铝锌钙硅合金粉中各组成成份质量百分比为: Al:Zn:Ca:Si =3-8:50-55:30-55:0.5-2。
5.根据权利要求1所述的一种防锈涂料,其特征在于:所述铝锌钙硅合金粉的平均粒径为30-100微米。
CN201310668547.4A 2013-12-11 2013-12-11 一种防锈涂料 Pending CN103788729A (zh)