CN103755338B - Environment-friendly ceramic material and preparation method thereof - Google Patents
Environment-friendly ceramic material and preparation method thereof Download PDFInfo
- Publication number
- CN103755338B CN103755338B CN201310715312.6A CN201310715312A CN103755338B CN 103755338 B CN103755338 B CN 103755338B CN 201310715312 A CN201310715312 A CN 201310715312A CN 103755338 B CN103755338 B CN 103755338B
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic material
- environment
- preparation
- friendlyceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses an environment-friendly ceramic material and a preparation method thereof. The environment-friendly ceramic material is prepared from the following raw materials in parts by weight: 10-20 parts of barium titanate, 10-30 parts of crop straws, 5-10 parts of magnesium oxide, 5-8 parts of silicon dioxide, 5-10 parts of titanium dioxide and 2-5 parts of aluminum blocks. The ceramic material prepared by using the crop straws as the raw materials has good performance; the ceramic manufacturing cost is reduced by adopting the ceramic material; waste biomasses are used in manufacturing industries, so that the effect of changing waste into valuable is truly realized.
Description
Technical field
The present invention relates to a kind of Environment-friendlyceramic ceramic material and preparation method thereof.
Background technology
Pottery liked by broad masses of the people deeply for a long time, and they have lot of advantages: the first, Heat stability is good, and heat transfer is slow; The second, chemical stability is good; Three, be easy to washing and keep clean; Four, water-intake rate is low.At present, the price of ceramic product is higher, and the raw material making pottery also compares shortage, needs to find new raw material.
Summary of the invention
For the deficiencies in the prior art, the invention provides a kind of Environment-friendlyceramic ceramic material and preparation method thereof.
The technical scheme taked for solving the present invention of prior art problem is: Environment-friendlyceramic ceramic material, comprises the following raw material counted by weight: barium titanate 10-20 part, agricultural crop straw 10-30 part, magnesium oxide 5-10 part, silicon-dioxide 5-8 part, titanium oxide 5-10 part, aluminium block 2-5 part.
Preferably, described agricultural crop straw is spartina alterniflora loisel's stalk.
The preparation method of above-mentioned Environment-friendlyceramic ceramic material, comprises the following steps:
(1) take above-mentioned raw materials by weight to put into ball mill and grind rear mistake 100 mesh sieve and obtain powder;
(2) after vacuumizing 5-10 minute under 750-800mmHg after above-mentioned powder slurrying, blank is obtained;
(3) blank is being carried out microwave drying at 30-45 DEG C, time of drying is 20-120min, sinters subsequently at 950-1200 DEG C, and sintering time is the Environment-friendlyceramic ceramic material of 30-40 hour.
Beneficial effect: the stupalith that the present invention utilizes agricultural crop straw to prepare for raw material, not only has good performance, also reduces and makes ceramic cost, by discarded biomass economy to production, really achieves and turns waste into wealth.
Embodiment
Below by specific embodiment, the present invention is further described in detail.
Embodiment 1
Environment-friendlyceramic ceramic material, comprises the following raw material counted by weight: barium titanate 10 parts, spartina alterniflora loisel's stalk 10 parts, 5 parts, magnesium oxide, silicon-dioxide 5 parts, titanium oxide 5 parts, aluminium block 2 parts.
The preparation method of above-mentioned Environment-friendlyceramic ceramic material, comprises the following steps:
(1) take barium titanate 10 parts by weight, spartina alterniflora loisel's stalk 10 parts, 5 parts, magnesium oxide, silicon-dioxide 5 parts, titanium oxide 5 parts, aluminium block 2 parts, put into ball mill and grind rear mistake 100 mesh sieve and obtain powder;
(2) after vacuumizing 5 minutes under 750mmHg after above-mentioned powder slurrying, blank is obtained;
(3) blank is being carried out microwave drying at 30 DEG C, time of drying is 20min, sinters subsequently at 950 DEG C, and sintering time is the Environment-friendlyceramic ceramic material of 30 hours.
Embodiment 2
Environment-friendlyceramic ceramic material, comprises the following raw material counted by weight: barium titanate 20 parts, spartina alterniflora loisel's stalk 30 parts, 10 parts, magnesium oxide, silicon-dioxide 8 parts, titanium oxide 10 parts, aluminium block 5 parts.
The preparation method of above-mentioned Environment-friendlyceramic ceramic material, comprises the following steps:
(1) take barium titanate 20 parts by weight, spartina alterniflora loisel's stalk 30 parts, 10 parts, magnesium oxide, silicon-dioxide 8 parts, titanium oxide 10 parts, aluminium block 5 parts, put into ball mill and grind rear mistake 100 mesh sieve and obtain powder;
(2) after vacuumizing 10 minutes under 800mmHg after above-mentioned powder slurrying, blank is obtained;
(3) blank is being carried out microwave drying at 45 DEG C, time of drying is 120min, sinters subsequently at 1200 DEG C, and sintering time is the Environment-friendlyceramic ceramic material of 40 hours.
Embodiment 3
Environment-friendlyceramic ceramic material, comprises the following raw material counted by weight: barium titanate 15 parts, spartina alterniflora loisel's stalk 20 parts, 8 parts, magnesium oxide, silicon-dioxide 6 parts, titanium oxide 8 parts, aluminium block 4 parts.
The preparation method of above-mentioned Environment-friendlyceramic ceramic material, comprises the following steps:
(1) take barium titanate 15 parts by weight, spartina alterniflora loisel's stalk 20 parts, 8 parts, magnesium oxide, silicon-dioxide 6 parts, titanium oxide 8 parts, aluminium block 4 parts, put into ball mill and grind rear mistake 100 mesh sieve and obtain powder;
(2) after vacuumizing 8 minutes under 780mmHg after above-mentioned powder slurrying, blank is obtained;
(3) blank is being carried out microwave drying at 40 DEG C, time of drying is 100min, sinters subsequently at 1000 DEG C, and sintering time is the Environment-friendlyceramic ceramic material of 35 hours.
The present invention carries out detected result as in the table below to Environment-friendlyceramic ceramic material.
In addition, the invention is not restricted to above-mentioned embodiment, as long as not exceeding in scope of the present invention, various mode can be taked to implement the present invention.
Claims (3)
1. Environment-friendlyceramic ceramic material, is characterized in that comprising the following raw material counted by weight: barium titanate 10-20 part, agricultural crop straw 10-30 part, magnesium oxide 5-10 part, silicon-dioxide 5-8 part, titanium oxide 5-10 part, aluminium block 2-5 part.
2. Environment-friendlyceramic ceramic material according to claim 1, is characterized in that: described agricultural crop straw is spartina alterniflora loisel's stalk.
3. the preparation method of Environment-friendlyceramic ceramic material according to claim 1, is characterized in that comprising the following steps:
(1) take above-mentioned raw materials by weight to put into ball mill and grind rear mistake 100 mesh sieve and obtain powder;
(2) after vacuumizing 5-10 minute under 750-800mmHg after above-mentioned powder slurrying, blank is obtained;
(3) blank is being carried out microwave drying at 30-45 DEG C, time of drying is 20-120min, sinters subsequently at 950-1200 DEG C, and sintering time is obtain Environment-friendlyceramic ceramic material in 30-40 hour.