CN103691933A - 一种金属粉末造粒方法 - Google Patents

一种金属粉末造粒方法 Download PDF

Info

Publication number
CN103691933A
CN103691933A CN201310743777.2A CN201310743777A CN103691933A CN 103691933 A CN103691933 A CN 103691933A CN 201310743777 A CN201310743777 A CN 201310743777A CN 103691933 A CN103691933 A CN 103691933A
Authority
CN
China
Prior art keywords
powder
pulverize
briquet
order
mesh sieves
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310743777.2A
Other languages
English (en)
Inventor
冯继明
蒋贤雷
陈少贤
陈克
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHEJIANG PATN CONTACT CO Ltd
Original Assignee
ZHEJIANG PATN CONTACT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG PATN CONTACT CO Ltd filed Critical ZHEJIANG PATN CONTACT CO Ltd
Priority to CN201310743777.2A priority Critical patent/CN103691933A/zh
Publication of CN103691933A publication Critical patent/CN103691933A/zh
Pending legal-status Critical Current

Abstract

一种金属粉末造粒方法，金属粉末进行合批或混合，将混合粉在模具里压制为坯块，压制相对密度大于等于75％，将坯块在粉碎机里进行粉碎，然后过80目筛和400目筛，80目筛上粉末继续粉碎，400目以下粉末重新进行造粒，即根据上述要求继续进行压制、粉碎、过筛，直至得到的粉末流动性良好、松装比大。与已有技术相比，本发明的有益效果体现于：造粒方法不加粘结剂，对原料没有影响，且在以后的加工过程中粉末流动或快速熔化时，混合物成分不会偏析，保证了成分的均匀性和各物质的弥散分布。

Description

一种金属粉末造粒方法
技术领域
本发明涉及一种金属粉末造粒方法，具体地说是一种金属粉末冶金领域中的粉末造粒方法。
背景技术
在粉末冶金材料中，要求各相或各物质分布均匀，颗粒细小，从而提高材料的性能。这就要求原始粉末细小，有的甚至为纳米粉末，这种粉末混合后，粒度细且粉末不具有流动性。但在以后的生产工艺要求中，需要粉末有一定的流动性和松装密度，这就需要对原始的混合粉末进行造粒；而现有的造粒方法主要是采用加入粘结剂进行造粒，由于有粘结剂的加入，不可避免地对材料有污染，且在后续的生产过程中(如烧结、热喷焊、热喷涂等)产生烟雾和气体，对材料和人体产生影响，特别是含有氧化物材料的混合粉末(如银氧化锡、银氧化锌等)影响更大，因为大部分粘结剂分解物为还原气氛，能使氧化物还原。
中国专利曾公开了一种“金属粉末或者陶瓷粉末的造粒及其制法以及以造粒粉末为原料的烧结材料制造方法”(公开号：CN1340392A，公开日：2002年3月20日)，作为结合材料使用具有溶胶粘度在浓度为2％时具有300mPa.s以上粘性的天然高分子多糖类。作为天然高分子多糖类特别希望是高粘度琼脂。
发明内容
本发明的目的在于克服现有技术存在的上述缺陷，提供一种金属粉末造粒方方法；该方法不加粘结剂，对原料没有影响，且在以后的加工过程中粉末流动或快速熔化时，混合物成分不会偏析，保证了成分的均匀性和各物质的弥散分布。
为实现上述目的，本发明采取的解决方案是：一种金属粉末造粒方法，金属粉末进行合批或混合，将混合粉在模具里压制为坯块，压制相对密度大于等于75％，将坯块在粉碎机里进行粉碎，然后过80目筛和400目筛，80目筛上粉末继续粉碎，400目以下粉末重新进行造粒，即根据上述要求继续进行压制、粉碎、过筛，直至得到的粉末流动性良好、松装比大。
所述的金属粉末或是单质金属粉末或是合金粉末或是两种或两种以上的粉末的金属混合粉末。
在粉末冶金材料中，一般采用微小的粉末进行混合，使成分充分均匀，颗粒弥散分布于基体中，在造粒过程中应尽量减少对原始粉末的污染和影响。本发明做到了这一点：不加粘结剂，对原料没有影响；选择粉碎研磨方法可得到合适的粒度、流动性和松装比。特别地在以后的加工过程中粉末流动或快速熔化(热喷焊、热喷涂)时，混合物成分不会偏析，保证了成分的均匀性和各物质的弥散分布。
与已有技术相比，本发明的有益效果体现于：造粒方法不加粘结剂，对原料没有影响，且在以后的加工过程中粉末流动或快速熔化时，混合物成分不会偏析，保证了成分的均匀性和各物质的弥散分布。
具体实施方式
实施例一：一种电解铜粉粉末造粒方法，将电解铜粉粉末进行合批，将合批粉在模具里压制为坯块(压制相对密度约为75％)，将坯块在粉碎机里进行粉碎，然后过80目筛和320目筛，80目筛上粉末继续粉碎，400目以下粉末重新进行造粒，即根据上述要求继续进行压制、粉碎、过筛，直至得到的粉末流动性良好、松装比大。
实施例二：一种银镍[AgNi(10)]粉末造粒方法，将90％(重量百分比)的电解银粉(-300目)与10％(重量百分比)的镍粉(平均粒径8μm)进行混合，将混合粉在模具里压制为坯块(压制相对密度约为85％)，将坯块在粉碎机里进行粉碎，然后过80目筛和400目筛，80目筛上粉末继续粉碎，400目以下粉末重新进行造粒，即根据上述要求继续进行压制、粉碎、过筛，直至得到的粉末流动性良好、成分均匀。

Claims (4)

1.一种金属粉末造粒方法，其特征是：一种金属粉末造粒方法，金属粉末进行合批或混合，将混合粉在模具里压制为坯块，压制相对密度大于等于75％，将坯块在粉碎机里进行粉碎，然后过80目筛和400目筛，80目筛上粉末继续粉碎，400目以下粉末重新进行造粒，即根据上述要求继续进行压制、粉碎、过筛，直至得到的粉末流动性良好、松装比大。
2.根据权利要求1所述的一种金属粉末造粒方法，其特征是：所述的金属粉末或是单质金属粉末或是合金粉末或是两种或两种以上的粉末的金属混合粉末。
3.一种电解铜粉粉末造粒方法，其特征是：将电解铜粉粉末进行合批，将合批粉在模具里压制为坯块，压制相对密度约为75％，将坯块在粉碎机里进行粉碎，然后过80目筛和320目筛，80目筛上粉末继续粉碎，400目以下粉末重新进行造粒，即根据上述要求继续进行压制、粉碎、过筛，直至得到的粉末流动性良好、松装比大。
4.一种银镍粉末造粒方法，其特征是：将重量百分比90％的-300目电解银粉与10％的平均粒径8μm镍粉进行混合，将混合粉在模具里压制为坯块，压制相对密度约为85％，将坯块在粉碎机里进行粉碎，然后过80目筛和400目筛，80目筛上粉末继续粉碎，400目以下粉末重新进行造粒，即根据上述要求继续进行压制、粉碎、过筛，直至得到的粉末流动性良好、成分均匀。
CN201310743777.2A 2013-12-18 2013-12-18 一种金属粉末造粒方法 Pending CN103691933A (zh)