CN103665481A - 一种耐磨性密封性优良的复合橡胶密封垫材料及其制备方法 - Google Patents

一种耐磨性密封性优良的复合橡胶密封垫材料及其制备方法 Download PDF

Info

Publication number
CN103665481A
CN103665481A CN201310583050.2A CN201310583050A CN103665481A CN 103665481 A CN103665481 A CN 103665481A CN 201310583050 A CN201310583050 A CN 201310583050A CN 103665481 A CN103665481 A CN 103665481A
Authority
CN
China
Prior art keywords
parts
gasket material
rubber
sealing gasket
wear resistance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310583050.2A
Other languages
English (en)
Inventor
朱兴堂
朱亮亮
陈军彦
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU TIMES ELECTRONICS Co Ltd
Original Assignee
BENGBU TIMES ELECTRONICS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU TIMES ELECTRONICS Co Ltd filed Critical BENGBU TIMES ELECTRONICS Co Ltd
Priority to CN201310583050.2A priority Critical patent/CN103665481A/zh
Publication of CN103665481A publication Critical patent/CN103665481A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐磨性密封性优良的复合橡胶密封垫材料，其特征在于，由下列重量份的原料制成：丁晴橡胶（N41）55-60、聚异戊二烯橡胶30-35、石棉纤维3-4、活性氧化锌3-4、防老剂D1-2、喷雾炭黑35-40、聚乙烯醇2-3、棕榈蜡4-6、抗氧剂10351-2、硫磺1.5-3、交联剂TAIC1.2-1.4、促进剂M1-2、促进剂BPP0.3-0.6、环氧亚麻子油4-5、环氧油酸丁酯3-4、沉淀法白炭黑14-18、改性凹凸棒土10-12；本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明配方合理，工艺简单，成本低，具有良好的耐油、耐磨、密封性能。

Description

一种耐磨性密封性优良的复合橡胶密封垫材料及其制备方法
技术领域
本发明涉及橡胶复合材料加工领域，特别是一种耐磨性密封性优良的复合橡胶密封垫材料及其制备方法。
背景技术
密封垫，是一种用于机械、设备、管道等内部，起密封作用的材料。目前使用的密封垫多为橡胶密封垫，其特点是：耐高温、耐臭氧、耐天然老化、耐真空、耐燃料油、耐润滑油、耐强氧化剂、耐药品性和电绝缘性能好，广泛用于国防工业和民用工业。但是现有的橡胶密封垫密封效果不理想、耐磨性较差、强度低等缺陷，已远不能满足现实要求。因此研发一种高性能橡胶密封垫已成为当务之急。
发明内容
本发明的目的是提供一种耐磨性密封性优良的复合橡胶密封垫材料及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种耐磨性密封性优良的复合橡胶密封垫材料，由下列重量份的原料制成：丁晴橡胶（N41）55-60、聚异戊二烯橡胶30-35、石棉纤维3-4、活性氧化锌3-4、防老剂D1-2、喷雾炭黑35-40、聚乙烯醇2-3、棕榈蜡4-6、抗氧剂10351-2、硫磺1.5-3、交联剂TAIC1.2-1.4、促进剂M1-2、促进剂BPP0.3-0.6、环氧亚麻子油4-5、环氧油酸丁酯3-4、沉淀法白炭黑14-18、改性凹凸棒土10-12；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土20-24、粘土9-12、1,6-己二异氰酸酯3-4、二缩三丙二醇二丙烯酸酯5-6、氧化镁3-4、氧化锌1-2、铝矾土5-6、硼化钒1-2、硅烷偶联剂KH-5501-2、二甲基氧化锡1-2、玉石粉8-10、花椒籽油1-2；制备方法是将凹凸棒土、粘土、铝矾土混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
本发明所述耐磨性密封性优良的复合橡胶密封垫材料，由以下具体步骤制成：将丁腈橡胶（N41）、聚异戊二烯橡胶、石棉纤维、活性氧化锌、防老剂D、环氧油酸丁酯加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至110-130℃，再加入喷雾炭黑、聚乙烯醇、棕榈蜡、抗氧剂1035、硫磺、交联剂TAIC、促进剂M，混炼6-8min，再加入沉淀法白炭黑、促进剂BPP、环氧亚麻子油继续混炼4-6min；加入其余剩余成分混炼5-6min，即得。
本发明的优异效果是：本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明配方合理，工艺简单，成本低，具有良好的耐油、耐磨、密封性能。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种耐磨性密封性优良的复合橡胶密封垫材料，由下列重量份（公斤）的原料制成：丁晴橡胶（N41）55、聚异戊二烯橡胶30、石棉纤维3、活性氧化锌3、防老剂D1、喷雾炭黑35、聚乙烯醇2、棕榈蜡4、抗氧剂10351、硫磺1.5、交联剂TAIC1.2、促进剂M1、促进剂BPP0.3、环氧亚麻子油4、环氧油酸丁酯3、沉淀法白炭黑14、改性凹凸棒土10；
所述改性凹凸棒土由下列重量份（公斤）的原料制成：凹凸棒土20、粘土9、1,6-己二异氰酸酯3、二缩三丙二醇二丙烯酸酯5、氧化镁3、氧化锌1、铝矾土5、硼化钒1、硅烷偶联剂KH-5501、二甲基氧化锡1、玉石粉8、花椒籽油1；制备方法是将凹凸棒土、粘土、铝矾土混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
本发明所述耐磨性密封性优良的复合橡胶密封垫材料，由以下具体步骤制成：将丁腈橡胶（N41）、聚异戊二烯橡胶、石棉纤维、活性氧化锌、防老剂D、环氧油酸丁酯加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至110-130℃，再加入喷雾炭黑、聚乙烯醇、棕榈蜡、抗氧剂1035、硫磺、交联剂TAIC、促进剂M，混炼6-8min，再加入沉淀法白炭黑、促进剂BPP、环氧亚麻子油继续混炼4-6min；加入其余剩余成分混炼5-6min，即得。
用本发明的密封垫材料与普通橡胶料物理性能对比如下表。
Figure BDA0000416320900000021
Figure BDA0000416320900000031
从表中可以看出用本发明的橡胶密封垫材料，综合性能比较好。

