CN103674665A - 鉴别tp347hfg的浸蚀液及鉴别方法 - Google Patents
鉴别tp347hfg的浸蚀液及鉴别方法 Download PDFInfo
- Publication number
- CN103674665A CN103674665A CN201310708556.1A CN201310708556A CN103674665A CN 103674665 A CN103674665 A CN 103674665A CN 201310708556 A CN201310708556 A CN 201310708556A CN 103674665 A CN103674665 A CN 103674665A
- Authority
- CN
- China
- Prior art keywords
- tp347hfg
- etching solution
- sample
- tp347h
- identifying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
鉴别TP347HFG的浸蚀液及鉴别方法。TP347HFG是在TP347H钢的基础上通过制造工艺改善得到的新的钢种，其与TP347H具有化学成分的相似性。TP347H通过控制固溶处理温度、保温时间、冷加工成型等方面，使晶粒来不及长大，形成较为细小的晶粒，可以达到7～10级的晶粒度，此时，其与TP347HFG会无法辨识。现有的鉴别TP347HFG的方法是电解浸蚀方法，其电解浸蚀液对环境有污染，由于采用电解方法，其步骤繁琐，成本比较高。本发明由下述原料组成：所述的浸蚀液包括1.25-5g的三氯化铁、30-40ml含量35%的浓盐酸、5-10ml过氧化氢、50-70ml水。本发明用于鉴别TP347HFG。
Description
技术领域：
本发明涉及一种鉴别TP347HFG的浸蚀液及鉴别方法。
背景技术：
细晶粒不锈钢TP347HFG是20 世纪80 年代日本住友公司开发的奥氏体热强钢。这种钢被推荐使用于蒸汽温度为566℃、压力为316kgf/cm2的过热器和再热器管道。它具有优异的抗整体腐蚀的特性，同时具有较高的蠕变断裂强度。TP347HFG是在TP347H钢的基础上通过制造工艺改善得到的新的钢种，其与TP347H具有化学成分的相似性，同时，其高温蠕变强度、耐腐蚀尤其是抗高温蒸汽腐蚀性能高于TP347H。TP347H通过控制固溶处理温度、保温时间、冷加工成型等方面，使晶粒来不及长大，形成较为细小的晶粒，可以达到7～10级的晶粒度，此时，其与TP347HFG会无法辨识。
与TP347H在生产工艺上的差别为：TP347H采用900-1000℃进行软化处理，最终进行不小于1100℃的固溶处理；TP347HFG软化处理温度约为1200-1300℃，最终进行不小于1180℃的固溶处理。所以TP347HFG的晶粒度不同于一般钢种，其在软化退火后形成具有较大晶粒度的组织状态(原始晶粒度)，此晶粒较大；最终成型加工后固溶处理，由于NbC等第二相粒子的弥散析出，非自发形核率高，形成7~10级的细小晶粒(实际晶粒度)。现有的鉴别TP347HFG的方法是电解浸蚀方法，其电解浸蚀液对环境有污染，由于采用电解方法，其步骤繁琐，成本比较高。
发明内容：
本发明的目的是提供一种鉴别TP347HFG的浸蚀液及鉴别方法。
上述的目的通过以下的技术方案实现：
一种鉴别TP347HFG的浸蚀液，:其组成包括1.25-5g的三氯化铁、30-40ml含量35%的浓盐酸、5-10ml过氧化氢、50-70ml水。
一种所述的鉴别TP347HFG的浸蚀液的鉴别方法，该方法包括如下步骤：将TP347HFG进行机械加工，取金相试样，试样进行磨制，磨制好的试样进行抛光，抛光后将试样浸入鉴别TP347HFG的浸蚀液中，所述的浸蚀液包括1.25-5g的三氯化铁、30-40ml盐酸、5-10ml过氧化氢、50-70ml水，所述的浸蚀液漫过所检验试样的检验面，检验面离开检验用容器壁，从而预防对检验面的浸蚀效果造成影响，试样在所述的浸蚀液中浸蚀5～20s，待试样检验面变色，在静水中漂洗，用热风吹干，试样若能显示出TP347HFG的原始变形奥氏体形貌，则该试样是TP347HFG，否则不是TP347HFG。
有益效果：
1. 本发明可以准确、可靠、简便地检测出TP347HFG，操作安全、简单，成本廉价，无污染。
经本发明处理后的TP347HFG试样，能清楚地显示出原始晶粒度，使TP347HFG可以和细晶粒的TP347H进行分辨，从而用来鉴别TP347HFG。
本发明更加简便，免去电解，直接浸泡，且成本更低，更加方便操作，且无污染。
附图说明：
附图1是在本发明的浸蚀液浸蚀后的TP347HFG原始晶粒度图。
附图2是在本发明的浸蚀液浸蚀后的细晶粒TP347H晶粒度图。
具体实施方式：
实施例1：
一种鉴别TP347HFG的浸蚀液，所述的浸蚀液包括1.25-5g的三氯化铁、30-40ml含量35%的浓盐酸、5-10ml过氧化氢、50-70ml水，各种物质可以按照重量比例增加或者减少，也可以单一的在基准值的30%上下，按重量比例浮动。
实施例2：
上述的鉴别TP347HFG的浸蚀液的鉴别方法，该方法包括如下步骤：将TP347HFG进行机械加工，取金相试样，试样进行磨制，磨制好的试样进行抛光，抛光后将试样浸入鉴别TP347HFG的浸蚀液中，所述的浸蚀液包括重量份数比为1.25-5g的三氯化铁、30-40ml35%盐酸、5-10ml过氧化氢、50-70ml水，所述的浸蚀液漫过所检验试样的检验面，检验面不贴在检验用容器壁上，从而预防对检验面的浸蚀效果造成影响，试样在所述的浸蚀液中浸蚀5～20s，待试样检验面变色，在静水中漂洗，用热风吹干，试样若能显示出TP347HFG的原始变形奥氏体形貌，则该试样是TP347HFG，否则不是TP347HFG。
实施例3：
所述的鉴别TP347HFG的浸蚀液的鉴别方法，图1为本发明提供的浸蚀后的TP347HFG原始晶粒度图片，隐约的白色晶界即为高温软化退火后的奥氏体晶界。图2为本发明提供的浸蚀后的细晶粒TP347H晶粒度图片，图片上未见原奥氏体晶界。
Claims (2)
1.一种鉴别TP347HFG的浸蚀液，其特征是:其组成包括1.25-5g的三氯化铁、30-40ml含量35%的浓盐酸、5-10ml过氧化氢、50-70ml水。
2.一种权利要求1所述的鉴别TP347HFG的浸蚀液的鉴别方法，其特征是: 该方法包括如下步骤：将TP347HFG进行机械加工，取金相试样，试样进行磨制，磨制好的试样进行抛光，抛光后将试样浸入鉴别TP347HFG的浸蚀液中，所述的浸蚀液包括1.25-5g的三氯化铁、30-40ml35%的盐酸、5-10ml过氧化氢、50-70ml水，所述的浸蚀液漫过所检验试样的检验面，检验面离开检验用容器壁，从而预防对检验面的浸蚀效果造成影响，试样在所述的浸蚀液中浸蚀5～20s，待试样检验面变色，在静水中漂洗，用热风吹干，试样若能显示出TP347HFG的原始变形奥氏体形貌，则该试样是TP347HFG，否则不是TP347HFG。