CN203066384U - Film covered aluminum alloy plate for building and decorating - Google Patents
Film covered aluminum alloy plate for building and decorating Download PDFInfo
- Publication number
- CN203066384U CN203066384U CN 201220601582 CN201220601582U CN203066384U CN 203066384 U CN203066384 U CN 203066384U CN 201220601582 CN201220601582 CN 201220601582 CN 201220601582 U CN201220601582 U CN 201220601582U CN 203066384 U CN203066384 U CN 203066384U
- Authority
- CN
- China
- Prior art keywords
- alloy plate
- aluminum alloy
- film
- building
- adhesive layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a film covered aluminum alloy plate for building and decorating. The film covered aluminum alloy plate comprises an aluminum alloy plate and is characterized in that an adhesive layer is arranged on the aluminum alloy plate, a highlight biaxially oriented polyethylene terephthalate (BOPET) film is arranged on the adhesive layer, the adhesive layer is a mono propylene water-soluble combined emulsion adhesive layer, and the thickness of the BOPET film is 0.25-0.35um. The film covered aluminum alloy plate for building and decoration is long in service life, environmental friendly, fireproofing, anti-condensation, anti-corrosion, capable of absorbing sounds and lights, heat retaining, high in transparency grade, high in gloss, low in haze, excellent in ultraviolet ray barrier property, good in laser anti-counterfeiting property and good in decoration effect.
Description
Technical field
The utility model relates to a kind of building and ornament materials, is specially a kind of building and decoration aluminium alloys overlay film sheet material.
Background technology
In modern architecture and the decoration, can use the metal level that some paste lining material under a lot of situations, such as the metal sheet sticking glass fiber or foamed plastic pasting, the advantage of this class material is elegant in appearance, waterproof, easy to use, be widely applied to now in large-area buildings such as factory building, office block and the decoration.But also there is shortcoming in above-mentioned two kinds of materials commonly used: at first be that bonding intensity is not high, generally use about half a year that coming off to a certain degree all can appear in the lining material on surface; Next is the unnecessary lining bed material that this class material produces in process of production, can not be recycling.
Summary of the invention
The utility model is at the problems referred to above, a kind of building is provided and decorates with aluminium alloys overlay film sheet material, have low, the excellent ultraviolet isolating performance of long service life, environmental protection, fire prevention, anti-condensation, corrosion-resistant, sound-absorbing, extinction, insulation, the high grade of transparency, high gloss, mist degree, radium-shine laser anti-counterfeit performance, beautiful decorative effect.
The technical solution of the utility model is: a kind of building and decoration comprise aluminium alloy plate with aluminium alloys overlay film sheet material, it is characterized in that: the layer of adhesive layer is arranged above the described aluminium alloy plate, at adhesive phase one floor height light polyester BOPET film is arranged.
Described adhesive phase is the water-soluble synthetic emulsion glue-line of propylene class copoly type.
The thickness of the bright polyester BOPET of described height film is 0.25～0.35um.
The beneficial effects of the utility model are: because the utility model is covered with high bright polyester BOPET film on the aluminium alloy plate surface, therefore, aluminium alloys overlay film sheet material has low, the excellent ultraviolet isolating performance of long service life, environmental protection, fire prevention, anti-condensation, corrosion-resistant, sound-absorbing, extinction, insulation, the high grade of transparency, high gloss, mist degree, radium-shine laser anti-counterfeit performance, beautiful decorative effect.Compared with prior art, the utlity model has following advantage, economic effect:
1) Corrosion Protection is strong, good corrosion resistance.High bright polyester BOPET film has played the protective effect that one deck covers, and also can not influence its normal decay resistance even coating surface scratches, and makes product antirust effectively, and prolong about 3～5 times than zinc-plated coil of strip application life.
2) has good clod wash deep-draw processing forming.Replace traditional wooden construction with steel plate, sturdy and durable, in light weight, convenient transportation can efficiently be constructed energy conservation.
3) the beautiful ornamental and wideer scope of selecting for use.Be applicable to the high bright polyester BOPET film that covers shades of colour, multiple colored shape, can reach the decorative effect of emulation skin, parian, wood-imitated products.
