CN103722855A - Method for manufacturing flocking cold-rolled printing steel plate - Google Patents
Method for manufacturing flocking cold-rolled printing steel plate Download PDFInfo
- Publication number
- CN103722855A CN103722855A CN201210407451.8A CN201210407451A CN103722855A CN 103722855 A CN103722855 A CN 103722855A CN 201210407451 A CN201210407451 A CN 201210407451A CN 103722855 A CN103722855 A CN 103722855A
- Authority
- CN
- China
- Prior art keywords
- cold
- steel sheet
- rolled steel
- flocking
- sheet material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a method for manufacturing a building plate which resists corrosion and weathering, prevents dew from dropping, and has a certain heat-preservation performance, in particular to a method for manufacturing a flocking cold-rolled printing steel plate. The manufacturing method comprises the following steps of material selection, plate surface pretreatment, drying treatment, printing, adhesive and epoxy zinc-rich paint mixture coating, electrostatic flocking, drying program and inspection and storage. The method is characterized in that villi for electrostatic flocking are aramid villi, and a plate surface treating agent is a HAS656 passivator. The product obtained through the method has good fireproofing properties. After testing, the product is certified by the fireproofing grade B-1 of national building materials, is completely environment-friendly and no-pollution, and is also certified by environmental-friendliness. The product can be directly used in a room, has strong upright pile feeling, is bright in color and gentle in hand feel, and has sound-absorbing and light-absorbing performances and a good light diffuse reflection effect.
Description
Technical field
The present invention relates under a kind of corrosion-resistant, against weather, Antidewing water droplet, have the manufacture method of the building board of certain heat-insulating property, especially a kind of flocking cold-rolled steel sheet blows the manufacture method of card material.
Background technology
In Modern Decorative decoration, in a lot of situations, use cold-rolled steel sheet material, such as the square cold-rolled steel buckle that Integral ceiling is used, the large area cold-rolled steel varnish board that wall decoration is used.Flocking cold-rolled steel sheet material can provide and have more luxurious decorative effect than existing product, and suede layer itself has certain water absorbing capacity, in the situation that ambient humidity is excessive, dew can be remained on to the surface of sheet material, prevents that water droplet from dripping.But flocking cold-rolled steel sheet material exists cut velvet sense not strong, dull coloring, particularly, along with the expansion of matte surface area, flocking cold-rolled steel sheet material does not reach good light diffuse effect.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art, provide a kind of flocking cold-rolled steel sheet to blow the manufacture method of card material, the flocking cold-rolled steel sheet that the method obtains blows card material to be had under long service life, Antidewing water droplet, with features such as nonmetal cashmere-planted layers, can plant according to the color of flower the length fine hair of respective color, make after flocking spend life-like, flocking cold-rolled steel sheet blows card material, and to have cut velvet sense strong, color glow, sense of touch is soft, good light diffuse effect.
According to technical scheme provided by the invention, the manufacture method that a kind of flocking cold-rolled steel sheet blows card material comprises the steps:
(1), material selection: material selection thickness is the cold-rolled steel sheet material that 0,5～1.8mm, width are 1000～1400mm;
(2), plate face pretreatment: plate face is clean, enter surface treatment board without the cold-rolled steel sheet material that is coated with oil processing, with plate face inorganic agent, cold-rolled steel sheet material is applied to pretreatment, the one side coating speed of plate face inorganic agent is: 10～40m/min, the one side coated weight of plate face inorganic agent is: 0.6～1.6g/m
2, during coating, plate face inorganic agent temperature is 15～25 ℃;
(3), drying and processing: the cold-rolled steel sheet material after coated board face inorganic agent enters baking oven and carries out drying and processing, and oven temperature is: 55～75 ℃, drying time is 8～12 seconds;
(4), blow flower: cold-rolled steel sheet material enters and blows colored program and blow flower, blows the slurry of multicolour and form flower type on the surface of cold-rolled steel sheet material, blows colored pressure and is: 4500～5500Pa, blow colored speed and be: 10～16m/min, blow flower amount and be: 37～57g/m
2;
(5), adhesive and the coating of epoxy zinc-rich paint mixture: the cold-rolled steel sheet material blowing after spending is entered to adhesive and epoxy zinc-rich paint mixture coating program, the mixture of curable water-borne acrylate adhesive and epoxy zinc-rich paint is coated on cold-rolled steel sheet material, the coating speed of curable water-borne acrylate adhesive and epoxy zinc-rich paint mixture is: 10～15m/min, one side coating weight is: 68～120g/m
2, during coating, the temperature of curable water-borne acrylate adhesive and epoxy zinc-rich paint mixture is: 15～25 ℃;
(6), electrostatic spinning: the cold-rolled steel sheet material after adhesive and the coating of epoxy zinc-rich paint mixture enters the flocking of electrostatic spinning program, the fine hair of selecting during electrostatic spinning is aramid fiber fine hair, the voltage of flocking machinery is 65～120KV, the electric current of flocking machinery is 50～90MA, and flocking gross weight is 75～120g/m
2;
(7), drying program: the flocking cold-rolled steel sheet after blowing colored electrostatic spinning blows card material and enters drying oven and carry out drying program, adhesive and epoxy zinc-rich paint are dried, allow fine hair be combined as a whole by adhesive and epoxy zinc-rich paint and cold-rolled steel sheet material, kiln temperatures is 120～150 ℃, and drying time is: 3.5～4.5min;
(8), check warehouse-in: after drying program, flocking cold-rolled steel sheet is blown to card material and according to standard, check, passed examination product warehouse-in.
