CN103660406A - Colorful flocked fabric and preparation method thereof - Google Patents
Colorful flocked fabric and preparation method thereof Download PDFInfo
- Publication number
- CN103660406A CN103660406A CN201410017665.3A CN201410017665A CN103660406A CN 103660406 A CN103660406 A CN 103660406A CN 201410017665 A CN201410017665 A CN 201410017665A CN 103660406 A CN103660406 A CN 103660406A
- Authority
- CN
- China
- Prior art keywords
- fine hair
- tapetum
- processing
- painted processing
- painted
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a colorful flocked fabric and a preparation method thereof, which comprises a base fabric layer, a flock layer is arranged on the base fabric layer, the flock layer consists of a ground color flock layer and a dyed flock layer which are uniformly blended, and the height difference between the dyed flock layer and the ground color flock layer is 0.1mm to 1.5mm; the height of the dyed flock layer is 0.7mm to 2.5mm, and the height of the ground color flock layer is 0.6mm to 1.0mm. The colorful flock of the colorful flocked fabric is vivid, bright, stereoscopic and rich in colors, various property indexes are excellent, in particular, both rubbing fastness and flocking fastness are good, the antistatic property meets the national standard, and the production process is environment-friendly and energy-saving.
Description
Technical field
The present invention relates to a kind of colour pile material and preparation method thereof, belong to the technical field of weaving face fabric.
Background technology
Flocked fiber used is mostly fibers material at present, less with natural fiber as flocked material, environmental-protecting performance is poor, easily in manufacturing process and later stage use procedure, produce environmental pollution, and current flocked fabric batt color is single, be faint in color, cannot satisfy the demands of consumers.
Number of patent application is that the application for a patent for invention of 201310378355.X discloses a kind of alginate fibre electrostatic flocking fabric and preparation method thereof, its fabric providing has the features such as outstanding fire-retardant, environmental protection, natural antibacterial, far infrared, radiation proof, high strength, acid and alkali-resistance, long service life, but this application for a patent for invention can only obtain the tapetum of single color, style is too single, cannot meet consumer's visual demand.Therefore, Some Enterprises is by implanting in base fabric through simple mixing after fine hair is painted at present, although there is different colors, the color producing through this kind of method is disorderly and unsystematic, there is no stereovision, even more not attractive in appearance than the fabric of single color.
Based on this, the inventor, through unlimited test and textual criticism in many ways, has researched and developed a kind of colour pile material and preparation method thereof, and the present invention produces thus.
Summary of the invention
For solving the above-mentioned technical problem of prior art, the object of this invention is to provide a kind of colour pile material, the bright-colored light of colour pile material of the present invention, rich color, stereovision are strong.
Another object of the present invention is to provide a kind of preparation method of colour pile material, and this preparation method is simple to operate, easily control, and the bright-colored light of colour pile material, rich color, the stereovision that make are strong.
For achieving the above object, the present invention is achieved by the following technical solutions:
A colour pile material, comprises bottom cloth layer, and described bottom cloth layer is provided with tapetum, and described tapetum comprises background color tapetum and the painted tapetum being evenly mixed, and described painted tapetum and the difference in height of background color tapetum are 0.1mm-1.5mm.
As preferably, described painted tapetum and the difference in height of background color tapetum are 0.5mm-1.0mm.
For reaching better stereovision, the difference in height of painted tapetum of the present invention and background color tapetum is 0.7mm.
As preferably, the height of described painted tapetum is 0.7mm-2.5mm, and the height of described background color tapetum is 0.6mm-1.0mm.
A preparation method for colour pile material, comprises the following steps:
(1) fibre bundle is cut into fine hair, and a part for fine hair is carried out to painted processing;
(2) fine hair after painted processing in step (1) is mixed by weight percentage with the fine hair that did not carry out painted processing;
(3) fine hair mixing in step (2) is implanted to bottom cloth layer.
As preferably, for making colour pile material stereovision of the present invention outstanding, the preparation method of described colour pile material, comprises the following steps:
(1) fibre bundle is cut into the fine hair of 0.7mm-2.5mm, and a part for fine hair is carried out to painted processing;
(2) fine hair after painted processing in step (1) is mixed by weight percentage with the fine hair that did not carry out painted processing, the described villus length that did not carry out painted processing is cut into 0.6mm-1.0mm;
(3) fine hair mixing in step (2) is implanted to bottom cloth layer.
