CN103668983A - 一种织物阻燃整理剂及其制备方法 - Google Patents

一种织物阻燃整理剂及其制备方法 Download PDF

Info

Publication number
CN103668983A
CN103668983A CN201310597239.7A CN201310597239A CN103668983A CN 103668983 A CN103668983 A CN 103668983A CN 201310597239 A CN201310597239 A CN 201310597239A CN 103668983 A CN103668983 A CN 103668983A
Authority
CN
China
Prior art keywords
retardant
fire
fabric
finishing agent
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310597239.7A
Other languages
English (en)
Other versions
CN103668983B (zh
Inventor
温明华
温一波
吴志芳
陈宇豪
陈利军
陶城
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Hengxin Knitting Printing & Dyeing Co., Ltd.
Original Assignee
JIANGSU BOBOXIONG TEXTILES CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU BOBOXIONG TEXTILES CO Ltd filed Critical JIANGSU BOBOXIONG TEXTILES CO Ltd
Priority to CN201310597239.7A priority Critical patent/CN103668983B/zh
Publication of CN103668983A publication Critical patent/CN103668983A/zh
Application granted granted Critical
Publication of CN103668983B publication Critical patent/CN103668983B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种织物阻燃整理剂及其制备方法，采用醇类、脂肪酯类、阻燃性纤维素纤维、烯酸类以及引发剂、阻燃剂等物质为原料，通过阶段性的加热反应制成，不仅进一步保证了织物的阻燃性能，且生产方法简单，原料成本低，易得常见。本发明适用于家庭中床上用品等各种家庭装饰布的使用，有效防止家庭火灾的蔓延，提高安全指数。

Description

一种织物阻燃整理剂及其制备方法
技术领域
本发明涉及纺织助剂领域，尤其涉及一种织物阻燃整理剂及其制备方法。
背景技术
为了预防火灾，家具、床上用品、各种家庭装饰布制用品应当优选具有阻燃性能的织物，然而，对于床上用品和家具等，棉花和聚氨酯泡沫等易燃材料会更加舒适。如何在防止织物易燃的同时不损害其舒适度是一个需要我们去顾全的解决问题的方法，然而目前很多阻燃针织面料都存在舒适度不够的缺陷，为获得舒适度和阻燃性能兼备的织物，一方面可从织物本身的材料进行合理优化设计来解决，另一方面还需从织物后整理剂的使用上着手，目前合适的织物阻燃整理剂仍有很大的开发空间。
因此，需要一种新的技术解决上述问题。
发明内容
发明目的：为了解决现有技术所存在的问题，本发明提供了一种增强织物阻燃性能的织物阻燃整理剂及其制备方法。
技术方案：为达到上述目的，本发明采用以下技术方案：一种织物阻燃整理剂，由以下组份按照质量分数组成：碳原子个数为3～8的醇类2～30份；碳原子个数为3～12的脂肪酯类5～40份；阻燃性纤维素纤维10～60份；烯酸类2～50份；引发剂0.2～6份；阻燃剂YS-F10300.5～10份；水2～100份。
更为优选的，所述醇类为苯乙醇、丙三醇、正丁醇中的一种或多种。
更为优选的，所述脂肪酯类为甲酸甲酯、丙烯酸乙酯、乙酸二甲基庚酯中的一种或多种。
更为优选的，所述阻燃性纤维素纤维为化学改性阻燃性纤维素纤维。
更为优选的，所述烯酸类为聚合物类烯酸。
上述一种织物阻燃整理剂的制备方法，包括以下步骤：首先将醇类与脂肪酯类在450℃下加热回流2～4h后得到中间体，再将中间体与烯酸类进行反应，反应条件为300℃加热2～3h后加入阻燃性纤维素纤维、引发剂、阻燃剂、水后升高温度至400℃继续加热1h后冷却至室温得到最终产物。
更进一步的，所述升高到400℃的温度升温速度为1～2℃/min。
有益效果：本发明所提供的一种织物阻燃整理剂及其制备方法，采用醇类、脂肪酯类、阻燃性纤维素纤维、烯酸类以及引发剂、阻燃剂等物质为原料，通过阶段性的加热反应制成，不仅进一步保证了织物的阻燃性能，且生产方法简单，原料成本低，易得常见。本发明适用于家庭中床上用品等各种家庭装饰布的使用，有效防止家庭火灾的蔓延，提高安全指数。
具体实施方式
下面结合具体实施例对本发明进行进一步说明：
实施例1：
一种织物阻燃整理剂，由以下组份按照质量分数组成：碳原子个数为苯乙醇2份；甲酸甲酯5份；化学改性阻燃性纤维素纤维10份；聚合物类烯酸2份；引发剂0.2份；阻燃剂YS-F10300.5份；水2份。
上述一种织物阻燃整理剂的制备方法，包括以下步骤：首先将醇类与脂肪酯类在450℃下加热回流2h后得到中间体，再将中间体与烯酸类进行反应，反应条件为300℃加热2h后加入阻燃性纤维素纤维、引发剂、阻燃剂、水后以1℃/min的升温速度升高温度至400℃继续加热1h后冷却至室温得到最终产物。
实施例2：
一种织物阻燃整理剂，由以下组份按照质量分数组成：丙三醇30份；丙烯酸乙酯40份；化学改性阻燃性纤维素纤维60份；聚合物类烯酸50份；引发剂6份；阻燃剂YS-F103010份；水100份。
上述一种织物阻燃整理剂的制备方法，包括以下步骤：首先将醇类与脂肪酯类在450℃下加热回流4h后得到中间体，再将中间体与烯酸类进行反应，反应条件为300℃加热3h后加入阻燃性纤维素纤维、引发剂、阻燃剂、水后以2℃/min的升温速度升高温度至400℃继续加热1h后冷却至室温得到最终产物。
实施例3：
一种织物阻燃整理剂，由以下组份按照质量分数组成：正丁醇16份；乙酸二甲基庚酯18份；化学改性阻燃性纤维素纤维35份；聚合物类烯酸25份；引发剂3份；阻燃剂YS-F10305份；水50份。
上述一种织物阻燃整理剂的制备方法，包括以下步骤：首先将醇类与脂肪酯类在450℃下加热回流3h后得到中间体，再将中间体与烯酸类进行反应，反应条件为300℃加热2.5h后加入阻燃性纤维素纤维、引发剂、阻燃剂、水后以1.5℃/min的升温速度升高温度至400℃继续加热1h后冷却至室温得到最终产物。
应当指出，以上具体实施方式仅用于说明本发明而不用于限制本发明的范围，在阅读了本发明之后，本领域技术人员对本发明的各种等价形式的修改均落于本申请所附权利要求所限定的范围。

