CN103741520A - 用于聚酯纤维的高温匀染剂 - Google Patents
用于聚酯纤维的高温匀染剂 Download PDFInfo
- Publication number
- CN103741520A CN103741520A CN201310678369.3A CN201310678369A CN103741520A CN 103741520 A CN103741520 A CN 103741520A CN 201310678369 A CN201310678369 A CN 201310678369A CN 103741520 A CN103741520 A CN 103741520A
- Authority
- CN
- China
- Prior art keywords
- parts
- acetate
- polyester fibers
- high temperature
- leveler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于聚酯纤维的高温匀染剂,由如下原料制成:1~2份聚甘油单硬脂酸酯,0.2份醋酸锌,1份十二烷基三甲基氯化铵,80份匀染剂,0.1份醋酸镁,12份聚酰胺,0.3份醋酸钙,5份聚乙二醇,0.2份醋酸锡,4.5份乙二醇,3份对苯二甲酸二甲酯,1份羟基丙基甲基纤维素。本发明用于聚酯纤维的高温匀染剂,其不仅使得聚酯纤维染色后的织物色泽更加匀和、鲜艳,具有良好的匀染效果,而且可以改善聚酯纤维的蓬松柔软感、抗静电性、平滑亲水性。
Description
技术领域
本发明涉及用于聚酯纤维的高温匀染剂。
背景技术
现有的高温匀染剂用于聚酯纤维织物染色效果并不理想。
发明内容
本发明的目的在于提供一种用于聚酯纤维的高温匀染剂,其不仅使得聚酯纤维染色后的织物色泽更加匀和、鲜艳,具有良好的匀染效果,而且可以改善聚酯纤维的蓬松柔软感、抗静电性、平滑亲水性。
为实现上述目的,本发明的技术方案是设计一种用于聚酯纤维的高温匀染剂,由如下原料制成:
1~2份聚甘油单硬脂酸酯,
0.2份醋酸锌,
1份十二烷基三甲基氯化铵,
80份匀染剂,
0.1份醋酸镁,
12份聚酰胺,
0.3份醋酸钙,
5份聚乙二醇,
0.2份醋酸锡,
4.5份乙二醇,
3份对苯二甲酸二甲酯,
1份羟基丙基甲基纤维素。
本发明的优点和有益效果在于:提供一种用于聚酯纤维的高温匀染剂,其不仅使得聚酯纤维染色后的织物色泽更加匀和、鲜艳,具有良好的匀染效果,而且可以改善聚酯纤维的蓬松柔软感、抗静电性、平滑亲水性。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
实施例1
一种用于聚酯纤维的高温匀染剂,由如下原料制成:
2份聚甘油单硬脂酸酯,
0.2份醋酸锌,
1份十二烷基三甲基氯化铵,
80份匀染剂,
0.1份醋酸镁,
12份聚酰胺,
0.3份醋酸钙,
5份聚乙二醇,
0.2份醋酸锡,
4.5份乙二醇,
3份对苯二甲酸二甲酯,
1份羟基丙基甲基纤维素。
实施例2
一种用于聚酯纤维的高温匀染剂,由如下原料制成:
1份聚甘油单硬脂酸酯,
0.2份醋酸锌,
1份十二烷基三甲基氯化铵,
80份匀染剂,
0.1份醋酸镁,
12份聚酰胺,
0.3份醋酸钙,
5份聚乙二醇,
0.2份醋酸锡,
4.5份乙二醇,
3份对苯二甲酸二甲酯,
1份羟基丙基甲基纤维素。
实施例3
一种用于聚酯纤维的高温匀染剂,由如下原料制成:
1.2份聚甘油单硬脂酸酯,
0.2份醋酸锌,
1份十二烷基三甲基氯化铵,
80份匀染剂,
0.1份醋酸镁,
12份聚酰胺,
0.3份醋酸钙,
5份聚乙二醇,
0.2份醋酸锡,
4.5份乙二醇,
3份对苯二甲酸二甲酯,
1份羟基丙基甲基纤维素。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.用于聚酯纤维的高温匀染剂,其特征在于,由如下原料制成:
1~2份聚甘油单硬脂酸酯,
0.2份醋酸锌,
1份十二烷基三甲基氯化铵,
80份匀染剂,
0.1份醋酸镁,
12份聚酰胺,
0.3份醋酸钙,
5份聚乙二醇,
0.2份醋酸锡,
4.5份乙二醇,
3份对苯二甲酸二甲酯,
1份羟基丙基甲基纤维素。