For reaching better preparation effect, the preparation method of colour pile material of the present invention, comprises the following steps:
(1) polyamide-fiber nylon fiber, modified dacron or mucilage materials tow being cut into length is 0.8-0.9mm, and fineness is the fine hair at 1.2 dawn, and a part for fine hair is carried out to painted white fine hair, green fine hair, red fine hair and/or the yellow fine hair of being processed into; (2), by step (1), carry out painted processing fine hair by weight percentage with the fine hair gummed that does not carry out painted processing, the described villus length that does not carry out painted processing is that 0.6mm-1.0mm, fineness were 3 dawn;
(3), in base fabric coated with adhesive, the thickness of described adhesive is 0.2-0.25mm;
(4) indoor at electrostatic spinning, adopt the flocking of high-voltage alternating generation of static electricity electric field, in high-voltage alternating electrostatic field by the fine hair in step (2) under the effect of electric field force and scribble the base fabric surface of adhesive in neat implantation step (3), and on high voltage electrode net and base fabric, the distance between the one side of oiling adhesive is 12-14.5cm;
(5) fabric step (4) being made, utilizes the anti-processing method of foaming type three to carry out three anti-processing.
Key point of the present invention is mixing and the mixed proportion thereof of painted fine hair, and for reaching bright-coloured light of the present invention, rich color, effect that stereovision is strong, the painted fine hair of different colours of the present invention mixes according to following ratio:
When base fabric color is black, the fine hair percentage by weight that carried out painted processing in described step (2) is as follows: the fine hair that does not carry out painted processing of white fine hair 5%-7%, green fine hair 1.5%-3.1%, red fine hair 0.6%-2.3%, yellow fine hair 0.5%-1.5% and surplus.
When base fabric color is purple, the fine hair percentage by weight that carried out painted processing in described step (2) is as follows: white fine hair 6%-8%, green fine hair 3%-4.5%, red fine hair 1.5%-2.3%, yellow fine hair 1.2%-2.6% and the fine hair that does not carry out painted processing.
When base fabric color is coffee color, the fine hair percentage by weight that carried out painted processing in described step (2) is as follows: white fine hair 8.5%-12%, green fine hair 2.1%-4.6%, red fine hair 1.4%-3.2%, yellow fine hair 0.3%-1.4% and the fine hair that does not carry out painted processing.
When base fabric color is rice white, the fine hair percentage by weight that carried out painted processing in described step (2) is as follows: white fine hair 6%-8.2%, green fine hair 2.4%-3.5%, red fine hair 1.3%-2.4%, yellow fine hair 1.1%-2.1% and the fine hair that does not carry out painted processing.
Beneficial effect of the present invention is as follows:
The preparation method of the colored fluff fabric of the present invention, the bright-coloured light of colored fine hair, the rich color making, has third dimension, and property indices is all excellent, especially fastness to rubbing and flocking fastness are all better, antistatic property meets national standard, and production technology environmental protection and energy saving, rare.
Accompanying drawing explanation
Fig. 1 is the structural representation of colored velvet fabric in the present invention;
Wherein, 1 is that bottom layer, 2 is that painted tapetum, 3 is background color tapetum;
Fig. 2 is the effect contrast figure of the product that makes of embodiment 1-3 and comparative example 1, comparative example 2.
The specific embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated, but protection scope of the present invention is not limited to this.
In the present invention, fine hair carries out forming painted tapetum after painted processing, and the fine hair that does not carry out painted processing forms background color tapetum.Raw material required for the present invention can make by disclosed mode in the specific embodiment of the invention, not disclosedly in the specific embodiment all can adopt commercially available prod or make by mode well known in the art.
