CN1037639C - 以银一氧化镉为基础的电接触材料及其生产工艺 - Google Patents

以银一氧化镉为基础的电接触材料及其生产工艺 Download PDF

Info

Publication number
CN1037639C
CN1037639C CN95111070A CN95111070A CN1037639C CN 1037639 C CN1037639 C CN 1037639C CN 95111070 A CN95111070 A CN 95111070A CN 95111070 A CN95111070 A CN 95111070A CN 1037639 C CN1037639 C CN 1037639C
Authority
CN
China
Prior art keywords
silver
cadmium oxide
contact material
ingot
colored
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN95111070A
Other languages
English (en)
Other versions
CN1128400A (zh
Inventor
林景兴
章景兴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin City Hongfa alloy material Co. Ltd.
Original Assignee
HONGFA ALLOY MATERIAL WORKS JIANGYIN
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=5078388&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=CN1037639(C) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by HONGFA ALLOY MATERIAL WORKS JIANGYIN filed Critical HONGFA ALLOY MATERIAL WORKS JIANGYIN
Priority to CN95111070A priority Critical patent/CN1037639C/zh
Publication of CN1128400A publication Critical patent/CN1128400A/zh
Application granted granted Critical
Publication of CN1037639C publication Critical patent/CN1037639C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

以银一氧化镉为基础的电接触材料及其生产工艺，它是在一种银基体中含有氧化镉，其成分范围为：Ag80-88%，CdO12-20%，Ni0.1-0.2%，各组成的总和为100%，其生产工艺为：将银锭、镉锭和镍锭置于熔炼炉中熔炼成铸锭，加工成碎屑，经高温高压氧化得到一种银氧化镉材料，碎屑在钢模中成型，然后在高温中挤压成一定规格的条材，再经拉拨便得到线材产品。本发明节约了贵金属银80%，且工艺流程短，设备投资少。

Description

以银一氧化镉为基础的电接触材料及其生产工艺
本发明涉及一种电接触材料及其生产工艺，尤其涉及一种以银氧化镉为基础的电接触材料及其生产工艺。
银氧化镉为基础的接触材料是一种重要的触点材料，它在1940年取得工业应用以来，根据电器产品的使用要求，目前已形成一个产品系列，即AgCaO8、AgCaO10和AgCdO12。其产品已广泛应用于额定电流为40～600A的交流接触器和额定电流小于100A的空气开关，以及重负载继电器和过流保护电器等。上述产品的生产方法有两种：即粉末冶金法和合金内氧化法。但上述方法生产的产品均存在各自的缺点：即粉末冶金法抗熔焊性好，但电寿命低；合金内部氧化法电寿命高，但由于其内外结构、性能不一致，因此其抗熔焊性差。因此，前者主要用于线路保护电器，后者主要用于控制电器。
本发明的目的在于提供一种CdO含量更高的银氧化镉电接触材料及其生产工艺。
本发明是这样实现的：一种以银一氧化镉为基础的电接触材料，它在一种银基体中含有氧化镉，其成份范围为：Ag80-88％，CdO12-20％，Ni0.1-0.2％，各组分的总和为100％。
上述以银一氧化镉为基础的电接触材料，该材料中还含有占总量0.01-0.15％的铝及锑。
上述以银一氧化镉为基础的电接触材料，组分中氧化镉的份额为13-19重量百分比(相对于材料的总重量)。
上述以银一氧化镉为基础的电接触材料中，组分中氧化镉的份额为13-19重量百分比(相对于材料的总重量)。
上述以银一氧化镉为基础的电接触材料，组分中氧化镉的份额为14-18重量百分比(相对于材料的总重量)。
上述以银一氧化镉为基础的电接触材料，组分中氧化镉的份额为15-18重量百分比(相对于材料的总重量)。
上述以银一氧化镉为基础的电接触材料，组分中氧化镉的份额为16.2-17.8重量百分比(相对于材料的总重量)。
本发明还可以是这样实现的：一种以银一氧化镉为基础的电接触材料的生产工艺，其工艺方法是：
将银锭、镉锭和镍锭置于熔炼炉中熔炼成铸锭，加工成碎屑，经高温高压氧化得到一种银氧化镉材料，碎屑在钢模中成型，然后在高温中挤压成一定规格的条材，再经过拉拨机拉拨得到线材产品。
上述高温高压氧化的温度为760-820℃，压力为4-6Kg/cm2，保温时间10-15小时，挤压成条材的加热温度为840-900℃。
与现有的以银一氧化镉为基础的电接触材料及其生产工艺相比，本发明由于采用了先氧化后挤压的生产工艺，使线材的内外结构性能一致，将以银一氧化镉为基础的电接触材料中的氧化镉含量由10-12％，提高到12-20％，且工艺流程短，设备投资少，并且与10-12％的银氧化镉具有同等的电气综合性能。因此节约了贵金属用银8％，具有很好的经济效益和社会效益。
线材的物理机械性能为：
规    格：Φ1.12-3.90mm
密    度：≥9.8g/cm3
硬    度：Hv4.9N＞700MPa
电 阻 率：≤2.7μΩ.cm
抗拉强度：＞220MPa
延 伸 率：＞6％
制成的AgCdO/Cu复合铆钉触头完全符合GB11098-89的各项技术要求。
图1为本发明的工艺流程图。
下面结合附图对本发明作一详细描述：
例一：
称取25.10Kg银锭和含镍10％的银镍合金0.62Kg，在中频感应炉在熔炼，随后加入4.756Kg的镉锭及占总量0.01-0.15％的铝及锑，清渣后铸成方锭或园锭，清除表面杂质及切去浇口，用车床或刨床或铣床加工成碎屑，装入高压容器中加热至760-800℃并注入4-5Kg/cm2的氧气，保持13-15小时，碎屑在钢模中压成Φ65mm长250mm的坯块，然后加热至860-880℃挤压成Φ4.0mm的条材，经拉拨机拉成Φ1.12-3.36mm的线材。
例二：
用例一的配料比熔炼铸成方锭，用轧机或挤压机制成片状合金带，用冲床或剪床制成碎片，装入高压容器中加热至800-820℃，并注入6Kg/cm2的氧气，保持10-12小时，再按例一中的成型、挤压条件，经拉拨后亦可制成Φ1.12-3.36mm的线材。

