CN103696282A - Production process of high-density nylon fabric - Google Patents
Production process of high-density nylon fabric Download PDFInfo
- Publication number
- CN103696282A CN103696282A CN201310652132.8A CN201310652132A CN103696282A CN 103696282 A CN103696282 A CN 103696282A CN 201310652132 A CN201310652132 A CN 201310652132A CN 103696282 A CN103696282 A CN 103696282A
- Authority
- CN
- China
- Prior art keywords
- agent
- production process
- working solution
- acid
- dyestuff degree
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production process of a high-density nylon fabric. The process comprises the following steps: (1) unwinding and sewing; (2) performing desizing pretreatment; (3) presetting at 170 DEG C, namely adding 5-6g/L isopropanolamine and a 30g/L anti-yellowing agent, wherein the liquid content is 40 percent; (4) dyeing; (5) fixing color, adding a 5g/L anion color fixing agent and 4g/L acetic acid, performing color fixing treatment for 50 minutes and washing with clear water; (6) dehydrating and scutching; (7) carrying out after finishing, namely adding a 30g/L water-proofing agent, a 5g/L silicone softening agent, a 8g/L crosslinking agent and 4g/L fatty alcohol-polyoxyethylene ether, wherein the liquid detention rate is 40 percent, the drying temperature is 120 DEG C and the baking temperature is 190 DEG C; and (8) calendering. By adopting the production process, the problems of easiness in high-temperature yellowing, poor ultraviolet resistance, poor water repellency, poor oil repellency, poor water washing resistance, low color fastness, not ideal downproofness and the like due to the adoption of a non-reasonable production process in the existing production process of high-density nylon fabrics are solved.
Description
Technical field
The present invention relates to highly dense nylon fabrics production technology.
Background technology
In existing highly dense nylon fabrics production process, easily there is the problems such as high temperature xanthochromia, UVResistant effect are not good, water and oil repellant water-wash resistance is poor, color fixation fastness weak, anti-chiseling down effect is undesirable.
Summary of the invention
The object of the present invention is to provide a kind of highly dense nylon fabrics production technology, solve in existing highly dense nylon fabrics production process due to unreasonable the brought easy generation high temperature xanthochromia of production technology, UVResistant effect is not good, water and oil repellant water-wash resistance is poor, a little less than color fixation fastness, the problem such as anti-chiseling down effect is undesirable.
For achieving the above object, technical scheme of the present invention is a kind of highly dense nylon fabrics production technology of design, comprises the steps:
1) debatching, margin to seam;
2) destarch pre-treatment;
3) pre-setting, adds 5-6g/L isopropanolamine, the anti-yellowing change agent of 30g/L, 170 ℃ of liquid carrying rate 40%, temperature;
4) dyeing, first dyes with A working solution and B working solution at normal temperatures, then with 4 ℃/min, is warming up to 85 ℃ and processes 1 hour, adds clear water washing; A working solution by the glacial acetic acid of 3g/L, the acid levelling agent of the anion nano assistant of dyestuff degree 3%, 5g/L, the ultraviolet absorber of dyestuff degree 7% form; B working solution by the acid navy blue of dyestuff degree 5%, red composition of acid sauce of the Indian yellow of dyestuff degree 7%, dyestuff degree 3%;
5) fixation, adds 5g/L anion color-fixing agent, 4g/L ice vinegar, fixation treatment 50 minutes, clear water washing;
6) dehydration, open-width;
7) after, arrange, add 30g/L waterproofing agent, 5g/L silicone body softener, 8g/L crosslinking agent, 4g/L fatty alcohol-polyoxyethylene ether, pick-up 40%, 120 ℃ of bake out temperatures, 190 ℃ of stoving temperatures;
8) press polish.
Advantage of the present invention and beneficial effect are: a kind of highly dense nylon fabrics production technology is provided, solve in existing highly dense nylon fabrics production process due to unreasonable the brought easy generation high temperature xanthochromia of production technology, UVResistant effect is not good, water and oil repellant water-wash resistance is poor, a little less than color fixation fastness, the problem such as anti-chiseling down effect is undesirable.
The specific embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples are only for technical scheme of the present invention is more clearly described, and can not limit the scope of the invention with this.