4) just like dropping on landing rapidly on the lotus leaf, the film surface keeps clean on the film surface for the superpower hydrophobic self-cleaning function of the high bright polyester BOPET film natural imitation circle lotus leaf of the nanostructured of uniqueness, the globule.
5) smooth film surface dirt and spot are difficult to adhere to, and the film surface is very easily cleaned.
6) superpower anti-ultraviolet function is arranged.
7) radium-shine laser anti-counterfeit function.
Description of drawings
Fig. 1 is structural representation of the present utility model.
Among the figure, 1. aluminium alloy plate, 2. adhesive phase, 3. high bright polyester BOPET film.
The specific embodiment:
Below in conjunction with accompanying drawing the utility model is further described.
As shown in Figure 1, a kind of building and decoration comprise aluminium alloy plate 1 with aluminium alloys overlay film sheet material, it is characterized in that: layer of adhesive layer 2 is arranged above the described aluminium alloy plate 1, at adhesive phase 2 floor height light polyester BOPET film 3 is arranged.
Described adhesive phase 2 is the water-soluble synthetic emulsion glue-lines of propylene class copoly type.
The thickness of the bright polyester BOPET of described height film 3 is 0.25～0.35um.
Below in conjunction with coating technique on aluminium alloy plate 1 the utility model specific implementation process is described:
(1), unreels: be that the coiled material of 0.5 millimeter aluminium alloy plate 1 places on the unwinding device and opens, shakeouts with thickness;
(2), preceding storing and correction: the aluminium alloy plate 1 after the uncoiling enters preceding storage device storing, then enters two roller deviation correcting device corrections;
(3), material preliminary treatment: aluminium alloy plate 1 enters the Passivation Treatment that the passivation device carries out aluminium alloy plate 1 surface, enters passivation drying unit, cooler bin then, dries, cooling processing;
(4), gluing: aluminium alloy plate 1 enters glue spreading apparatus, adopts the water-soluble synthetic emulsification sol of propylene class copoly type as adhesive, and being coated on aluminium alloy plate 1 surface becomes adhesive phase 2;
(5), overlay film: the aluminium alloy plate 1 behind the gluing moves to film covering device and covers high bright polyester BOPET film 3, and the thickness of high bright polyester BOPET film 3 is 0.25um;
(6), oven dry: the aluminium alloy plate 1 behind the overlay film is dried processing at drying unit;
(7), arrangement: the unnecessary water-soluble synthetic emulsification sol of propylene class copoly type in aluminium alloy plate 1 surface is brushed at collating unit;
(8), cooling: the aluminium alloy plate 1 after cooling unit is with overlay film carries out cooling processing;
(9), hot pressing: by a pair of active rubber roll of hot-press arrangement, passive steel rider the overlay film on aluminium alloy plate 1 surface is carried out hot-pressing processing, reach combined strength bination greater than 0.5kg/cm
2
(10), back storing and correction: the aluminium alloy plate 1 behind the overlay film enters back storage device storing, then enters two roller deviation correcting device corrections;
(11), cleaning: by cleaning apparatus cleaning is carried out on aluminium alloy plate 1 surface and handled;
(12), rolling: the aluminium alloy plate 1 behind the overlay film enters wrap-up and is wound into finished product.
A kind of building and the technical performance of decorating with aluminium alloys overlay film sheet material and conventional composite plate compare
This shows, the utility model product has low, the excellent ultraviolet isolating performance of long service life, environmental protection, fire prevention, anti-condensation, corrosion-resistant, sound-absorbing, extinction, insulation, the high grade of transparency, high gloss, mist degree, radium-shine laser anti-counterfeit performance, beautiful decorative effect.
Claims (3)
1. build and decorate with aluminium alloys overlay film sheet material for one kind, comprise aluminium alloy plate, it is characterized in that: the layer of adhesive layer is arranged above the described aluminium alloy plate, at adhesive phase one floor height light polyester BOPET film is arranged.
2. a kind of building according to claim 1 and decorating with aluminium alloys overlay film sheet material, it is characterized in that: described adhesive phase is the water-soluble synthetic emulsion glue-line of propylene class copoly type.
3. a kind of building according to claim 1 and decorating with aluminium alloys overlay film sheet material, it is characterized in that: the thickness of the bright polyester BOPET of described height film is 0.25～0.35um.