embodiment 1
The preparation method of colour pile material of the present invention, comprises the following steps:
(1) polyamide-fiber nylon fibre bundle being cut into length is 1.5mm, and fineness is the polyamide-fiber nylon fine hair at 1.2 dawn, and polyamide-fiber nylon fine hair moisture content is 12%; Carry out conductive processing, and a part is wherein carried out to painted processing;
(2) redness, yellow, green and the white polyamide-fiber nylon fine hair that in step (1), carried out painted processing are mixed with the fine hair that did not carry out painted processing by different percentage by weights, the tapetum height that does not carry out painted processing is 0.8mm, and fineness was 3 dawn;
(3), in base fabric coated with adhesive, the thickness of adhesive is 0.2mm;
(4) indoor at electrostatic spinning, adopt the flocking of 450,000 volts of high-voltage alternating generation of static electricity electric fields, in high-voltage alternating electrostatic field by the fine hair in step (2) under the effect of electric field force and scribble the base fabric surface of adhesive in neat implantation step (3), and on high voltage electrode net and base fabric, the distance between the one side of oiling adhesive is 12cm;
(5) fabric step (4) being made, utilize foaming machine by the three-proof finishing agent processing of foaming, blowing agent is fluorocarbon polymer finishing agent, by the mode of blade coating, be coated onto fabric surface, then carry out drying and processing, the equipment speed of service is 10m/min, and bake out temperature is 130 ℃ of risings successively, and drying time is 4 minutes.
Painted processing in step (1) comprises the following steps:
A, dyestuff is added in dye vat, then add 3% glacial acetic acid, be warming up to after 100 ℃, be incubated 0.2 hour;
B, water in step a is discharged, with the water of putting into 40 ℃ after cold water washing;
C, in step b, add inorganic agent, constant temperature went out cylinder after 25 minutes, dewatered, dries, screens, mixes hair;
Inorganic agent in step c comprises following component: in 100 kilograms of fine hair, and the alum that percentage by weight is 3.5%, 0.8% tannin, 0.4% potash, 4% bright color-fixing agent, 0.4% softening agent, 0.8% aluminium colloidal sol, 1.2% magnesium sulfate, 1.6% carbon ammonium and 0.1% antistatic additive;
Adhesive in step (3) makes by the following method: in emulsifying kettle, by centrifugal pump, add 18kg acrylic acid, 60kg ethyl acrylate, 200kg butyl acrylate, 100kg methyl acrylate, 16kg N-hydroxypropyl, 20kg emulsifying agent and 566kg deionized water, by being steam heated to 20 ℃, carry out emulsion reaction, react after 0.8 hour, material is squeezed into head tank raw material for standby; Then by feeding intake, add ammonium persulfate, and drip deionized water and above-mentioned head tank raw material simultaneously, Steam Heating keeps reaction temperature at 65 ℃, and dropwise reaction, after 2.6 hours, is incubated 0.9 hour, material is cooled to 38 ℃ after completion of the reaction, and blowing is filling.
For making color of the trichomes more gorgeous, when base fabric color is black, the polyamide-fiber nylon fine hair percentage by weight that carried out painted processing in step (2) is as follows: the polyamide-fiber nylon fine hair that does not carry out painted processing of white polyamide-fiber nylon fine hair 5%, green polyamide-fiber nylon fine hair 1.5%, red polyamide-fiber nylon fine hair 0.6%, yellow polyamide-fiber nylon fine hair 0.5% and surplus.
For making color of the trichomes more gorgeous, when base fabric color is purple, the polyamide-fiber nylon fine hair percentage by weight that carried out painted processing in step (2) is as follows: the polyamide-fiber nylon fine hair that does not carry out painted processing of white polyamide-fiber nylon fine hair 6%, green polyamide-fiber nylon fine hair 3%, red polyamide-fiber nylon fine hair 1.5%, yellow polyamide-fiber nylon fine hair 1.2% and surplus.
For making color of the trichomes more gorgeous, when base fabric color is coffee color, the polyamide-fiber nylon fine hair percentage by weight that carried out painted processing in step (2) is as follows: the polyamide-fiber nylon fine hair that does not carry out painted processing of white polyamide-fiber nylon fine hair 8.5%, green polyamide-fiber nylon fine hair 2.1%, red polyamide-fiber nylon fine hair 1.4%, yellow polyamide-fiber nylon fine hair 0.3% and surplus.
For making color of the trichomes more gorgeous, when base fabric color is rice white, the polyamide-fiber nylon fine hair percentage by weight that carried out painted processing in step (2) is as follows: the polyamide-fiber nylon fine hair that does not carry out painted processing of white polyamide-fiber nylon fine hair 6%, green polyamide-fiber nylon fine hair 2.4%, red polyamide-fiber nylon fine hair 1.3%, yellow polyamide-fiber nylon fine hair 1.1% and surplus.
