CN103665694A - 一种氧气胶管 - Google Patents
一种氧气胶管 Download PDFInfo
- Publication number
- CN103665694A CN103665694A CN201310649298.4A CN201310649298A CN103665694A CN 103665694 A CN103665694 A CN 103665694A CN 201310649298 A CN201310649298 A CN 201310649298A CN 103665694 A CN103665694 A CN 103665694A
- Authority
- CN
- China
- Prior art keywords
- accounts
- agent
- oxygen
- rubber
- oxygen hose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明揭示了一种氧气胶管,由丙烯酸酯橡胶和添加剂加工制成,所述添加剂包括增韧剂、增塑剂、耐化学药品剂、耐候剂以及偶联剂,所述增韧剂为羧基丁腈橡胶,所述增塑剂为邻苯二甲酸二癸酯,所述耐化学药品剂为丁苯橡胶,所述耐候剂为硫代二丙酸二月桂酯,所述偶联剂为缩水甘油迷氧基丙基三甲氧基硅烷。通过在丙烯酸酯橡胶中添加多种添加剂,使制得的氧气胶管具有胶管柔软、弯曲性好、耐氧气腐蚀性好、耐候性、抗压性好、质量好的特点。
Description
技术领域
本发明涉及橡胶制品,具体涉及一种氧气胶管。
背景技术
随着冶金行业的发展,各类焊接器械上通常都采用输送氧气来作为原料,而作为供各类型的焊接器械作熔焊切割金属输送氧气用的氧气胶管则是需要满足很多的使用需求。现有的胶管由于各种材质原料和性能不同,制得的产品性能不能满足现有的使用需求,如胶管质量、胶管的软硬度、耐压性、耐候性、耐老化性、耐化学药品性等方面,如胶管经受不住以上各种情况则容易发生损坏,缩短使用寿命。
发明内容
本发明的目的在于提供一种胶管柔软、弯曲性好、耐氧气腐蚀性好、耐候性、抗压性好、质量好的氧气胶管。
本发明的技术方案是,一种氧气胶管,由丙烯酸酯橡胶和添加剂加工制成,所述添加剂包括增韧剂、增塑剂、耐化学药品剂、耐候剂以及偶联剂,所述增韧剂为羧基丁腈橡胶,所述增塑剂为邻苯二甲酸二癸酯,所述耐化学药品剂为丁苯橡胶,所述耐候剂为硫代二丙酸二月桂酯,所述偶联剂为缩水甘油迷氧基丙基三甲氧基硅烷,所述氧气胶管各成分所占重量百分比分别为:所述丙烯酸酯橡胶占83.7%-88%,所述羧基丁腈橡胶占3.1%-3.8%,所述邻苯二甲酸二癸酯占2.5%-3.3%,所述丁苯橡胶占1.8%-2.6%,所述硫代二丙酸二月桂酯占1.4%-2.3%,所述缩水甘油迷氧基丙基三甲氧基硅烷占3.2%-4.3%。
在本发明一个较佳实施例中,所述氧气胶管各成分所占重量百分比具体为:所述丙烯酸酯橡胶占87.5%,所述羧基丁腈橡胶占3.2%,所述邻苯二甲酸二癸酯占2.6%,所述丁苯橡胶占1.9%,所述硫代二丙酸二月桂酯占1.5%,所述缩水甘油迷氧基丙基三甲氧基硅烷占3.3%。
在本发明一个较佳实施例中,所述氧气胶管各成分所占重量百分比具体为:所述丙烯酸酯橡胶占84.2%,所述羧基丁腈橡胶占3.7%,所述邻苯二甲酸二癸酯占3.2%,所述丁苯橡胶占2.5%,所述硫代二丙酸二月桂酯占2.2%,所述缩水甘油迷氧基丙基三甲氧基硅烷占4.2%。
