CN103741483A - 一种金属花纹画布 - Google Patents

一种金属花纹画布 Download PDF

Info

Publication number
CN103741483A
CN103741483A CN201310679750.1A CN201310679750A CN103741483A CN 103741483 A CN103741483 A CN 103741483A CN 201310679750 A CN201310679750 A CN 201310679750A CN 103741483 A CN103741483 A CN 103741483A
Authority
CN
China
Prior art keywords
parts
turn
rotating speed
uniformly dispersed
dispersion machine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310679750.1A
Other languages
English (en)
Other versions
CN103741483B (zh
Inventor
陈卫宏
陈祎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Fenghuang painting material technology Co.,Ltd.
Original Assignee
WUXI PHOENIX DRAWING MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUXI PHOENIX DRAWING MATERIALS CO Ltd filed Critical WUXI PHOENIX DRAWING MATERIALS CO Ltd
Priority to CN201310679750.1A priority Critical patent/CN103741483B/zh
Publication of CN103741483A publication Critical patent/CN103741483A/zh
Application granted granted Critical
Publication of CN103741483B publication Critical patent/CN103741483B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种金属花纹画布，制备方法如下：（1）将清胶涂于织物的表面，然后在烘箱温度100-120℃下烘干，得到清胶层；（2）接着底层涂料涂于清胶层的表面，然后在烘箱温度90-100℃下烘干，得到底层涂料层；（3）然后再在底层涂料层上涂金属反光面涂料，然后在烘箱温度70-85℃下烘干，织物穿过烘箱的速度为6米/分到7米/分。本画布耐磨损，防水性能好，不易脱色，色彩鲜艳均匀，饱和度和垂感好。

Description

一种金属花纹画布
技术领域
本发明涉及绘画用品技术领域，尤其是涉及一种具有金属花纹的画布。
背景技术
传统画布一般都是白色底，虽可用于传统绘画，但用于现代抽象派等装饰画时，白底画布无法发挥出效果。而彩色底纹的画布可以色彩鲜艳，可以省去画家画背景的麻烦，背景色由涂层工艺直接完成，色彩均匀，具有饱和度，垂感好，用于装饰效果比白色底的画布效果要好。但是目前彩色底纹的画布种类单一，大都为各种色彩的搭配，难以满足市场需求。
发明内容
针对现有技术存在的上述问题，本申请人提供了一种金属花纹画布。本画布耐磨损，防水性能好，不易脱色，色彩鲜艳均匀，饱和度和垂感好。
本发明的技术方案如下：
一种金属花纹画布，制备方法如下：
A、清胶的制作：
（1）将纯丙乳液20份、去离子水10份，在转速为2000-3000转/min的分散机中分散均匀；
（2）在上个步骤制备的混合溶液中加入清浆20份，在转速为3000-3500转/min的分散机中分散均匀；
B、底层涂料的制作：
（1）将碳酸钙400份、滑石粉50份、998钛白粉50份、去离子水150份，在转速为2000-3000转/min的分散机中分散均匀；
（2）在上个步骤制备的混合溶液中加入纺织乳液150份、清浆100份，在转速为3000-3500转/min的分散机中分散均匀；
（3）在上个步骤制备的混合溶液中加入分散剂4份、消泡剂1份、增白剂1份、乳化助剂1份，成膜助剂5份，在转速为3000-3500转/min的分散机中分散均匀；
C、金属反光面涂料的制作：
（1）将碳酸钙200份、998钛白粉200份、二氧化硅15份、金属珠光粉200份、去离子水200份，在转速为2000-3000转/min的分散机中分散均匀；
（2）在上个步骤制备的混合溶液中加入纺织乳液350份、清浆100份，在转速为3000-3500转/min的分散机中分散均匀；
（3）在上个步骤制备的混合溶液中加入分散剂4份、消泡剂1份、增白剂1份、乳化助剂5份、成膜助剂5份、甘油5份，在转速为2000-3000转/min的分散机中分散均匀；
D、将步骤A、B、C制作的三种涂料通过涂层机均匀在织物上，制成金属反光涂层画布：
（1）将步骤A制作的清胶涂于织物的表面，在100-120℃的烘箱中烘干；
（2）接着将步骤B制作的底层涂料涂于清胶层的表面，在90-100℃的烘箱中烘干；
（4）最后再在面层涂料层涂上步骤D制作的金属反光面涂料，在70-85℃的烘箱中烘干，织物穿过烘箱的速度为6米/分到7米/分。
所述纺织乳液为水性聚氨酯乳液。所述清浆为聚乙烯醇。所述乳化助剂为AMP-95。
所述分散剂为TX-4、消泡剂为二甲基硅油、增白剂为二苯乙烯、成膜助剂为丙二醇丁醚。
本发明有益的技术效果在于：
1、本发明在金属粉层里特别添加低分子乳化助剂AMP-95，使颜料分散性更为充分，也有助于提高光泽，使画布表面金属花纹亮度好，更能展开艺术画框灵感发挥，手感好，布面柔软，具有画面饱和度，同时赋予涂料极优异的PH稳定性。
2、本发明在配方中特别选用纺织乳液：水性聚氨酯乳液（APU），使用热塑性聚氨酯乳液特别具有容易成膜，耐低温，弹性好、柔软等优点。
3、本发明采用无填充物清浆：聚乙烯醇涂层艺术油画布及其生产工艺，可以使具有表面性能优良，具有抗氧化性，对油画、丙烯画、水彩、水粉等绘画颜料的亲合力高。
4、本发明采用水性涂料消泡剂，在极低浓度下保持高效，极端PH条件下保持稳定有效，良好的稳定性，不易破乳，良好的分散性，水溶性能优良，防止微生物生长，无毒性，不会燃烧。
具体实施方式
本发明制备了一种金属花纹画布，制备方法如下：
A、清胶的制作：
（1）将纯丙乳液20份、去离子水10份，在转速为2000-3000转/min的分散机中分散均匀；
（2）在上个步骤制备的混合溶液中加入清浆20份，在转速为3000-3500转/min的分散机中分散均匀；
B、底层涂料的制作：
（1）将碳酸钙400份、滑石粉50份、998钛白粉50份、去离子水150份，在转速为2000-3000转/min的分散机中分散均匀；
（2）在上个步骤制备的混合溶液中加入纺织乳液150份、清浆100份，在转速为3000-3500转/min的分散机中分散均匀；
（3）在上个步骤制备的混合溶液中加入分散剂4份、消泡剂1份、增白剂1份、乳化助剂1份，成膜助剂5份，在转速为3000-3500转/min的分散机中分散均匀；
C、金属反光面涂料的制作：
（1）将碳酸钙200份、998钛白粉200份、二氧化硅15份、金属珠光粉200份、去离子水200份，在转速为2000-3000转/min的分散机中分散均匀；
（2）在上个步骤制备的混合溶液中加入纺织乳液350份、清浆100份，在转速为3000-3500转/min的分散机中分散均匀；
（3）在上个步骤制备的混合溶液中加入分散剂4份、消泡剂1份、增白剂1份、乳化助剂5份、成膜助剂5份、甘油5份，在转速为2000-3000转/min的分散机中分散均匀；
D、将步骤A、B、C制作的三种涂料通过涂层机均匀在织物上，制成金属反光涂层画布：
（1）将步骤A制作的清胶涂于织物的表面，在100-120℃的烘箱中烘干；
（2）接着将步骤B制作的底层涂料涂于清胶层的表面，在90-100℃的烘箱中烘干；
（4）最后再在面层涂料层涂上步骤D制作的金属反光面涂料，在70-85℃的烘箱中烘干，织物穿过烘箱的速度为6米/分到7米/分。
所述纺织乳液为水性聚氨酯乳液。所述清浆为聚乙烯醇。所述乳化助剂为AMP-95。所述分散剂为TX-4、消泡剂为二甲基硅油、增白剂为二苯乙烯、成膜助剂为丙二醇丁醚。所述织物为棉麻织物，如纯棉面料。 

