CN103773214A - 一种防水涂料及其制备工艺 - Google Patents

一种防水涂料及其制备工艺 Download PDF

Info

Publication number
CN103773214A
CN103773214A CN201410038740.4A CN201410038740A CN103773214A CN 103773214 A CN103773214 A CN 103773214A CN 201410038740 A CN201410038740 A CN 201410038740A CN 103773214 A CN103773214 A CN 103773214A
Authority
CN
China
Prior art keywords
parts
waterproof paint
butadiene
stirring
polyoxyethylene glycol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201410038740.4A
Other languages
English (en)
Inventor
葛红军
徐丽梅
杨伟东
邱玉梅
沙嘉敏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Sutong Separation Engineering & Technology Co Ltd
Original Assignee
Nantong Sutong Separation Engineering & Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong Sutong Separation Engineering & Technology Co Ltd filed Critical Nantong Sutong Separation Engineering & Technology Co Ltd
Priority to CN201410038740.4A priority Critical patent/CN103773214A/zh
Publication of CN103773214A publication Critical patent/CN103773214A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种防水涂料及其制备工艺，该涂料是由以下质量份的各组分组成：水性聚氨酯80-105份、天然橡胶15-27份、聚乙二醇1-12份、松节油8-18份、石英粉7-17份、去离子水13-25份、增稠剂1-10份、丁苯胶15-32份、氢氧化铝1-9份、三氧化二锑1-9份。制备方法：按照上述质量份，将聚乙二醇、氢氧化铝和三氧化二锑混合，搅拌分散，加入天然橡胶和丁苯胶，充分搅拌，将水性聚氨酯倒入，充分搅拌后加入剩余原料，搅拌至均匀，即得所述防水涂料。本发明涂抹稳定，防水性强，具有很好的附着力。

