CN103756564A - Preparation method of paint - Google Patents
Preparation method of paint Download PDFInfo
- Publication number
- CN103756564A CN103756564A CN201310705229.0A CN201310705229A CN103756564A CN 103756564 A CN103756564 A CN 103756564A CN 201310705229 A CN201310705229 A CN 201310705229A CN 103756564 A CN103756564 A CN 103756564A
- Authority
- CN
- China
- Prior art keywords
- preparation
- titanium dioxide
- parts
- paint
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation method of paint and belongs to the field of synthesizing industrial dye. Raw material preparation comprises the steps of sieving titanium dioxide through fine mesh gauze, uniformly stirring chrome yellow in the titanium dioxide, heating the titanium dioxide to 60-90 DEG C in an iron container, and cooling for later use; sequentially adding resin and methyl benzotriazole to the raw materials, uniformly mixing, adding a setting agent, and grinding the set raw materials in a ball mill for three times. The preparation method disclosed by the invention is simple in process and low in raw material cost; the paint, which is made from pure natural resin components, has good film-forming effect and strong adhesion, thus overcoming a shortcoming of long production cycle because of easily bubbling in original paint production; and the preparation method is applicable to decoration of all building houses.
Description
technical fieldthe present invention relates to a kind of preparation method of coating, belong to the synthetic field of industrial dyestuff.
background technologycoating is one of fuel common in industry, is widely used in house decoraton, finishing.According to different work demanding criteria; the kind of coating used hundreds of, its effect is all to form film at body surface, and by this film, plays the effect of protective layer; the function ratio of common existing coating is more diversified, can play insulation, antirust, mildew-resistant or heat-resisting effect.But in the preparation process of these coating, because the fusion reaction of various chemical feedstockss there will be foaming phenomenon, can significantly reduce surface tension, thereby reduce the coating result of coating.
summary of the inventionthe present invention is in order to make up above-mentioned technological deficiency, a kind of preparation method of coating is provided, and coating film-formation result prepared by this kind of method is good, strong adhesion, make up the easy defect that occurs bubbling and extend manufacture cycle in original coating material production, be applicable to the decorations in all buildings.
To achieve these goals, the technical solution adopted in the present invention is: a kind of preparation method of coating, is characterized in that coating comprises the following composition in mass parts:
25-45 parts of resins
20-30 parts of titanium dioxides
10-15 parts of chrome yellow
5-10 parts of tolyltriazole
Described resin is rosin, st-yrax.
Concrete preparation method is:
Preparation of raw material
With the crocus cloth titanium dioxide that sieves, chrome yellow is put into titanium dioxide and stir, put into container made of iron and heat 60-90 degrees Celsius, cooling rear standby;
Above-mentioned raw materials is added to resin, tolyltriazole successively, mix, put into setting agent, the raw material after sizing is put into ball mill grinding three times.
Beneficial effect of the present invention is: the method preparation technology is simple, raw materials cost is low, coating adopts pure natural resinous principle, film-formation result is good, strong adhesion, make up the easy defect that occurs bubbling and extend manufacture cycle in original coating material production, be applicable to the decorations in all buildings.
Embodiment
A preparation method for coating, is characterized in that coating comprises the following composition in mass parts:
22 parts of resins
28 parts of titanium dioxides
13 parts of chrome yellow
8 parts of tolyltriazole
Described resin is rosin, st-yrax;
Concrete preparation method is:
Preparation of raw material
With the crocus cloth titanium dioxide that sieves, chrome yellow is put into titanium dioxide and stir, put into container made of iron and heat 60-90 degrees Celsius, cooling rear standby;
Above-mentioned raw materials is added to resin, tolyltriazole successively, mix, put into setting agent, the raw material after sizing is put into ball mill grinding three times.
Claims (1)
1. a preparation method for coating, is characterized in that coating comprises the following composition in mass parts:
25-45 parts of resins
20-30 parts of titanium dioxides
10-15 parts of chrome yellow
5-10 parts of tolyltriazole
Described resin is rosin, st-yrax;
Concrete preparation method is:
Preparation of raw material
With the crocus cloth titanium dioxide that sieves, chrome yellow is put into titanium dioxide and stir, put into container made of iron and heat 60-90 degrees Celsius, cooling rear standby;
Above-mentioned raw materials is added to resin, tolyltriazole successively, mix, put into setting agent, the raw material after sizing is put into ball mill grinding three times.