CN103689800B - 一种核桃壳颗粒复合嘴棒 - Google Patents
一种核桃壳颗粒复合嘴棒 Download PDFInfo
- Publication number
- CN103689800B CN103689800B CN201310645671.9A CN201310645671A CN103689800B CN 103689800 B CN103689800 B CN 103689800B CN 201310645671 A CN201310645671 A CN 201310645671A CN 103689800 B CN103689800 B CN 103689800B
- Authority
- CN
- China
- Prior art keywords
- walnut shell
- shell particle
- tip stick
- walnut
- prepared
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种核桃壳颗粒复合嘴棒。核桃壳经过微波膨胀、粉碎造粒、烘焙、调制后得到所述的核桃壳颗粒。将核桃壳颗粒应用于卷烟滤嘴中,添加量为嘴棒总重量的15~50%,制备得到二元复合嘴棒应用于卷烟中。通过实际应用表明,能够有效降低卷烟烟气中的焦油、烟碱、苯酚、巴豆醛等成分。本发明操作简便、成本低廉,具有良好地应用前景。
Description
技术领域
本发明属于卷烟材料技术领域,涉及卷烟过滤嘴嘴棒,具体是涉及一种能够降低卷烟烟气中有害成分的核桃壳颗粒复合嘴棒。
背景技术
有着“木本油料之王”称号的核桃具有极高的营养价值和良好的医疗保健作用,位列世界4大干果之首。云南是中国的核桃主要产区,现已拥有核桃种植面积1832万亩,目前产量已超过30万吨,约占全国产量的1/3、世界产量的16%,若取仁率按55%计算,则每年至少产生核桃壳13.5万吨。若集中的核桃壳被丢弃或被焚烧,造成资源的极大浪费。核桃壳含有大量的木质素、纤维素、半纤维素以及核桃醌、氢化胡桃醌,β-葡萄糖甙、鞣质、没食子酸等化学成分,具有抗菌、抗出血、抗氧化作用,可用做油脂抗氧化剂。核桃壳表面疏松多孔的结构,具有良好的吸附性能,科研工作者也对核桃壳进行改性或将其转化为活性碳后用于滤器的滤料及废气、污水处理等,能够很好的吸附重金属染料等化学污染物质。因此,加强对核桃壳的综合利用,可以避免资源的浪费,不仅可以有效处理固体废弃物,而且能够变废为宝。
随着吸烟与健康的问题越来越受到关注,如何提高卷烟的吸食安全性,降低卷烟烟气中的有害成分、提高抽吸的舒适感就成为各卷烟生产企业研发的热点。但关于利用核桃壳为原料制备能够有效降低卷烟烟气中焦油、烟碱、苯酚、巴豆醛等化学成分的多孔材料方面的报道较少,这也是本领域尚待解决的技术难题。
发明内容
本发明的目的在于针对现有技术的不足,提供一种能够有效降低卷烟主流烟气中部分有害成分的核桃壳颗粒复合嘴棒。
本发明的目的通过下述技术方案予以实现。
*除非另有说明,本发明中所采用的百分数均为质量百分数。
一种核桃壳颗粒复合嘴棒,通过以下步骤的方法制得:
(1)将含水率为20%~25%的核桃壳,置于微波膨胀设备中,在功率1200~1500W条件下膨胀60~90s;
(2)膨胀后的核桃壳用蒸馏水反复喷洒,调节含水率至12%~18%,并放置于室温下平衡6~8小时,备用;
(3)将平衡好的核桃壳粉碎至40~60目颗粒,置于80℃的烘箱中烘烤30~60分钟,保持颗粒水分在10~12%之间,备用;
(4)按重量份称取5~8份丙二醇、0~5份丙三醇和10~20份纯净水,搅拌均匀后备用;
(5)将步骤(4)制备的溶液按照1.5~1.8%的比例均匀地喷洒到步骤(3)所制备的颗粒中,在室温下放置6~10小时,即得到所需的核桃壳颗粒;
(6)将所制得的核桃壳颗粒通过复合滤棒成型机均匀地添加到卷烟滤嘴中,制备得到二元复合嘴棒。