Claims (10)

1、一种以银一氧化镉为基础的电接触材料，它在一种银基体中含有氧化镉，其特征在于该材料中含有：Ag80-88％，CdO12-20％，Ni0.1-0.2％，各组分的总和为100％。
2、根据权利要求1所述的一种以银一氧化镉为基础的电接触材料，其特征在于该材料中还含有占总量0.01-0.15％的铝及锑。
3、根据权利要求1或2所述的一种以银一氧化镉为基础的电接触材料，其特征在于组分中氧化镉的份额为13-19重量百分比(相对于材料的总重量)。
4、根据权利要求1或2所述的一种以银一氧化镉为基础的电接触材料，其特征在于组分中氧化镉的份额为14-18重量百分比(相对于材料的总重量)。
5、根据权利要求1或2所述的一种以银一氧化镉为基础的电接触材料，其特征在于组分中氧化镉的份额为15-18重量百分比(相对于材料的总重量)。
6、根据权利要求1或2所述的一种以银一氧化镉为基础的电接触材料，其特征在于组分中氧化镉的份额为16.2-17.8重量百分比(相对于材料的总重量)。
7、根据权利要求1或2所述的一种以银一氧化镉为基础的电接触材料，其特征在于组分中氧化镉的份额为16.5-17.5重量百分比(相对于材料的总重量)。
8、一种以银一氧化镉为基础的电接触材料的生产工艺，其特征在于其工艺方法是：
将银锭、镉锭和镍锭置于熔炼炉中熔炼成铸锭，加工成碎屑，经高温高压氧化得到一种银氧化镉材料，再在钢模中成型，然后在高温中挤压成一定规格的条材，再经过拉拨便得到线材产品。
9、根据权利要求8所述的一种以银一氧化镉为基础的电接触材料的生产工艺，其特征在于高温高压氧化的温度为760-820℃，并注入4-6Kg/cm2的氧气，保持10-15小时，挤压成条材的加热温度为840-900℃。
10、根据权利要求8所述的一种以银一氧化镉为基础的电接触材料的生产工艺，其特征在于高温高压氧化的温度为800-820℃，并注入5-6Kg/cm2的氧气，保持8-12小时，挤压成条材的加热温度为860-880℃。
CN95111070A 1995-06-10 1995-06-10 以银一氧化镉为基础的电接触材料及其生产工艺 Expired - Fee Related CN1037639C (zh)