CN104647520A - Multi-effect treatment agent for wood fireproofing - Google Patents
Multi-effect treatment agent for wood fireproofing Download PDFInfo
- Publication number
- CN104647520A CN104647520A CN201310592091.8A CN201310592091A CN104647520A CN 104647520 A CN104647520 A CN 104647520A CN 201310592091 A CN201310592091 A CN 201310592091A CN 104647520 A CN104647520 A CN 104647520A
- Authority
- CN
- China
- Prior art keywords
- treatment agent
- effect treatment
- boric acid
- inorganic agent
- wood protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a multi-effect treatment agent for wood fireproofing. The multi-effect treatment agent for wood fireproofing comprises, by mass, 30-50% of guanylurea phosphate, 5-20% of boric acid, 5-30% of boric acid, 3-8% of sodium molybdate, 0.5-3% of triethanolamine, 0.1-2% of chlorothalonil and 0.1-1% of pentaerythritol. Compared with treatment agents in the prior art, the multi-effect treatment agent disclosed in the invention has the efficacies of fire retardation, smoke inhibition, anticorrosion and mildew resistance, and has the advantages of simple preparation technology, use convenience and low cost.
Description
Technical field
The present invention relates to wood treatment agent technical field, the multiple-effect inorganic agent of specifically a kind of fire retarding wood protection.
Background technology
The life of timber and people, produce closely bound up, be now widely used in the fields such as building, interior decoration, furniture, but timber easily burns and there is disaster hidden-trouble, therefore most important to the fire prevention treatment measures of timber.According to character and the purposes of timber, surface application methods and infusion process two kinds are adopted usually to fire retarding wood protection treatment measures, its drug-treated agent used is all anti-flaming dope or fire retardant, and the fire retarding wood protection inorganic agent great majority that market uses at present are all described fire retardants, these fire retardants often only have single fire resistance, not obvious in the effect of the protective treatment of other side to timber.
Summary of the invention
The object of the present invention is to provide the multiple-effect inorganic agent of a kind of flame-retardant smoke inhibition, anticorrosion, mildew-resistant, stable performance and economic and practical fire retarding wood protection.
The technical solution adopted for the present invention to solve the technical problems is: a kind of multiple-effect inorganic agent of fire retarding wood protection, and its component by mass percent proportioning is: guanyl-urea-phosphate 30% ~ 50%, boric acid 5% ~ 20%, diammonium hydrogen phosphate 5% ~ 30%, sodium molybdate 3% ~ 8%, triethanolamine 0.5% ~ 3%, Bravo 0.1% ~ 2%, pentaerythrite 0.1% ~ 1%.
The preparation method of the multiple-effect inorganic agent of a kind of fire retarding wood protection of the present invention is: take each component by mass percent proportioning, after mixing, adding water and being made into mass concentration is 15% ~ 25% solution, then 70 DEG C ~ 130 DEG C are heated to, react 0.5 ~ 4 hour, after being cooled to room temperature again, obtain the present invention.
The invention has the beneficial effects as follows, compared with prior art, the present invention has fire-retardant, to press down cigarette, anticorrosion, mildew-resistant multiple efficacies to timber, and its preparation technology is simple, and easy to use, cost is low.
Detailed description of the invention
Technical scheme of the present invention is further illustrated below in conjunction with concrete preferred embodiment.
A multiple-effect inorganic agent for fire retarding wood protection, its component by mass percent proportioning is: guanyl-urea-phosphate 40%, boric acid 20%, diammonium hydrogen phosphate 26%, sodium molybdate 8%, triethanolamine 3%, Bravo 2%, pentaerythrite 1%.
Its preparation method is: take each component by mass percent proportioning, and after mixing, adding water and being made into mass concentration is 15% ~ 25% solution, is then heated to 70 DEG C ~ 130 DEG C, reacts 0.5 ~ 4 hour, then after being cooled to room temperature, obtains the present invention.
Claims (2)
1. the multiple-effect inorganic agent of a fire retarding wood protection, it is characterized in that, its component by mass percent proportioning is: guanyl-urea-phosphate 30% ~ 50%, boric acid 5% ~ 20%, diammonium hydrogen phosphate 5% ~ 30%, sodium molybdate 3% ~ 8%, triethanolamine 0.5% ~ 3%, Bravo 0.1% ~ 2%, pentaerythrite 0.1% ~ 1%.
2. the preparation method of the multiple-effect inorganic agent of a kind of fire retarding wood protection according to claim 1, it is characterized in that, comprise the following steps: take each component by mass percent proportioning, after mixing, adding water and being made into mass concentration is 15% ~ 25% solution, is then heated to 70 DEG C ~ 130 DEG C, reacts 0.5 ~ 4 hour, after being cooled to room temperature again, obtain the present invention.