The colour pile material making in the present embodiment, comprise bottom cloth layer 1, bottom cloth layer 1 is provided with tapetum, tapetum comprises background color tapetum 2 and the painted tapetum 3 being evenly mixed, painted tapetum 3 is 0.7mm with the difference in height of background color tapetum 2, and wherein the height of painted tapetum 3 is 1.5mm, and the height of background color tapetum 2 is 0.8mm, stereovision is very strong, and bright-colored, rich color.
embodiment 2
The preparation method of colour pile material of the present invention, comprises the following steps:
(1) modified dacron tow being cut into length is 2.5mm, and fineness is the modified dacron fine hair at 1.2 dawn, and modified dacron fine hair moisture content is 15%; Carry out conductive processing, and wherein a part is carried out painted processing;
(2) redness, yellow, green and the white modified dacron fine hair that in step (1), carried out painted processing are mixed with the modified dacron fine hair that did not carry out painted processing by different percentage by weights, the height of naps that did not carry out painted processing is that 1.0mm, fineness were 3 dawn;
(3), in base fabric coated with adhesive, the thickness of adhesive is 0.25mm;
(4) indoor at electrostatic spinning, adopt the flocking of 500,000 volts of high-voltage alternating generation of static electricity electric fields, in high-voltage alternating electrostatic field by the fine hair in step (2) under the effect of electric field force and scribble the base fabric surface of adhesive in neat implantation step (3), and on high voltage electrode net and base fabric, the distance between the one side of oiling adhesive is 14.5cm;
(5) fabric step (4) being made, utilize foaming machine by the three-proof finishing agent processing of foaming, blowing agent is fluorocarbon polymer finishing agent, by the mode of blade coating, be coated onto fabric surface, then carry out drying and processing, the equipment speed of service is 10m/min, and bake out temperature is 150 ℃ of risings successively, and drying time is 5 minutes.
Painted processing in step (1) comprises the following steps:
A, dyestuff is added in dye vat, then add 4% glacial acetic acid, be warming up to after 100 ℃, be incubated 6 hours;
B, water in step a is discharged, with the water of putting into 65 ℃ after cold water washing;
C, in step b, add inorganic agent, constant temperature went out cylinder after 50 minutes, dewatered, dries, screens, mixes hair;
Inorganic agent in step c comprises following component: in 100 kilograms of fine hair, and the alum that percentage by weight is 8.5%, 2.32% tannin, 1.5% potash, 7% bright color-fixing agent, 1.5% softening agent, 2.4% aluminium colloidal sol, 3.6% magnesium sulfate, 3.8% carbon ammonium and 0.9% antistatic additive;
Adhesive in step (3) makes by the following method: in emulsifying kettle, by centrifugal pump, add 18kg acrylic acid, 60kg ethyl acrylate, 200kg butyl acrylate, 100kg methyl acrylate, 16kg N-hydroxypropyl, 20kg emulsifying agent and 566kg deionized water, by being steam heated to 45 ℃, carry out emulsion reaction, react after 1.2 hours, material is squeezed into head tank raw material for standby; Then by feeding intake, add ammonium persulfate, and drip deionized water and above-mentioned head tank raw material simultaneously, Steam Heating keeps reaction temperature at 75 ℃, and dropwise reaction, after 5.1 hours, is incubated 2.5 hours, material is cooled to 43 ℃ after completion of the reaction, and blowing is filling.
For making color of the trichomes more gorgeous, when base fabric color is black, the modified dacron fine hair percentage by weight that carried out painted processing in step (2) is as follows: the modified dacron fine hair that does not carry out painted processing of white modified dacron fine hair 7%, green modified dacron fine hair 3.1%, red modified dacron fine hair 2.3%, yellow modified dacron fine hair 1.5% and surplus.
For making color of the trichomes more gorgeous, when base fabric color is purple, the modified dacron fine hair percentage by weight that carried out painted processing in described step (2) is as follows: the modified dacron fine hair that does not carry out painted processing of white modified dacron fine hair 8%, green modified dacron fine hair 4.5%, red modified dacron fine hair 2.3%, yellow modified dacron fine hair 2.6% and surplus.
