CN103756591A - Glue for producing corrugated case at high speed and preparation method thereof - Google Patents
Glue for producing corrugated case at high speed and preparation method thereof Download PDFInfo
- Publication number
- CN103756591A CN103756591A CN201310730170.0A CN201310730170A CN103756591A CN 103756591 A CN103756591 A CN 103756591A CN 201310730170 A CN201310730170 A CN 201310730170A CN 103756591 A CN103756591 A CN 103756591A
- Authority
- CN
- China
- Prior art keywords
- parts
- glue
- starch
- water
- caustic soda
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to glue and particularly relates to glue for producing a corrugated case at high speed and a preparation method thereof. The glue is prepared from following raw materials in parts by weight: 175-225 parts of starch, 700-800 parts of water, 4.5-6.5 parts of sodium hydroxide, 3-4.5 parts of borax, 4-6 parts of a stabilizing agent and 3-5 parts of a drying agent, wherein the starch is corn starch or cassava starch. According to the glue for producing the corrugated case at high speed, a starch additive is added to be used as an auxiliary material to make up of defects of a crude rubber production method; the bonding quality of a paper board is improved and the problems that the paper board is soft and bent, the speed cannot be accelerated and the like are solved, so that the vehicle speed of a high-speed production line of the corrugated case is improved to 50%; the process flow is simple, the utilization is safe and reliable and the production cost is low so that the technological requirements of high-speed production line of the corrugated case are met.
Description
technical field:
The present invention relates to a kind of glue, particularly a kind of glue for Corrugated Box high-speed production and preparation method thereof.
background technology:
The application of carton, Corrugated Box is more and more extensive.First the quality of Corrugated Box depends on the quality of corrugated cardboard, and the corrugated cardboard of high-quality is the prerequisite of making qualified carton.Quality of corrugated is relevant with the state of the art of temperature, web tension, tackiness agent and operator in making processes.
At present, in Corrugated Box production line, the tackiness agent of corrugated cardboard is mainly used Starch Adhesive, body paper is to consist of multiple fiber molecule, and starch adhesive is penetrated into fiber and forms the glue nail of root top shape from the surperficial pore of paper, between lining paper and stupefied peak, by glue, is followed closely effectively and is bonded together.And Starch Adhesive prepared by the raw ripe adhesive process of tradition can not adapt to the demand of high-speed production far away, high-strength corrugated board papery is better, tightness is high, and top sizing pore is blocked, and general glue perviousness is poor, easily occur false sticky, bubble, the quality problems such as come unstuck, consume starch too much, thereby cause that productivity is low, production cost is high, unstable product quality.
summary of the invention:
The deficiency existing in order to solve prior art, the invention provides a kind of glue for Corrugated Box high-speed production, and bond properties is good, paperboard bonding quality is improved, at utmost to adapt to the processing requirement of Corrugated Box high-speed production lines.
For solving the problems of the technologies described above, the present invention takes following technical scheme: a kind of glue for Corrugated Box high-speed production, and the raw material that contains following parts by weight:
175 ~ 225 parts of starch
700 ~ 800 parts, water
4.5 ~ 6.5 parts, caustic soda
3 ~ 4.5 parts of boraxs
4 ~ 6 parts of stablizers
3 ~ 5 parts, siccative
The present invention for the preferred parts by weight of glue Raw of Corrugated Box high-speed production is: 200 parts of starch, 750 parts, water, 5.5 parts, caustic soda, 3.5 parts of boraxs, 5 parts of stablizers, 5 parts, siccative.
Described starch is W-Gum or tapioca (flour).
The consumption situation of described siccative is adjusted according to the variation of weather.
The method of the glue for Corrugated Box high-speed production described in preparation comprises the following steps:
(1) caustic soda is added to the water and is reacted, make caustic soda completely soluble in water;
(2) starch is stirred after 5min, slowly add water-soluble caustic soda to stir and reach finite concentration;
(3) in uniform stirring, add borax, stablizer, siccative, and mix stirring 20min, get product.
Glue for Corrugated Box high-speed production prepared by the present invention, to add starch additive as auxiliary material, make up the defect of rubber making method, not only improved paperboard bonding quality, improved cardboard soft, bending, be unable to lift the problems such as high speed, make the Corrugated Box high-speed production lines speed of a motor vehicle bring up to 50%, and technical process is simple, safe and reliable, low production cost, thus be adapted to the processing requirement of Corrugated Box high-speed production lines.
embodiment:
Below by embodiment, technical scheme of the present invention is described in further detail.
Embodiment 1
Preferably, first according to following weight ratio, choose raw material: 96% caustic soda of the starch of 200 weight parts, the water of 750 weight parts, 5.5 weight parts, 95% borax of 3.5 weight parts, the stablizer of 5 weight parts, the siccative of 5 weight parts, stand-by.Wherein, described starch is W-Gum.