Description

一种防水涂料及其制备工艺
技术领域
本发明属化工领域，尤其涉及一种防水涂料。
背景技术
在化工生产中，防水涂料在常温下呈无固定形状的粘稠状液体高分子合成材料，经涂布后，通过溶剂的挥发或水分的蒸发或反应固化后在基层表面可形成坚韧的防水涂膜的材料。但目前应用在化工设备和管道上的涂料其耐水性和耐久性效果并不理想，使用寿命短，经过风吹日晒就会出现脱皮等现象，因此提高防水涂料的性能尤为重要。
发明内容
针对现有技术存在的不足，本发明所要解决的技术问题是，提供一种防水效果好，使用寿命长的防水涂料。
为解决上述技术问题，本发明所采用的技术方案是：一种防水涂料，由以下质量份的各组分组成：水性聚氨酯80-105份、天然橡胶15-27份、聚乙二醇1-12份、松节油8-18份、石英粉7-17份、去离子水13-25份、增稠剂1-10份、丁苯胶15-32份、氢氧化铝1-9份、三氧化二锑1-9份。
优选的，一种防水涂料，由以下质量份的各组分组成：水性聚氨酯85-100份、天然橡胶18-25份、聚乙二醇5-8份、松节油10-16份、石英粉9-15份、去离子水17-22份、增稠剂5-8份、丁苯胶21-29份、氢氧化铝3-7份、三氧化二锑2-7份。
更优选的，一种防水涂料，由以下质量份的各组分组成：水性聚氨酯95份、天然橡胶21份、聚乙二醇6份、松节油12份、石英粉12份、去离子水20份、增稠剂7份、丁苯胶25份、氢氧化铝4份、三氧化二锑5份。
一种防水涂料的制备方法，包括以下步骤：
按照上述质量份，将聚乙二醇、氢氧化铝和三氧化二锑混合，搅拌分散，加入天然橡胶和丁苯胶，充分搅拌，将水性聚氨酯倒入，充分搅拌后加入剩余原料，搅拌至均匀，即得所述防水涂料。
本发明的优点是涂抹稳定，防水性强，具有很好的附着力。
具体实施方式
实施例1
一种防水涂料，有以下质量份的各组分组成：水性聚氨酯80份、天然橡胶15份、聚乙二醇1份、松节油8份、石英粉7份、去离子水13份、增稠剂1份、丁苯胶15份、氢氧化铝1份、三氧化二锑1份。
制备方法：按照上述质量份，将聚乙二醇、氢氧化铝和三氧化二锑混合，搅拌分散，加入天然橡胶和丁苯胶，充分搅拌，将水性聚氨酯倒入，充分搅拌后加入剩余原料，搅拌至均匀，即得所述防水涂料。
实施例2
一种防水涂料，有以下质量份的各组分组成：水性聚氨酯105份、天然橡胶27份、聚乙二醇12份、松节油18份、石英粉17份、去离子水25份、增稠剂10份、丁苯胶32份、氢氧化铝9份、三氧化二锑9份。
实施例3
一种防水涂料，有以下质量份的各组分组成：水性聚氨酯85份、天然橡胶18份、聚乙二醇5份、松节油10份、石英粉9份、去离子水17份、增稠剂5份、丁苯胶21份、氢氧化铝3份、三氧化二锑2份。
制备方法：按照上述质量份，将聚乙二醇、氢氧化铝和三氧化二锑混合，搅拌分散，加入天然橡胶和丁苯胶，充分搅拌，将水性聚氨酯倒入，充分搅拌后加入剩余原料，搅拌至均匀，即得所述防水涂料。
实施例4
一种防水涂料，有以下质量份的各组分组成：水性聚氨酯100份、天然橡胶25份、聚乙二醇8份、松节油16份、石英粉15份、去离子水22份、增稠剂8份、丁苯胶29份、氢氧化铝7份、三氧化二锑7份。
制备方法：按照上述质量份，将聚乙二醇、氢氧化铝和三氧化二锑混合，搅拌分散，加入天然橡胶和丁苯胶，充分搅拌，将水性聚氨酯倒入，充分搅拌后加入剩余原料，搅拌至均匀，即得所述防水涂料。
实施例5
一种防水涂料，有以下质量份的各组分组成：水性聚氨酯95份、天然橡胶21份、聚乙二醇6份、松节油12份、石英粉12份、去离子水20份、增稠剂7
份、丁苯胶25份、氢氧化铝4份、三氧化二锑5份。
制备方法：按照上述质量份，将聚乙二醇、氢氧化铝和三氧化二锑混合，搅拌分散，加入天然橡胶和丁苯胶，充分搅拌，将水性聚氨酯倒入，充分搅拌后加入剩余原料，搅拌至均匀，即得所述防水涂料。
实施例1-5所得产品性能测试见表1：
表1

Claims (4)

1.一种防水涂料，其特征在于：由以下质量份的各组分组成：水性聚氨酯80-105份、天然橡胶15-27份、聚乙二醇1-12份、松节油8-18份、石英粉7-17份、去离子水13-25份、增稠剂1-10份、丁苯胶15-32份、氢氧化铝1-9份、三氧化二锑1-9份。
2.根据权利要求1所述的一种防水涂料，其特征在于由以下质量份的各组分组成：水性聚氨酯85-100份、天然橡胶18-25份、聚乙二醇5-8份、松节油10-16份、石英粉9-15份、去离子水17-22份、增稠剂5-8份、丁苯胶21-29份、氢氧化铝3-7份、三氧化二锑2-7份。
3.根据权利要求1所述的一种防水涂料，其特征在于由以下质量份的各组分组成：水性聚氨酯95份、天然橡胶21份、聚乙二醇6份、松节油12份、石英粉12份、去离子水20份、增稠剂7份、丁苯胶25份、氢氧化铝4份、三氧化二锑5份。
4.一种根据权利要求1至3任何一项所述的防水涂料的制造工艺，其特征在于：按上述质量份，将聚乙二醇、氢氧化铝和三氧化二锑混合，搅拌分散，加入天然橡胶和丁苯胶，充分搅拌，将水性聚氨酯倒入，充分搅拌后加入剩余原料，搅拌至均匀，即得所述防水涂料。
CN201410038740.4A 2014-01-26 2014-01-26 一种防水涂料及其制备工艺 Withdrawn CN103773214A (zh)