CN103739096A - 一种锅炉用缓蚀阻垢剂 - Google Patents

一种锅炉用缓蚀阻垢剂 Download PDF

Info

Publication number
CN103739096A
CN103739096A CN201410036889.9A CN201410036889A CN103739096A CN 103739096 A CN103739096 A CN 103739096A CN 201410036889 A CN201410036889 A CN 201410036889A CN 103739096 A CN103739096 A CN 103739096A
Authority
CN
China
Prior art keywords
parts
corrosion
boiler
scale inhibitor
kaolin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410036889.9A
Other languages
English (en)
Inventor
刘晓萍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410036889.9A priority Critical patent/CN103739096A/zh
Publication of CN103739096A publication Critical patent/CN103739096A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种锅炉用缓蚀阻垢剂，包括如下重量分数的组分：纳米改性高岭土6～10份、添加剂15～30份、水溶液60～70份、聚马来酸酐10～15份、硫酸锌0.2～0.8份、烷基醚1～4份、氨基磺酸5～10份、腐殖酸钠0.1～1份。本发明的锅炉用缓蚀阻垢剂原料来源广泛，生产成本低，阻垢效率高，腐蚀率低，耐高温，使用方便，特别适用于热水锅炉水处理，可大大延长锅炉使用寿命。

Description

一种锅炉用缓蚀阻垢剂
技术领域
本发明涉及化工水处理领域，具体地涉及一种锅炉用缓蚀阻垢剂。
背景技术
锅炉设备在长期使用后不可避免会出现结垢、锈蚀等现象，控制结垢是工业水处理的一大使命。所谓控制结垢，就是控制工业水运行过程中由于不稳定而产生的碳酸钙垢，由于“不配伍”而产生的硫酸钡、硫酸锶垢，由于采用聚磷酸盐、磷酸盐以及锌盐为缓蚀剂与水中的钙离子结合而生成的磷酸钙或磷酸锌垢，以及由于腐蚀而产生的氧化铁垢、因带入泥沙引起的沉积结构和因微生物菌藻产生的微生物大量繁殖。有机磷酸盐由于具有缓蚀和阻垢双重功能二成为首选品种，但仅靠有机膦酸盐的缓蚀作用效果仍不够理想，还需要加入与其有协同作用的缓蚀剂。目前，常用阻垢剂虽然在一定程度上可以解决工业锅炉水处理的结构问题，但仍然存在很多缺点，他们对水中的钙离子容忍度不高，在含铁和含油的水中阻垢能力下降，与其他税处理缓蚀阻垢剂的复配、配伍性能不尽如人意，不能达到锅炉阻垢的技术要求。
发明内容
发明目的：为解决现有技术中存在的技术问题，本发明提出一种锅炉用缓蚀阻垢剂。
技术内容：为实现上述技术目的，本发明提出一种锅炉用缓蚀阻垢剂，包括如下重量分数的组分：纳米改性高岭土6～10份、添加剂15～30份、水60～70份、聚马来酸酐10～15份、硫酸锌0.2～0.8份、烷基醚1～4份、氨基磺酸5～10份、腐殖酸钠0.1～1份。
优选地，所述锅炉用缓蚀阻垢剂包括纳米改性高岭土8份、添加剂20份、水65份、聚马来酸酐13份、硫酸锌00.5份、烷基醚3份、氨基磺酸7份、腐殖酸钠0.5份。
所述的纳米改性高岭土为碱性改性处理的煤系高岭土。
其中，所述碱性改性处理的步骤为：向煤系高岭土中加入NaOH和水，其中，以煤系高岭土中的SiO2的质量为基准，NaOH、H2O与SiO2的质量比为(1～3)∶(3～8)∶(15～20)，然后加入0.5wt％的氧化锆，搅拌升温至80～100℃，恒温3～5h，过滤，用去离子水充分洗涤，90～120℃烘干即得改性高岭土。
优选地，所述添加剂为苯磺酸钠、聚乙烯比咯烷酮、聚磷酸钠中的一种或多种。
胡敏酸钠和水溶性硫化元素具有缓蚀阻垢特性，产品水溶性好，扩散迅速，无毒无味，即使发生引用，也不会造成中毒现象，成本低廉，实用简单，同时具有防止供热管路结垢的作用。腐殖酸钠的作用与腐殖酸有关，腐殖酸是一种天然的有机高分子化合物，它含有较多的各类活性基团，这些活性基团决定了腐殖酸具有弱酸性、亲水性、离子交换性、络合性、氧化还原性及生理活性等，不但对各类垢型有络合溶解作用，而且对悬浮物具有分散和乳化作用。
有益效果：与现有技术相比，本发明的锅炉用缓蚀阻垢剂通过使用纳米改性高岭土、聚马来酸酐、硫酸锌、烷基醚、氨基磺酸和腐殖酸钠进行复配，充分发挥出各组分将的协同作用，制备出阻垢效果好的阻垢剂。
本发明的锅炉用缓蚀阻垢剂原料来源广泛，生产成本低，阻垢效率高，腐蚀率低，耐高温，使用方便，特别适用于热水锅炉水处理，可大大延长锅炉使用寿命。
具体实施方式
下述实施例中使用的化学试剂均为常规试剂。
实施例1纳米改性高岭土的制备。
取煤系高岭土(含量为SiO250wt％)30g，加入2g的NaOH和70g的水，搅拌均匀，然后加入0.3g的氧化锆，搅拌升温至90℃，恒温4h，过滤，用去离子水充分洗涤，100℃烘干即得改性高岭土。
实施例2纳米改性高岭土的制备。
取煤系高岭土(含量为SiO250wt％)40g，加入3g的NaOH和80g的水，搅拌均匀，然后加入0.5g的氧化锆，搅拌升温至100℃，恒温3h，过滤，用去离子水充分洗涤，120℃烘干即得改性高岭土。
实施例3锅炉用缓蚀阻垢剂的制备。
一种锅炉用缓蚀阻垢剂，包括如下重量分数的组分：纳米改性高岭土(实施例1)8份、苯磺酸钠20份、水65份、聚马来酸酐13份、硫酸锌0.5份、烷基醚3份、氨基磺酸7份、腐殖酸钠0.5份。将上述配方量的组分混合均匀，即得。
实施例4锅炉用缓蚀阻垢剂的制备。
一种锅炉用缓蚀阻垢剂，包括如下重量分数的组分：纳米改10份、纳米改性高岭土(实施例2)10份、聚乙烯比咯烷酮15份、水65份、聚马来酸酐10份、硫酸锌0.8份、烷基醚1份、氨基磺酸10份、腐殖酸钠0.2份。将上述配方量的组分混合均匀，即得。
实施例5锅炉用缓蚀阻垢剂的制备。
一种锅炉用缓蚀阻垢剂，包括如下重量分数的组分：纳米改性高岭土(实施例2)6份、聚磷酸钠30份、水70份、聚马来酸酐15份、硫酸锌0.3份、烷基醚4份、氨基磺酸6份、腐殖酸钠0.9份。将上述配方量的组分混合均匀，即得。
实施例6锅炉用缓蚀阻垢剂的制备。
一种锅炉用缓蚀阻垢剂，包括如下重量分数的组分：纳米改性高岭土(实施例1)8份、聚磷酸钠25份、水65份、聚马来酸酐12份、硫酸锌0.6份、烷基醚3份、氨基磺酸8份、腐殖酸钠1份。将上述配方量的组分混合均匀，即得。

