CN103739985A - PVC decorative plate - Google Patents
PVC decorative plate Download PDFInfo
- Publication number
- CN103739985A CN103739985A CN201310658027.5A CN201310658027A CN103739985A CN 103739985 A CN103739985 A CN 103739985A CN 201310658027 A CN201310658027 A CN 201310658027A CN 103739985 A CN103739985 A CN 103739985A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvc decorative
- pvc
- decorative plate
- lead
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a PVC decorative plate. The PVC decorative plate comprises following ingredients, by mass, 100 parts of PVC, 5 to 8 parts of MBS, 1 to 3 parts of carbon black, 2 to 4 parts of DOP, 50 to 80 parts of active heavy calcium carbonate, 4 to 6 parts of CPE, 1 to 5 parts of epoxidized soybean oil, 5 to 7 parts of tribasic lead sulfate, 2 to 5 parts of dibasic lead phosphate, 4 to 6 parts of a modifier, 1 to 4 parts of paraffin, 2 to 3 parts of barium stearate, and 0.5 to 1 part of lead stearate. Product relative density ranges from 0.9 to 0.95, bending strength ranges from 55 to 65MPa, impact strength ranges from 380 to 400MPa, tensile strength ranges from 80 to 85MPa, oxygen index ranges from 30 to 35%. The PVC decorative plate is high in hardness, is antistatic, can be used for replacing existing materials continuously, and large-scaled production is realized.
Description
Technical field
The application belongs to plastic material field, relates in particular to a kind of PVC decorative board.
Background technology
PVC decorative board has the features such as lightweight, heat insulation, insulation, moistureproof, fire-retardant, easy construction.Specification, color, pattern are various, are rich in ornamentally, can be applicable to the decoration of room interior wall and furred ceiling, are one of finishing material being most widely used in plastic materials; PVC finishing material product mainly contains: the monochromatic film cosmetic sheet of PVC, PVC is high temperature resistant cabin interior trim film, PVC transparent film, PVC vacuum forming cosmetic sheet, smooth decorating film of PVC etc.
PVC decorative board quality is light, heat insulation, insulation, moistureproof, fire-retardant, acid and alkali-resistance, anticorrosive.Stability, dielectricity are good, durable, anti-aging, easily welding and bonding.Bending strength and impelling strength are strong, and while breaking, extensibility is higher.Smooth surface, lovely luster, be rich in ornamentally, decorative applications face is wider; Construction technology is simple, easy for installation, along with the development of social city, technicalization, hommization, designs a kind of flexural strength high, and the high PVC section bar of shock strength, to meet the need of market, is very important.
Summary of the invention
the technical problem solving:
The application, for existing PVC decorative board flexural strength and the technical problem such as shock strength is low, provides a kind of PVC decorative board.
technical scheme:
A kind of PVC decorative board, be comprised of following raw materials according, take mass fraction representation as PVC100 part; MBS5-8 part; Carbon black 1-3 part; DOP2-4 part; Active water-ground limestone 50-80 part; CPE4-6 part; Epoxy soybean oil 1-5 part; Tribasic lead sulfate is 5-7 part; Dibasic lead phosphite is 2-5 part; Properties-correcting agent 4-6 part; Paraffin 1-4 part; Barium stearate 2-3 part; Lead stearate 0.5-1 part.
As a preferred technical solution of the present invention: described PVC decorative board, its moiety, take mass fraction representation as: its composition take mass fraction representation as PVC100 part; MBS6.5 part; 2 parts of carbon blacks; DOP3 part; 65 parts of active water-ground limestones; CPE5 part; 3 parts of epoxy soybean oils; Tribasic lead sulfate is 6 parts; Dibasic lead phosphite is 3.5 parts; 5 parts of properties-correcting agent; 2.5 parts, paraffin; 2.5 parts of barium stearates; 0.8 part of lead stearate.
As a preferred technical solution of the present invention: described properties-correcting agent adopts ACR.
beneficial effect:
A kind of PVC decorative board of the present invention adopts above technical scheme compared with prior art, has following technique effect: 1, product relative density 0.9-0.95, flexural strength 55-65MPa; 2, shock strength 380-400MPa; 3, tensile strength 80-85MPa, oxygen index 30-35%; 4, product hardness is high, antistatic, can the not division of history into periods of widespread production replace current material.
Embodiment
embodiment 1:
A kind of PVC decorative board, its composition is take mass fraction representation as PVC100 part; MBS5 part; 1 part of carbon black; DOP2 part; 50 parts of active water-ground limestones; CPE4 part; 1 part of epoxy soybean oil; Tribasic lead sulfate is 5 parts; Dibasic lead phosphite is 2 parts; 4 parts of ACR properties-correcting agent; 1 part, paraffin; 2 parts of barium stearates; 0.5 part of lead stearate.
Product relative density 0.9, flexural strength 55MPa; Shock strength 380MPa; Tensile strength 80MPa, oxygen index 30%.
embodiment 2:
A kind of PVC decorative board, its composition is take mass fraction representation as PVC100 part; MBS8 part; 3 parts of carbon blacks; DOP4 part; 80 parts of active water-ground limestones; CPE6 part; 5 parts of epoxy soybean oils; Tribasic lead sulfate is 7 parts; Dibasic lead phosphite is 5 parts; 6 parts of ACR properties-correcting agent; 4 parts, paraffin; 3 parts of barium stearates; 1 part of lead stearate.
Product relative density 0.92, flexural strength 60MPa; Shock strength 390MPa; Tensile strength 83MPa, oxygen index 33%.
embodiment 3:
A kind of PVC decorative board, is characterized in that: its composition is take mass fraction representation as PVC100 part; MBS6.5 part; 2 parts of carbon blacks; DOP3 part; 65 parts of active water-ground limestones; CPE5 part; 3 parts of epoxy soybean oils; Tribasic lead sulfate is 6 parts; Dibasic lead phosphite is 3.5 parts; 5 parts of ACR properties-correcting agent; 2.5 parts, paraffin; 2.5 parts of barium stearates; 0.8 part of lead stearate.
Product relative density 0.95, flexural strength 65MPa; Shock strength 400MPa; Tensile strength 85MPa, oxygen index 35%.
Composition all components in above embodiment all can business be bought.
Above-described embodiment is just for content of the present invention is set forth, rather than restriction, and therefore any change in implication and the scope suitable with claims of the present invention, all should think to be included in the scope of claims.
Claims (3)
1. a PVC decorative board, is characterized in that: its composition is take mass fraction representation as PVC100 part; MBS5-8 part; Carbon black 1-3 part; DOP2-4 part; Active water-ground limestone 50-80 part; CPE4-6 part; Epoxy soybean oil 1-5 part; Tribasic lead sulfate is 5-7 part; Dibasic lead phosphite is 2-5 part; Properties-correcting agent 4-6 part; Paraffin 1-4 part; Barium stearate 2-3 part; Lead stearate 0.5-1 part.
2. a kind of PVC decorative board according to claim 1, is characterized in that: its composition is take mass fraction representation as PVC100 part; MBS6.5 part; 2 parts of carbon blacks; DOP3 part; 65 parts of active water-ground limestones; CPE5 part; 3 parts of epoxy soybean oils; Tribasic lead sulfate is 6 parts; Dibasic lead phosphite is 3.5 parts; 5 parts of properties-correcting agent; 2.5 parts, paraffin; 2.5 parts of barium stearates; 0.8 part of lead stearate.
3. a kind of PVC decorative board according to claim 1, is characterized in that: described properties-correcting agent adopts ACR.