CN104650670A - Low-cost high-performance fireproof paint - Google Patents
Low-cost high-performance fireproof paint Download PDFInfo
- Publication number
- CN104650670A CN104650670A CN201310592859.1A CN201310592859A CN104650670A CN 104650670 A CN104650670 A CN 104650670A CN 201310592859 A CN201310592859 A CN 201310592859A CN 104650670 A CN104650670 A CN 104650670A
- Authority
- CN
- China
- Prior art keywords
- low
- performance
- cost
- cost high
- fireproof paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses low-cost high-performance fireproof paint. The low-cost high-performance fireproof paint comprises, by mass, 30-40% of vinyl acetate emulsion, 10-15% of melamine polyphosphate, 15-25% of pentaerythritol, 2-8% of boric acid, 2-15% of aluminum hydroxide, 2-15% of montmorillonite, 2-6% of sodium molybdate, 0.1-1% of an aluminum-titanium composite coupling agent and 0.1-1% of pentaerythritol stearate. The low-cost high-performance fireproof paint has the advantages of cheap and easily available raw materials, low cost, no halogen, no toxicity, good coated object flame retardation, smoke inhibition, wear resistance, wear resistance, heat resistance, aging resistance, coating toughness and high bonding intensity, can be used for fireproof coating on the surfaces of timber and a steel structure, has good use effects and is economic.
Description
Technical field
The present invention relates to frie retardant coating technical field, specifically a kind of low-cost and high-performance frie retardant coating.
Background technology
Frie retardant coating is a kind ofly coated in body surface, can reduces, retardance fire rapid spread flammable by painting surface and the kind coating in order to improve coated article body fire endurance.Because frie retardant coating difficulty itself is fired or do not fire, there is better protecting effect when meeting fire to base material, for fire extinguishing and personnel withdraw the time won.Therefore its investigation and application has been caused to the great attention of countries in the world.Along with the development of society and the progress of science and technology, kind and the range of application of frie retardant coating constantly expand.And the low cost of frie retardant coating, high-performance, low stain, the energy-conservation hot subject having become social concerns, be also the later important development direction of frie retardant coating, and be suitable for the needs of socio-economic development.
Summary of the invention
The object of the present invention is to provide a kind of low-cost and high-performance frie retardant coating.
The technical solution adopted for the present invention to solve the technical problems is: a kind of low-cost and high-performance frie retardant coating, and its component by mass percent proportioning is: acetate emulsion 30% ~ 40%, melamine polyphosphate 10% ~ 15%, tetramethylolmethane 15% ~ 25%, boric acid 2% ~ 8%, aluminium hydroxide 2% ~ 15%, polynite 2% ~ 15%, Sodium orthomolybdate 2% ~ 6%, aluminium titanium composite coupler 0.1% ~ 1%, pentaerythritol stearate 0.1% ~ 1%.
The preparation method of a kind of low-cost and high-performance frie retardant coating of the present invention, comprises the following steps:
(1) each component is taken by mass percent proportioning;
(2), by aluminium hydroxide, polynite and aluminium titanium composite coupler add a material temperature degree in the mixing machine of 80 DEG C ~ 120 DEG C, and stir 10 ~ 60 minutes under rotating speed 3000 ~ 6000 revs/min, be cooled to greenhouse, discharging is stand-by;
(3), acetate emulsion, melamine polyphosphate, tetramethylolmethane, boric acid, Sodium orthomolybdate and pentaerythritol stearate is added in the reactor, and add the material that step (2) obtains, make fully to grind Agitation and mixing evenly after, discharging, obtains the present invention.
The invention has the beneficial effects as follows, compared with prior art, cheaper starting materials of the present invention is easy to get, cost is low, not halogen-containing composition, toxicological harmless, and to coated object have well fire-retardant, press down cigarette, anticorrosion antiwear, heat-resisting, ageing-resistant and coating is tough and tensile, cohesive strength advantages of higher, can be used for the fire prevention coating on the surface such as timber, steel construction, result of use is good, and economical.
Embodiment
Technical scheme of the present invention is further illustrated below in conjunction with concrete preferred embodiment.
A kind of low-cost and high-performance frie retardant coating, its component by mass percent proportioning is: acetate emulsion 37%, melamine polyphosphate 15%, tetramethylolmethane 15%, boric acid 5%, aluminium hydroxide 10%, polynite 10%, Sodium orthomolybdate 6%, aluminium titanium composite coupler 1%, pentaerythritol stearate 1%.
Its preparation method is: (1) takes each component by mass percent proportioning; (2), by aluminium hydroxide, polynite and aluminium titanium composite coupler add a material temperature degree in the mixing machine of 80 DEG C ~ 120 DEG C, and stir 10 ~ 60 minutes under rotating speed 3000 ~ 6000 revs/min, be cooled to greenhouse, discharging is stand-by; (3), acetate emulsion, melamine polyphosphate, tetramethylolmethane, boric acid, Sodium orthomolybdate and pentaerythritol stearate is added in the reactor, and add the material that step (2) obtains, make fully to grind Agitation and mixing evenly after, discharging, obtains the present invention.
Claims (2)
1. a low-cost and high-performance frie retardant coating, it is characterized in that, its component by mass percent proportioning is: acetate emulsion 30% ~ 40%, melamine polyphosphate 10% ~ 15%, tetramethylolmethane 15% ~ 25%, boric acid 2% ~ 8%, aluminium hydroxide 2% ~ 15%, polynite 2% ~ 15%, Sodium orthomolybdate 2% ~ 6%, aluminium titanium composite coupler 0.1% ~ 1%, pentaerythritol stearate 0.1% ~ 1%.
2. a kind of low-cost and high-performance frie retardant coating according to claim 1, is characterized in that, comprise the following steps:
(1) each component is taken by mass percent proportioning;
(2), by aluminium hydroxide, polynite and aluminium titanium composite coupler add a material temperature degree in the mixing machine of 80 DEG C ~ 120 DEG C, and stir 10 ~ 60 minutes under rotating speed 3000 ~ 6000 revs/min, be cooled to greenhouse, discharging is stand-by;
(3), acetate emulsion, melamine polyphosphate, tetramethylolmethane, boric acid, Sodium orthomolybdate and pentaerythritol stearate is added in the reactor, and add the material that step (2) obtains, make fully to grind Agitation and mixing evenly after, discharging, obtains the present invention.