添加量优选为嘴棒总重量的15~50%。
与现有技术相比,本发明具有以下优点:
1.采用核桃壳为原料,绿色环保,变废为宝,产品质量稳定;
2.所述核桃壳颗粒复合嘴棒应用于卷烟中,能够有效降低卷烟烟气中焦油、烟碱、苯酚、巴豆醛等化学成分。
3.本发明操作简便、原料易得、成本低廉,具有良好地应用前景。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白,以下结合实施例,对本发明作进一步详细说明。应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不是对本发明技术方案的限定。
实施例1
称取100g核桃壳,调节水分为20%,然后置于微波膨胀设备中,在1200w功率下膨胀60秒,将膨胀后的核桃壳用蒸馏水反复喷洒,使核桃壳的含水率为15%,并于室温下放置6小时后将其粉碎为40目的颗粒,同时将所制备的核桃壳颗粒放置于80℃的烘箱中烘烤30分钟左右,使颗粒的含水率为10%左右,然后将含有8份丙二醇、15份蒸馏水的混合溶液按照1.5%的比例均匀的喷洒到核桃壳颗粒中,于室温下放置6小时,即得到所需的核桃壳颗粒。
实施例2
称取2kg核桃壳,调节水分为25%,然后置于微波膨胀设备中,在1500w功率下膨胀90秒,将膨胀后的核桃壳用蒸馏水反复喷洒,使核桃壳的含水率为15%,并于室温下放置8小时后将其粉碎为60目的颗粒,将所制备的核桃壳颗粒放置于80℃的烘箱中烘烤60分钟左右,使颗粒的含水率为12%左右,然后将含有5份丙二醇、5份丙三醇、20份蒸馏水的混合溶液按照1.8%的比例均匀的喷洒到核桃壳颗粒中,与室温下放置10小时,即得到所需的核桃壳颗粒。
应用实施例1
在复合嘴棒成型机制备复合嘴棒的过程中,添加嘴棒重量25%实施例1制备的核桃壳颗粒,制备得到核桃壳颗粒嘴棒,以二元嘴棒的方式制备成卷烟,与对照空白样品的加工工艺条件相同,同时进行卷烟成分检测。结果表明:卷烟烟气中焦油降低8.3%、烟碱降低13.6%、苯酚降低22.6%,巴豆醛降低19.8%。对样品与对照进行感官评价表明,该样品明显能够丰富卷烟自然香气,对卷烟整体风格特征无明显影响。
应用实施例2
在复合嘴棒成型机制备复合嘴棒的过程中,添加嘴棒重量35%实施例2制备的核桃壳颗粒,制备得到核桃壳颗粒嘴棒,以二元嘴棒的方式制备成卷烟,与对照空白样品的加工工艺条件相同,同时进行卷烟成分检测。结果表明:卷烟烟气中焦油降低10.6%、烟碱降低9.8%,、苯酚降低24.5%、巴豆醛降低21.7%。对样品与对照进行感官评价表明,该样品明显能够丰富卷烟自然香气,对卷烟整体风格特征无明显影响。
以上所述仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等,均应包含在本发明的保护范围之内。
Claims (2)
1.一种核桃壳颗粒复合嘴棒,通过以下步骤的方法制得:
(1)将含水率为20%~25%的核桃壳,置于微波膨胀设备中,在功率1200~1500W条件下膨胀60~90s;
(2)膨胀后的核桃壳用蒸馏水反复喷洒,调节含水率至12%~18%,并放置于室温下平衡6~8小时,备用;
(3)将平衡好的核桃壳粉碎至40~60目颗粒,置于80℃的烘箱中烘烤30~60分钟,保持颗粒水分在10~12%之间,备用;
(4)按重量份称取5~8份丙二醇、0~5份丙三醇和10~20份纯净水,搅拌均匀后备用;
(5)将步骤(4)制备的溶液按照1.5~1.8%的质量比均匀地喷洒到步骤(3)所制备的颗粒中,在室温下放置6~10小时,即得到所需的核桃壳颗粒;
(6)将所制得的核桃壳颗粒通过复合滤棒成型机均匀地添加到卷烟滤嘴中,制备得到二元复合嘴棒。
2.根据权利要求1所述的核桃壳颗粒复合嘴棒,其特征在于:所述的核桃壳颗粒的添加量为嘴棒总重量的15~50%。