CN104277528A - Fireproof corrosion-resistant paint for steel structure - Google Patents
Fireproof corrosion-resistant paint for steel structure Download PDFInfo
- Publication number
- CN104277528A CN104277528A CN201410449387.9A CN201410449387A CN104277528A CN 104277528 A CN104277528 A CN 104277528A CN 201410449387 A CN201410449387 A CN 201410449387A CN 104277528 A CN104277528 A CN 104277528A
- Authority
- CN
- China
- Prior art keywords
- parts
- steel structure
- good
- corrosion
- resistant paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to fireproof corrosion-resistant paint for a steel structure. The technical scheme adopted by the invention is as follows: the fireproof corrosion-resistant paint for the steel structure comprises the following components: vinylidene chloride, polyamide resin, chlorinated paraffin, a composite flame retardant, melamine, succinic acid, aluminum phosphate, mica, silicon carbide micro powder, borax, cellulosic fiber, sodium silicate, pentaerythritol, 1,2-propylene glycol, 10% silicone oil, a flatting agent, a preservative, a defoaming agent and acetone. The paint has the beneficial effects of high mechanical strength, good impact resistance, excellent fire resistance, good corrosion resistance, good weather resistance, good adhesive force and low cost.
Description
Technical field
The present invention relates to a kind of steel structure fireproofing corrosion resistant coating, belong to technical field of coatings.
Background technology
When 450-650 degree Celsius, steel generally will lose supporting capacity, deform.Therefore some steel are also needed to do flameproof protection to it.Conventional method applies one deck frie retardant coating at steel surface.But the frie retardant coating of routine is only the surface being simply coated in steel, although reach fp object, but leave the hidden danger of corrosion.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of steel structure fireproofing corrosion resistant coating, and this coating solves in conventional coating use procedure the anticorrosion defect improperly existed.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
A kind of steel structure fireproofing corrosion resistant coating, it is characterized in that: the component comprising following weight part, vinylidene chloride 10-15 part, polyamide resin 8-12 part, clorafin 15-25 part, composite flame-retardant agent 10-15 part, trimeric cyanamide 15-25 part, succsinic acid 0.5-1 part, poly aluminium phosphate 0.5-1.0 part, mica 10-15 part, silicon carbide micro-powder 5-10 part, borax 2-6 part, cellulosic fibre 3-8 part, water glass 1-3 part, tetramethylolmethane 0.5-1.5 part, 1, 2-propylene glycol 2-8 part, 10% silicone oil 0.1-2 part, flow agent 0.1-0.6 part, sanitas 0.1-0.6 part, defoamer 0.1-0.6 part, acetone 30-45 part.
Further, described a kind of steel structure fireproofing corrosion resistant coating, its preferred version comprises the component of following weight part, vinylidene chloride 13 parts, polyamide resin 9 parts, clorafin 18 parts, composite flame-retardant agent 14 parts, trimeric cyanamide 18 parts, succsinic acid 0.8 part, poly aluminium phosphate 0.7 part, 13 parts, mica, silicon carbide micro-powder 8 parts, borax 4 parts, cellulosic fibre 6 parts, water glass 2 parts, tetramethylolmethane 1 part, 1,2-propylene glycol 6 parts, 10% silicone oil 1.5 parts, flow agent 0.4 part, sanitas 0.4 part, defoamer 0.4 part, 38 parts, acetone.
The coating adopting technique scheme to produce has following beneficial effect, and physical strength is high, good impact resistance, and fire performance is excellent, and corrosion resistance is good, weathering resistance energy consumption, and sticking power is good, and cost is low.
Embodiment
Below in conjunction with concrete implementation column, the present invention is set forth further, but do not limit the present invention.
Embodiment 1
A kind of steel structure fireproofing corrosion resistant coating, is characterized in that: the component comprising following weight part, vinylidene chloride 15 parts, polyamide resin 12 parts, clorafin 25 parts, composite flame-retardant agent 15 parts, trimeric cyanamide 25 parts, succsinic acid 0.5 part, poly aluminium phosphate 0.5 part, 10 parts, mica, silicon carbide micro-powder 5 parts, borax 6 parts, cellulosic fibre 8 parts, water glass 3 parts, tetramethylolmethane 1.5 parts, 1,2-propylene glycol 8 parts, 10% silicone oil 2 parts, flow agent 0.6 part, sanitas 0.1 part, defoamer 0.6 part, 45 parts, acetone.
Embodiment 2
A kind of steel structure fireproofing corrosion resistant coating, is characterized in that: the component comprising following weight part, vinylidene chloride 10 parts, polyamide resin 8 parts, clorafin 15 parts, composite flame-retardant agent 15 parts, trimeric cyanamide 25 parts, succsinic acid 0.5 part, poly aluminium phosphate 0.5 part, 10 parts, mica, silicon carbide micro-powder 10 parts, borax 2 parts, cellulosic fibre 8 parts, water glass 1 part, tetramethylolmethane 1.5 parts, 1,2-propylene glycol 2 parts, 10% silicone oil 0.1 part, flow agent 0.1 part, sanitas 0.1 part, defoamer 0.1 part, 30 parts, acetone.
Embodiment 3
A kind of steel structure fireproofing corrosion resistant coating, is characterized in that: the component comprising following weight part, vinylidene chloride 13 parts, polyamide resin 9 parts, clorafin 18 parts, composite flame-retardant agent 14 parts, trimeric cyanamide 18 parts, succsinic acid 0.8 part, poly aluminium phosphate 0.7 part, 13 parts, mica, silicon carbide micro-powder 8 parts, borax 4 parts, cellulosic fibre 6 parts, water glass 2 parts, tetramethylolmethane 1 part, 1,2-propylene glycol 6 parts, 10% silicone oil 1.5 parts, flow agent 0.4 part, sanitas 0.4 part, defoamer 0.4 part, 38 parts, acetone.
Claims (2)
1. a steel structure fireproofing corrosion resistant coating, it is characterized in that: the component comprising following weight part, vinylidene chloride 10-15 part, polyamide resin 8-12 part, clorafin 15-25 part, composite flame-retardant agent 10-15 part, trimeric cyanamide 15-25 part, succsinic acid 0.5-1 part, poly aluminium phosphate 0.5-1.0 part, mica 10-15 part, silicon carbide micro-powder 5-10 part, borax 2-6 part, cellulosic fibre 3-8 part, water glass 1-3 part, tetramethylolmethane 0.5-1.5 part, 1, 2-propylene glycol 2-8 part, 10% silicone oil 0.1-2 part, flow agent 0.1-0.6 part, sanitas 0.1-0.6 part, defoamer 0.1-0.6 part, acetone 30-45 part.
2. steel structure fireproofing corrosion resistant coating according to claim 1, is characterized in that: its preferred version comprises the component of following weight part, vinylidene chloride 13 parts, polyamide resin 9 parts, clorafin 18 parts, composite flame-retardant agent 14 parts, trimeric cyanamide 18 parts, succsinic acid 0.8 part, poly aluminium phosphate 0.7 part, 13 parts, mica, silicon carbide micro-powder 8 parts, borax 4 parts, cellulosic fibre 6 parts, water glass 2 parts, tetramethylolmethane 1 part, 1,2-PD 6 parts, 10% silicone oil 1.5 parts, flow agent 0.4 part, sanitas 0.4 part, defoamer 0.4 part, 38 parts, acetone.