The invention has the beneficial effects as follows: there is a kind of senior cut velvet sense on the surface that flocking cold-rolled steel sheet blows card material, the ornamental of the intention of this uniqueness and its colorful outward appearance is best suited for as the ventilation duct exposing.Flocking cold-rolled steel sheet blows card material and has the characteristics such as heat insulation, Antidewing and water retaining function, and special-shaped roof corrugated plating, flat-top roof corrugated plating that arbitrarily manufacturing dimension differs make it with extraneous building one integrated mass and increase aesthetic feeling.Flocking cold-rolled steel sheet blows card material and has good absorbing sound and lowering noise performance, and effectively reduce the extraneous wind importing into and make an uproar and other noises, be the ideal material of meeting room, control room, central station of floating dock, broadcasting studio.
Method products obtained therefrom of the present invention has good fire line, after testing, passed through national building materials fire-protection rating B-1 level and authenticated, environmental protection completely, pollution-free, also pass through environmental certification, can be directly used in indoorly, there is cut velvet sense strong, color glow, feel is soft, sound-absorbing and photo absorption performance and good light diffuse effect.
The specific embodiment:
Below in conjunction with specific embodiment, the invention will be further described.
Embodiment 1
The manufacture method that a kind of flocking cold-rolled steel sheet of the present invention blows card material comprises the steps:
(1), material selection: material selection thickness is the cold-rolled steel sheet material that 0.5m, width are 1400mm;
(2), plate face pretreatment: plate face is clean, be that the cold-rolled steel sheet material that 0.5mm, width are 1400mm enters the plate face pretreatment that surface treatment board carries out coated board face inorganic agent without the thickness that is coated with oil processing, the plate face inorganic agent applying is the HAS656 passivator that ippon company produces, the one side coating speed of plate face inorganic agent is: 10m/min, the one side coated weight of plate face inorganic agent is: 1.6g/m
2, during coating, plate face inorganic agent temperature is 15 ℃;
(3), drying and processing: the cold-rolled steel sheet material after coated board face inorganic agent enters baking oven and carries out drying and processing, and oven temperature is; 55 ℃, drying time is 8 seconds;
(4), blow flower: cold-rolled steel sheet material enters and blows colored program and blow flower, blows the slurry of multicolour and form flower type on the surface of cold-rolled steel sheet material, blows colored pressure and is: 4500Pa, blow colored speed and be: 10m/min, blow flower amount and be: 57g/m
2;
(5), adhesive and the coating of epoxy zinc-rich paint mixture: the cold-rolled steel sheet material blowing after spending is entered to adhesive and epoxy zinc-rich paint mixture coating program, the mixture of curable water-borne acrylate adhesive and epoxy zinc-rich paint is coated on cold-rolled steel sheet material, the coating speed of curable water-borne acrylate adhesive and epoxy zinc-rich paint mixture is: 10m/min, one side coating weight is: 120g/m
2, during coating, the temperature of curable water-borne acrylate adhesive and epoxy zinc-rich paint mixture is: 15 ℃;
(6), electrostatic spinning: the cold-rolled steel sheet material after adhesive and the coating of epoxy zinc-rich paint mixture enters the flocking of electrostatic spinning program, the fine hair of selecting during electrostatic spinning is aramid fiber fine hair, the voltage of flocking machinery is 65KV, and the electric current of flocking machinery is 50MA, and flocking gross weight is 75g/m
2;
(7), drying program: the flocking cold-rolled steel sheet after blowing colored electrostatic spinning blows card material and enters drying oven and carry out drying program, adhesive and epoxy zinc-rich paint are dried, allow fine hair be combined as a whole by adhesive and epoxy zinc-rich paint and cold-rolled steel sheet material, kiln temperatures is 120 ℃, and drying time is: 3.5min;
(8), check warehouse-in: after drying program, flocking cold-rolled steel sheet is blown to card material and according to standard, check, passed examination product warehouse-in.
