CN103709852B - 一种耐海洋气候防锈涂料 - Google Patents
一种耐海洋气候防锈涂料 Download PDFInfo
- Publication number
- CN103709852B CN103709852B CN201310672826.8A CN201310672826A CN103709852B CN 103709852 B CN103709852 B CN 103709852B CN 201310672826 A CN201310672826 A CN 201310672826A CN 103709852 B CN103709852 B CN 103709852B
- Authority
- CN
- China
- Prior art keywords
- emulsion
- silicon
- barium
- aluminium
- alloy powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种耐海洋气候防锈涂料，由以下组分按重量份数组成：乳液30-45份、硅铝钡钙合金粉20-25份、纳米二氧化硅3-9份、粘结剂2-5份、防腐防霉剂0.3-0.8份、分散剂0.2-0.4份、增稠剂1-1.5份、附着力促进剂2-4份、耐盐雾助剂2-5份；其中所述乳液为聚偏氟乙烯乳液、聚四氟乙烯乳液中的一种或两种的混合，所述乳液的固含量为40-55%，采用疏水性乳液、硅铝钡钙合金粉与粘结剂、分散剂、防腐防霉剂、耐盐雾剂等组合，并选用了适合该系统的附着力促进剂，施工简单，可喷涂，刷涂，并且涂层具有耐腐蚀、耐磨性，适合于恶劣的海洋气候，为各种海洋工程部件提供了优异的防绣方法。
Description
技术领域
本发明涉及一种防锈涂料，具体涉及一种耐海洋气候防锈涂料。
背景技术
在现代工业和日常生活中，各种腐蚀随处可见，尤其是海洋中工程装备处于潮湿、高盐、多风、强气流环境中，为极端恶劣环境，裸露在外的部件容易受到严重的腐蚀，使其使用寿命降低，成分增加。
因此，开发既具有防水、耐强紫外线、耐盐、耐强气流等性能的耐海洋气候的涂料十分重要。
发明内容
为解决上述问题，本发明公开了如下技术方案：
一种耐海洋气候防锈涂料，由以下组分按重量份数组成：
乳液30-45份、硅铝钡钙合金粉20-25份、纳米二氧化硅3-9份、粘结剂2-5份、防腐防霉剂0.3-0.8份、分散剂0.2-0.4份、增稠剂1-1.5份、附着力促进剂2-4份、耐盐雾助剂2-5份；其中所述乳液为聚偏氟乙烯乳液、聚四氟乙烯乳液中的一种或两种的混合，所述乳液的固含量为40-55%。
进一步的，所述粘结剂为为磷酸盐胶粘剂。
进一步的，所述增稠剂为羟乙基纤维素。
进一步的，所述纳米二氧化硅的平均粒径为30-50nm。
进一步的，所述硅铝钡钙合金粉中各组成成份质量百分比为：Si：Al：Ba：Ca=3-8：50-55：30-55：0.5-2。
进一步的，所述硅铝钡钙合金粉的平均粒径为30-100微米。
本发明的积极效果在于：采用疏水性乳液、硅铝钡钙合金粉与粘结剂、分散剂、防腐防霉剂、耐盐雾剂等组合，并选用了适合该系统的附着力促进剂，使其按配比混合成为耐海洋气候的防锈涂料，施工简单，可喷涂，刷涂，并且涂层具有耐腐蚀、耐磨性，适合于恶劣的海洋气候，为各种海洋工程部件提供了优异的防绣方法。
具体实施方式
下面结合实施例详细说明本发明的技术方案，但保护范围并不受此限制。
实施例1
固含量为40%的聚偏氟乙烯乳液30份、硅铝钡钙合金粉25份、纳米二氧化硅9份、磷酸盐胶粘剂2份、防腐防霉剂0.3份、分散剂0.2份、羟乙基纤维素1.5份、附着力促进剂2份、耐盐雾助剂2份；其中，纳米二氧化硅的平均粒径为30-50nm，硅铝钡钙合金粉中各组成成份质量百分比为：Si：Al：Ba：Ca=8：50：55：0.5。
实施例2
固含量为55%聚四氟乙烯乳液45份、硅铝钡钙合金粉25份、纳米二氧化硅9份、磷酸盐胶粘剂5份、防腐防霉剂0.8份、分散剂0.4份、羟乙基纤维素1.5份、附着力促进剂4份、耐盐雾助剂5份；其中，进一步的，纳米二氧化硅的平均粒径为30-50nm，硅铝钡钙合金粉中各组成成份质量百分比为：Si：Al：Ba：Ca=8：55：30：2。
实施例3
聚偏氟乙烯乳液、聚四氟乙烯质量比为2：1的乳液40份、硅铝钡钙合金粉25份、纳米二氧化硅5份、磷酸盐胶粘剂4份、防腐防霉剂0.5份、分散剂0.3份、羟乙基纤维素1.5份、附着力促进剂3份、耐盐雾助剂4份；其中所述乳液的固含量为45%，纳米二氧化硅的平均粒径为30-50nm，硅铝钡钙合金粉中各组成成份质量百分比为：Si：Al：Ba：Ca=6：53：40：1。
Claims (1)
1.一种耐海洋气候防锈涂料，其特征在于：由以下组分按重量份数组成：
乳液30-45份、硅铝钡钙合金粉20-25份、纳米二氧化硅3-9份、粘结剂2-5份、防腐防霉剂0.3-0.8份、分散剂0.2-0.4份、增稠剂1-1.5份、附着力促进剂2-4份、耐盐雾助剂2-5份；其中所述乳液为聚偏氟乙烯乳液、聚四氟乙烯乳液中的一种或两种的混合，所述乳液的固含量为40-55%；
所述粘结剂为磷酸盐胶粘剂；
所述增稠剂为羟乙基纤维素；
所述纳米二氧化硅的平均粒径为30-50nm；
所述硅铝钡钙合金粉中各组成成份质量百分比为：Si：Al：Ba：Ca=3-8：50-55：30-55：0.5-2；
所述硅铝钡钙合金粉的平均粒径为30-100微米。