Claims (7)

1.一种织物阻燃整理剂，其特征在于由以下组份按照质量分数组成：碳原子个数为3～8的醇类2～30份；碳原子个数为3～12的脂肪酯类5～40份；阻燃性纤维素纤维10～60份；烯酸类2～50份；引发剂0.2～6份；阻燃剂YS-F10300.5～10份；水2～100份。
2.根据权利要求1所述的一种织物阻燃整理剂，其特征在于：所述醇类为苯乙醇、丙三醇、正丁醇中的一种或多种。
3.根据权利要求1所述的一种织物阻燃整理剂，其特征在于：所述脂肪酯类为甲酸甲酯、丙烯酸乙酯、乙酸二甲基庚酯中的一种或多种。
4.根据权利要求1所述的一种织物阻燃整理剂，其特征在于：所述阻燃性纤维素纤维为化学改性阻燃性纤维素纤维。
5.根据权利要求1所述的一种织物阻燃整理剂，其特征在于：所述烯酸类为聚合物类烯酸。
6.如权利要求1所述的一种织物阻燃整理剂的制备方法，其特征在于包括以下步骤：首先将醇类与脂肪酯类在450℃下加热回流2～4h后得到中间体，再将中间体与烯酸类进行反应，反应条件为300℃加热2～3h后加入阻燃性纤维素纤维、引发剂、阻燃剂、水后升高温度至400℃继续加热1h后冷却至室温得到最终产物。
7.根据权利要求6所述的一种织物阻燃整理剂的制备方法，其特征在于：所述升高到400℃的温度升温速度为1～2℃/min。
CN201310597239.7A 2013-11-22 2013-11-22 一种织物阻燃整理剂及其制备方法 Expired - Fee Related CN103668983B (zh)