The method of the glue for Corrugated Box high-speed production described in preparation comprises the following steps:
(1) caustic soda is added to the water and is reacted, make caustic soda completely soluble in water;
(2) starch is stirred after 5min, slowly add water-soluble caustic soda to stir and reach finite concentration;
(3) in uniform stirring, add borax, stablizer, siccative, and mix stirring 20min, get product.
Embodiment 2
First according to following weight ratio, choose raw material: 96% caustic soda of the starch of 200 weight parts, the water of 750 weight parts, 5.5 weight parts, 95% borax of 3.5 weight parts, the stablizer of 5 weight parts, the siccative of 5 weight parts, stand-by.Wherein, described starch is tapioca (flour).
The method of the glue for Corrugated Box high-speed production described in preparation comprises the following steps:
(1) caustic soda is added to the water and is reacted, make caustic soda completely soluble in water;
(2) starch is stirred after 5min, slowly add water-soluble caustic soda to stir and reach finite concentration;
(3) in uniform stirring, add borax, stablizer, siccative, and mix stirring 20min, get product.
Embodiment 3
First according to following weight ratio, choose raw material: 96% caustic soda of the starch of 225 weight parts, the water of 800 weight parts, 6.5 weight parts, 95% borax of 4.5 weight parts, the stablizer of 6 weight parts, the siccative of 5 weight parts, stand-by.Wherein, described starch is W-Gum.
The method of the glue for Corrugated Box high-speed production described in preparation comprises the following steps:
(1) caustic soda is added to the water and is reacted, make caustic soda completely soluble in water;
(2) starch is stirred after 5min, slowly add water-soluble caustic soda to stir and reach finite concentration;
(3) in uniform stirring, add borax, stablizer, siccative, and mix stirring 20min, get product.
Embodiment 4
First according to following weight ratio, choose raw material: 96% caustic soda of the starch of 175 weight parts, the water of 700 weight parts, 4.5 weight parts, 95% borax of 3 weight parts, the stablizer of 4 weight parts, the siccative of 4 weight parts, stand-by.Wherein, described starch is W-Gum.
The method of the glue for Corrugated Box high-speed production described in preparation comprises the following steps:
(1) caustic soda is added to the water and is reacted, make caustic soda completely soluble in water;
(2) starch is stirred after 5min, slowly add water-soluble caustic soda to stir and reach finite concentration;
(3) in uniform stirring, add borax, stablizer, siccative, and mix stirring 20min, get product.
In Corrugated Box high-speed production lines, the Starch Adhesive that under the same terms prepared by the raw ripe adhesive process of tradition contrasts about the vehicle speed condition of adhesive applicator, corrugation A machine and corrugation B machine with the glue of embodiments of the invention 1 ~ 4 as a control group, as table 1: unit is: (cm
3/ s)
| ? | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Control group |
| Adhesive applicator | 120 | 119 | 100 | 102 | 65 |
| Corrugation A machine | 100 | 100 | 91.5 | 92 | 60 |
| Corrugation B machine | 95 | 95 | 90 | 89.5 | 55 |
According to the data analysis of above table 1, draw: glue of the present invention is with respect to the glue of control group, the speed of a motor vehicle of adhesive applicator, corrugation A machine and corrugation B machine has improved 40% ~ 50%, therefore, the gelatinization point of Corrugating Machine reduces relatively in process of production, not only can improve paperboard bonding quality, improved cardboard soft, bending, be unable to lift the problems such as high speed, and effectively reduce production cost, thereby be more adapted to the processing requirement of Corrugated Box high-speed production lines.
Claims (4)
1. the glue for Corrugated Box high-speed production, it is characterized in that the raw material that contains following parts by weight: 175 ~ 225 parts of starch, 700 ~ 800 parts, water, 4.5 ~ 6.5 parts, caustic soda, 3 ~ 4.5 parts of boraxs, 4 ~ 6 parts of stablizers, 3 ~ 5 parts, siccative.
2. the glue for Corrugated Box high-speed production according to claim 1, is characterized in that: the preferred parts by weight of described raw material are: 200 parts of starch, 750 parts, water, 5.5 parts, caustic soda, 3.5 parts of boraxs, 5 parts of stablizers, 5 parts, siccative.
3. the glue for Corrugated Box high-speed production according to claim 1 and 2, is characterized in that: described starch is W-Gum or tapioca (flour).
4. the method for the glue for Corrugated Box high-speed production of preparation as described in claim 1 ~ 3, is characterized in that, comprises the following steps:
Caustic soda is added to the water and is reacted, make caustic soda completely soluble in water;
Starch is stirred after 5min, slowly add water-soluble caustic soda to stir and reach finite concentration;
In uniform stirring, add borax, stablizer, siccative, and mix stirring 20min, get product.