CN103643563A - Dyeing and finishing process for protein fiber-containing blended knitted fabric - Google Patents
Dyeing and finishing process for protein fiber-containing blended knitted fabric Download PDFInfo
- Publication number
- CN103643563A CN103643563A CN201310623079.9A CN201310623079A CN103643563A CN 103643563 A CN103643563 A CN 103643563A CN 201310623079 A CN201310623079 A CN 201310623079A CN 103643563 A CN103643563 A CN 103643563A
- Authority
- CN
- China
- Prior art keywords
- minutes
- dyeing
- add
- heated
- discharge water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a dyeing and finishing process for a protein fiber-containing blended knitted fabric. The dyeing and finishing process comprises the following steps: (1) putting silk cotton into a refining solution prepared by mixing sodium diethylhexyl sulfosuccinate and sodium carbonate in the ratio of 1:1 for refining, heating at the speed of 5 DEG C per minute to 95 DEG C, preserving heat for 30 minutes, and draining water; (2) adding hot water of 70 DEG C, adding 1.5-2 g/L alkyl polyglycol ether and 2-3 g/L sodium hexametaphosphate, heating at the speed of 5 DEG C per minute to 95 DEG C, preserving heat for 25 minutes, and draining water; (3) adding 1 g/mL glacial acetic acid, heating to 60 DEG C, preserving heat for 25 minutes, and draining water; (4) dyeing; (5) adding 1.5 g/L glacial acetic acid and performing acid washing; (6) adding 1-2 g/L cocoalkyl diethanol amide, heating to 85 DEG C, preserving heat for 35 minutes, and draining water; and (7) adding 4 g/L silicic acid softening agent, raising the temperature to 60 DEG C, preserving heat for 45 minutes, discharging and sizing. The dyeing and finishing process has the advantages of consistent dye-uptake rate, high flatness, freeness from the phenomenon of dyeing defect and capability of ensuring the color fastness.
Description
Technical field
The present invention relates to the dyeing and finishing technology containing azelon blended fabric.
Background technology
Real silk is a kind of protein fibre, and it has kept trophism and the naturality of silk fabrics.At present, common dyeing, dyeing rate is different, easily produces look flower and spends grey effect.
Summary of the invention
The object of the present invention is to provide a kind of dyeing and finishing technology containing azelon blended fabric, dyeing dye-uptake is consistent, and flatness is good, does not spend ash and look flower phenomenon, can guarantee COLOR FASTNESS.
For achieving the above object, technical scheme of the present invention is a kind of dyeing and finishing technology containing azelon blended fabric of design, comprises the steps:
1) silk-cotton is put into the refining solution refining being mixed by 1:1 by iodate butanedioic acid dibutyl ester sodium salt and soda ash, with 5 ℃/min, be heated to 95 ℃ of constant temperature 30 minutes, discharge water;
2) add the hot water of 70 ℃, then add the alkyl polyoxyethylene ether of 1.5-2g/L and the calgon of 2-3g/L, with 5 ℃/min, be heated to 95 ℃ of constant temperature 25 minutes, discharge water;
3) add the glacial acetic acid of 1g/ml, be heated to 60 ℃ of constant temperature 25 minutes, discharge water;
4) dyeing: add successively the sulfonated castor oil of water, 2g/L, move 8 minutes, 50min linearity adds dyestuff, is heated to 40 ℃ with 5 ℃/min, 50min linearity adds sodium sulphate, level dyeing 20 minutes, and 50min linearity adds soda ash, with 5 ℃/min, be warming up to 85 ℃, be incubated 15 minutes, discharge water;
5) add the glacial acetic acid of 1.5g/L to carry out pickling;
6) add the coconut oil alkyl diethanolamide of 1-2g/L, be heated to 85 ℃ of insulations 35 minutes, discharge water;
7) add the silicic acid softener of 4g/L, be warming up to 60 ℃ of constant temperature 45 minutes, go out cylinder sizing.
Advantage of the present invention and beneficial effect are: a kind of dyeing and finishing technology containing azelon blended fabric is provided, and dyeing dye-uptake is consistent, and flatness is good, do not spend ash and look flower phenomenon, can guarantee COLOR FASTNESS.
The specific embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples are only for technical scheme of the present invention is more clearly described, and can not limit the scope of the invention with this.
The concrete technical scheme of implementing of the present invention is:
Embodiment 1
A dyeing and finishing technology containing azelon blended fabric, comprises the steps:
1) silk-cotton is put into the refining solution refining being mixed by 1:1 by iodate butanedioic acid dibutyl ester sodium salt and soda ash, with 5 ℃/min, be heated to 95 ℃ of constant temperature 30 minutes, discharge water;
2) add the hot water of 70 ℃, then add the alkyl polyoxyethylene ether of 1.5g/L and the calgon of 2g/L, with 5 ℃/min, be heated to 95 ℃ of constant temperature 25 minutes, discharge water;
3) add the glacial acetic acid of 1g/ml, be heated to 60 ℃ of constant temperature 25 minutes, discharge water;
4) dyeing: add successively the sulfonated castor oil of water, 2g/L, move 8 minutes, 50min linearity adds dyestuff, is heated to 40 ℃ with 5 ℃/min, 50min linearity adds sodium sulphate, level dyeing 20 minutes, and 50min linearity adds soda ash, with 5 ℃/min, be warming up to 85 ℃, be incubated 15 minutes, discharge water;
5) add the glacial acetic acid of 1.5g/L to carry out pickling;
6) add the coconut oil alkyl diethanolamide of 1g/L, be heated to 85 ℃ of insulations 35 minutes, discharge water;
7) add the silicic acid softener of 4g/L, be warming up to 60 ℃ of constant temperature 45 minutes, go out cylinder sizing.