The concrete technical scheme of implementing of the present invention is:
Embodiment 1
A highly dense nylon fabrics production technology, comprises the steps:
1) debatching, margin to seam;
2) destarch pre-treatment;
3) pre-setting, adds 6g/L isopropanolamine, the anti-yellowing change agent of 30g/L, 170 ℃ of liquid carrying rate 40%, temperature;
4) dyeing, first dyes with A working solution and B working solution at normal temperatures, then with 4 ℃/min, is warming up to 85 ℃ and processes 1 hour, adds clear water washing; A working solution by the glacial acetic acid of 3g/L, the acid levelling agent of the anion nano assistant of dyestuff degree 3%, 5g/L, the ultraviolet absorber of dyestuff degree 7% form; B working solution by the acid navy blue of dyestuff degree 5%, red composition of acid sauce of the Indian yellow of dyestuff degree 7%, dyestuff degree 3%;
5) fixation, adds 5g/L anion color-fixing agent, 4g/L ice vinegar, fixation treatment 50 minutes, clear water washing;
6) dehydration, open-width;
7) after, arrange, add 30g/L waterproofing agent, 5g/L silicone body softener, 8g/L crosslinking agent, 4g/L fatty alcohol-polyoxyethylene ether, pick-up 40%, 120 ℃ of bake out temperatures, 190 ℃ of stoving temperatures;
8) press polish.
Embodiment 2
A highly dense nylon fabrics production technology, comprises the steps:
1) debatching, margin to seam;
2) destarch pre-treatment;
3) pre-setting, adds 5g/L isopropanolamine, the anti-yellowing change agent of 30g/L, 170 ℃ of liquid carrying rate 40%, temperature;
4) dyeing, first dyes with A working solution and B working solution at normal temperatures, then with 4 ℃/min, is warming up to 85 ℃ and processes 1 hour, adds clear water washing; A working solution by the glacial acetic acid of 3g/L, the acid levelling agent of the anion nano assistant of dyestuff degree 3%, 5g/L, the ultraviolet absorber of dyestuff degree 7% form; B working solution by the acid navy blue of dyestuff degree 5%, red composition of acid sauce of the Indian yellow of dyestuff degree 7%, dyestuff degree 3%;
5) fixation, adds 5g/L anion color-fixing agent, 4g/L ice vinegar, fixation treatment 50 minutes, clear water washing;
6) dehydration, open-width;
7) after, arrange, add 30g/L waterproofing agent, 5g/L silicone body softener, 8g/L crosslinking agent, 4g/L fatty alcohol-polyoxyethylene ether, pick-up 40%, 120 ℃ of bake out temperatures, 190 ℃ of stoving temperatures;
8) press polish.
Embodiment 3
A highly dense nylon fabrics production technology, comprises the steps:
1) debatching, margin to seam;
2) destarch pre-treatment;
3) pre-setting, adds 5.6g/L isopropanolamine, the anti-yellowing change agent of 30g/L, 170 ℃ of liquid carrying rate 40%, temperature;
4) dyeing, first dyes with A working solution and B working solution at normal temperatures, then with 4 ℃/min, is warming up to 85 ℃ and processes 1 hour, adds clear water washing; A working solution by the glacial acetic acid of 3g/L, the acid levelling agent of the anion nano assistant of dyestuff degree 3%, 5g/L, the ultraviolet absorber of dyestuff degree 7% form; B working solution by the acid navy blue of dyestuff degree 5%, red composition of acid sauce of the Indian yellow of dyestuff degree 7%, dyestuff degree 3%;
5) fixation, adds 5g/L anion color-fixing agent, 4g/L ice vinegar, fixation treatment 50 minutes, clear water washing;
6) dehydration, open-width;
7) after, arrange, add 30g/L waterproofing agent, 5g/L silicone body softener, 8g/L crosslinking agent, 4g/L fatty alcohol-polyoxyethylene ether, pick-up 40%, 120 ℃ of bake out temperatures, 190 ℃ of stoving temperatures;
8) press polish.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. highly dense nylon fabrics production technology, is characterized in that, comprises the steps:
1) debatching, margin to seam;
2) destarch pre-treatment;
3) pre-setting, adds 5-6g/L isopropanolamine, the anti-yellowing change agent of 30g/L, 170 ℃ of liquid carrying rate 40%, temperature;
4) dyeing, first dyes with A working solution and B working solution at normal temperatures, then with 4 ℃/min, is warming up to 85 ℃ and processes 1 hour, adds clear water washing; A working solution by the glacial acetic acid of 3g/L, the acid levelling agent of the anion nano assistant of dyestuff degree 3%, 5g/L, the ultraviolet absorber of dyestuff degree 7% form; B working solution by the acid navy blue of dyestuff degree 5%, red composition of acid sauce of the Indian yellow of dyestuff degree 7%, dyestuff degree 3%;
5) fixation, adds 5g/L anion color-fixing agent, 4g/L ice vinegar, fixation treatment 50 minutes, clear water washing;
6) dehydration, open-width;
7) after, arrange, add 30g/L waterproofing agent, 5g/L silicone body softener, 8g/L crosslinking agent, 4g/L fatty alcohol-polyoxyethylene ether, pick-up 40%, 120 ℃ of bake out temperatures, 190 ℃ of stoving temperatures;
8) press polish.