CN103666134A - Water-based antirust flame-retardant paint - Google Patents
Water-based antirust flame-retardant paint Download PDFInfo
- Publication number
- CN103666134A CN103666134A CN201310579811.7A CN201310579811A CN103666134A CN 103666134 A CN103666134 A CN 103666134A CN 201310579811 A CN201310579811 A CN 201310579811A CN 103666134 A CN103666134 A CN 103666134A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- water
- flame
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-based antirust flame-retardant paint which consists of the following components in parts by weight: 20-40 parts of perchloroethylene resin, 10-12 parts of hydroxyethyl cellulose, 10-15 parts of fluorocarbon resin, 3-5 parts of acetone, 5-7 parts of aluminum tripolyphosphate, 8-15 parts of silicon carbide powder, 4-6 parts of lead tetroxide, 6-12 parts of antirust pigment and 20-30 parts of distilled water. The water-based antirust flame-retardant paint disclosed by the invention has the advantages that the obtained film of the paint is not burnt easily, and the coating does not change after staying at a constant temperature of 550 DEG C for 4 hours, thus fireproof and flame-retardant properties are excellent, and the paint can be used in high-temperature environment; the chemical corrosion resistance is relatively strong, and the salt fog resistance, alkali resistance (10% sodium hydroxide solution) and acid resistance (6% hydrochloric acid) do not change within 500 hours; the coating is flat and bright and beautiful and elegant and has strong decorative property.
Description
Technical field
The invention belongs to paint field, be specifically related to a kind of waterborne anti-rust anti-flaming dope.
Background technology
Silicon fluoride paint have lower surface can, resistant, non-viscosity are good, also have excellent snappiness, shock-resistance and weathering resistance, wear resistance is better, not easy to wear, corrosion-resistant, can effectively resist acid, alkali, salt corrosion.Silicon fluoride paint is widely used in the every field such as external wall, bridge, oil, chemical industry, pipeline, storage tank and power plant, the application of Qi power plant is mainly circuit and all kinds of relevant power-supply unit, and electric power circuit is once skin is corroded and has huge potential safety hazard, therefore it is prevented
The research of fire and rustless property is significant.The preservative effect of current fluorine silicon protective system is not good enough, and the anticorrosion life-span is shorter,
Flame retardant resistance is also short of.
Summary of the invention
The deficiency existing for prior art, technical problem to be solved by this invention is, provides a kind of, can effectively prevent that coated article from corrosion occurring and expose, and when transmitting line is aging, can effectively prevent the generation waterborne anti-rust anti-flaming dope of fire while there is potential safety hazard.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of protective system, is grouped into by the one-tenth of following weight part:
Supervinyi chloride resin 20～40;
Natvosol 10～12;
Fluorocarbon resin 10～15;
Acetone 3～5;
Aluminium triphosphate 5～7;
Silicon carbide powder 8～15;
Tri-lead tetroxide 4～6;
Rust-stabilising pigment 6～12;
Distilled water 20～30.
The advantage of waterborne anti-rust anti-flaming dope of the present invention is: coating gained of the present invention is filmed nonflammable, 550 ℃ of constant temperature 4h, and coating is unchanged, therefore its fire retardant performance is superior, can in hot environment, use; Chemical resistance is stronger, and 500h is unchanged for salt fog resistance, alkali resistance (10% sodium hydroxide solution), acid resistance (6% hydrochloric acid soln); Coating smooth of the present invention, elegant in appearance, ornamental strong.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further details;
A waterborne anti-rust anti-flaming dope, is grouped into by the one-tenth of following weight part:
Supervinyi chloride resin 20～40;
Natvosol 10～12;
Fluorocarbon resin 10～15;
Acetone 3～5;
Aluminium triphosphate 5～7;
Silicon carbide powder 8～15;
Tri-lead tetroxide 4～6;
Rust-stabilising pigment 6～12;
Distilled water 20～30.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, the variation of making, remodeling, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (1)
1. a waterborne anti-rust anti-flaming dope, is characterized in that, by the one-tenth of following weight part, is grouped into:
Supervinyi chloride resin 20～40;
Natvosol 10～12;
Fluorocarbon resin 10～15;
Acetone 3～5;
Aluminium triphosphate 5～7;
Silicon carbide powder 8～15;
Tri-lead tetroxide 4～6;
Rust-stabilising pigment 6～12;
Distilled water 20～30.