CN103665619A - 一种抗弯曲绝热ps泡沫塑料及其制备方法 - Google Patents

一种抗弯曲绝热ps泡沫塑料及其制备方法 Download PDF

Info

Publication number
CN103665619A
CN103665619A CN201310631190.2A CN201310631190A CN103665619A CN 103665619 A CN103665619 A CN 103665619A CN 201310631190 A CN201310631190 A CN 201310631190A CN 103665619 A CN103665619 A CN 103665619A
Authority
CN
China
Prior art keywords
parts
bending
adiabatic
butane
hcfc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310631190.2A
Other languages
English (en)
Other versions
CN103665619B (zh
Inventor
姚炎华
朱鹏
葛亮
刘晓磊
奚年英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANDONG XINGLU CHEMICAL Co.,Ltd.
Original Assignee
NANTONG REPAIR-AIR CHEMISTRY BIOENGINEERING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG REPAIR-AIR CHEMISTRY BIOENGINEERING Co Ltd filed Critical NANTONG REPAIR-AIR CHEMISTRY BIOENGINEERING Co Ltd
Priority to CN201310631190.2A priority Critical patent/CN103665619B/zh
Publication of CN103665619A publication Critical patent/CN103665619A/zh
Application granted granted Critical
Publication of CN103665619B publication Critical patent/CN103665619B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗弯曲绝热PS泡沫塑料及其制备方法,其中抗弯曲绝热PS泡沫塑料以重量组分计包括PS105-120份,铝粉3-8份,滑石粉0.5-1份,丁烷8-12份,氯代甲烷4-8份,液体石蜡2-5份,HCFC-141b5-10份,稳定剂0.5-3份;制备方法为将PS、铝粉和滑石粉在180-200℃下混合均匀,然后加入HCFC-141b、丁烷和氯代甲烷,冷却到100-110℃,然后加入液体石蜡和稳定剂,混合均匀,通过挤出机进行挤出,得到发泡材料。本发明提供的抗弯曲绝热PS泡沫塑料经测定具有很好的抗弯曲性能与绝热性能。

Description

一种抗弯曲绝热PS泡沫塑料及其制备方法
技术领域
    本发明属于材料技术领域,具体涉及一种抗弯曲绝热PS泡沫塑料及其制备方法。
背景技术
泡沫塑料为由大量气体微孔分散于固体塑料中而形成的一类高分子材料,具有质轻、隔热、吸音、减震等特性,且介电性能优于基体树脂,用途很广。几乎各种塑料均可作成泡沫塑料,发泡成型已成为塑料加工中一个重要领域。
目前常用的泡沫塑料抗弯性与绝热性能一般,在需要高抗弯性与绝热性材料领域的应用较少,因此需要开发一种具有高抗弯曲性与绝热性的塑料泡沫,扩大其应用范围。
 
发明内容
本发明的目的在于为了克服以上现有技术的不足而提供一种抗弯曲绝热PS泡沫塑料及其制备方法。
本发明是通过以下技术手段实现的:
一种抗弯曲绝热PS泡沫塑料, 以重量组分计包括PS 105-120份,铝粉3-8份,滑石粉0.5-1份,丁烷8-12份,氯代甲烷4-8份,液体石蜡2-5份,HCFC-141b 5-10份,稳定剂0.5-3份。
所述的抗弯曲绝热PS泡沫塑料,可以优选为以重量组分计包括:PS 113-118份,铝粉4-6份,滑石粉0.6-1份,丁烷9-11份,氯代甲烷5-7份,液体石蜡3-5份,HCFC-141b 6-8份,稳定剂2-3份。
所述的抗弯曲绝热PS泡沫塑料,所述的稳定剂可以为钙锌稳定剂。
一种以上所述的抗弯曲绝热PS泡沫塑料的制备方法,按照以下步骤进行:
(1)按照重量份称取各组分;
(2)将PS、铝粉和滑石粉在180-200℃下混合均匀,然后加入HCFC-141b、丁烷和氯代甲烷,冷却到100-110℃,然后加入液体石蜡和稳定剂,混合均匀,通过挤出机进行挤出,得到发泡材料。
 
