CN103666713A - General emulsified cutting fluid and preparation method thereof - Google Patents
General emulsified cutting fluid and preparation method thereof Download PDFInfo
- Publication number
- CN103666713A CN103666713A CN201310654017.4A CN201310654017A CN103666713A CN 103666713 A CN103666713 A CN 103666713A CN 201310654017 A CN201310654017 A CN 201310654017A CN 103666713 A CN103666713 A CN 103666713A
- Authority
- CN
- China
- Prior art keywords
- cutting fluid
- parts
- water
- polyoxyethylene sorbitan
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A general emulsified cutting fluid is prepared from the following raw materials: by weight, 1-2 parts of monoisopropanolamine, 4-6 parts of 2-amino-2-methyl-1-propanol, 3-4 parts of triphenyl phosphite, 1-2 parts of cyanuric acid zinc, 1-2 parts of lignosulfonate, 1-2 parts of 2,6-butylated hydroxytoluene, 0.4-1.0 part of polyoxyethylene sorbitan monooleate, 20-23 parts of kerosene, 6-8 parts of an additive and 200 parts of water; the general emulsified cutting fluid forms a stable emulsification system, and is good in cooling, lubrication and cleaning properties, through the use of the cyanuric acid zinc, the general emulsified cutting fluid can effectively prevent metal corrosion, as well as has a strong ability for inhibition of bacteria, fungi and mold, the service life of the cutting fluid is prolonged, and the production cost is reduced. The general emulsified cutting fluid is non-corrosive to most metals, alloys, silicon wafers and other materials, and is high in applicability.
Description
Technical field
The present invention relates to cutting fluid technical field, relate in particular to a kind of general emulsion cutting fluid and preparation method thereof.
Background technology
Cutting fluid should possess good cooling performance, lubricity, rustless property, oil removing cleaning function, anti-corrosion function, easily dilutable feature.Cutting fluid can be divided into two classes, oil soluble cutting fluid and water-soluble metalworking liquid at present.General oil soluble cutting fluid lubrication performance is good, but poor cooling performance, and contain large amount of organic, contaminate environment.Although some water-soluble metalworking liquid cooling performances are good, there is again the poor problem of oilness and rust-proof effect, therefore research and development have concurrently oilness, cooling, rust-preventing characteristic, easy cleaning, nontoxic, tasteless, non-corrosive to human body, to equipment not burn into the non-staining cutting fluid of environment is just seemed to very important.
Summary of the invention
The object of the present invention is to provide a kind of general emulsion cutting fluid and preparation method thereof, that this cutting fluid has is corrosion-free, use range wide, the feature of good antimicrobial effect.
Technical scheme of the present invention is as follows:
A kind of general emulsion cutting fluid, it is characterized in that being made by the raw material of following weight part: monoisopropanolamine 1-2,2-amino-2-methyl-1-propanol 4-6, triphenyl phosphite 3-4, cyanuric acid zinc 1-2, sulfonated lignin 1-2,2,6 ditertiary butyl p cresol 1-2, polyoxyethylene sorbitan monooleate 0.4-1.0, kerosene 20-23, auxiliary agent 6-8, water 200; Described auxiliary agent is made by the raw material of following weight part: polyoxyethylene sorbitan monooleate 2-3, aluminum nitride powder 0.1-0.2, boric acid 2-3, morpholine 1-2, water glass 1-2, silane coupling agent KH-5601-2, Potassium Persulphate 1-2, peach gum 3-4, water 20-24; Preparation method be Potassium Persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 ℃, stirring reaction 1-2 hour, obtains.
The preparation method of described general emulsion cutting fluid, is characterized in that comprising the following steps: water, sulfonated lignin, polyoxyethylene sorbitan monooleate are mixed, be heated to 40-50 ℃; Under 3000-4000 rev/min of stirring, add 2-amino-2-methyl-1-propanol, triphenyl phosphite, kerosene, auxiliary agent, continue to be heated to 70-80 ℃, stir 10-15 minute; Add other remaining components, continue to stir 15-25 minute, obtain.
Beneficial effect of the present invention
The emulsification system that cutting fluid of the present invention forms is stable, and cooling, oilness, cleaning are good, by using cyanuric acid zinc, effectively prevent metallic corrosion, bacterium, fungi, mould are had to very strong inhibition ability simultaneously, extended the work-ing life of cutting fluid, reduce production costs.Cutting fluid of the present invention is corrosion-free to materials such as most metals, alloy, silicon chips, and suitability is strong.
Embodiment
A kind of general emulsion cutting fluid, by following weight part (kilogram) raw material make: monoisopropanolamine 1.5,2-amino-2-methyl-1-propanol 5, triphenyl phosphite 3.5, cyanuric acid zinc 1.5, sulfonated lignin 1.5,2,6 ditertiary butyl p cresol 1.5, polyoxyethylene sorbitan monooleate 0.8, kerosene 22, auxiliary agent 7, water 200; Described auxiliary agent by following weight part (kilogram) raw material make: polyoxyethylene sorbitan monooleate 2, aluminum nitride powder 0.1, boric acid 2, morpholine 1, water glass 2, silane coupling agent KH-5601, Potassium Persulphate 1, peach gum 3, water 20; Preparation method be Potassium Persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 ℃, stirring reaction 1-2 hour, obtains.
The preparation method of described general emulsion cutting fluid, comprises the following steps: water, sulfonated lignin, polyoxyethylene sorbitan monooleate are mixed, be heated to 45 ℃; Under 3500 revs/min of stirrings, add 2-amino-2-methyl-1-propanol, triphenyl phosphite, kerosene, auxiliary agent, continue to be heated to 75 ℃, stir 13 minutes; Add other remaining components, continue to stir 20 minutes, obtain.
The general emulsion cutting fluid testing data that this embodiment obtains is as follows:
Claims (2)
1. a general emulsion cutting fluid, it is characterized in that being made by the raw material of following weight part: monoisopropanolamine 1-2,2-amino-2-methyl isophthalic acid-propyl alcohol 4-6, triphenyl phosphite 3-4, cyanuric acid zinc 1-2, sulfonated lignin 1-2,2,6 ditertiary butyl p cresol 1-2, polyoxyethylene sorbitan monooleate 0.4-1.0, kerosene 20-23, auxiliary agent 6-8, water 200; Described auxiliary agent is made by the raw material of following weight part: polyoxyethylene sorbitan monooleate 2-3, aluminum nitride powder 0.1-0.2, boric acid 2-3, morpholine 1-2, water glass 1-2, silane coupling agent KH-560 1-2, Potassium Persulphate 1-2, peach gum 3-4, water 20-24; Preparation method be Potassium Persulphate is water-soluble after, then add other leftover materials, stir 10-15 minute, be heated to 70-80 ℃, stirring reaction 1-2 hour, obtains.
2. the preparation method of general emulsion cutting fluid according to claim 1, is characterized in that comprising the following steps: water, sulfonated lignin, polyoxyethylene sorbitan monooleate are mixed, be heated to 40-50 ℃; Under 3000-4000 rev/min of stirring, add 2-amino-2-methyl isophthalic acid-propyl alcohol, triphenyl phosphite, kerosene, auxiliary agent, continue to be heated to 70-80 ℃, stir 10-15 minute; Add other remaining components, continue to stir 15-25 minute, obtain.