本发明所述为一种氧气胶管,通过在丙烯酸酯橡胶中添加多种添加剂,使制得的氧气胶管具有胶管柔软、弯曲性好、耐氧气腐蚀性好、耐候性、抗压性好、质量好的特点。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
本发明所述为一种氧气胶管,由丙烯酸酯橡胶和添加剂加工制成,所述添加剂包括增韧剂、增塑剂、耐化学药品剂、耐候剂以及偶联剂,所述增韧剂为羧基丁腈橡胶,所述增塑剂为邻苯二甲酸二癸酯,所述耐化学药品剂为丁苯橡胶,所述耐候剂为硫代二丙酸二月桂酯,所述偶联剂为缩水甘油迷氧基丙基三甲氧基硅烷,所述氧气胶管各成分所占重量百分比分别为:所述丙烯酸酯橡胶占83.7%-88%,所述羧基丁腈橡胶占3.1%-3.8%,所述邻苯二甲酸二癸酯占2.5%-3.3%,所述丁苯橡胶占1.8%-2.6%,所述硫代二丙酸二月桂酯占1.4%-2.3%,所述缩水甘油迷氧基丙基三甲氧基硅烷占3.2%-4.3%。
进一步地,所述氧气胶管各成分所占重量百分比具体为:所述丙烯酸酯橡胶占87.5%,所述羧基丁腈橡胶占3.2%,所述邻苯二甲酸二癸酯占2.6%,所述丁苯橡胶占1.9%,所述硫代二丙酸二月桂酯占1.5%,所述缩水甘油迷氧基丙基三甲氧基硅烷占3.3%。
进一步地,所述氧气胶管各成分所占重量百分比具体为:所述丙烯酸酯橡胶占84.2%,所述羧基丁腈橡胶占3.7%,所述邻苯二甲酸二癸酯占3.2%,所述丁苯橡胶占2.5%,所述硫代二丙酸二月桂酯占2.2%,所述缩水甘油迷氧基丙基三甲氧基硅烷占4.2%。
本发明所述为一种氧气胶管,通过在丙烯酸酯橡胶中添加多种添加剂,使制得的氧气胶管具有胶管柔软、弯曲性好、耐氧气腐蚀性好、耐候性、抗压性好、质量好的特点。
以上所述仅为本发明的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本领域的技术人员在本发明所揭露的技术范围内,可不经过创造性劳动想到的变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (3)
1.一种氧气胶管,由丙烯酸酯橡胶和添加剂加工制成,其特征在于:所述添加剂包括增韧剂、增塑剂、耐化学药品剂、耐候剂以及偶联剂,所述增韧剂为羧基丁腈橡胶,所述增塑剂为邻苯二甲酸二癸酯,所述耐化学药品剂为丁苯橡胶,所述耐候剂为硫代二丙酸二月桂酯,所述偶联剂为缩水甘油迷氧基丙基三甲氧基硅烷,所述氧气胶管各成分所占重量百分比分别为:所述丙烯酸酯橡胶占83.7%-88%,所述羧基丁腈橡胶占3.1%-3.8%,所述邻苯二甲酸二癸酯占2.5%-3.3%,所述丁苯橡胶占1.8%-2.6%,所述硫代二丙酸二月桂酯占1.4%-2.3%,所述缩水甘油迷氧基丙基三甲氧基硅烷占3.2%-4.3%。
2.根据权利要求1所述的氧气胶管,其特征在于:所述氧气胶管各成分所占重量百分比具体为:所述丙烯酸酯橡胶占87.5%,所述羧基丁腈橡胶占3.2%,所述邻苯二甲酸二癸酯占2.6%,所述丁苯橡胶占1.9%,所述硫代二丙酸二月桂酯占1.5%,所述缩水甘油迷氧基丙基三甲氧基硅烷占3.3%。
3.根据权利要求1所述的氧气胶管,其特征在于:所述氧气胶管各成分所占重量百分比具体为:所述丙烯酸酯橡胶占84.2%,所述羧基丁腈橡胶占3.7%,所述邻苯二甲酸二癸酯占3.2%,所述丁苯橡胶占2.5%,所述硫代二丙酸二月桂酯占2.2%,所述缩水甘油迷氧基丙基三甲氧基硅烷占4.2%。