The product that the present embodiment obtains has good fire line, and after testing, passed through national building materials fire-protection rating B-1 level and authenticated, environmental protection completely, pollution-free, also pass through environmental certification.
Embodiment 2
The manufacture method that a kind of flocking cold-rolled steel sheet of the present invention blows card material comprises the steps:
(1), material selection: material selection thickness is the cold-rolled steel sheet material that 1.8mm, width are 1000mm;
(2), plate face pretreatment: plate face is clean, be 1 without the thickness that is coated with oil processing, the cold-rolled steel sheet material that 8mm, width are 1000mm enters the plate face pretreatment that surface treatment board carries out coated board face inorganic agent, the plate face inorganic agent applying is the HAS656 passivator that ippon company produces, the one side coating speed of plate face inorganic agent is: 40m/min, the one side coated weight of plate face inorganic agent is: 0.6g/m
2, during coating, plate face inorganic agent temperature is 25 ℃;
(3), drying and processing: the cold-rolled steel sheet material after coated board face inorganic agent enters baking oven and carries out drying and processing, and oven temperature is: 75 ℃, drying time is 12 seconds;
(4), blow flower: cold-rolled steel sheet material enters and blows colored program and blow flower, blows the slurry of multicolour and form flower type on the surface of cold-rolled steel sheet material, blows colored pressure and is: 5500Pa, blow colored speed and be: 16m/min, blow flower amount and be: 37g/m
2;
(5), adhesive and the coating of epoxy zinc-rich paint mixture: the cold-rolled steel sheet material blowing after spending is entered to adhesive and epoxy zinc-rich paint mixture coating program, the mixture of curable water-borne acrylate adhesive and epoxy zinc-rich paint is coated on cold-rolled steel sheet material, the coating speed of curable water-borne acrylate adhesive and epoxy zinc-rich paint mixture is: 15m/min, one side coating weight is: 68g/m
2, during coating, the temperature of curable water-borne acrylate adhesive and epoxy zinc-rich paint mixture is: 25 ℃;
(6), electrostatic spinning: the cold-rolled steel sheet material after adhesive and the coating of epoxy zinc-rich paint mixture enters the flocking of electrostatic spinning program, the fine hair of selecting during electrostatic spinning is aramid fiber fine hair, the voltage of flocking machinery is 120KV, and the electric current of flocking machinery is 90MA, and flocking gross weight is 120g/m
2;
(7), drying program: the flocking cold-rolled steel sheet after blowing colored electrostatic spinning blows card material and enters drying oven and carry out drying program, adhesive and epoxy zinc-rich paint are dried, allow fine hair be combined as a whole by adhesive and epoxy zinc-rich paint and cold-rolled steel sheet material, kiln temperatures is 150 ℃, and drying time is: 4.5min;
(8), check warehouse-in: after drying program, flocking cold-rolled steel sheet is blown to card material and according to standard, check, passed examination product warehouse-in.
The product that the present embodiment obtains has good fire line, and after testing, passed through national building materials fire-protection rating B-1 level and authenticated, environmental protection completely, pollution-free, also pass through environmental certification.