Embodiment 2
A dyeing and finishing technology containing azelon blended fabric, comprises the steps:
1) silk-cotton is put into the refining solution refining being mixed by 1:1 by iodate butanedioic acid dibutyl ester sodium salt and soda ash, with 5 ℃/min, be heated to 95 ℃ of constant temperature 30 minutes, discharge water;
2) add the hot water of 70 ℃, then add the alkyl polyoxyethylene ether of 2g/L and the calgon of 3g/L, with 5 ℃/min, be heated to 95 ℃ of constant temperature 25 minutes, discharge water;
3) add the glacial acetic acid of 1g/ml, be heated to 60 ℃ of constant temperature 25 minutes, discharge water;
4) dyeing: add successively the sulfonated castor oil of water, 2g/L, move 8 minutes, 50min linearity adds dyestuff, is heated to 40 ℃ with 5 ℃/min, 50min linearity adds sodium sulphate, level dyeing 20 minutes, and 50min linearity adds soda ash, with 5 ℃/min, be warming up to 85 ℃, be incubated 15 minutes, discharge water;
5) add the glacial acetic acid of 1.5g/L to carry out pickling;
6) add the coconut oil alkyl diethanolamide of 2g/L, be heated to 85 ℃ of insulations 35 minutes, discharge water;
7) add the silicic acid softener of 4g/L, be warming up to 60 ℃ of constant temperature 45 minutes, go out cylinder sizing.
Embodiment 3
A dyeing and finishing technology containing azelon blended fabric, comprises the steps:
1) silk-cotton is put into the refining solution refining being mixed by 1:1 by iodate butanedioic acid dibutyl ester sodium salt and soda ash, with 5 ℃/min, be heated to 95 ℃ of constant temperature 30 minutes, discharge water;
2) add the hot water of 70 ℃, then add the alkyl polyoxyethylene ether of 1.8g/L and the calgon of 2.3g/L, with 5 ℃/min, be heated to 95 ℃ of constant temperature 25 minutes, discharge water;
3) add the glacial acetic acid of 1g/ml, be heated to 60 ℃ of constant temperature 25 minutes, discharge water;
4) dyeing: add successively the sulfonated castor oil of water, 2g/L, move 8 minutes, 50min linearity adds dyestuff, is heated to 40 ℃ with 5 ℃/min, 50min linearity adds sodium sulphate, level dyeing 20 minutes, and 50min linearity adds soda ash, with 5 ℃/min, be warming up to 85 ℃, be incubated 15 minutes, discharge water;
5) add the glacial acetic acid of 1.5g/L to carry out pickling;
6) add the coconut oil alkyl diethanolamide of 1.2g/L, be heated to 85 ℃ of insulations 35 minutes, discharge water;
7) add the silicic acid softener of 4g/L, be warming up to 60 ℃ of constant temperature 45 minutes, go out cylinder sizing.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. containing the dyeing and finishing technology of azelon blended fabric, it is characterized in that, comprise the steps:
1) silk-cotton is put into the refining solution refining being mixed by 1:1 by iodate butanedioic acid dibutyl ester sodium salt and soda ash, with 5 ℃/min, be heated to 95 ℃ of constant temperature 30 minutes, discharge water;
2) add the hot water of 70 ℃, then add the alkyl polyoxyethylene ether of 1.5-2g/L and the calgon of 2-3g/L, with 5 ℃/min, be heated to 95 ℃ of constant temperature 25 minutes, discharge water;
3) add the glacial acetic acid of 1g/ml, be heated to 60 ℃ of constant temperature 25 minutes, discharge water;
4) dyeing: add successively the sulfonated castor oil of water, 2g/L, move 8 minutes, 50min linearity adds dyestuff, is heated to 40 ℃ with 5 ℃/min, 50min linearity adds sodium sulphate, level dyeing 20 minutes, and 50min linearity adds soda ash, with 5 ℃/min, be warming up to 85 ℃, be incubated 15 minutes, discharge water;
5) add the glacial acetic acid of 1.5g/L to carry out pickling;
6) add the coconut oil alkyl diethanolamide of 1-2g/L, be heated to 85 ℃ of insulations 35 minutes, discharge water;
7) add the silicic acid softener of 4g/L, be warming up to 60 ℃ of constant temperature 45 minutes, go out cylinder sizing.