For making color of the trichomes more gorgeous, when base fabric color is coffee color, the modified dacron fine hair percentage by weight that carried out painted processing in described step (2) is as follows: the modified dacron fine hair that does not carry out painted processing of white modified dacron fine hair 12%, green modified dacron fine hair 4.6%, red modified dacron fine hair 3.2%, yellow modified dacron fine hair 1.4% and surplus.
For making color of the trichomes more gorgeous, when base fabric color is rice white, the modified dacron fine hair percentage by weight that carried out painted processing in described step (2) is as follows: the modified dacron fine hair that does not carry out painted processing of white modified dacron fine hair 8.2%, green modified dacron fine hair 3.5%, red modified dacron fine hair 2.4%, yellow modified dacron fine hair 2.1% and surplus.
The colour pile material making in the present embodiment, comprise bottom cloth layer 1, bottom cloth layer 1 is provided with tapetum, tapetum comprises background color tapetum 2 and the painted tapetum 3 being evenly mixed, painted tapetum 3 is 1.5mm with the difference in height of background color tapetum 2, and wherein the height of painted tapetum 3 is 2.5mm, and the height of background color tapetum 2 is 1.0mm, stereovision is very strong, and bright-colored, rich color.
embodiment 3
The preparation method of colour pile material of the present invention, comprises the following steps:
(1) mucilage materials tow being cut into length is 0.7mm, and fineness is the mucilage materials fine hair at 1.2 dawn, and mucilage materials fine hair moisture content is 13.5%, carries out conductive processing, and a part is wherein carried out to painted processing;
(2) redness, yellow, green and the white mucilage materials fine hair that in step (1), carried out painted processing are mixed with the mucilage materials fine hair that does not carry out painted processing by weight percentage, the mucilage materials height of naps that does not carry out painted processing is that 0.6mm, fineness were 3 dawn;
(3), in base fabric coated with adhesive, the thickness of adhesive is 0.225mm;
(4) indoor at electrostatic spinning, adopt the flocking of 47.5 ten thousand volts of high-voltage alternating generation of static electricity electric fields, in high-voltage alternating electrostatic field by the fine hair in step (2) under the effect of electric field force and scribble the base fabric surface of adhesive in neat implantation step (3), and on high voltage electrode net and base fabric, the distance between the one side of oiling adhesive is 13.25cm;
(5) fabric step (4) being made, utilize foaming machine by the three-proof finishing agent processing of foaming, blowing agent is fluorocarbon polymer finishing agent, by the mode of blade coating, be coated onto fabric surface, then carry out drying and processing, the equipment speed of service is 10m/min, and bake out temperature is 140 ℃ of risings successively, and drying time is 4.5 minutes.
Painted processing in described step (1) comprises the following steps:
A, dyestuff is added in dye vat, then add 3.5% glacial acetic acid, be warming up to after 100 ℃, be incubated 3.1 hours;
B, water in step a is discharged, with the water of putting into 52.5 ℃ after cold water washing;
C, in step b, add inorganic agent, constant temperature went out cylinder after 37.5 minutes, dewatered, dries, screens, mixes hair;
Inorganic agent in step c comprises following component: in 100 kilograms of fine hair, and the alum that percentage by weight is 6%, 1.56% tannin, 0.95% potash, 5.5% bright color-fixing agent, 0.95% softening agent, 1.6% aluminium colloidal sol, 2.4% magnesium sulfate, 2.7% carbon ammonium and 0.5% antistatic additive;
Adhesive in step (3) makes by the following method: in emulsifying kettle, by centrifugal pump, add 18kg acrylic acid, 60kg ethyl acrylate, 200kg butyl acrylate, 100kg methyl acrylate, 16kg N-hydroxypropyl, 20kg emulsifying agent and 566kg deionized water, by being steam heated to 32.5 ℃, carry out emulsion reaction, react after 1.0 hours, material is squeezed into head tank raw material for standby; Then by feeding intake, add ammonium persulfate, and drip deionized water and above-mentioned head tank raw material simultaneously, Steam Heating keeps reaction temperature at 70 ℃, and dropwise reaction, after 3.85 hours, is incubated 1.7 hours, material is cooled to 40.5 ℃ after completion of the reaction, and blowing is filling.