Claims (2)

1.一种耐磨性密封性优良的复合橡胶密封垫材料，其特征在于，由下列重量份的原料制成：丁晴橡胶（N41）55-60、聚异戊二烯橡胶30-35、石棉纤维3-4、活性氧化锌3-4、防老剂D1-2、喷雾炭黑35-40、聚乙烯醇2-3、棕榈蜡4-6、抗氧剂1035 1-2、硫磺 1.5-3、交联剂 TAIC1.2-1.4、促进剂M1-2、促进剂BPP 0.3-0.6、环氧亚麻子油4-5、环氧油酸丁酯3-4、沉淀法白炭黑14-18、改性凹凸棒土10-12；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土20-24、粘土9-12、1,6-己二异氰酸酯3-4、二缩三丙二醇二丙烯酸酯5-6、氧化镁3-4、氧化锌1-2、铝矾土5-6、硼化钒1-2、硅烷偶联剂KH-550 1-2、二甲基氧化锡1-2、玉石粉8-10、花椒籽油1-2；制备方法是将凹凸棒土、粘土、铝矾土混合放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
2.根据权利要求1所述耐磨性密封性优良的复合橡胶密封垫材料，其特征在于，由以下具体步骤制成：将丁腈橡胶（N41 ）、聚异戊二烯橡胶、石棉纤维、活性氧化锌、防老剂D、环氧油酸丁酯加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至110-130℃，再加入喷雾炭黑、聚乙烯醇、棕榈蜡、抗氧剂1035 、硫磺、交联剂 TAIC、促进剂M，混炼6-8min，再加入沉淀法白炭黑、促进剂BPP、环氧亚麻子油继续混炼4-6min；加入其余剩余成分混炼5-6min，即得。
CN201310583050.2A 2013-11-18 2013-11-18 一种耐磨性密封性优良的复合橡胶密封垫材料及其制备方法 Pending CN103665481A (zh)