CN105440856A - Environment-friendly fire-retardant coating - Google Patents
Environment-friendly fire-retardant coating Download PDFInfo
- Publication number
- CN105440856A CN105440856A CN201510987445.8A CN201510987445A CN105440856A CN 105440856 A CN105440856 A CN 105440856A CN 201510987445 A CN201510987445 A CN 201510987445A CN 105440856 A CN105440856 A CN 105440856A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- retardant coating
- epoxy resin
- silicon oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly fire-retardant coating, comprising the following raw materials in parts by mass: 11-14 parts of expanded perlite, 13-18 parts of aluminium silicate fibers, 8-15 parts of pentaerythritol, 7-9 parts of chlorinated paraffin, 40-50 parts of acrylate elastic emulsion, 4-7 parts of nano silicon oxide, 9-14 parts of ethylene glycol, 7-10 parts of magnesium hydroxide, 5-9 parts of silicate glass, 20-30 parts of epoxy resin, 6-8 parts of dimethyl silicone oil, and 12-18 parts of isobutyl ketone. The environment-friendly fire-retardant coating disclosed by the invention is good in fire resistance, high-temperature-resistant, strong in adhesive force, good in environmental friendliness and low in cost and has no seasoning crack.
Description
Technical field
The present invention relates to material of construction, particularly relate to a kind of environment-friendly fireproof coating.
Background technology
Frie retardant coating is the fireproofing passiveness material of brushing on protected object surface, and any protected object has the ultimate value of bearing big fire test, and whatsoever the building of structure has met fiery of long duration all can collapse.The effect of frie retardant coating is the effect playing isolation in protected object surface, delays the time of building collapse, for rescue and fire extinguishing win the valuable time.
Summary of the invention
For solving above-mentioned Problems existing, the invention provides a kind of fire line good, high temperature resistant, strong adhesion, without dry and cracked, the feature of environmental protection is good, environment-friendly fireproof coating with low cost.
The technical scheme that the present invention solves the problems of the technologies described above employing is: a kind of environment-friendly fireproof coating, comprises the raw material of following mass fraction:
Pearlstone 11-14 part, aluminum silicate fiber 13-18 part, tetramethylolmethane 8-15 part, clorafin 7-9 part, acrylic ester elastic emulsion 40-50 part, nano silicon oxide 4-7 part, ethylene glycol 9-14 part, magnesium hydroxide 7-10 part, silicate glass 5-9 part, epoxy resin 20-30 part, dimethyl silicone oil 6-8 part, isobutyl ketone 12-18 part.
Preferably, above-mentioned environment-friendly fireproof coating, comprises the raw material of following mass fraction:
Pearlstone 13 parts, aluminum silicate fiber 16 parts, tetramethylolmethane 11 parts, clorafin 8 parts, acrylic ester elastic emulsion 45 parts, nano silicon oxide 5 parts, ethylene glycol 12 parts, magnesium hydroxide 9 parts, silicate glass 7 parts, epoxy resin 25 parts, dimethyl silicone oil 7 parts, isobutyl ketone 15 parts.
The beneficial effect that technical solution problem of the present invention is brought is: fire line of the present invention is good, high temperature resistant, strong adhesion, and without dry and cracked, the feature of environmental protection is good, with low cost.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further details.
Embodiment 1
A kind of environment-friendly fireproof coating, comprises the raw material of following mass fraction:
Pearlstone 11 parts, aluminum silicate fiber 13 parts, tetramethylolmethane 8 parts, clorafin 7 parts, acrylic ester elastic emulsion 40 parts, nano silicon oxide 4 parts, ethylene glycol 9 parts, magnesium hydroxide 7 parts, silicate glass 5 parts, epoxy resin 20 parts, dimethyl silicone oil 6 parts, isobutyl ketone 12 parts.
Embodiment 2
A kind of environment-friendly fireproof coating, comprises the raw material of following mass fraction:
Pearlstone 13 parts, aluminum silicate fiber 16 parts, tetramethylolmethane 11 parts, clorafin 8 parts, acrylic ester elastic emulsion 45 parts, nano silicon oxide 5 parts, ethylene glycol 12 parts, magnesium hydroxide 9 parts, silicate glass 7 parts, epoxy resin 25 parts, dimethyl silicone oil 7 parts, isobutyl ketone 15 parts.
Embodiment 3
A kind of environment-friendly fireproof coating, comprises the raw material of following mass fraction:
Pearlstone 14 parts, aluminum silicate fiber 18 parts, tetramethylolmethane 15 parts, clorafin 9 parts, acrylic ester elastic emulsion 50 parts, nano silicon oxide 7 parts, ethylene glycol 14 parts, magnesium hydroxide 10 parts, silicate glass 9 parts, epoxy resin 30 parts, dimethyl silicone oil 8 parts, isobutyl ketone 18 parts.
Although above-mentioned, the specific embodiment of the present invention is described; but not limiting the scope of the invention; one of ordinary skill in the art should be understood that; on the basis of technical scheme of the present invention, those skilled in the art do not need to pay various amendment or distortion that creative work can make still within protection scope of the present invention.
Claims (2)
1. an environment-friendly fireproof coating, is characterized in that: the raw material comprising following mass fraction:
Pearlstone 11-14 part, aluminum silicate fiber 13-18 part, tetramethylolmethane 8-15 part, clorafin 7-9 part, acrylic ester elastic emulsion 40-50 part, nano silicon oxide 4-7 part, ethylene glycol 9-14 part, magnesium hydroxide 7-10 part, silicate glass 5-9 part, epoxy resin 20-30 part, dimethyl silicone oil 6-8 part, isobutyl ketone 12-18 part.
2. environment-friendly fireproof coating according to claim 1, is characterized in that: the raw material comprising following mass fraction:
Pearlstone 13 parts, aluminum silicate fiber 16 parts, tetramethylolmethane 11 parts, clorafin 8 parts, acrylic ester elastic emulsion 45 parts, nano silicon oxide 5 parts, ethylene glycol 12 parts, magnesium hydroxide 9 parts, silicate glass 7 parts, epoxy resin 25 parts, dimethyl silicone oil 7 parts, isobutyl ketone 15 parts.