For making color of the trichomes more gorgeous, when base fabric color is black, the mucilage materials fine hair percentage by weight that carried out painted processing in described step (2) is as follows: the mucilage materials fine hair that does not carry out painted processing of white mucilage materials fine hair 6%, green mucilage materials fine hair 2.3%, red mucilage materials fine hair 1.45%, yellow mucilage materials fine hair 1.0% and surplus.
For making color of the trichomes more gorgeous, when base fabric color is purple, the mucilage materials fine hair percentage by weight that carried out painted processing in described step (2) is as follows: the mucilage materials fine hair that does not carry out painted processing of white mucilage materials fine hair 7%, green mucilage materials fine hair 3.75%, red mucilage materials fine hair 1.9%, yellow mucilage materials fine hair 1.9% and surplus.
For making color of the trichomes more gorgeous, when base fabric color is coffee color, the mucilage materials fine hair percentage by weight that carried out painted processing in described step (2) is as follows: the mucilage materials fine hair that does not carry out painted processing of white mucilage materials fine hair 10.25%, green mucilage materials fine hair 3.35%, red mucilage materials fine hair 2.3%, yellow mucilage materials fine hair 0.85% and surplus.
For making color of the trichomes more gorgeous, when base fabric color is rice white, the mucilage materials fine hair percentage by weight that carried out painted processing in described step (2) is as follows: the mucilage materials fine hair that does not carry out painted processing of white mucilage materials fine hair 7.1%, green mucilage materials fine hair 2.95%, red mucilage materials fine hair 1.85%, yellow mucilage materials fine hair 1.6% and surplus.
The colour pile material making in the present embodiment, comprise bottom cloth layer 1, bottom cloth layer 1 is provided with tapetum, tapetum comprises background color tapetum 2 and the painted tapetum 3 being evenly mixed, painted tapetum 3 is 0.1mm with the difference in height of background color tapetum 2, and wherein the height of painted tapetum 3 is 0.7mm, and the height of background color tapetum 2 is 0.6mm, stereovision is very strong, and bright-colored, rich color.
performance test
Get respectively the colour pile material that embodiment 1,2 and 3 makes and test, by AATCC16 test color fastness to light, press AATCC165 and test fastness to rubbing, test according to GB/21196.1
Flocking fastness;
Change in size and appearance after laundering: get three samples with entering test, by GB/8628, GB/T8629, GB/T8630 standard, carry out, select 5A program, total charging 2Kg, drying means F, baking temperature is no more than 40 ℃, average, and estimate the stereovision of painted tapetum and background color tapetum.Test result sees the following form 1.
Table 1
comparative example 1
The disclosed method of application for a patent for invention that is 201310378355.X by application number makes fabric.
comparative example 2
The fine hair that carried out painted processing is mixed in rear implantation base fabric by simple, make colored fluff fabric.
The fabric that the colored fluff fabric that embodiment 1,2,3 is made and comparative example 1 and comparative example 2 make carries out the contrast of outward appearance, and comparing result is shown in Fig. 2.
As can be seen from Table 1; the colour pile material property indices that the present invention makes is all excellent; especially fastness to rubbing and flocking fastness are all better; the key technical indexes reaches I class and II class index request in the environmental protection industry standard HJ/T 307-2006 of the People's Republic of China (PRC), and antistatic property meets national standard.
As can be seen from Figure 2 the fabric color, making in comparative example 1 is single, attractive in appearance not; Although the fabric making in comparative example 2 has overcome the single defect of color, color is disorderly and unsystematic, there is no stereovision; The bright-coloured light of colored fluff fabric making in embodiment of the present invention 1-3, rich color, by the control to the mixed proportion of painted fine hair and background color fine hair, control to the difference in height of painted tapetum and background color tapetum, there is very strong third dimension, and production technology environmental protection and energy saving, rare.
Above-described embodiment is only for the inventive concept of the present invention of explaining, but not restriction to rights protection of the present invention, allly utilizes this design to carry out the change of unsubstantiality to the present invention, all should fall into protection scope of the present invention.