Claims (4)

1.一种锅炉用缓蚀阻垢剂，其特征在于，包括如下重量分数的组分：纳米改性高岭土6～10份、添加剂15～30份、水60～70份、聚马来酸酐10～15份、硫酸锌0.2～0.8份、烷基醚1～4份、氨基磺酸5～10份、腐殖酸钠0.1～1份。
2.根据权利要求1所述的锅炉用缓蚀阻垢剂，其特征在于，所述的纳米改性高岭土为碱性改性处理的煤系高岭土。
3.根据权利要求2所述的锅炉用缓蚀阻垢剂，其特征在于，所述碱性改性处理的步骤为：向煤系高岭土中加入NaOH和水，其中，以煤系高岭土中的SiO2的质量为基准，NaOH、H2O与SiO2的质量比为(1～3)∶(60～80)∶(15～20)，然后加入0.5wt％的氧化锆，搅拌升温至80～100℃，恒温3～5h，过滤，用去离子水充分洗涤，90～120℃烘干即得改性高岭土。
4.根据权利要求1所述的锅炉用缓蚀阻垢剂，其特征在于，所述添加剂为苯磺酸钠、聚乙烯比咯烷酮、聚磷酸钠中的一种或多种。
CN201410036889.9A 2014-01-26 2014-01-26 一种锅炉用缓蚀阻垢剂 Pending CN103739096A (zh)