具体实施方式:
实施例1
一种抗弯曲绝热PS泡沫塑料, 以重量组分计包括PS 105份,铝粉3份,滑石粉0.5份,丁烷8份,氯代甲烷4份,液体石蜡2份,HCFC-141b 5份,钙锌稳定剂0.5份。
以上所述的抗弯曲绝热PS泡沫塑料按照以下步骤进行制备:
(1)按照重量份称取各组分;
(2)将PS、铝粉和滑石粉在180℃下混合均匀,然后加入HCFC-141b、丁烷和氯代甲烷,冷却到100℃,然后加入液体石蜡和稳定剂,混合均匀,通过挤出机进行挤出,得到发泡材料。
实施例2
一种抗弯曲绝热PS泡沫塑料,以重量组分计包括:PS 113份,铝粉4份,滑石粉0.6份,丁烷9份,氯代甲烷5份,液体石蜡3份,HCFC-141b 6份,钙锌稳定剂2份。
以上所述的抗弯曲绝热PS泡沫塑料按照以下步骤进行制备:
(1)按照重量份称取各组分;
(2)将PS、铝粉和滑石粉在185℃下混合均匀,然后加入HCFC-141b、丁烷和氯代甲烷,冷却到105℃,然后加入液体石蜡和稳定剂,混合均匀,通过挤出机进行挤出,得到发泡材料。
实施例3
一种抗弯曲绝热PS泡沫塑料,以重量组分计包括:PS 115份,铝粉5份,滑石粉0.8份,丁烷10份,氯代甲烷6份,液体石蜡4份,HCFC-141b 7份,钙锌稳定剂2份。
以上所述的抗弯曲绝热PS泡沫塑料按照以下步骤进行制备:
(1)按照重量份称取各组分;
(2)将PS、铝粉和滑石粉在190℃下混合均匀,然后加入HCFC-141b、丁烷和氯代甲烷,冷却到110℃,然后加入液体石蜡和稳定剂,混合均匀,通过挤出机进行挤出,得到发泡材料。
实施例4
一种抗弯曲绝热PS泡沫塑料,以重量组分计包括:PS 118份,铝粉6份,滑石粉1份,丁烷11份,氯代甲烷7份,液体石蜡5份,HCFC-141b 8份,钙锌稳定剂3份。
以上所述的抗弯曲绝热PS泡沫塑料按照以下步骤进行制备:
(1)按照重量份称取各组分;
(2)将PS、铝粉和滑石粉在195℃下混合均匀,然后加入HCFC-141b、丁烷和氯代甲烷,冷却到110℃,然后加入液体石蜡和稳定剂,混合均匀,通过挤出机进行挤出,得到发泡材料。
实施例5
一种抗弯曲绝热PS泡沫塑料, 以重量组分计包括PS 120份,铝粉8份,滑石粉1份,丁烷12份,氯代甲烷8份,液体石蜡5份,HCFC-141b 10份,钙锌稳定剂3份。
以上所述的抗弯曲绝热PS泡沫塑料按照以下步骤进行制备:
(1)按照重量份称取各组分;
(2)将PS、铝粉和滑石粉在200℃下混合均匀,然后加入HCFC-141b、丁烷和氯代甲烷,冷却到110℃,然后加入液体石蜡和稳定剂,混合均匀,通过挤出机进行挤出,得到发泡材料。
    对以上实施例制备得到的抗弯曲绝热PS泡沫塑料进行性能测试,结果见下表:
项目 实施例1 实施例2 实施例3 实施例4 实施例5
弯曲强度(MPa) 513 525 519 522 519
导热率mW/mK 2.2 2.1 2.1 2.2 2.1
拉伸强度(MPa) 85 89 88 88 86
伸长率(%) 0.6 0.5 0.6 0.6 0.7
    从以上数据可以看出,本发明提供的抗弯曲绝热PS泡沫塑料弯曲强度达到了513MPa以上,导热率达到了2.1mW/mK左右,拉伸强度达到了88MPa左右,伸长率为0.6%左右,具有很好的抗弯曲性能与绝热性能。

Claims (4)

1.一种抗弯曲绝热PS泡沫塑料,其特征在于,以重量组分计包括:PS 105-120份,铝粉3-8份,滑石粉0.5-1份,丁烷8-12份,氯代甲烷4-8份,液体石蜡2-5份,HCFC-141b 5-10份,稳定剂0.5-3份。
2.根据权利要求1所述的抗弯曲绝热PS泡沫塑料,其特征在于,以重量组分计包括:PS 113-118份,铝粉4-6份,滑石粉0.6-1份,丁烷9-11份,氯代甲烷5-7份,液体石蜡3-5份,HCFC-141b 6-8份,稳定剂2-3份。
3.根据权利要求1或2所述的抗弯曲绝热PS泡沫塑料,其特征在于,所述的稳定剂为钙锌稳定剂。
4.一种权利要求1或2所述的抗弯曲绝热PS泡沫塑料的制备方法,其特征在于,按照以下步骤进行:
(1)按照重量份称取各组分;
(2)将PS、铝粉和滑石粉在180-200℃下混合均匀,然后加入HCFC-141b、丁烷和氯代甲烷,冷却到100-110℃,然后加入液体石蜡和稳定剂,混合均匀,通过挤出机进行挤出,得到发泡材料。
CN201310631190.2A 2013-12-02 2013-12-02 一种抗弯曲绝热ps泡沫塑料及其制备方法 Active CN103665619B (zh)