Claims (11)
1. a colour pile material, it is characterized in that: comprise bottom cloth layer, described bottom cloth layer is provided with tapetum, and described tapetum comprises background color tapetum and the painted tapetum being evenly mixed, and described painted tapetum and the difference in height of background color tapetum are 0.1mm-1.5mm.
2. colour pile material as claimed in claim 1, is characterized in that: described painted tapetum and the difference in height of background color tapetum are 0.5mm-1.0mm.
3. colour pile material as claimed in claim 2, is characterized in that: described painted tapetum and the difference in height of background color tapetum are 0.7mm.
4. colour pile material as claimed in claim 1, is characterized in that: the height of described painted tapetum is 0.7mm-2.5mm, and the height of described background color tapetum is 0.6mm-1.0mm.
5. a preparation method for colour pile material, is characterized in that comprising the following steps:
(1) fibre bundle is cut into fine hair, and a part for fine hair is carried out to painted processing;
(2) fine hair after painted processing in step (1) is mixed by weight percentage with the fine hair that did not carry out painted processing;
(3) fine hair mixing in step (2) is implanted to bottom cloth layer.
6. the preparation method of colour pile material as claimed in claim 5, is characterized in that comprising the following steps:
(1) fibre bundle is cut into the fine hair of 0.7mm-2.5mm, and a part for fine hair is carried out to painted processing;
(2) fine hair after painted processing in step (1) is mixed by weight percentage with the fine hair that did not carry out painted processing, the described villus length that did not carry out painted processing is cut into 0.6mm-1.0mm;
(3) fine hair mixing in step (2) is implanted to bottom cloth layer.
7. the preparation method of colour pile material as claimed in claim 6, is characterized in that comprising the following steps:
(1) polyamide-fiber nylon fiber, modified dacron or mucilage materials tow being cut into length is that 0.8-0.9mm, fineness are the fine hair at 1.2 dawn, and a part for fine hair is carried out to painted white fine hair, green fine hair, red fine hair and/or the yellow fine hair of being processed into; (2), by the fine hair after painted processing in step (1) by weight percentage with the fine hair gummed that does not carry out painted processing, the described villus length that does not carry out painted processing is cut into 0.6mm-1.0mm, fineness was 3 dawn;
(3), in base fabric coated with adhesive, the thickness of described adhesive is 0.2-0.25mm;
(4) indoor at electrostatic spinning, adopt the flocking of high-voltage alternating generation of static electricity electric field, in high-voltage alternating electrostatic field by the fine hair in step (2) under the effect of electric field force and scribble the base fabric surface of adhesive in neat implantation step (3), and on high voltage electrode net and base fabric, the distance between the one side of oiling adhesive is 12-14.5cm;
(5) fabric step (4) being made, utilizes the anti-processing method of foaming type three to carry out three anti-processing.
8. the preparation method of colour pile material as claimed in claim 7, it is characterized in that: when base fabric color is black, the fine hair percentage by weight that carried out painted processing in described step (2) is as follows: the fine hair that does not carry out painted processing of white fine hair 5%-7%, green fine hair 1.5%-3.1%, red fine hair 0.6%-2.3%, yellow fine hair 0.5%-1.5% and surplus.
9. the preparation method of colour pile material as claimed in claim 7, it is characterized in that: when base fabric color is purple, the fine hair percentage by weight that carried out painted processing in described step (2) is as follows: white fine hair 6%-8%, green fine hair 3%-4.5%, red fine hair 1.5%-2.3%, yellow fine hair 1.2%-2.6% and the fine hair that does not carry out painted processing.
10. the preparation method of colour pile material as claimed in claim 7, it is characterized in that: when base fabric color is coffee-like, the fine hair percentage by weight that carried out painted processing in described step (2) is as follows: white fine hair 8.5%-12%, green fine hair 2.1%-4.6%, red fine hair 1.4%-3.2%, yellow fine hair 0.3%-1.4% and the fine hair that does not carry out painted processing.
11. preparation methods of colour pile material as claimed in claim 7, it is characterized in that: when base fabric color is rice white, the fine hair percentage by weight that carried out painted processing in described step (2) is as follows: white fine hair 6%-8.2%, green fine hair 2.4%-3.5%, red fine hair 1.3%-2.4%, yellow fine hair 1.1%-2.1% and the fine hair that does not carry out painted processing.