Embodiment 3
The manufacture method that a kind of flocking cold-rolled steel sheet of the present invention blows card material comprises the steps:
(1), material selection: material selection thickness is the cold-rolled steel sheet material that 1.3mm, width are 1200mm;
(2), plate face pretreatment: plate face is clean, be that the cold-rolled steel sheet material that 1.3mm, width are 1200mm enters the plate face pretreatment that surface treatment board carries out coated board face inorganic agent without the thickness that is coated with oil processing, the plate face inorganic agent applying is the HAS656 passivator that ippon company produces, the one side coating speed of plate face inorganic agent is: 25m/min, the one side coated weight of plate face inorganic agent is: 1.1g/m
2, during coating, plate face inorganic agent temperature is 20 ℃;
(3), drying and processing: the cold-rolled steel sheet material after coated board face inorganic agent enters baking oven and carries out drying and processing, and oven temperature is: 65 ℃, drying time is 10 seconds;
(4), blow flower: cold-rolled steel sheet material enters and blows colored program and blow flower, blows the slurry of multicolour and form flower type on the surface of cold-rolled steel sheet material, blows colored pressure and is: 5000Pa, blow colored speed and be: 13m/min, blow flower amount and be: 47g/m
2;
(5), adhesive and the coating of epoxy zinc-rich paint mixture: the cold-rolled steel sheet material blowing after spending is entered to adhesive and epoxy zinc-rich paint mixture coating program, the mixture of curable water-borne acrylate adhesive and epoxy zinc-rich paint is coated on cold-rolled steel sheet material, the coating speed of curable water-borne acrylate adhesive and epoxy zinc-rich paint mixture is: 12m/min, one side coating weight is: 90g/m
2, during coating, the temperature of curable water-borne acrylate adhesive and epoxy zinc-rich paint mixture is: 20 ℃;
(6), electrostatic spinning: the cold-rolled steel sheet material after adhesive and the coating of epoxy zinc-rich paint mixture enters the flocking of electrostatic spinning program, the fine hair of selecting during electrostatic spinning is aramid fiber fine hair, the voltage of flocking machinery is 90KV, and the electric current of flocking machinery is 70MA, and flocking gross weight is 100g/m
2;
(7), drying program: the flocking cold-rolled steel sheet after blowing colored electrostatic spinning blows card material and enters drying oven and carry out drying program, adhesive and epoxy zinc-rich paint are dried, allow fine hair be combined as a whole by adhesive and epoxy zinc-rich paint and cold-rolled steel sheet material, kiln temperatures is 140 ℃, and drying time is: 4.0min;
(8), check warehouse-in: after drying program, flocking cold-rolled steel sheet is blown to card material and according to standard, check, passed examination product warehouse-in.
The product that the present embodiment obtains has good fire line, and after testing, passed through national building materials fire-protection rating B-1 level and authenticated, environmental protection completely, pollution-free, also pass through environmental certification.
Claims (3)
1. the manufacture method that a flocking cold-rolled steel sheet blows card material comprises the steps:
(1), material selection: material selection thickness is the cold-rolled steel sheet material that 0.5～1.8mm, width are 1000～1400mm;
(2), plate face pretreatment: plate face is clean, enter surface treatment board without the cold-rolled steel sheet material that is coated with oil processing, with plate face inorganic agent, cold-rolled steel sheet material is applied to pretreatment, the one side coating speed of plate face inorganic agent is: 10～40m/min, the one side coated weight of plate face inorganic agent is: 0.6～1.6g/m
2, during coating, plate face inorganic agent temperature is 15～25 ℃;
(3), drying and processing: the cold-rolled steel sheet material after coated board face inorganic agent enters baking oven and carries out drying and processing, and oven temperature is: 55～75 ℃, drying time is 8～12 seconds;
(4), blow flower: cold-rolled steel sheet material enters and blows colored program and blow flower, blows the slurry of multicolour and form flower type on the surface of cold-rolled steel sheet material, blows colored pressure and is: 4500～5500Pa, blow colored speed and be: 10～16m/min, blow flower amount and be: 37～57g/m
2;
(5), adhesive and the coating of epoxy zinc-rich paint mixture: the cold-rolled steel sheet material blowing after spending is entered to adhesive and epoxy zinc-rich paint mixture coating program, the mixture of curable water-borne acrylate adhesive and epoxy zinc-rich paint is coated on cold-rolled steel sheet material, the coating speed of curable water-borne acrylate adhesive and epoxy zinc-rich paint mixture is: 10～15m/min, one side coating weight is: 68～120g/m
2, during coating, the temperature of curable water-borne acrylate adhesive and epoxy zinc-rich paint mixture is: 15～25 ℃;
(6), electrostatic spinning: the cold-rolled steel sheet material after adhesive and the coating of epoxy zinc-rich paint mixture enters the flocking of electrostatic spinning program, the fine hair of selecting during electrostatic spinning is aramid fiber fine hair, the voltage of flocking machinery is 65～120KV, the electric current of flocking machinery is 50～90MA, and flocking gross weight is 75～120g/m
2;
(7), drying program: the flocking cold-rolled steel sheet after blowing colored electrostatic spinning blows card material and enters drying oven and carry out drying program, adhesive and epoxy zinc-rich paint are dried, allow fine hair be combined as a whole by adhesive and epoxy zinc-rich paint and cold-rolled steel sheet material, kiln temperatures is 120～150 ℃, and drying time is: 3.5～4.5min;
(8), check warehouse-in: after drying program, flocking cold-rolled steel sheet is blown to card material and according to standard, check, passed examination product warehouse-in.
2. the manufacture method that a kind of flocking cold-rolled steel sheet according to claim 1 blows card material, is characterized in that: the fine hair of described electrostatic spinning is aramid fiber fine hair.
3. the manufacture method that a kind of flocking cold-rolled steel sheet according to claim 1 blows card material, is characterized in that: described plate face inorganic agent is HAS656 passivator.