Claims (4)

1.一种金属花纹画布，其特征在于制备方法如下：
A、清胶的制作：
（1）将纯丙乳液20份、去离子水10份，在转速为2000-3000转/min的分散机中分散均匀；
（2）在上个步骤制备的混合溶液中加入清浆20份，在转速为3000-3500转/min的分散机中分散均匀；
B、底层涂料的制作：
（1）将碳酸钙400份、滑石粉50份、998钛白粉50份、去离子水150份，在转速为2000-3000转/min的分散机中分散均匀；
（2）在上个步骤制备的混合溶液中加入纺织乳液150份、清浆100份，在转速为3000-3500转/min的分散机中分散均匀；
（3）在上个步骤制备的混合溶液中加入分散剂4份、消泡剂1份、增白剂1份、乳化助剂1份，成膜助剂5份，在转速为3000-3500转/min的分散机中分散均匀；
C、金属反光面涂料的制作：
（1）将碳酸钙200份、998钛白粉200份、二氧化硅15份、金属珠光粉200份、去离子水200份，在转速为2000-3000转/min的分散机中分散均匀；
（2）在上个步骤制备的混合溶液中加入纺织乳液350份、清浆100份，在转速为3000-3500转/min的分散机中分散均匀；
（3）在上个步骤制备的混合溶液中加入分散剂4份、消泡剂1份、增白剂1份、乳化助剂5份、成膜助剂5份、甘油5份，在转速为2000-3000转/min的分散机中分散均匀；
D、将步骤A、B、C制作的三种涂料通过涂层机均匀在织物上，制成金属反光涂层画布：
（1）将步骤A制作的清胶涂于织物的表面，在100-120℃的烘箱中烘干；
（2）接着将步骤B制作的底层涂料涂于清胶层的表面，在90-100℃的烘箱中烘干；
（4）最后再在面层涂料层涂上步骤C制作的金属反光面涂料，在70-85℃的烘箱中烘干，织物穿过烘箱的速度为6米/分到7米/分。
2.根据权利要求1所述的金属花纹画布，其特征在于所述纺织乳液为水性聚氨酯乳液。
3.根据权利要求1所述的金属花纹画布，其特征在于所述清浆为聚乙烯醇。
4.根据权利要求1所述的金属花纹画布，其特征在于所述乳化助剂为AMP-95。
CN201310679750.1A 2013-12-15 2013-12-15 一种金属花纹画布 Active CN103741483B (zh)